• Polymer(Korea)
• /
• v.25 no.3
• /
• pp.435-440
• /
• 2001

The objective of this study was to examine the effect of oxidation inhibitor contents on the work of adhesion, fracture toughness, and impact strength of the unidirectional carbon-carbon composites (C/C composites). The molybdenum disilicide ($MoSi_2$) used as an oxidation inhibitor was impregnated with phenolic resins to improve the anti-oxidation properties of the composites in different concentrations of 4, 12 and 20 wt%. Based on Wilhelmy equation, the work of adhesion of C/C composites was calculated by contact angle methods. Fracture toughness and impact strength were pressured by three-point bending test for the critical intensity factor ($K_IC$) and Izod test method, respectively. As a result, the composites made with $MoSi_2$ resulted in an increasing of both fracture toughness and impact strength. Especially, the composites made with 12 wt% $MoSi_2$ content showed the highest value of London dispersive component, $W_A\;^L$, in work of adhesion, resulting from improving the interfacial adhesion force among fibers, filler, and matrix in this system.

• Composites Research
• /
• v.32 no.3
• /
• pp.148-157
• /
• 2019

In this study, $C_f/SiC$, $SiC_f/SiC$ and $C_f-SiC_f/SiC$ ceramic composites reinforcing carbon fiber, SiC fiber and hybrid fiber were fabricated by hybrid TGCVI and PIP process. After the thermal shock cycle, 3-point bending and Oxy-Acetylene torch test, their mechanical behavior, oxidation and erosion resistance were evaluated. The $C_f/SiC$ composite showed a decrease in mechanical property along with increasing temperature, a pseudo-ductile fracture mode and a large quantity of erosion. The $SiC_f/SiC$ composite exhibited stronger mechanical property and lower erosion rate compared to the $C_f/SiC$, but brittle fracture mode. On the other hand, hybrid type of $C_f-SiC_f/SiC$ composite gave the best mechanical property, more ductile failure mode than the $SiC_f/SiC$, and lower erosion rate than the $C_f/SiC$. During the Oxy-Acetylene torch test, the $SiO_2$ formed by reaction of the SiC matrix with oxygen prevented further oxidation or erosion of the fibers for $C_f-SiC_f/SiC$ and $SiC_f/SiC$ composites particularly. In conclusion, if a hybrid composite with low porosity is prepared, this material is expected to have high applicability as a high temperature thermo-structural composite under high temperature oxidation atmosphere by improving low mechanical property due to the oxidation of $C_f/SiC$ and brittle fracture mode of $SiC_f/SiC$ composite.

• The korean journal of orthodontics
• /
• v.33 no.2 s.97
• /
• pp.121-130
• /
• 2003

The purpose of this study was to evaluate the possibile clinical application of electroplating to increase diameter of an orthodontic wire, through examining the change of physical properties. The diameter of stainless steel orthodontic wire was increased from 0.016 inch to 0.018 inch by electroplating in a bath of nickel sulfate 100g/L, nickel chloride 60g/L, boric acid 30g/L, and sodium chloride 50g/L, under the conditions of 1.7V, $25\~29^{\circ}C\;and\;3.1\~3.3pH$. During the electroplating, the rate of diameter increase was measured every minute. To investigate uniformity, the diameter was measured at three different locations of each wire specimen aster electroplating. An X-ray diffraction test was performed to analyze the nature of the electroplated metal. Following heat treatment to improve adhesion between the wire and electroplated metal, a three-point bending test was conducted to compare stiffness, field strength, and ultimate strength among four wire groups; 0.016 inch, electroplated 016, electroplated and heat-treated 016, and 0.018 inch wires. Through the comparison of each wire group, following results were obtained. 1. In the load-deflection graph, the curve of the electroplated group was Placed between that of the 0.016 inch group and the 0.018 inch group, and the owe was closer to the 0.018 inch group by heat treatment. 2. In the electroplated and heat-treated 016 wire group, the values of stiffness, yield strength and ultimate strength showed higher tendency than in the original 0.016 Inch group. Stiffness and ultimate strength showed statistically significant differences between two groups. 3. Stiffness, yield strength, and ultimate strength of electroplated wire presented lower values than those of 0.018 inch wire group. 4. Stiffness, yield strength, and ultimate strength of electroplated and heat-treated wire showed higher tendency than those of electroplated wire group, and ultimate strength showed statistically significant difference between two groups. 5. After electroplating, the difference in diameter between the three locations was within $0.1\~0.3\%$ variation, and showed no statistical significance.