• Restorative Dentistry and Endodontics
• /
• v.34 no.5
• /
• pp.397-405
• /
• 2009

This study compared the effect of an activator, intermediate bonding resin and low-viscosity flowable resin on the microtensile bond strength of a self-curing composite resin used with two-step total etching adhesives. Twenty extracted permanent molars were used. The teeth were assigned randomly to nine groups (n=10) according to the adhesive system and application of additional methods (activator, intermediate adhesive, flowable resin). The bonding agents and additional applications of each group were applied to the dentin surfaces. Self-curing composite resin buildups were made for each tooth to form a core, 5mm in height. The restored teeth were then stored in distilled water at room temperature for 24h before sectioning. The microtensile bond strength of all specimens was examined. The data was analyzed statistically by one-way ANOVA and a Scheffe's test. The application of an intermediate bonding resin (Optibond FL adhesive) and low-viscosity flowable resin (Tetric N-flow) produced higher bond strength than that with the activator in all groups. Regardless of the method selected, Optibond solo plus produced the lowest ${\mu}TBS$ to dentin. The failure modes of the tested dentin bonding agents were mostly adhesive failure but there were some cases showed cohesive failure in the resin.

• Restorative Dentistry and Endodontics
• /
• v.31 no.1
• /
• pp.20-29
• /
• 2006

The purpose of this study was to analyze the stress distribution aspect of unrestored and restored combined shape (wedge shape occulusally and saucer shape gingivally) class V cavity, which found frequently in clinical cases. A maxillary second permolar restored with a combined shape class V composite restorations were modeled using the three dimensional finite element method. Static occlusal load of 170 N was applied on lingual incline of buccal cusp at the angle of $45^{\circ}$ with the longitudinal axis of the tooth. And three dimensional finite element analysis was taken by ANSYS (Version 6.0, Swanson Analysis System Co., Houston, U.S.A) program which represent the stress distribution on unrestored and restored cavity wall and margin. The conclusions were as follows. 1. Compared to the unrestored cavity, Von Mises stress at the cementoenamel junction and line angle of the cavity base were reduced and in restored cavity. 2. Von Mises stress at the occlusal and cervical cavity margin and wall were increased in restored cavity in comparison with the unrestored cavity. 3. In the hybrid and hybrid/flowable composite resin restoration, Von Mises stress at the cementoenamel junction and line angle of the cavity base were reduced more than in the flowable restoration. 4. In the hybrid and hybrid/flowable composite resin restoration, Von Mises stress at the occlusal and cervical cavity margin and wall were increased more than in the flowable restoration.

• Restorative Dentistry and Endodontics
• /
• v.32 no.6
• /
• pp.542-549
• /
• 2007

The purpose of this study was to evaluate the difference in the surface roughness after polishing and to evaluate the difference in color stability after immersion in a dye solution among four types of composite resin materials. Four light-polymerized composite resins(Shade A2) with different sized filler content(a nanofilled, a hybrid, a microfilled, a flowble) were used. Average surface roughness (Ra) was measured with a surface roughness tester (Surftest Formtracer) before and after polishing with aluminum oxide abrasive discs(Super-Snap). Color of specimens before and after staining with 2% methylene blue solution were measured using spectrophotometer(CM-3700d) with SCI geometries. The results of Ra and ${\Delta}E$ were analyzed by one-way analysis of variance(ANOVA), a Scheffe multiple comparison test and Student t-test(p=0.05). After polishing, Ra values were decreased regardless of type of composite resins. In surface roughness after polishing and color stability after staining, nanofilled composite resin was not different with other composite resins except flowable resins.

• Restorative Dentistry and Endodontics
• /
• v.34 no.6
• /
• pp.467-476
• /
• 2009

The aim of this study was to measure the dentinal tubular fluid flow (DFF) during and after amalgam and composite restorations. A newly designed fluid flow measurement instrument was made. A third molar cut at 3 mm apical from the CEJ was connected to the flow measuring device under a hydrostatic pressure of 15 $cmH_2O$. Class I cavity was prepared and restored with either amalgam (Copalite varnish and Bestaloy) or composite (Z-250 with ScotchBond MultiPurpose: MP, Single Bond 2: SB, Clearfil SE Bond: CE and Easy Bond: EB as bonding systems). The DFF was measured from the intact tooth state through restoration procedures to 30 minutes after restoration, and re-measured at 3 and 7days after restoration. Inward fluid flow (IF) during cavity preparation was followed by outward flow (OF) after preparation, In amalgam restoration, the OF changed to IF during amalgam filling and slight OF followed after finishing. In composite restoration, application CE and EB showed a continuous OF and air-dry increased rapidly the OF until light-curing, whereas in MP and SB, rinse and dry caused IF and OF, respectively. Application of hydrophobic bonding resin in MP and CE caused a decrease in flow rate or even slight IF. Light-curing of adhesive and composite showed an abrupt IF. There was no statistically significant difference in the reduction of DFF among the materials at 30 min. 3 and 7 days after restoration (p > 0.05).

• Proceedings of the KACD Conference
• /
• 2008.05a
• /
• pp.235-245
• /
• 2008

The aim of this study was to develop a method for measuring the slumping resistance of resin composites and to relate it to the rheological characteristics. Five commercial hybrid composites (Z100. Z250. DenFil, Tetric Ceram. ClearFil) and a nanofill composite (Z350) were used to make disc-shaped specimens of 2 mm thickness. An aluminum mold with square shaped cutting surface was pressed onto the composite discs to make standardized imprints. The imprints were light-cured either immediately (non-slumped) or after waiting for 3 minutes at $25^{\circ}C$ (slumped). White stone replicas were made and then scanned for topography using a laser 3-D profilometer. Slumping resistance index (SRI) was defined as the ratio of the groove depth of the slumped specimen to that of the non-slumped specimen. The pre-cure viscoelasticity of each composite was evaluated by an oscillatory shear test and normal stress was measured by a squeeze test using a rheometer. Flow test was also performed using a flow tester. Correlation analysis was performed to investigate the relationship between the viscoelastic properties and the SRI. SRI varied between the six materials (Z100 < DenFil < Z250 < ClearFil < Tetric Ceram < Z350). The SRI was strongly correlated with the viscous (loss) shear modulus G' but not with the loss tangent. Also. slumping resistance was more closely related to the resistance to shear flow than to the normal stress. Slumping tendency could be quantified using the imprint method and SRI. The index may be applicable to evaluate the clinical handling characteristics of composites.

• Restorative Dentistry and Endodontics
• /
• v.33 no.3
• /
• pp.235-245
• /
• 2008

The aim of this study was to develop a method for measuring the slumping resistance of resin composites and to relate it to the rheological characteristics. Five commercial hybrid composites (Z100, Z250, DenFil, Tetric Ceram, ClearFil) and a nanofill composite (Z350) were used to make disc-shaped specimens of 2 mm thickness. An aluminum mold with square shaped cutting surface was pressed onto the composite discs to make standardized imprints. The imprints were light-cured either immediately (non-slumped) or after waiting for 3 minutes at $25{\circ}C$ (slumped). White stone replicas were made and then scanned for topography using a laser 3-D profilometer. Slumping resistance index (SRI) was defined as the ratio of the groove depth of the slumped specimen to that of the nonslumped specimen. The pre-cure viscoelasticity of each composite was evaluated by an oscillatory shear test and normal stress was measured by a squeeze test using a rheometer. Flow test was also performed using a flow tester. Correlation analysis was performed to investigate the relationship between the viscoelastic properties and the SRI. SRI varied between the six materials (Z100 < DenFil < Z250 < ClearFil < Tetric Ceram < Z350). The SRI was strongly correlated with the viscous (loss) shear modulus G' but not with the loss tangent. Also, slumping resistance was more closely related to the resistance to shear flow than to the normal stress. Slumping tendency could be quantified using the imprint method and SRI. The index may be applicable to evaluate the clinical handling characteristics of composites.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.37 no.4
• /
• pp.412-421
• /
• 2010

As a most conservative, minimally invasive trial against early caries lesions, resin infiltration concept has been introduced and studied mainly about effective materials and pre-treatment methods of surface layers to arrest the lesion effectively, which is still going on. This study was performed with an aim of evaluating the efficacy of arresting the caries process in the natural incipient lesions in spite of removing the surface layers and we obtained the results as follows: 1. It was revealed that infiltration groups(1, 3, 5) showed lower radio-density decline between pre- and posttreatment than control groups(2, 4, 6)(p<0.05). 2. Group 5, in which the surface layer was removed with hydrochloric acid, showed the most significant anticariogenic effect(p<0.05). 3. Under SEM evaluation after infiltration, group 1 and 3 showed more irregular destruction and intensive loss of surface layers than group 5. In conclusion, it was thought resin infiltration can be an effective tool against the early caries lesions although surface layers are removed.

• Restorative Dentistry and Endodontics
• /
• v.27 no.2
• /
• pp.122-134
• /
• 2002

목적 : 근관 치료의 최종 목적인 근관계의 영구적인 충전을 위해 사용되는 근관 봉함제는 많은 연구와 개선을 거쳐서 현재는 다양한 성분의 봉함제가 시판되고 있다. 이중에서 레진이 주성분인 봉함제는 조작이 편리하고 흐름성이 좋으며 근관의 벽에 높은 밀폐성을 보이고 충분한 작업시간과 높은 방사선 불투과성을 가지는 장점을 가짐에도 불구하고 높은 초기 생체 독성을 나타내는 단점을 가지고 있다. 본 실험에서는 기존의 상용화된 제품 중 레진이 주성분인 두 종류의 봉함제(AH 26, AH plus)와 산화아연이 주성분인 봉함제(Pulp Canal Sealer EWT)와 국내에서 새로이 개발한 제품으로서 레진이 주성분인 두 종류의 봉함제(Adseal-1,2)를 생체조직에 매식하여 국소적인 반응을 비교하여 생체친화성을 알아보고자 하였다. 방법 : 수종 봉함제의 생체 친화성을 알아보기 위하여 64마리의 Sprague-Dawley rat을 사용하였다. 봉함제의 피하조직 매식을 위해 길이와 직경이 각각 5와 1.5mm인 폴리에틸렌 테프론 관을 사용하였으며 이를 에탄올과 증류수로 세척 한 후 고압증기멸균을 시행하였다. Rat에 대하여 케타민으로 복강내 마취를 시행한 후 배부를 면도하고 iodine으로 소독한 다음 네 곳에 절개를 시행하였으며 blunt dissection을 통해 깊이 10mm이상의 피하조직 pocket을 형성하였다. 각각의 봉함제를 제조사의 지시 에 따라 혼합 후 즉시 멸균된 테프론 관에 주사기를 이용하여 담은 다음에 봉함제가 흐르지 않게 유의하며 pocket내로 삽입하였으며 이때 16개의 관을 대조군으로 사용하기 위해 봉함제를 넣지 않은 상태로 삽입하였다. 이 후 절개 부위를 surgical gut suture로 봉합하였으며 1주일 후에 발사하였다. Rat을 1, 2, 4, 12주 후에 각 군 당 세 마리 씩 에테르 흡입을 통해 희생하였으며 이 때 한 마리씩의 대조군도 포함시켰다. 이 후 매식된 관을 주위 조직과 함께 제거하고 포르말린에서 48시간 고정시킨 후 파라핀에 포매한 다음에 micro-tome을 사용하여 6$\mu\textrm{m}$로 serial section을 시행하였다. 정중선 부위의 시편에 Hematoxylin-Eosin staining을 시행한 후 Olsson, Orstavik 그리고 Mjor 등의 방법에 따라 조직학적 변화를 관찰한 후 slight(1), moderate(2), severe inflammation(3)의 단계로 분류하였다. 얻어진 결과를 통계처리 프로그램인 Jandel사의 Sigmastat을 이용하여 Kruskal Wallis Test로 통계처리를 하였다. 결과 : (Table omitted) 결론 : 1) Pulp Canal Sealer를 제외한 모든 군에서 시간이 지남에 따라 유의성 있게 염증이 감소되는 양상을 보였다(p<0.05). 2) Pulp Canal Sealer는 1주, 2주, 12주에서 강한 염증반응을 보였다. 3) AH 26과 AH Plus에서는 1주, 2주에서 강한 염증반응을 보였으나 12주에서는 염증반응이 감소하였다. 4) 새로 개발된 봉함제 Adseal-1,2는 1주, 2주에서는 가장 약한 염증반응을 보이나 4주, 12주 후에는 AH Plus와 비슷한 수준의 염증 반응을 보였다. 5) Pulp Canal Sealer를 제외한 모든 군에서 인정할 만한 생체친화성을 보였다. 6) Adseal-2가 Adseal-1에 비하여 전반적으로 낮은 염증반응을 보였다. 7) 각 군간 결과의 차이에 통계적 유의성은 없었다(p>0.05).

• Journal of the korean academy of Pediatric Dentistry
• /
• v.29 no.3
• /
• pp.469-477
• /
• 2002

One of the major deficiencies of composite restorative resins is their insufficient resistance to wear. Of the multitude of factors that have been associated with wear, subsurface degradation within the restoration is considered to be one. The aim of this study was to evaluate the resistance to degradation of four commercial composite resins in an alkaline solution. The brands studied were Z100(3M), Clearfil AP-X(Kuraray), Tetric Ceram(Vivadent), Aelit flo(Bisco). Resistance to degradation was evaluated on the basis of the following parameters: (a) mass loss(%) - determined from pre-and post-exposure specimen weights: (b) Si loss(ppm) - obtained from ICP-AE analysis of solution exposed to specimens; and (c) degradation depth(${\mu}m$) - measured microscopically (SEM) from polished circular sections of exposed specimens. The results were as follows: 1. The sequence of the mass loss was in ascending order by AE, EL, TC, Z100. There was statistically significant difference of mass loss between AE, CL group and TC, Z100 group(p<0.05). 2. The sequence of the degree of degradation layer depth was in ascending order by AE, CL, TC, Z100. But there was no statistically significant difference of degree of degradation layer depth between AE and CL(p<0.05). 3. For the Si concentration, Z100 was the highest of all. 4. The correlation coefficient between mass loss and degradation depth was relatively high(r=0.71 p<0.05).

• Restorative Dentistry and Endodontics
• /
• v.26 no.1
• /
• pp.86-94
• /
• 2001

기존의 광중합기는 높은 광강도를 제공함으로써 광중합 복합레진을 최대한 단축된 시간내의 중합을 목표로 하였다. 이러한 높은 광강도는 복합레진의 중합깊이, 중합률면에서는 우수하나 중합 반응속도가 빠름으로 인해 중합시 응력 발생이 높아진다는 일련의 보고가 있다. 최근에는 광중합 속도를 늦춤으로써 변연적합도 및 중합시 응력 발생을 낮추는 새로운 중합방법들이 제시되고 있다. 이에 본 실험에서는 광조사 강도의 변화가 광중합 복합레진의 중합반응 과정에 미치는 영향 및 중합된 복합레진의 중합률에 대한 영향을 분석하고자 하였다. 5개의 혼합형 광중합 복합레진 (Z-100, Spectrum, Z-250, Clearfil AP-X, P-60)을 사용하였으며 중합시 적용된 광조사 강도에 따라 6개의 실험군으로 정의하였다. 실험군과 이에 따른 광조사 방법은 다음과 같다. 1군은 110mW/$\textrm{cm}^2$로 40초 중합, 2군 210mW/$\textrm{cm}^2$로 40초 중합, 3군 410mW/$\textrm{cm}^2$로 40초 중합, 4군 620mW/$\textrm{cm}^2$로 40초 중합, 5군 110mW/$\textrm{cm}^2$로 10초 중합 후 1분 뒤 620mW/$\textrm{cm}^2$로 30초 중합, 6군 210mW/$\textrm{cm}^2$로 10초 중합 후 1분 뒤 410mW/$\textrm{cm}^2$로 30초 중합하였다. 광중합시 중합 반응 양상에 관한 분석은 시차주사 열계량기를 이용하여 37$^{\circ}C$ 항온상태에서 10분간의 열흐름곡선을 기록하였다. 기록된 열흐름곡선에서 중합 반응시 나타나는 중합열 및 최대 중합열에 이르는 시간을 기록하여 중합반응 속도를 측정하였다. 중합된 복합레진의 중합률은 Fourier Transform Infrared Spectrometer(FTIR)를 이용하였으며 2mm 두께의 복합레진 하방에서의 중합률을 측정하였다. 측정된 결과는 ANOVA 및 Student-Newman-Keuls 방법을 이용하여 유의성을 검증하였다. 실험결과 다음과 같은 결론을 얻었다. 1. 광중합 복합레진 중합시 광조사 강도가 증가할수록 중합열은 증가하였으나 통계적 유의성은 보이지 않았다 (p>0.05). 2. 최대 중합열에 이르는 시간은 광조사 강도가 증가할수록 단축되었다. 이단계 중합방법을 사용한 경우 중합반응 속도를 감소시킬 수 있음을 보였다. 3. 광조사 강도가 증가할수록 중합률은 증가하였다. 이단계 중합방법을 사용한 경우 연속적인 고광강도를 사용한 경우와 유사한 높은 중합률을 보였다. 4. 중합률면에서 광중합복합레진의 중합시 400mW/$\textrm{cm}^2$ 이상의 광강도가 필요한 것으로 나타났다.