• Resources Recycling
• /
• v.26 no.5
• /
• pp.39-47
• /
• 2017

In this study, the precipitation of rare earth-sodium sulfate with sodium sulfate was conducted in order to separate rare earth from Fe in rare earth sulfate solution. Neodymium (Nd) was easily precipitated as Nd-sulfate salt with sodium sulfate, on the other hand, excessive sodium sulfate was needed for the precipitation of Dy-sulfate salt. Also neodymium not only promoted the precipitation of dysprosium sulfate salt but also increased recovery of dysprosium sulfate salt in sulfuric acid solution. At the condition of $60^{\circ}C$ precipitation temperature, 3 h reaction time, 7 equivalents sodium sulfate, the recovery of neodymium and dysprosium sulfate salt was 99.7% and 94.3% respectively from the sulfuric acid solution containing Nd of 23.39 mg/ml and Dy of 8.67 mg/ml. Lastly, from the results of separation of Dy to Nd by the method of sulfate double salt, the effect of salting out with NaCl is important to increase the grade of Dy, and 98.7% of Dy grade could be obtained in this study.

• Resources Recycling
• /
• v.30 no.2
• /
• pp.31-38
• /
• 2021

To investigate the separation of La(III) from sulfuric acid solutions containing Fe(III), rare earth double salt precipitation experiments were performed by adding sodium sulfate. In this work, the effect of sodium sulfate, Fe(III), and La(III) concentrations; reaction temperature; and time was investigated. The extent of precipitation of La(III) was proportional to the concentrations of Na+ and SO42- in the solution. As the reaction temperature increased to 100 ℃, the extent of precipitation of La(III) increased. The extent of precipitation of Fe(III) decreased with increasing reaction time. The concentration ratio of Fe(III) to La(III) did not have a significant effect on the precipitation of La(III). Our results indicate that it is possible to separate La(III) from a ferric sulfate solution through selective precipitation by adding sodium sulfate.

• Resources Recycling
• /
• v.14 no.6 s.68
• /
• pp.3-9
• /
• 2005

In this study, the separation and recovery of cerium hydroxide was investigated from the wasted cerium polishing powders. Waste cerium polishing powder contains $64.5\;wt\%$ of rare earth oxide and the content of cerium oxide is $36.5\;wt\%$. Since cerium oxide, $56.3\%$ of rare earths, is the most stable state in rare earth, the dissolution of cerium oxide in acid solution is not easy. Therefore the process of rare earth oxide by sulfation and water leaching was examined in order to increase the recovery of rare earth. Rare earth elements were recovered in the form of $\Re{\cdot}Na(SO_{4})_{2}$ by the addition of sodium sulfate to leached solution. The slurry of rare earth hydroxide was prepared by the addition of $\Re{\cdot}Na(SO_{4})_{2}$ to sodium hydroxide solution. After the oxidation of cerous hydroxide($CE(OH)_{3}$) to ceric hydroxide($CE(OH)_{3}$) by aeration, ceric hydroxide was separated from other rare earth hydroxides by controlling the acidity of solution.

• Applied Chemistry for Engineering
• /
• v.9 no.3
• /
• pp.407-412
• /
• 1998

This study was carried out to investigate the optimum leaching conditions for the sulfation and water leaching, and separation of cerium from rare earth elements in leached solution by acid-adjusting method. The optimum conditions for the sulfation and water leaching from bastnasite concentrates are that the equivalent ration of sulfuric acid to concentrates is 2.5, calcination temperature and time are $600^{\circ}C$ and 2 hrs respectively, and the pulp density in the water leaching is 9.1%. The yield of rare earth oxide is about 93% at the above condition. The process of recovery of cerium hydroxide from leached solution by acid-adjusting method was carried out as following steps. The first step is the oxidation of the solution at pH 5 by using twice the equivalent of $H_2O_2$ solution as an oxidant. The second step is the precipitation to obtain cerium complex salt and cerium hydroxide after lowering the solution to pH 2. The last step is the oxidation-precipitation by using equivalent of $H_2O_2$ solution. From these results, it was possible to prepare cerium hydroxide with the yield of 60% and the quality of 80%.