• 소성∙가공
• /
• 제19권6호
• /
• pp.378-386
• /
• 2010

Nowadays there has been great interest in using heat treated cast material for press dies due to several advantages like reduction in die production costs. However, in hot press forming processes H13 forged tool steel is mostly used. Cooling performance of dies in hot press forming processes is considered as an important factor of study and also the IHTC parameter between cast material die and sheet metal should be considered as an essential. In the present study, the IHTC was calculated for the sheet metal in the hot press forming process with cast and forged material dies. The temperature measurements were performed for the sheet metal, casting and forged material dies by applying various contact pressure in hot press forming. IHTC was calculated and studied by adopting the inverse heat convection method in DEFORM-2D. Each IHTC was considered as a function of contact time and contact pressure. The experimental data were compared with calculated data obtained from the proposed equation and references.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2009년도 춘계학술대회 논문집
• /
• pp.334-336
• /
• 2009

An elastic-plasticity model during the austenitic decomposition was derived and implemented to incorporate the two important deformation behaviors observed during the phase transformations: the volumetric strain and transformation induced plasticity due to the temperature change and phase transformation. To obtain transformed phase volume fractions during cooling, the fourth order Runge-Kutta method was used to solve the Kirkaldy's phase kinetics model which is function of temperature, austenitic grain size and chemical composition. The volumetric strain was calculated by considering the densities of constituent phases, while the transformation induced plasticity was based on the micro-plasticity due to the volume mismatch between soft austenitic phase and other harder phases. The constitutive equations were implemented into the implicit finite element software and a simple boundary value problem was chosen as a model problem to validate the effect of transformation plasticity on the deformation behavior of steel under cooling from high temperature. It was preliminary concluded that the transformation plasticity plays a critical role in relaxing the developed stress during forming and thus reducing the magnitude of springback.

• 대한금속재료학회지
• /
• 제47권10호
• /
• pp.667-674
• /
• 2009

High temperature wear of STD 61 tool steels sliding against the Al-9%Si coated steels used for hot press forming has been studied in comparison with that of the tool steels sliding against the uncoated steels. Wear tests have been performed using a pin-on-disc configuration under an applied normal load of 50N for 20 min with heating the coated and uncoated steels up to 800$^{\circ}C$. It was found on the worn surface of the STD 61 tool steels sliding against the Al-9%Si coated steels that the formation of the glazed layers containing Al transferred from the coated tribopair may contribute to a reduction of the coefficient of friction, and detachment in part occur due to delamination wear, resulting in higher specific wear rate. On the other hand the Fe-oxide wear debris entrapped on the softer surface of the uncoated steels can act as a tribosurface, leading to decreased adhesive wear of the STD 61 tool steels, resulting in a lower specific wear rate.

• Composites Research
• /
• 제35권2호
• /
• pp.75-79
• /
• 2022

본 연구에서는 충격에 의해 파손된 열가소성 유리 섬유 강화 복합재료의 재성형을 통한 물성변화를 조사하였다. 복합재료 시편은 유리섬유 부직포와 폴리프로필렌 필름을 이용하여 핫 프레스 압축 성형 공정을 통해 제작하였다. 총 3번의 낙하 충격 테스트를 진행하였으며, 시편의 물성을 확인하기 위하여 인장시험, 굽힘시험, 낙하충격시험, 시차주사열량계, 주사전자현미경 측정을 진행하였다. 그 결과, 재활용 단계가 반복될수록 결정화도, 인장강도, 탄성계수, 굴곡강도는 증가하였으나 충격특성은 크게 감소하였다.

• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2004년도 학술대회지
• /
• pp.347-351
• /
• 2004

[ $Si_3N_4$ ] composites have been extensively studied for engineering ceramics, because it has excellent room and high temperature strength, wear resistance properties, good resistance to oxidation, and good thermal and chemical stability. In the present work, carbon short fiber reinforced $Si_3N_4$ ceramics were fabricated by hot press method in $N_2$ atmosphere at $1800^{\circ}C$ using $Al_2O_3\;and\;Y_2O_3$ as sintering additives. Content of carbon short fiber was $0\%,\;0.1\%\;and\;0.3\%$. The composites were evaluated in terms of density, flexural strength and elastic modulus through the 3-point bending test at room temperature. Also, The wear behavior was determined by the pin on disk wear tester using silicon nitride ball. Experimental density and flexural strength decreased with increasing content of carbon fiber. But specific modulus increased with increasing content of carbon fiber. In addition, friction coefficient and specific wear loss decreased with increasing content of carbon short fiber by reason of interfacial defects between matrix and fiber.

• 폴리머
• /
• 제38권5호
• /
• pp.645-649
• /
• 2014

사출성형품의 잔류응력 형성의 원인은 사출성형공정 중 재료가 받는 높은 온도변화와 전단응력이다. 케미컬 크랙킹 테스트는 잔류응력을 측정하는 방법 중의 하나이며 크랙은 잔류응력의 크기에 따라 형성된다. 본 연구에서는 시편이 받고있는 응력과 케미컬 크랙킹과의 관계를 연구하였다. 변형지그를 설계하고 이를 이용하여 시편에 변형을 주어 응력을 가하였다. 시편은 폴리카보네이트를 이용하여 핫 프레스로 제작하였고 시편의 제작 중에 형성된 잔류응력을 제거하기 위해 어닐링을 하였다. 시편을 변형지그에 고정시키고 시편에 크랙을 유도하기 위해 이를 솔벤트에 담궜다. 솔벤트는 tetrahydrofuran과 methyl alcohol을 이용하여 제조하였다. 시편에서 변형에 따라 응력이 증가할수록 크랙의 빈도수와 밀도가 증가하였다. 본 연구의 결과는 케미컬 크랙킹 방법으로 폴리카보네이트 사출성형품의 잔류응력을 정량적으로 측정하는데 활용될 수 있다.

• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2004년도 학술대회지
• /
• pp.266-270
• /
• 2004

SiC materials have been extensively studied for high temperature components in advanced energy system and advanced gas turbine because it has excellent high temperature strength, low coefficient of thermal expansion, good resistance to oxidation and good thermal and chemical stability etc. However, the brittle characteristics of SiC such as low fracture toughness and low strain-to fracture still impose a severe limitation on practical applications of SiC materials. For these reasons, SiC/SiC composites can be considered as a promising for various structural materials, because of their good fracture toughness compared with monolithic SiC ceramics. But, high temperature and pressure lead to the degradation of the reinforcing jiber during the hot pressing. Therefore, reduction of sintering temperature and pressure is key requirements for the fabrication of SiC/SiC composites by hot pressing method. In the present work, monolithic Liquid Phase Sintered SiC (LPS-SiC) was fabricated by hot pressing method in Ar atmosphere at $1800^{\circ}C$ under 20MPa using $Al_2O_3,\;Y_2O_3\;and\;SiO_2$ as sintering additives in order to low sintering temperature and sintering pressure. The starting powder was high purity $\beta-SiC$ nano-powder with all average particle size of 30mm. The characterization of LPS-SiC was investigated by means of SEM and three point bending test. Base on the composition of sintering additives-, microstructure- and mechanical property correlation, tire compositions of sintering additives are discussed.

• Composites Research
• /
• 제35권3호
• /
• pp.182-187
• /
• 2022

본 논문은 다층 PCB에 사용되는 프리프레그의 물성을 파악하여 제시한 두께 실험식을 통해 PCB의 두께를 예측하기 위한 연구를 수행하였다. 프리프레그는 물성과 동박 잔존율에 의해서 PCB 제작시 두께가 감소하기 때문에 두께 실험식을 통한 정확한 PCB의 두께 예측이 필요하다. 두께 실험식에 사용되는 프리프레그의 밀도를 파악하기 위해 질량 및 두께를 측정하여 밀도를 도출하였다. 이후 CCL을 제작하기 위해 프리프레그와 동박을 적층하여 핫 프레스기를 사용하였고 광학현미경과 마이크로미터를 사용하여 두께를 측정하였다. 또한 동박 잔존율에 따른 두께 변화를 측정하기 위해 회로밀도를 다르게 구성하여 8층 PCB를 설계하였고 두께 측정 결과와 두께 실험식으로 도출된 두께를 비교하여 두께 실험식을 검증하였다. 비교 결과 CCL의 경우 2.56%, 다층 PCB의 경우 4.48%의 오차를 보였고 이를 통해 두께실험식의 신뢰성을 확인하였다.

• Composites Research
• /
• 제37권3호
• /
• pp.190-196
• /
• 2024

분리판은 바나듐 레독스 흐름전지(VRFB) 스택 내 셀의 전기적 통로 및 구조적 지지 역할 수행하는 매우 중요한 부품 중 하나이다. 흑연 소재는 전기 전도성이 뛰어나 분리판에 주로 사용되지만, 셀 스택에서 전극과 분리판 사이에 높은 계면 접촉 저항(ICR)이 발생하여 VRFB의 성능에 심각한 제한이 존재한다. 본 연구에서는 ICR의 한계를 해결할 수 있는 일체형 전극-분리판 조립체를 개발하는 것을 목표로 하였다. 일체형 조립체는 핫 프레스 방법을 활용하여 열가소성 및 열경화성 폴리머와 단일 탄소 펠트를 사용하여 제작하였다. 실험 결과, 일체형 조립체가 연속적인 전기 경로로 인해 감소된 전체 저항을 나타냄을 확인하였다. 또한, 충/방전 셀 테스트 결과에서 일체형 조립체는 향상된 셀 성능을 보여주었다. 따라서 개발된 일체형 전극-분리판 조립체는 기존의 분리판 및 전극 조립체를 대체할 수 있을 것으로 판단된다.