• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.4
• /
• pp.633-641
• /
• 2021

The study performed long-term performacne evaluation on the hot mix asphalt using the steel slag aggregates and Reclaimed Asphalt Pavement (RAP). The laboratory comparative evaluation was conducted between conventional Hot Mix Asphalt (HMA) which is entitled WC-2 and HMA containing steel slag and RAP which is entitled ES WC-2(R). Dynamic stability test, dynamic modulus test, and fatigue crack test were conducted during the comparative evaluation process. The dynamic stability test result showed that ES WC-2(R) was 140% higher than WC-2. It is noted that ES WC-2(R) showed no inflection point whereas WC-2 showed inflection point during the dynamic stability test which implies ES WC-2(R) has the higher moisture susceptability than WC-2. The dynamic modulus of ES WC-2(R) were 342.3%, 486.7%, and 350.0% higher than WC-2 at medium temperature of 21℃, low temperature of -10℃, and high temperature of 38℃ respectively. The test result showed that rutting resistance of ES WC-2(R) is higher than WC-2 at all temperature spectrum. The fatigue resistance of ES WC-2(R) were 31.7%, 325.3%, 899.9% higher at low stress level, medium stress level, and high stress level, respectively. The test result showed that ES WC-2(R) is higher than WC-2 at all stress levels. Based on the laboratory comparative evaluation, The in-situ scale Accelerated Pavement Test (APT) was conducted comparing WC-2 and WC-2(R). APT found that the rutting resistance of WC-2(R) was 45% higher than WC-2.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.1
• /
• pp.119-127
• /
• 2014

The application of sulfur polymer emulsion (SPE) as an acrylate substitute for semi-rigid pavement grout was evaluated, and the performance improvement by employing PVA fibers were also evaluated. The result indicated that the filling ratio of semi-rigid pavement material decreased as the fiber content increased, but it was measured to be 92~94% in every mixing condition, which satisfies the target performance, 90%. The maximum Marshall stability value of semi-rigid pavement material was measured to be 25.4 kN, which is about 4.7 times higher than the Korean Standard required for semi-rigid pavement material, 5.0 kN. The dynamic stability evaluation of semi-rigid pavement material indicated that the resistance to deformation from the wheel tracking test was improved by an SPE substitution, and in every mixing condition, the deformation converged to a constant value after 45 minutes with the same dynamic stability of 31,500 times/mm. The strain at the flexural failure was about 0.53%, which shows superior rigidity to asphalt pavements. The examination of abrasion resistance and impact resistance showed that the loss ratio was 9.8~6.0% in every mixing condition, which indicates a good abrasion resistance. Also, when fiber content ratio was 0.3%, the impact resistance was 2.82 times higher compared to plain (i.e., when fibers were not added). In the limited range of this study, an SPE substitution ratio of 30% was found to be an optimal level considering the mechanical and durability performance. In addition, it is thought that semi-rigid pavement material with superior performance could be manufactured if fiber content ratio up to 0.3% is applied depending on the purpose of use.

• International Journal of Highway Engineering
• /
• v.12 no.2
• /
• pp.17-23
• /
• 2010

Since the relatively stiff binder shows a higher tensile strength as well as higher rutting resistance, it is believed that the binder stiffness is an important factor for rutting and tensile strength of asphalt mixtures. The typical tensile property is measured by indirect tensile strength (ITS) test at $25^{\circ}C$ and the rutting resistance is most widely measured by wheel tracking (WT) test at $60^{\circ}C$. The deformation strength ($S_D$) is newly developed property to estimate rut resistance of asphalt concretes at $60^{\circ}C$. The ITS and $S_D$ are very simple to measure by static test techniques, but the WT is measured by repeated loading procedure which requires relatively longer time and more efforts. Since these three properties are highly dependent upon the binder stiffness, it may be possible to estimate one property from another. Therefore, this study investigate the possibility of estimating the rutting characteristics (measured by WT test) by ITS or $S_D$ test, and the ITS by $S_D$. Because of binder stiffness effect, in the WT estimation by ITS, a tendency was observed for the higher ITS mixture to have the lower rut depth, giving $R^2{\fallingdotseq}$0.6, on the average. The ITS estimation by $S_D$ showed $R^2{\fallingdotseq}$0.64, and the WT estimation by SD showed $R^2{\fallingdotseq}$0.84, which is highest correlation among the three. Therefore, it was concluded that there is relatively good possibility of estimating WT result by $S_D$, and even though $R^2$ is somewhat low, there is some correlation between WT and ITS.