• Journal of the Korean Society of Clothing and Textiles
• /
• v.31 no.5 s.164
• /
• pp.659-669
• /
• 2007

The purpose of this study was to investigate the degradation of silk fabrics dyed with gardenia and sappanwood by Ultraviolet Light(UV). To asses the effect of uv on dyed silk fabrics, physical and chemical properties of samples were explored. K/S value rapidly decreased with increasing exposure time. Mordanting improved ultraviolet-cut ability and the sappanwood dyed samples were superior to those of gardenia dyed in ultraviolet-cut ability. Color progressively faded away as uv exposure time increased, accordingly, $L^*,\;a^*,\;b^*$, H/VC, ${\Delta}E$ were changed. Morphological change observed with SEM represented degradation of silk fabrics from the outer fibril to the inner fibril. Tensile Strength abruptly decreased as uv exposure time increased and the mordanted samples showed higher tensile strength than the unmordanted. FT-IR analysis confirmed that main peaks at 3297 and $1704cm^{-1}$ band for silk fabric were due to N-H and C=O stretching, gardenia peaks at 1654 and $668cm^{-1}$ band representing C=O(ester), C=C(alken) and O-C=O(carboxylic acids) of crocin and sappanwood peaks at $1715cm^{-1}$ band representing C=O(cyclic keton) of brazilin appeared on the samples exposed for 14 days, but these peaks indicating colorants after 28 days of uv exposure faded away due to prolonged exposure of uv.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.45 no.4
• /
• pp.300-309
• /
• 2017

A spacecraft obtains a reaction momentum required for an orbit correction and an attitude control by exhausting a combustion gas through a small thruster in space. If the exhaust plume collides with spacecraft surfaces, it is very important to predict the exhaust plume behavior of the thruster when designing a satellite, because a generated disturbance force/torque, a heat load and a surface contamination can yield a life shortening and a reduction of the spacecraft function. The purpose of the present study is to ensure the core technology required for the spacecraft design by analyzing numerically the exhaust gas behavior of the 10 N class bipropellant thruster for an attitude control of the spacecraft. To do this, calculation results of chemical equilibrium reaction between a MMH for fuel and a NTO for oxidizer, and continuum region of the nozzle inside are implemented as inlet conditions of the DSMC method for the exhaust plume analysis. From these results, it is possible to predict a nonequilibrium expansion such as a species separation and a backflow in the vicinity of the bipropellant thruster nozzle.

• Journal of the Korean Wood Science and Technology
• /
• v.37 no.4
• /
• pp.388-396
• /
• 2009

In our study, the potential of okara as an ingredient of new bio-based adhesives was investigated for the production of fancy-veneered flooring boards. Okara was hydrolyzed by 1% sulfuric acid solution (AC) and 1% sodium hydroxide solution (AK). Phenol formaldehyde (PF) prepolymers were prepared as a cross-linker of okara hydrolyzates. Then, okara-based adhesive resins were formulated with 35% AC, 35% AK and 30% PF prepolymer on solid content basis. The adhesive resins were applied on high-density fiberboards (HDF) with the spread rate of $300g/m^2$. After that, oak fancy veneers are covered on the HDF, and then pressed with the pressure of $7kg/m^2$ at $120^{\circ}C$. The experimental variables were three mole ratios of formaldehyde to phenol (1.8, 2.1, 2.4), three assembly time (0, 10, 20 min), and two press time (90 sec, 120 sec), respectively. The fancy-veneered high-density fiberboards were tested by dry tensile strength, glueline failure by wetting and formaldehyde emission. Tensile strength of the boards exceeded the requirement of KS standard. The formaldehyde emissions were approached at the E0 level specified in KS standard. Based on these results, okara can be used as an ingredient of environmentally friendly adhesive resin systems for the production of flooring boards.

• Economic and Environmental Geology
• /
• v.56 no.6
• /
• pp.629-646
• /
• 2023

Host rock of Cheonjeon-ri petroglyph is shale belonging to the Daegu Formation of Cretaceous Gyeongsang Supergroup. The rocks were hornfelsified by thermal alteration, and shows high density and hardness. The petroglyph forms weathered zone with certain depth, and has difference in mineral and chemical composition from the unweathered zone. As the physical deterioration evaluations, most of cracks on the surface appear parallel to the bedding, and are concentrated in the upper part with relatively low density. Breakout parts are occurred in the upper and lower parts of the petroglyph, accounting for 6.0% of the total area and occurs to have been created by the wedging action of cracks crossing. The first exfoliation parts occupying the surface were 23.8% of the total area, the second exfoliations covered with 9.3%, and the exfoliation parts with three or more times were calculated as 3.4%. It is interpreted that this is not due to natural weathering, and the thermal shock caused by the cremation custom here in the past. As the ultrasonic properties, the petroglyph indicates highly strength in the horizontal direction parallel to bedding, and the area with little physical damage recorded mean of 4,684 m/s, but the area with severe cracks and exfoliations showed difference from 2,597 to 3,382 m/s on average. Physical deterioration to the Cheonjeon-ri petroglyph occurred to influence by repeated weathering, which caused the rock surface to become more severe than the inside and the binding force of minerals to weaken. Therefore, it can be understood that when greater stress occurs in the weathered zone than in the unweathered zone, the relatively weathered surface loses its support and exfoliation occurs.

• Journal of Conservation Science
• /
• v.26 no.3
• /
• pp.295-310
• /
• 2010

Since wall paintings in Maitreya Hall of Geumsan-sa temple had displayed a serious state of damage and deterioration, a detailed examination such as structural analysis of the wall, cause of damage, and the state of deterioration have been thoroughly conducted before the conservation treatment has commenced. The most seriously deteriorated part of the wall paintings was the south wall of the building in particular in its painted and surface layer. The painted layer had formed its own layer of thick, which has been separation from the surface layer. As such problem developed the whole surface layer has been separated from the wall. The problem has been caused by two reasons: 1. the heavy weight of the roof section and it caused cracks and damage on the wall; 2. the loss of function of consolidating material and it caused discolouring and the separation of surface layer from the wall. The cause of damage on the painted and surface layers can be assumed in two ways: 1. its surrounding environment such as the change of temperature and humidity level and ultraviolet rays ; 2. the loss of mechanical function of consolidating material, synthetic resin which had been applied in the past conservation treatment. The separation of layers from the wall and cracks was caused by the mistake in choosing an applicable consolidating material and dismantling technique which had ignored a different characteristic of the wall painting of Korean buddhist temples.

• Journal of Life Science
• /
• v.14 no.1
• /
• pp.45-50
• /
• 2004

To investigate the effect of the cell wall on the pigmentation and branching in Aspergillus nidulans, ultrastructure of cell wall in suppressor mutant of the null pigmentation (SU-NPG, SU602) has been examined. Scanning electron microgrphs (SEM) revealed that the most outer layer of conidia wall peeled off in SU-NPG on day 6 from the complete conidiation. They also showed that hyphal growth and branching were not well developed in SU-NPG. Transmission electron micrographs (TEM) showed that the plasma membrane was not crenulated and the hyphal wall was thick in SU-NPG. These results indicated that the ultrastructure of cell wall in SU-NPC might be modified. Cytochemical analysis showed that the cell wall in SU-NPG was differentiated into Cl, C3, C2 and C4 layer in conidia and H1, H3, H2 and H4 layer in hyphae. C3 layer and H3 layer existed in SU-NPG. The increment of the diameter in SU-NPG hyphae might be caused by the thickness of H3 layer. These results suggest that SU-NPG may have an immature but the differentiated structure for the pigmentation in cell wall.

• Journal of Conservation Science
• /
• v.26 no.4
• /
• pp.445-458
• /
• 2010

The deterioration and structural damage such as exfoliation, cracks, and separation of painted layer on the wall paintings of Maitreya Hall in Geumsan-sa temple have been accelerated since it was re-positioned to the original place after the dismantling from the building in 1993. The examination of which result and analysis described in this study, is a preliminary survey for establishing conservation plan of the wall paintings. It aimed at the understanding of the physical and chemical characteristics of the materials applied in the 1993 conservation. The research focused on the south walls which displayed the worst condition compared to other walls. Samples for the examination for the understanding of micro-structure, chemical composition, cristalisation, and particle distribution, were collected for finishing, middle, and consolidated layers of the walls between pillars and the ones between brackets. Those samples were collected from separated fragments of the walls. The sample analysis displayed that: 1. the 1993 conservation used the similar type of weathered soil as the original for the finishing layer, and such soil and sand for the middle layer; 2. those walls are composed of a group of mineral particles which are relatively equal in size and shape and in their distribution; 3. the mineral particles were cohered forming solid aggregate due to the application of acrylic resin for the reinforcement on the wall. The main composition of crystalisation on the first and the second reinforcement layers of the back walls were lime plaster ($CaSO_4{\cdot}2H_2O$). The overall examination confirmed that the priority of the future conservation treatment should be given to the removal of the first and the second layers of reinforcement and the treatment on the back walls which were partially consolidated.

• Corrosion Science and Technology
• /
• v.8 no.2
• /
• pp.53-61
• /
• 2009

In this study, both evaluations by visual imaging for exterior view of coating and by EIS were executed for epoxy primer coated specimens deteriorated by accelerated test, and comparison and analysis were carried out for 2 evaluation methods. In the comparison between total damaged area ratio acquired by image processing method and deterioration point, higher deterioration points were appeared for rusted specimens than for non-rusted specimens. It is attributed that deterioration point per unit area ratio given for rust is higher than for peeling. In the comparison between total damaged area ratio and EIS result, impedance of coating was largely decreased as about TEX>$10^4{\Omega}{\cdot}cm^2$ or less when rust area ratio is more than about 0.1%, and blistering area ratio is more than about 3%. Charge transfer resistance ($R_{ct}$) and double layer capacitance ($C_{dl}$) values were appeared for all specimens except 2 ones, which shows that water is accumulated and steel substrate is corroded at coated film-steel interface. In the comparison between deterioration point and EIS result, more than 10 points as deterioration point were given for specimens of below $10^6{\Omega}{\cdot}cm^2$ of impedance at low frequency. For specimens deteriorated by NORSOK cyclic test, impedance was lowest of all, though deterioration point was not high. It is thought to be attributed that coating system and accelerated deterioration condition of cyclic tested specimens were different from those of main specimens. From the result, it is thought that coating resistance can be relatively more decreased than deterioration degree estimated from exterior view under more severe corrosion environment or in the present of more complex deterioration factors.

• Journal of Conservation Science
• /
• v.16 s.16
• /
• pp.77-88
• /
• 2004

This study evaluates the occurrences, phyfical weathering and biological deterioration on rock properties during the dissection process an object of stone pagoda in the Mireuksaji temple site. For restoration and conservation, all kinds of rock properties are carried out detailed scientific investigation and diagnosis. Constituting rocks of the pagoda composed mainly of equi-granular medium grained biotite that rock properties presumed to be use about 3,000 materials. Main external properties of the pagoda are total 446 materials, and the rock properties under the concentration load on the each floors occurred with overlapping fracture, weathering and deteriorations. The 84 materials show highly degraded about $18.8\%$ among the external properties. Representative physicochemical deteriorations are fracture, loss, break, exfoliation, degradation, grain shaped dissolution, relief surface, discoloration and hydroxide precipitates, in this study, the deterioration state of each properties give a precisely description and analysis. Coverage of lichen and algae on the rock surface represented about $85\%$. As the some properties, biological contaminants withered up when spray rock surface with diluted cleaning chemicals. Results of the study are utilized an application for restoration system and detailed investigation during the dissection process of stone cultural properties.

• Journal of the Microelectronics and Packaging Society
• /
• v.19 no.1
• /
• pp.55-60
• /
• 2012

In order to develop electroless-plated Nickel Phosphate (Ni-P) as a contact material for high efficient low-cost silicon solar cells, we evaluated the effect of ambient thermal annealing on the degradation behavior of interfacial adhesion energy between electroless-plated Ni-P and silicon solar cell wafers by applying 4-point bending test method. Measured interfacial adhesion energies decreased from 14.83 to 10.83 J/$m^2$ after annealing at 300 and $600^{\circ}C$, respectively. The X-ray photoelectron spectroscopy analysis suggested that the bonding interface was degraded by environmental residual oxygen, in which the oxidation inhibit the stable formation of Ni silicide phase between electroless-plated Ni-P and silicon interface.