• The Journal of Korean Academy of Prosthodontics
• /
• v.31 no.3
• /
• pp.317-349
• /
• 1993

This study investigated the effect of filler particle size and weight% on mechanical properties of dental core porcelain. In alumina, variation in particle size and weight% and in zirconia, variation in weight%, all specimens were tested three-point bending strength, transmittance, thermal expansion coefficient, porosity and shrinkage and observed with SEM and analysed with X-ray diffractometer. In order to develop shrink-free porcelain, after firing alumina only, glass wasinfiltrated. And aluminum was added to alumina with the expanding character of aluminum oxidize into alumina, and was followed by second firing of glass infiltration procedure. Then mechanical properties were observed. The results of this study were obtained as follows. 1. The bending strength of zirconia was higher than that of alumina, and $5{\mu}m$ alumina had highest strength in variation of particle size of alumina. Except for $5{\mu}m$ alumina, increased with weight%, bending strength increased up to 80% and decreased at 90%. In case of glass infiltration, bending strength was slight higher than 80% and 90% of $5{\mu}m$ alumina. 2. Transmittance increased with increase of shrinkage, decrease of porosity, and with increase of filler size and had no direct correlation with weight%. 3. Thermal expansion coefficient of alumina group was $7.42\sim8.64\times10^{-6}/^{\circ}C$ and that of zirconia group was $9.83\sim12.11\times10^{-6}/^{\circ}C$ and the latter was higher than the former. 4. In x-ray diffraction analysis, alumina group and zirconia group increased $Al_2O_3$ peak and $t-ZrO_2$ peak with increase of weight%. The second phase(cristobalite peak) was observed in zirconia 40% group. 5. Porosity of zirconia was lower than that of alumina and $5{\mu}m$ alumina group had many pores with SEM. In case of low filler content, fracture occurred in glass and high filler content, in glass and filler. In case of aluminum addition to alumina, small oxidised aluminum was observed. 6. Zirconia group had high shrinkage than alumina group, and mixed group of alumina group had high shrinkage. In case of glass infiltration, shrinkage decreased and aluminum addition to alumina group was almost shrink-free.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2001.05a
• /
• pp.180-183
• /
• 2001

Glass fiber reinforced plastic(CFHP) tent pole fabricated by the pultrusion process with unidirectional glass fiber is two times as heavy as aluminum tent pole owing to the low specific modulus The first objective of this research is the design the high strength and light weight tent pole compete with. the second is the develope glass fiber carbon fiber hybrid tent pole pultrusion process. the third is the evaluate the mechanical properties of the hybrid tent pole compare to these of the duralumin tent pole.

• Computers and Concrete
• /
• v.17 no.4
• /
• pp.553-566
• /
• 2016

Fracture energy is one of the key parameters reveal cracking resistance and fracture toughness of concrete. The main purpose of this study is to determine fracture behavior, mechanical properties and microstructural analysis of high strength basalt fiber reinforced concrete (HSFRC). For this purpose, three-point bending tests were performed on notched beams produced using HSFRCs with 12 mm and 24mm fiber length and 1, 2 and $3kg/m^3$ fiber content in order to determine the value of fracture energy. Fracture energies of the notched beam specimens were calculated by analyzing load versus crack mouth opining displacement curves by the help of RILEM proposal. The results show that the effects of basalt fiber content and fiber length on fracture energy are very significant. The splitting tensile and flexural strength of HSFRC increased with increasing fiber content whereas a slight drop in flexural strength was observed for the mixture with 24mm fiber length and $3kg/m^3$ fiber content. On the other hand, there was no significant effect of fiber addition on the compressive strength and modulus of elasticity of the mixtures. In addition, microstructural analysis of the three components; cement paste, aggregate and basalt fiber were performed based on the Scanning Electron Microscopy and Energy-Dispersive X-ray Spectroscopy examinations.

• Journal of the Korean Ceramic Society
• /
• v.38 no.12
• /
• pp.1123-1131
• /
• 2001

The sintering behaviors of the renewed $Al_2$O$_3$ceramics were investigated as functions of the addition amount and particle size of recycling $Al_2$O$_3$powder, such as crushed powder of structural $Al_2$O$_3$ceramics and waste $Al_2$O$_3$adsorbent, were investigated. Pure $Al_2$O$_3$sample was fabricated by sintered at 1,$650^{\circ}C$ for 5h and it was crushed into powder (-40${\mu}{\textrm}{m}$and +40${\mu}{\textrm}{m}$ in particle size) by thermal shock treatment and crushing. Then, 10~50wt% of crushed $Al_2$O$_3$powder and waste $Al_2$O$_3$adsorbent were mixed with pure $Al_2$O$_3$powder and were subjected to re-sintering to renewed $Al_2$O$_3$sample. The density and the 3-point bending strength increased with increasing the sintering temperature without regard to the addition amount and particle size of recycling $Al_2$O$_3$powder, and that of the samples at the same sintering temperature decreased with increasing the addition amount and particle size of recycling $Al_2$O$_3$powder. Samples over 200 Mpa of 3-point bending strength were obtained by mixing ~30wt% of crushed $Al_2$O$_3$powder(-40${\mu}{\textrm}{m}$), ~20wt% of crushed $Al_2$O$_3$powder (+40${\mu}{\textrm}{m}$) and 10wt% of waste $Al_2$O$_3$adsorbent. 5~20wt% of waste glass powder containing renewed $Al_2$O$_3$samples for densification were fabricated by sintered at 1200~1$650^{\circ}C$ for 5h. The temperature of maximum density and 3-point bending strength decreased with increasing the addition amount of waste glass powder, however, these samples at above 140$0^{\circ}C$ showed lower density and bending strength than renewed $Al_2$O$_3$samples. The addition of waste glass powder did not improved the densification of renewed $Al_2$O$_3$sample.

• The Journal of the Korean dental association
• /
• v.53 no.9
• /
• pp.644-655
• /
• 2015

Purpose: This study was conducted to evaluate the effect of the fixture abutment connection type and diameter on the screw joint stability in external butt joint for 2nd surgery and internal cone connected type implant system for 1st and 2nd surgery using ultimate fracture strength. Materials and Methods: USII system, SSII system and GSII system of Osstem Implant were used. Each system used the fixture with two different diameters and cement-retained abutments, and tungsten carbide / carbon coated abutment screws were used. Disc shaped stainless steel metal tube was attached using resin-based temporary cement. The experimental group was divided into seven subgroups, including the platform switching shaped specimen that uses a regular abutment in the fixture with a wide diameter in USII system. A static load was increased to the metal tube at 5mm deviated point from the implant central axis until it reached the compression bending strength at a rate of 1mm/min. Then the deformations and patterns of fracture in threaded connection were compared. Results and Conclusion: 1. In the comparison between the Regular diameter, compression bending strength of SSII system was higher than USII system and GSII system. There was no significant difference between USII system and GSII system. 2. In the comparison between wide diameter, compression bending strength was increased in the order of GSII system, USII system, and SSII system. 3. In comparison between the implant diameter, compression bending strength of the wide diameter was greater than the regular diameter in any system(P<0.05). 4. There was no significant difference between the platform switching (III group) and the regular diameter (I group) in USII system. 5. In USII system, fracture of abutment screw and deformation of both fixture and abutment were observed in I, II and III subgroups. 6. Failure pattern of SSII system, which was the fracture of abutment screw and deformation of the abutment and fixture, was observed in both IV and V subgroups. Fracture of some fixtures was observed in subgroup V. 7. Failure pattern of GSII system, which was the fracture of the abutment screw and deformation of the fixture and the abutment, was observed in both VI and VII subgroups. Apart from other subgroups, subgroup VII demonstrated no bending neither the fracture at the top of the fixture. The compressive deformation of internal slope in the fixture was the only thing observed in subgroup VII.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.32 no.3
• /
• pp.169-175
• /
• 2016

Purpose: Direct splinting material should have high flexural strength to withstand force during mastication and low modulus of elasticity to provide some movement while force applied for relief of stress. The purpose of this study was to compare flexural strength and modulus of elasticity of several resinous splinting materials. Materials and Methods: Four materials; Super-Bond C&B, G-FIX, G-aenial Universal Flo, FiltekTM Z350 XT; were used in this study. Fifteen rectangular bar specimens of each material were prepared. Three-point bending test were performed to determine physical properties. Maximum load at fracture was recorded and flexural strength and modulus of elasticity were calculated. One-way analysis of variance (ANOVA) and Scheffe's tests at a 0.05 level of significance were conducted on all test results. Results: Statistical analysis reveals that Super-Bond C&B had significant low mean value for flexible strength and the other three materials showed no significant difference. For modulus of elasticity, Super-Bond C&B exhibited statistically lower modulus of elasticity. G-FIX presented intermediate result, showing statistically higher modulus of elasticity than Super-Bond C&B but lower than G-aenial Universal Flo and FiltekTM Z350 XT. There was no significant difference on modulus of elasticity between G-aenial Universal Flo and FiltekTM Z350 XT. Conclusion: Using a G-FIX, the newly commercially available splinting material, which shows higher fracture resistance properties comparable to flowable and restorative composite resin and a relatively flexible nature might be a beneficial for stabilizing teeth mobility.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2001.05a
• /
• pp.34-37
• /
• 2001

This study developed Fiber/Particle Hybrid MMCs and analyzed their mechanical properties. Using $\textrm{Al}_2\textrm{O}_3f$ and $\textrm{Al}_2\textrm{O}_3p$ with the fiber to particle ratio of 1:1, 1:3, 1:5 hybrid preform and MMCs are fabricated. For the analysis of the mechanical properties, three point bending tests were preformed for the preform and tensile test for the MMCs. The experimental results show that the hybrid MMCs can be successfully fabricated using the equipment of fiber preform fabrication system and squeeze casting method. And as the amount of particle in hybrid MMCs increases, the tensile strength, elastic modulus and the volume fraction of reinforcement increases.

• Journal of the Korean Ceramic Society
• /
• v.30 no.4
• /
• pp.265-272
• /
• 1993

Effect of mixing homogeneity in powder mixtures of Si3N4 and sintering additive (10mol% YAG) prepared by coprecipitation on the mechanical properties of pressureless-sintered body was investigated. Sintering was performed in a graphtie furnace at 1850℃ for 0.5h under 0.15MPa N2 atmosphere using Si3N4 powder bed. Results from the measurement of Young's modulus, Vickers hardness, 4-point-bending strength, and KIC for the coprecipitation-treated (CP) and the mechanically-mixed specimens(MM) showed that a remarkable improvement in flexural strength and Weibull parameter can be achieved for the CPspecimens: (677±68MPa, 12.0) for CP samples and (539±108MPa, 5.5) for MM. Other properties were almost same irrespective of preparation methods.

• Journal of Power System Engineering
• /
• v.2 no.3
• /
• pp.41-48
• /
• 1998

This study was aimed at development of fabrication process of functionally graded materials(FGM), consisting of metal and ceramic by thermal spraying method. NiCrAIY/$Al_2O_3$ FGM were made by using plasma spraying onto the SS400 carbon steel substrate. And mechanical properties such as microhardness, thermal shock resistance and adhesive strength of the coating layer were investigated. Adhesive strength was evaluated by acoustic emission method. It was resulted that NiCrAIY/$Al_2O_3$ FGM made by thermal spraying method showed excellent thermal shock resistance and adhesive strength compared to the other lamellar structures of sprayed coatings and that AE is useful tool to evaluate the defect of thermal sprayed coating layer.

• Journal of Power System Engineering
• /
• v.15 no.6
• /
• pp.67-72
• /
• 2011

In the present study, crack healing effect and residual stress of $Al_2O_3$ ceramics were investigated by changing the sintering temperature and heat treatment conditions. And also it was investigated that the influence of different filler loadings of nano-sized SiC particles on the crack healing behavior of $Al_2O_3$ ceramics. The test samples were characterized by three point bend flexural tests to evaluate their mechanical properties. The morphological changes were studied by FE-SEM and EDS. The test results indicated that the $Al_2O_3$ with nano-sized SiC ceramics sintered at $1800^{\circ}C$ were showed highest density. Sintering temperature at $1800^{\circ}C$, the bending strength of heat treatment in air atmosphere specimens showed about 42 % increment in comparison to the un-heat treated specimens. The cracked specimens can be healed by heat treatment in vacuum atmosphere but the crack healing effect of $Al_2O_3$ ceramics, which is heat treated in air atmosphere was higher than that of heat treated in vacuum atmosphere. $Al_2O_3$ with 30 wt% of SiC ceramics indicated higher crack healing ability than that with 15 wt% of SiC ceramics. The FE-SEM images showed that the median cracks and pores were disappeared after heat treatment in air.