• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2001.11a
• /
• pp.141-145
• /
• 2001

Sn-3.5Ag 무연 솔더에 Cu를 첨가한 3원계 합금을 만든 후 압연과 열처리한 후 크리프 특성을 연구하였다. 모든 솔더 합금에서 1차 크리프는 거의 관찰되지 않았으며, 2차와 3차 크리프가 대부분을 차지하였고, 최소 크리프 변형율은 Cu 함량이 0.75 wt %에서 최소이었고, 응력 지수는 약 4이었으며, 파단 시간 또한 0.75 wt% Cu에서 가장 길었다. 크리프 기구는 격자 확산에 의한 전위의 상승과 전위 활주에 의한 고온 크리프임을 앞 수 있었으며, Cu의 첨가는 1 wt% 가지 연성에 큰 영향을 주지 않았으나, 1.5 wt% 첨가했을 경우 연성은 크게 감소하였다.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.23 no.7 s.166
• /
• pp.1120-1128
• /
• 1999

An elastic-viscoplastic finite element analysis is performed to investigate detailed growth behavior of creep cracks and the numerical results are compared with experimental results. In Cr-Mo steel stress fields obtained from the crack growth method by mesh translation were compared with both cases that the secondary creep rate is only used as creep material property and the primary creep rate is included. Analytical stress fields, Riedel-Rice(RR) field, Hart-Hui-Riedel(HR) field and Prime(named in here) field, and the results obtained by numerical method were evaluated in details. Time vs. stress at crack tip was showed and crack tip stress fields were plotted. These results were compared with analytical stress fields. There is no difference of stress distribution at remote region between the case of 1st creep rate+2nd creep rate and the case of 2nd creep rate only. In case of slow velocity of crack growth, the effect of 1st creep rate is larger than the one of fast crack growth rate. Stress fields at crack tip region we, in order, Prime field, HR field and RR field from crack tip.

• The Journal of Engineering Geology
• /
• v.19 no.2
• /
• pp.165-175
• /
• 2009

This study is concerned with creep characteristics of red shale in the Haman Formation by the single stage and multi stage loading tests. Creep constants in the Griggs's experiential equation, ${\epsilon}_t$= a+$b{\cdot}log$ t + $c{\cdot}t$, are determined by regression analysis on the total data obtained. The transition time between the primary and second creep means the time when the differential value of $b{\cdot}log$ t is equal to the differential value of $c{\cdot}t$. The correlation equation between loads (${\sigma}$%) and creep constants is deduced from the three times multi stage loading tests. Also a failure time under each loads is anticipated from creep constants and maximum strain at the failure.

• Journal of Advanced Marine Engineering and Technology
• /
• v.22 no.4
• /
• pp.490-497
• /
• 1998

An elast-biscoplastic finite element analysis is performed to investigate detailed growth behavior of creep cracks and the numerical results are compared with experimental results. The results of mesh translation method are compared with those of node release method. Load line displancement curve obtained from the crack growth analysis by mesh translation shows the improved results than that obtained from the crack growth by node release method when the secondary creep rate is only used as creep material property. The results of accounting for primary creep rate and instantaneous plasticity shows a good agreement with the experimental result.

• The Journal of Engineering Geology
• /
• v.13 no.2
• /
• pp.227-238
• /
• 2003

Understanding of a creep behavior in rocks under a constant load, due to visco-elastic properties of rock, is an essential element to predict a long term ground deformation. In order to clarify the creep characteristics of the mudstone in Duho formation at Pohang basin, deposited during Tertiary, a series of laboratory tests including physical properties, unconfined compressive strength and uniaxial creep tests, was performed. The mudstone showed a higher creep potential due to 26% of clay minerals such as illite and chlorite. The unconfined compressive strength of the rock was $462{\;}kg/\textrm{cm}^2$ in average, and four creep tests were performed under constant stress of 40 to 70 % of the strength. The creep constants in the empirical and theoretical equations were deduced from the time-strain curves obtained from the tests. Among the several equations, the empirical equation proposed by Griggs and theoretical equation of Burger’s model are appreciated as the best one to express the creep behavior of the mudstone. Instantaneous elastic strain was linearly increased with stress level but strain velocity during the first creep is decreased with a similar pattern by time lapse regardless the stress level.

• Journal of Welding and Joining
• /
• v.16 no.4
• /
• pp.83-91
• /
• 1998

Cracking problems which high temperature plant components suffer during long-term service, occur very often at welded locations. The crack occurs due to accumulated creep damage near fusion line or at heat affected zone (HAZ). However, most of the studies on creep crack growth behavior have been performed with matrix metal not wit welded metal due to the difficulty of interpreting the test results. In this study, creep crack growth rates were measured with C(T) specimens whose cracks were formed along the fusion line or HAZ. The measured crack growth rates were characterized by {TEX}$C_{t}${/TEX}-parameter derived for elastic-primary-secondary creeping material. Since contribution of primary creep was significant for the tested 1Cr-0.5Mo steel, its effect was carefully studied. Effects of crack tip plasticity and material aging were also discussed.

• Journal of the Computational Structural Engineering Institute of Korea
• /
• v.12 no.2
• /
• pp.171-184
• /
• 1999

이 논문은 시공단계를 고려한 콘크리트 프레임 구조물의 거동 해석을 다루고 있다. 고층건물의 경우 하루에 시공이 완료되지 않으므로 각 시공단계에 따라 콘크리트의 시간의존적 현상은 다르게 발생된다. 이를 위하여 이 논문에서는 일반적인 프레임 해석기법에 콘크리트의 시간의존적 특성을 고려하였다. 이 연구에 도입된 해석기법은 단면을 가상의 층으로 나누고 각층은 일축상태로 가정한 적층단면을 사용하였다. 요소는 평면 보요소를 사용하였으며 강성행렬은 변위법을 바탕으로 유도하였고 전체적인 구조해석은 비선형 구조해석 방법의 하나인 복합법을 사용하였다. 콘크리트의 시간의존적 특성을 고려하기 위하여 단면의 각 층에서 크리프와 건조수축에 의한 변형률을 계산하였으며 크리프는 크리프 Compliance의 전개에 기본을 둔 1차 순환적 단계 알고리즘을 사용하였다. 끝으로 이 연구에서 제안된 해석모델을 이용하여 프레임해석 및 기둥축소에 관한 예제를 해석하였다.

• Journal of Power System Engineering
• /
• v.6 no.1
• /
• pp.55-60
• /
• 2002

There has been no report on the life prediction for gas turbine materials at high temperatures based on the creep properties and their relationship with the AE(acoustic emission) properties as a means of real-time non-destructive testing. One of the important issues is thus to develop a reliable method of evaluating creep properties by the AE technique. In this paper, the real-time evaluation of high temperature creep time and AE cumulative counts for nickel-based superalloy Udimet 720 was performed on round-bar type specimens under pure load at the temperatures of 811, 922 and 977K. The total AE cumulative counts until the starting point of secondary creep($N_1$) and that of tertiary creep($N_2$) have quantitative relationship with the tertiary creep time and the rupture time. It is thus possible to construct the life prediction system based on creep and the prevention system of tertiary creep by using AE technique.

• Journal of Korea Foundry Society
• /
• v.41 no.6
• /
• pp.505-515
• /
• 2021

Creep properties of directionally solidified Ni-based superalloy CM247LC under various temperature and stress conditions have been investigated. In the heat-treated specimen, some portion of eutectic γ-γ' remained, and uniform cubic γ' was observed in the dendrites. At low temperature (750℃) and high stress condition, a large amount of deformation occurred during the primary creep, while the tertiary creep region accounted for most of the creep deformation under high temperature and low stress condition. γ' particles are sheared by dislocation dissociated into super lattice partial dislocations separated by stacking faults at 750℃. No stacking faults in γ' were found at and above 850℃ due to the temperature dependence of the stacking fault energy. Raft structure of γ' was found after creep test at high temperature of 950℃ and 1000℃. At 850℃, the deformation mechanism was shown to be dependent on the stress condition, and so rafting was observed only under low stress condition.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.3
• /
• pp.251-257
• /
• 2011

This paper deals with the statistical properties of parameters B and q in the creep crack growth rate (CCGR) law, da/dt=B$(C^*)^q$, in Mod. 9Cr-1Mo (ASME Gr.91) steel which is considered a candidate materials for fabricating next generation nuclear reactors. The CCGR data were obtained by creep crack growth (CCG) tests performed on 1/2-inch compact tension (CT) specimens under an applied load of 5000N at a temperature of $600^{\circ}C$. The CCG behavior was analyzed statistically using the empirical equation between CCGR, da/dt and the creep fracture mechanics parameter, $C^*$. The B and q values were determined for each specimen by the least-squares fitting method. The probability distribution functions for B and q were investigated using normal, log-normal, and Weibull distributions. As far as this study is considered, it can be appeared that B and q followed the log-normal and Weibull distributions. Moreover, a strong positive linear correlation was found between B and q.