• 한국세라믹학회지
• /
• 제31권6호
• /
• pp.629-636
• /
• 1994

The ferrimagnetic glass-ceramics in the system Fe2O3-CaO-SiO2 for hyperthermia were investigated. Glasses could be prepared up to the content of 40 wt% of Fe2O3 and below the weight ratio of 1.0 of CaO/SiO2. The maximum saturation magnetization and the maximum coercive force were 29.85 emu/g and 340.1 Oe respectively, for a glass 40Fe2O3.20CaO.40SiO2 composition heat-treated at 95$0^{\circ}C$ for 8 hours. And for a glass 40Fe2O3.30CaO.30SiO2 composition the maximum saturation magnetization and the maximum coercive force were 18.47 emu/g and 374.4 Oe heat-treated at 1,00$0^{\circ}C$ and 90$0^{\circ}C$ for 8 hours respectively. The maximum hysteresis loss was 1,726.3 cal/g for a glass 40Fe2O3.20CaO.40SiO2 composition heat-treated at 95$0^{\circ}C$ for 8 hours. It was found that the ferrimagnetic Fe2O3.CaO.SiO2 glass-ceramics was little injurious to human body as results of biocompatibility test and biotoxicity test.

• 한국재료학회지
• /
• 제12권3호
• /
• pp.176-181
• /
• 2002

Fabrication of ${\beta}-FeSi_2$ was attempted by making use of the combined process of mechanical alloying (MA) and spark plasma sintering (SPS). MA was performed under the Ar gas atmosphere using mixed powders of pure iron and silicon having the mole fraction of 1:2. SPS process was performed at 800-85$0^{\circ}C$ with the applied pressure of 50MPa and the holding time was ranging from 0 to 30min. The mechanically alloyed powder by cyclic operation of rotor for 15hrs consisted of $\varepsilon$-FeSi and Si phases. When this mechanically alloyed powder was sintered by SPS process above 85$0^{\circ}C$, $\varepsilon$-FeSi and ${\alpha}-Fe_2Si_5$ phase were formed. Bulk product sintered at 82$0^{\circ}C$ for 30min consisted of ${beta}-FeSi_2$ phase with a small fraction of $\varepsilon$-FeSi and the density of sintered specimen was 75.3% theoretical density. It was considered that the MA/SPS combined process was effective for the preparation of ${\beta}-FeSi_2$ without heat treatment process after sintering.

• Journal of Magnetics
• /
• 제13권4호
• /
• pp.170-172
• /
• 2008

Fe-6.5% Si alloys have good magnetic properties due to their high electrical resistivity, very low magneto-striction, and low crystalline anisotropy. Despite their strong potential, these alloys have seldom been used in magnetic applications because of the very poor ductility of Si-steel above 3.0 wt% Si [1-4]. It is difficult to achieve compressed Fe-6.5% Si powder cores with excellent properties because of the low density due to poor ductility. In compressed powder cores, high density is essential in order to obtain high magnetization and permeability. In this study, an attempt was made to produce Fe-3%Si powder cores because the Fe-3.0 wt% Si alloys have relatively good magnetic properties and room temperature ductility. Gas atomized Fe-3.0 wt% Si powder was compressed into toroid shape cores. By reducing the Si content to 3.0 wt%, the hysteresis loss could be greatly reduced and thus the total core loss could be minimized. The total core loss is 600 mW/$cm^3$ at 0.1 T and 50 kHz.

• 한국주조공학회지
• /
• 제25권3호
• /
• pp.128-133
• /
• 2005

The effects of Mn and Cr on the crystallization behaviors of Fe-bearing intennetallics in A356 alloy were studied. Coarse and acicular ${\beta}-Al_{5}$FeSi phase in A356-0.20wt.%Fe alloy was modified into small ${\alpha}$-Al(Fe,Mn)Si and ${\alpha}$-Al(Fe,Cr)Si phases in response to Mn and Cr addition, respectively. Increasing of Mn addition amount elevates the crystallizing temperature of ${\alpha}$-Al(Fe,Mn)Si and the Mn/Fe ratio in the ${\alpha}$-Al(Fe,Mn)Si. Cr is more effective to modify ${\beta}-Al_{5}$FeSi in comparison with Mn. ${\alpha}$-Al(Fe,Mn)Si phase had BCC/SC dual structure.

• Bulletin of the Korean Chemical Society
• /
• 제33권8호
• /
• pp.2567-2573
• /
• 2012

We successfully synthesized $Fe_3O_4@SiO_2$ nanoparticles with ultrathin silica layer of $1.0{\pm}0.5$ nm that polyethyleneimine (PEI) with low molecular weight of 2.0-4.0 kDa was covalently conjugated with the resulting $Fe_3O_4@SiO_2$ nanoparticles by silane coupling reaction. The PEI-$Fe_3O_4@SiO_2$ nanoparticles were further used as gene delivery vector for a human fibroblast cell (IMR-90) line. Gene transfection efficiency of the PEI-$Fe_3O_4@SiO_2$ complexes did not increase remarkably after magnetofection; however, the addition of Lipofectamine 2000 significantly increased the transfection efficiency of the PEI-$Fe_3O_4@SiO_2$ complexes. We believe that the present approach could be utilized for magnetofection as alternative to $Fe_3O_4$ nanoparticles conjugated with the PEI of high molecular weight thanks to its relatively low cytotoxicity and high transfection efficiency.

• 한국정보통신학회논문지
• /
• 제10권9호
• /
• pp.1663-1670
• /
• 2006

펄스 전기증착법에 의해 단결정 Fe 박막을 n-Si(111) 기판위에 직접 성장시켰다. CV 분석 을 통해 $Fe^{2+}n-Si(111)$ 계면은 쇼트키 장벽 형성에 따른 다이오드 특성을 가진다는 사실을 알 수 있었다. 또한 인가 전압에 따른 전기용량의 변화를 보여주는 Mott-Schottky chottky(MS) 관계식을 이용하여 전해질 내에서 n-Si(111) 기판의 flat-band potential(EFB)을 조사하였으며, 0.1M $FeCl_2$ 전해질 내에서 EFB와 산화-환원 전위는 각각 -0.526V 과 -0.316V 임을 알 수 있었다. Fe/n-Si(111) 계면반응 시, Fe 증착 초기 단계에서의 핵 형성과 성장 운동학은 과도전류 특성을 이용하여 조사하였으며, 과도전류 특성을 통해 Fe 박막의 성장모드는 "instantaneous nucleation and 3-dimensional diffusion limited growth"임을 알 수 있었다. 주파수가 300Hz, 최대 전압이 1.4V인 펄스 전압을 이용하여 n-Si(111) 기판위에 Fe를 직접 전기 증착 시켰으며, 형 성 된 Fe 박막은 단결정 ${\alpha}-Fe$로 Si 기판위에 ${\alpha}-Fe(110)/Si(111)$의 격자 정합성을 가지고 성장하였음을 XRD 분석을 통해 확인하였다.

• 한국재료학회지
• /
• 제8권2호
• /
• pp.141-146
• /
• 1998

Ball mill을 이용하여 Ar 분위기에서 기계적 합금법으로 $Fe_{ 5}$$Si_{x}$ $B_{5-x}$ 분말을 제조하고, 제조된 분말을 연속 진공 열처리 시킨 후 Si첨가에 따른 결정구조 및 자기적성질을 조사하였다. 250시간 볼밀처리한 Fe$_{5}$ $B_{5}$ 합금에서 전체적으로 비정질 구조가 형성되었으나 일부분에 결정질이 존재하고 있었으며, $800^{\circ}C$에서 2시간 열처리하면 FeB와 $Fe_{2}$B 상이 혼재된 구조를 얻었다. 250시간 볼밀처리한 $Fe_{5}$ $Si_{2}$$B_{3}$합금에서 전체적으로 비정질 구조를 얻을 수 있었고, 이 시료를 2시간, $800^{\circ}C$로 열처리 하였을 때 $Fe_{2}$B상은 사라지고, 대부분 FeB의 균질한 상을 나타내었다. $Fe_{5}$ $B_{5}$ /조성에서는 분말 입자크기가 약 $1\mu\textrm{m}$이었으나, Si이 첨가되면 분말 입자크기가 약 $10\mu\textrm{m}$로 커졌다. Si의 첨가에 의해서 비정질상의 형성을 촉진시켜 단일 FeB상의 합성시간을 단축시킬 수 있었다.

• 한국광물학회지
• /
• 제20권4호
• /
• pp.367-376
• /
• 2007

에이니그마타이트($Na_4(Fe^{2+},Ti,Fe^{3+}){_{12}}(Fe^{3+},Si){_{12}}O_{40}$)는 Na가 풍부한 알칼리 화성암에 흔히 산출되는 광물이며, 분지 개방형 단쇄형 규산염광물로 분류된다. 3개의 산출이 다른 자연산 에이니그마타이트를 대상으로 뫼스바우어 분광분석을 실시하였으며 상세한 결정화학적 연구가 수행되었다. 뫼스바우어 분광분석 결과 9개의 흡수선이 분리되었는데, 3쌍의 흡수선은 팔면체 자리를 점유하는 $Fe^{2+}$의 피크이며, 저속도 구간의 독립적인 2개의 흡수선과 대응하는 한 개의 중첩된 흡수선은 각각 사면체와 팔면체 자리의 $Fe^{3+}$의 피크로 밝혀졌다. $Fe^{2+}$와 $Fe^{3+}$의 정확한 함량비에 의해 화학분석치가 재계산되었으며, Fe 양이온의 사면체 자리와 팔면체 자리에 대한 정확한 자리점유율로 상세한 결정화학적 정보를 제공하였다. 상당한 함량의 $Fe^{3+}/tet$는 사면체 자리점유에 있어 $Fe^{3+}$가 $Al^{3+}$보다 우위를 보여준다. 결정화학적로 규명된 에이니그마타이트(AEN1)의 상세한 화학조성은 $(Na_{3.97}Ca_{0.03})(Ca_{0.11}Mn_{0.59}Fe^{2+}{_{8.07}}Ti_{2.07}Mg_{0.70}Fe^{3+}{_{0.43}}Al_{0.04})(Fe^{3+}{_{0.56}}Al_{0.18}Si_{11.26})O_{40}$으로 밝혀졌다.

• 한국자기학회지
• /
• 제19권2호
• /
• pp.62-66
• /
• 2009

연자성 금속재료인 $Fe_{94}Si_5Cr_1$을 30시간 볼밀 한 후 주사전자현미경을 사용하여 관찰한 결과 볼밀 가공한 FeSiCr의 입자들이 구형에서 편상으로 변함을 확인하였다. FeSiCr을 실리콘 고무와 혼합하여 핸드폰용 전파흡수체를 제조하고 network analyzer을 이용하여 두께에 따른 FeSiCr-고무 전파흡수체의 전파흡수특성 및 재료정수를 측정하였으며, 그들의 상관관계를 비교 조사하였다. 그 결과 sheet형 전파흡수체 두께에 따라서 정합주파수가 낮은 주파수 대역으로 shift 됨을 알 수 있고, 1.3 mm의 두께로 제조한 전파흡수체에서는 이동통신주파수 대역인 1.86 GHz에서 -8.3 dB의 반사손실을 보여주었다.

• 한국주조공학회지
• /
• 제10권3호
• /
• pp.225-234
• /
• 1990

Spheroidal graphite cast irons which are Fe-3%C-(4－6)%Si-(0－0.5)%Mo were studied to improve not only heat resistance but also mechanical properties. With increasing Mo content, the graphitization was decreased and carbide volume fraction was increased. The graphite spheroidization ratio was not decreased in Fe-3%C-6%Si-Mo system cast iron with increasing Mo content, but that was decreased in Fe-3%C-4%Si-Mo system and Fe-3%C-5%Si-Mo system cast irons. Hardness was increased with the Si and Mo contents. At constant Si content, tensile strength was increased with increasing Mo content, but that was decreased at 6%Si. In the experiment of oxidation, weight gain was decreased as the Si and/or Mo content increased, but increased at 1.5%Mo content.