• Journal of the Korean Ceramic Society
• /
• v.37 no.8
• /
• pp.792-798
• /
• 2000

Alumina composites reinforced with SiC whiskers only or combinded with TiC particles were prepared by hot-pressing at 1850$^{\circ}C$ for 1h. The mechanical properties and microstructures of composites were investigated in this study. By of addition either 20 vol% SiC whiskers or 20 vol% TiC particles, the flexural strength fo alumina was increased from 360 MPa to 650 MPa or 730 MPa, respectively, and the KIC was also increased from 3.5 MPa$.$m1/2 to 5.5MPa$.$m1/2 or 4.4MPa$.$m1/2, respectively. In the case of composites with 20 vol% SiC whiskers and 2 vol% TiC particles. The flexural strength and KIC showed relatively high value of 800 MPa and 5.3MPa$.$m1/2, respectively. The improvement of mechanical properties was considered to be due to both the smaller average grain size and the crack deflection.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.12 no.6
• /
• pp.329-334
• /
• 2002

The $CaTio_3$powder with perovskite structure was synthesized by mixing anatase $TiO_2$and $Ca(OH)_2$powders as starting materials, and KOH or NaOH as mineralizer, followed by hydrothermal method. The change of crystal structure, particle shape and size of the synthesized $CaTiO_3$powder was investigated with kind and concentration of mineralizer. It was found that the spherical particles of 0.7 $\mu$m were obtained when using 1N KOH and the hexahedrons particles of 3$\mu$m were obtained for the case of using 10 N KOH. With increasing KOH concentration, the particle shape was changed from sphere to hexahedrons and its size also increased. When using 1 N NaOH, the powder was consisted of 0.5~1 $\mu$m particle in size, whereas hexahedrons of 1~4 $\mu$m and whiskers more than 10$\mu$m in size was obtained for the 10 N NaOH solution. With increasing NaOH concentration, the particle shape was varied from hexahedrons to whiskers, showing the similar result with the KOH case. It was confirmed from EDS analysis that Na element, which was detected in hexahedrones was not contained in the whiskers.

• Journal of Wetlands Research
• /
• v.20 no.3
• /
• pp.272-280
• /
• 2018

Existing toxicity assessment researches were rarely studied on assessment of the abnormal behavior that affecting survival. Therefore, the study used anti-predator response of amphibians larvae, based on behavioral understanding, to assess toxicity in fullerene nanowhisker(FNW) and fullerene nanowhisker-silver nanoparticle composites(FNW-Ag). The experiment was conducted by dividing the groups not exposed to nanomaterials and exposed to nanomaterials at five concentrations(FNW: $10{\mu}g/ml$, FNW: $100{\mu}g/ml$, FNW: $500{\mu}g/ml$ FNW-Ag: $10{\mu}g/ml$, FNW: $50{\mu}g/ml$). As a result, there were no differences in normal activity except those exposed to concentrations of FNW-Ag $50{\mu}g/ml$, but there were statistically significant differences in anti-predator response except those exposed to concentrations of FNW $10{\mu}g/ml$. That is, exposed of nanomaterials does not affect ordinary movements, but analyses based on behavioral understandings have shown that it has an influence on the anti-predator response. It is therefore considered necessary to have animal behavioral analysis method performed in the assessment of eco-toxic experiment.

• Korean Journal of Materials Research
• /
• v.15 no.10
• /
• pp.644-651
• /
• 2005

The thermal analysis of $Al(OH)_3-SiO_2-AIF_3$ system was done. The thermal behaviors of components and the effect of moisture on the formation of mullite were investigated via TG-DTA and XRD analysis. The mixture of $Al(OH)_3,\;SiO_2,\;AIF_3$showed two endothermic peaks with drastic weight loss and one exothermic peak. Fluorotopaz was formed at $800^{\circ}C$ and turned into mullite completely at $1100^{\circ}C$. But the mixture $Al_2O_3$ of or dehydrated $Al(OH)_3$ and $SiO_2$ could not form mullite even at $1200^{\circ}C$ in which the crystalline phases were $\alpha-Al_2O_3$ ana cristobalite. It was found that the synthesized mullite was aciculate shaped single crystalline whisker.

• Tribology and Lubricants
• /
• v.9 no.2
• /
• pp.49-55
• /
• 1993

The dry sliding wear properties of the sintered Cu-10 wt%Sn bronze alloys reinforced with $SiC_w$ and $SiC_p$ were investigated by a pin-on-disc wear testing machine. The worn surfaces and the cross sections of the wear specimens and the wear debris were observed by SEM to study the effect of the variation of the ceramic phase contents in the composite and the wear condition on the wear behaviors. The wear of bronze matrix was dominated by the adhesive wear. The transition from mild to severe wear was found in the bronze matrix specimens at the applied load higher than 20N where the surface delamination caused the severe wear. The addition of $SiC_w$ and $SiC_p$ reinforcements in the romposites was proved to reduce the wear rate by the matrix strengthening at the applied load higher than 20N. SiC whiskers having a large length to diameter ratio which hold the deformed matrix were effective to hinder the crack propagation near the worn surface. Thus the maximum wear resistance was obtained in the composite reinforced by $SiC_w$ at the higher applied load.

• Korean Journal of Materials Research
• /
• v.14 no.9
• /
• pp.649-654
• /
• 2004

In this paper, the fracture toughness and mechanisms of failure in a random SiC-whisker/$Al_{2}O_3$ ceramic composite were investigated using in situ observations during mode I(opening) loading. $SiC_{w}/Al_{2}O_3$ composite was obtained by hot press sintering of $Al_{2}O_3$ powder and SiC whisker as the matrix and reinforcement, respectively. The whisker and powder were mixed using a turbo mill. The composite was produced at SiC whisker volume fraction of $0.3\%$. Compared with monolithic $Al_{2}O_3$, fracture toughness enhancement was observed in $SiC_{w}/Al_{2}O_3$ composite. This improved fracture toughness was attributed to SiC whisker bridging and crack deflection. $SiC_{w}/Al_{2}O_3$ composite exhibited typically brittle fracture behavior, but a fracture process zone was observed in this composite. This means that the load versus load-line displacement curve of $SiC_{w}/Al_{2}O_3$ composite from a fracture test may involve a small non-linear region near the peak load.

• Journal of Korea Foundry Society
• /
• v.21 no.6
• /
• pp.359-365
• /
• 2001

The superplastic behavior of whisker reinforced aluminum alloy matrix composites fabricated by squeeze casting as one of high pressure routes was investigated. The preforms of ${\alpha}-Si_3N_4$ and ${\beta}-SiC$ whiskers without any binder as a reinforcement were used. The matrix materials were 2024 and 7075 aluminum alloys. For the purpose of optimum superplastic condition, respectively, the whiskers volume fraction, extrusion temperature, tensile test temperature and initial strain rate were changed. Fracture surface of tested specimens were observed by SEM. By the results, it became possible to produce superplastic composites by applying only a hot extrusion process to composites obtained by the squeeze casting. The superplastic composites developed are ${\alpha}-Si_3N_4w/7075$, ${\alpha}-Si_3N_4w/2024$ and ${\beta}-SiCw/2024$ systems at high strain rate.

• Journal of the Korean Ceramic Society
• /
• v.45 no.2
• /
• pp.132-137
• /
• 2008

The main purpose of this study is enhancing the filtering efficiency, performance and durability of filter by growing SiC whiskers on cordierite honeycomb substrate. The experiment was performed by Chemical Vapor Infiltration (CVI) in order to control pore morphology of substrate. Increasing the mechanical strength of porous substrate is one of important issues. The formation of "networking structure" in the pore of porous substrate increased mechanical strength. The high pressure gas injection to the specimen showed that a little of whiskers were separated from substrate but additional film coating enhanced the stability of whisker at high pressure gas injection. Particle trap test was performed. More nano-particle was trapped by whisker growth at the pore of substrate. Therefore it is expected that the porous cordierite which deposited the SiC whisker will be the promising material for the application as filter trapping the nano-particles.

• Journal of Korea Foundry Society
• /
• v.16 no.6
• /
• pp.537-549
• /
• 1996

This study aims at investigating the correlation of microstructure and mechanical properties of the AZ91 Mg/Al borate whisker composites fabricated by squeeze csting technique with a variation of applied pressure. Microstructure observation and in-situ fracture tests were conducted on the composites to identify the microfracture process. Detailed microstructural analyses indicated that the grain refinement could be achieved with applied pressure and the little change in volume fraction on reinforcing whiskers could be carried out. It was also found clearly from in-situ observation of crack initiation and propagation that in the composite processed by the lower applied pressure, microcracks were initiated earily at whisker/matrix interfaces, thereby resulting in the drop in strength. In the composite processed by the higher applied pressure, on the other hand, planar slip lines were well developed in the matrix, and then propagated through whiskers without whisker/matrix decohesion. Thus, the effect of the applied pressure on microstructure and mechanical properties can be explained by grain refinement, increased amounts of reinforcements, and improvement of whisker/matrix interfacial strength as the applied pressure in increased.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.19 no.7
• /
• pp.1619-1629
• /
• 1995

The Al/Al$_{2}$O$_{3}$ SiC and Al/Al$_{2}$O$_{3}$/C hybrid metal matrix composites (MMCs) were fabricated by squeeze infiltration method. Uniform distribution of reinforcements were found in the microstructure of metal matrix composites. Mechanical tests were carried out under various test conditions to clearly identify mechanical behavior of MMCs, and the wear mechanism of Al/Al$_{2}$O$_{3}$/(SiC or C) hybrid metal matrix composites were investigated. The tensile strength and hardness of hybrid composites was resulted in increasing compared with those of the unreinforced matrix alloy. Wear resistance was strongly dependent upon kinds of fiber, volume fraction and sliding speed. The wear resistance of metal matrix composites was remarkably improved by the addition of reinforcements. Especially, the wear resistance of the hybrid composites of carbon fibers was more effective than in the composites reinforced with alumina and SiC whiskers of reinforcements. This was due to the effect of carbon fiber on the solid lubrication. Wear mechanisms of hybrid composites were suggested from wear surface analyses. The major wear mechanism of hybrid composites was the abrasive wear at low to intermediate sliding speed, and the melting wear at intermediate to high sliding speed.