• Journal of Korea Foundry Society
• /
• v.18 no.5
• /
• pp.462-466
• /
• 1998

Interest in rapid solidification of magnesium alloys stems from the fact that conventional ingot metallurgy alloys exhibit poor strength, ductility, and corrosion resistance. Such properties can be improved by microstructural refinement via rapid solidification processing. Mg-5wt%Zn alloys have been produced as continuous strips by melt overflow technique and the strips were consolidated by hot extrusion. The yield stress, tensile strengh and ductility obtained in asextruded Mg-5wt%Zn alloy were ${\sigma}_{0.2}=152\;MPa$, ${\sigma}_{T.S{\cdot}}=263\;MPa$ and ${\varepsilon}=21.8%$. In order to evaluate the influence of additional elements on mechanical properties, Th and Zr were added in rapidly solidified Mg-5wt%Zn alloy. An 130% increase in yield stress of as-extruded Mg-5wt%Zn-3wt%Th-1wt%Zr alloy was attributed to grain refinement by rapid solidification and elemental addition.

• Journal of ILASS-Korea
• /
• v.18 no.4
• /
• pp.169-175
• /
• 2013

Hydrotreated biodiesel (HBD) would be one of the promising alternative fuels instead of current biodiesel. In this study, spray characteristics in terms of spray penetration and spray angle were conducted experimentally including calculated SMDs as well. The ambient pressures of 1, 3, and 5 MPa and injection pressures of 30, 80, and 130 MPa were introduced and the fuels employed were petro-diesel, and 2, 10, 20, 30, and 50% for hydrotreated biodiesel, respectively. The result of this study found that the more HBD blended diesels have the slightly shorter spray tip penetration lengths especially on the lowest injection pressure and at the highest ambient pressure, but have the larger spray angles and SMDs than petro-diesel. Consequently, this study found that HBD has a little bit merits and demerits of macro- and micro- spray patterns compared to petro-diesel.

• Journal of the Korean Ceramic Society
• /
• v.37 no.9
• /
• pp.915-920
• /
• 2000

합성과 동시에 소결이 이루어지는 HPCS법을 이용하여 TiB$_2$-W 복합체를 텅스텐의 함량 변화에 다라 제조하여 이 복합체의 미세구조 및 기계적 물성에 대하여 연구하였다. 이 연구 결과, 텅스텐의 함량증가에 따라 삼성분 붕화 화합물인 TiWB$_2$의 상이 증가하였으며, 이 상의 증가에 따라 기계적 물성이 향상되었다. 60 MPa의 압력과 130$0^{\circ}C$, 3000 A에서 소결한 TiB$_2$-30vol% W 복합체에서 상대밀도, 강도, 경도 값은 각각 97.2%, 411.5 MPa, 22.36 GPa로 가장 우수한 물성을 얻을 수 있었다.

• Journal of the Korean Society of Mechanical Technology
• /
• v.13 no.4
• /
• pp.125-130
• /
• 2011

Technological mode progress demands the use of materials at high temperature and pressure. Constant load creep tests have been carried out over the range of stresses at high temperatures. One of the most critical factors in considering such applications as the most critical one is the creep behavior. In order to investigate the creep behavior in this study, the stress exponents during creep were determined over the temperature range of $275^{\circ}C$ to $325^{\circ}C$ and the stress range of 36MPa to 72MPa. The applicability of modified Monkman-Grant relationship was also discussed.

• Journal of the Microelectronics and Packaging Society
• /
• v.11 no.2 s.31
• /
• pp.23-28
• /
• 2004

We utilized Ag capping layer for fluxless bonding. To investigate the effect of Ag capping layer, two sets of sample were used. One set was bare In and Sn solders. The other set was In and Sn solders with Ag capping layer. In ($10{\mu}m$) and Sn ($10{\mu}m$) solders were deposited on Cu/Ti/Si substrate using thermal-evaporation, and Ag ($0.1{\mu}m$) capping layers were deposited on In and Sn solders. Solder joints were made by joining two In and Sn deposited specimens at $130^{\circ}C$ for 30 s under 0.8, 1.6, 3.2 MPa using thermal compression bonder. The contact resistance was measured using four-point probe method. The shear strength of the solder joints was measured by the shear test of cross-bar sample in the direction. The microstructure of the solder joints was characterized with SEM and EDS. In and Sn solders without Ag capping layers were only bonded at $130^{\circ}C$ under high bonding pressure. Also the shear strength of the In-Sn solder joints under was lower than that of the Ag/In-Ag/Sn solder joints. The resistance of the solder joints was $2-4\;m{\Omega}$ The solder joints consisted of In-rich phase and Sn-rich phase and the intermixed compounds were found at the interface. As bonding pressure increased, the intermixed compounds formed more.

• Journal of the Korean Ceramic Society
• /
• v.38 no.1
• /
• pp.9-14
• /
• 2001

본 연구는 우리나라 하동지방에서 다량으로 산출되는 저급 Kaoline을 활용하여 Mullite를 합성하는데 목적이 있다. 저질 Kolin을 AlF$_3$와 충분히 혼합한 후 130$0^{\circ}C$에서 반응시키면 거의 순간적으로 Mullite의 합성이 가능하였으며 이때에 얻어진 Mullite는 X-ray 회절결과 순수한 Mullite 단일상으로 나타났으며 소결체의 특성에 보면 1$600^{\circ}C$ 3시간 소결 후 비중은 2.8g/$m^2$이며 굽힘강도는 170 MPa을 나타내었다.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.33 no.2
• /
• pp.173-180
• /
• 2013

Compacted graphite iron(CGI), also known as vermicular graphite iron, is a metal which is gaining popularity in applications that require either greater strength, or lower weight than cast iron. Recently compacted graphite iron has been used for diesel engine blocks. Considering that using in exhaust manifold of the diesel engine, CGI340 was conducted the heat treatment during 1 hour to 96 hours from 873 to 1273 K. Mechanical characteristics were evaluated. The obtained results are as follows; The tensile strength of the heat treated specimens showed overall lower tensile strength than that of the base metal. Tensile strength decreases with increasing of heat treatment time, and the higher heat treatment temperature and the longer time, were more reduced. The fatigue limit by the ultrasonic fatigue test was approximately 130 MPa of base metal, 100 MPa of 1173 K (96 hrs) specimen, respectively. The hardness decreases with increasing heat treatment time, and the higher the heat treatment temperature was lowered hardness distribution. In CGI340, average hardness of nodular graphite was 120 Hv, average hardness of vermicular graphite was 114 Hv. This showed lower hardness than the base structure ferrite. The nodular graphite and vermicular graphite according to the heat treatment temperature and time didn't have a consistent change. However, the grain size of base structure grew with increasing of heat treatment time.

• Journal of the Korean Ceramic Society
• /
• v.16 no.4
• /
• pp.213-224
• /
• 1979

The present work was undertaken: (1) to determine if CaO-partially stabilized $ZrO_2$ prepared by Hot Petroleum Drying Method would show better ionic conductor as an oxygen sensor in molten metals than that prepared by Oxide Wet Mixing Method and than CaO-fully stabilized $ZrO_2$, and (2) to understand the nature of conduction mechanism of CaO-partially stabilized $ZrO_2$ by a comparison of measured electrical conductivity data with theory on defect structure of pure monoclinic $ZrO_2$ and fully stabilized cubic $ZrO_2$. The DC electrical conductivity was measured by 3-probe technique and the AC electrical conductivity by 2-probe technique as a function of temperature in the range 973-1373 K and oxygen partial pressure in the range 10-1-10-25Mpa. The results of the experiments were as follows: 1. CaO-partially stabilized $ZrO_2$ prepared by Hot petroleum Drying Method showed at T=1094-1285 K and $Po_2$=10-7-10-25 MPa a nearly ionic conduction with 4 times higher conductivity than that prepared by Oxide Wet Mixing Method. 2. High-oxygen pressure conductivity tends toward a Po_2^{+1/5}-Po_2^{+1/6}$dependence. An analysis of possible defect structures suggests that CaO-partially stabilized $ZrO_2$ has an anti-Frenkel defect in which singly or doubly ionized oxygen interstitials and defect electrons predominate at T=1094-1285 K and $Po_2$=10-1-10-7MPa. 3. The activation energy for pure electron hole-conduction and ionic conduction of CaO-partially stabilized $ZrO_2$ was found to be 130 KJ/mol at T=973-1373 K, $Po_2$=2, 127 10-2 MPa(air) and 153KJ/mol at T=1094-1285 K respectively.

• Korean Journal of Materials Research
• /
• v.9 no.7
• /
• pp.735-739
• /
• 1999

In this study we investigated stress development and shrinkage of thickness for a single $PbTiO_3$(PT) layer prepared by sol-gel processing. Changes of microhardness for multideposited PT layers with temperatures are also monitored to understand the densification of thin films. Single PT layer shrank rapidly from room temperature to$ 220^{\circ}C$ yielding 83% of total shrinkage observed up to $500^{\circ}C$. A tensile stress of ~75MPa developed in an as-spun layer, and increased steadily beyond $130^{\circ}C$ until it reaches the maximum value of 147MPa at $250^{\circ}C$. The significant decrease of tensile stress in the film beyond $370^{\circ}C$ indicates that thermal expansion mismatch between the film and the substrate dominates the stress behavior in this temperature range. Microhardness of the multideposited coatings also increased rapidly above $300^{\circ}C$ regardless of the pyrolysis temperatures used. Large amount of perovskite phase formed in multideposited coatings after $550^{\circ}C$ may be due partly to enhanced homogeneous nucleation in the thicker coating.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.20 no.6
• /
• pp.91-97
• /
• 2016

Evaluation on the test of actual concrete member to confirm the fire resistance of the concrete member using ultra-high strength concrete is required. However, test equipment which has large loading capacity is needed to the actual member experiment. So, many researchers evaluated the fire performance through analytical studies using the material models. This study experimentally evaluated strain properties on ultra-high-strength concrete of 80, 130 and 180 MPa with heating and examined to apply the existing strain model about ultra-high-strength concrete. As a results, constants are drawn by method of least squares applying experimental values and calculated values by the existing strain model, it proposed strain model that can be applied to ultra-high-strength concrete.