• Magazine of the Korea Concrete Institute
• /
• v.11 no.4
• /
• pp.39-45
• /
• 1999

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.13 no.1 s.53
• /
• pp.97-105
• /
• 2009

Development and use of blended cement concrete is gaining more importance in the construction industry with reference to durability mainly due to the pore refinement and reduction in permeability. Cracks play a major role on important parameters like permeability, rate of chloride ingress, compressive strength and thus affect the reinforcement corrosion protection. Furthermore, when a crack occurs in the cover concrete, the corrosion of the steel reinforcement may be accelerated because the deterioration causing factors can pass through the crack. In recent years the effect of cracking on the penetration of concrete has been the subject of numerous investigations. Therefore assessing the service life using blended concrete becomes obviously in considering the durability. In the present study, the corrosion assessment of composite concrete beams with and without crack with of 0.3mm using OPC, 30% PFA, 60% GGBS, 10% SF was performed using half cell potential measurement, galvanic potential measurement, mass loss of steel over a period of 60days under marine environmental conditions and the results were discussed in detail.

• Journal of the Korea Concrete Institute
• /
• v.17 no.5 s.89
• /
• pp.743-750
• /
• 2005

High performance concrete containing silica fume for use in bridge deck overlay emerged as a viable type of bridge deck overlay that economic advantage in construction. They have gained acceptance in Europe, America and Canada in a relatively short time due to their low cost. In this study, high-performance concretes containing silica fume were tested and evaluated in the laboratory to assess their applicability for use in bridge deck overlay. It was conducted with experiments of mechanical and durability characteristics in compressive strength, flexural strength, chloride permeability, abrasion resistance, repeated freezing and thawing cycles and deicing salt scaling resistance. Laboratory test result describe that high-performance concrete containing silica fume for bridge deck overlay application shows most outstanding capacity.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.661-664
• /
• 2008

The structure which is located in special surroundings like ocean-environment is physically and chemically eroded by seawater or salt damage, and then concrete-structure becomes deteriorated by iron corrosion and swelling pressure which leads to remarkably decline durability due to cracks and exploitation. As a measure against salt damage, it is actively being examined to use the blended cement that controls salt damage and fix chloride in the process of hydration. In this study, therefore, to examine the property of marine concrete added admixture, marine concrete is manufactured by adding high-strength admixture(omega2000) by 0, 5, 10, and 15% to low heat-blended cement. Then it shows that the compressive strength of manufactured marine cement tends to increase and chloride penetration resistance improves.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.14 no.4
• /
• pp.160-168
• /
• 2010

Recently, there are a lot of researches related to the high-fluidity concrete (HFC) with field applications. However, most applications and studies are with concretes with high strength level so there are little studies about durability evaluations such as chloride ion penetration properties with normal strength concrete. Therefore, to evaluate the durability of HFC with normal strength level, this study performed the chloride ion penetration test and observed the micro pore distribution with normal strength HFC which contains limestone powder. Experimental results showed that most micro-pores have diameters between 0.005 to 0.05 ${\mu}m$ with HFCs using limestone powder and the average diameter becomes larger with the increase of limestone powder content. Also, it was shown that, with the increase of the limestone powder content, penetration depth and diffusion coefficient of chloride ion increased and diffusion coefficient had good relationships with compressive strength and average pore diameter with the coefficient of determination over 0.90.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.1
• /
• pp.117-124
• /
• 2010

The aggregate, which does not satisfy the standard of KS F 2573, was selected for this investigation. The 28day compressive strength of recycled aggregate concrete without pozzolan material was 21.7MPa, which was less than the strength of concrete made with crushed stone. However, the compressive strength at 28 days was improved by mixing early rapid hardening cement to the cement at the weight ratio of 2.5%. Furthermore, the compressive strength at 91 days and 180 days increased significantly by adding fly ash, slag powder, and diatom powder. The tensile strength of recycled aggregate concrete with pozzolan material also increased about 40% compared to the general concrete. Futhermore, the shrinkage and creep of recycled aggregate concrete with fly ash and slag powder was a little decreased that of recycled aggregate concrete with fly ash and diatom powder. Relationship between compressive strength and creep coefficient was shown to the linear relation like as ${\sigma}_c=-30CF+404$.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.8 no.2
• /
• pp.185-194
• /
• 2004

In recent years, construction company makes inroads into the world construction market, and receives the order of extra-large concrete structure under marine environment in south-east asia specially. At this point of time, to enhance the quality of concrete, we research the High Strength Concrete (HSC) containing mineral admixtures. In this study, therefore, HSC with various combination of ordinary portland cement(OPC), blast-furnace slag(SG), silica fume(SF), and expansion admixture(SS) are cured 23 and $35^{\circ}C$ considering the site weather, and are cured in water for 3, 7 or 56 days respectively. Test results show that the HSC cured at $35^{\circ}C$ gains higher early-age strength but eventually gains lower later-age strength compare with the HSC cured at $23^{\circ}C$. Especially, HSC with combination of OPC+SG+SF+SS or OPC+SG+SF show very excellent resistance of chloride penetration. The permeability of HSC was therefore enhanced as because of containing the proper content of SG, SF, and SS and making dense micro-structure of HSC.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.16 no.6
• /
• pp.113-123
• /
• 2012

The technology developed for the decrease of applying loads and self-weight of a structure is to improve conventional Foam Cement Banking Method (FCB) by applying mixed slurry of bottom ash, cement and foams. Since the foam-mixed concrete, which is a major material of the Bottom ash-mixed Light weight concrete Banking method (BLB) developed, contains mineral admixture such as cement, the behavior shows time-dependent deformation and deterioration of durability due to environmental exposure. Thus, this study is subject to figure out the characteristics of long-termed behavior and durability of the developed method by carrying out experiments for schemed parameters, which are considered to be factors affecting mainly on concrete's characteristics from mechanical analysis. As results of tests, it was found that the developed concrete offers higher resistance than conventional foamed concrete in terms of long-termed behaviors associated with drying shrinkage and creep, and durability problems of freeze-thaw and carbonation processes, especially with addition of bottom ash.

• Resources Recycling
• /
• v.23 no.3
• /
• pp.13-20
• /
• 2014

Nowadays, due to the development of industrial and civil engineering technology, enlargement and diversification of concrete structures are being tried. At the same time, the hydration heat generated during the construction of large structures lead to thermal crack, which is occurs causing a problem that durability degradation. In this paper, in order to study the durability and reducing hydration heat of concrete according to the types of cement, that is ordinary portland cement, fly ash cement mixed with a two-component, ternary blend cement mixed with fly ash and blast furnace slag and low heat cement concrete are produced, and compare and analyze the results using property, durability and hydration characteristics, ternary blend cement is appeared to be the most excellent in durability and reduction of hydration heat, and it was determined suitable for construction of mass concrete and requiring durability.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.2 no.3
• /
• pp.247-254
• /
• 2014

The present study prepared lightweight foam-soil concrete mixtures classified into three groups. Considering the sustainablility, workability, and compressive strength development of such concrete, high-volume supplementary cementitious materials (SCMs) were used as follows: 20% cement, 15% fly ash, and 65% ground granulated blast-furnace slag. As main test parameters selected for achieving the compressive strength of 1MPa and dry density of $1,000kg/m^3$, the unit solid content (dredged soil and binder) ranged between 900 and $1,807kg/m^3$, and soil-to-binder ratio varied between 3.0 and 7.0. Test results revealed that the flow of the lightweight foam-soil concrete tended to decrease with the increase of unit soil content. The compressive strength of such concrete increased with the increase with the unit binder content, whereas it decreased as soil-to-binder ratio increased, indicating that the compressive strength can be formulated as a function of its dry density and soil-to-binder ratio.