• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.241-242
• /
• 2012

산화아연 씨앗층을 졸-겔 스핀코팅법으로 석영기판위에 증착시킨 후, 수열합성법을 이용하여 갈륨의 양을 0에서 2.0 at.% 으로 변화를 주어 갈륨이 도핑된 산화아연 나노막대를 성장하였다. 산화아연과 갈륨이 도핑된 산화아연 나노막대의 구조적 광학적 특성을 조사하기 위해 field-emission scanning electron microscopy, X-ray diffraction (XRD), photoluminescence (PL), 그리고 ultraviolet-visible spectroscopy를 이용하였다. 일정한 산화아연과 갈륨이 도핑된 산화아연 나노막대는 육각형형태로 성장하였다. XRD 데이터로부터, 산화아연과 갈륨이 도핑된 산화아연 나노막대의 스트레스는 각각 -0.022 (0 at.%), 0.097 (0.5 at.%), 0.165 (1.0 at.%), 0.177 (1.5 at.%), 0.182 GPa (2.0 at.%) 였다. PL 스펙트라에서 얻어진 반가폭(The full width at half maximum)은 갈륨의 양이 0에서 2.0 at.%로 증가함에 따라 127에서 171 meV로 증가하였다. Urbach 에너지는 68 (0 at.%), 97 (0.5 at.%), 108 (1.0 at.%), 104 (1.5 at.%), 127 meV (2.0 at.%)였다.

• Journal of Korean Ophthalmic Optics Society
• /
• v.5 no.1
• /
• pp.1-6
• /
• 2000

This study was to calculate spot size, focus shift and optical focus by use of OSLO when 3 wavelength, ${\omega}{\upsilon}_1=0.588{\mu}$, ${\omega}{\upsilon}_2=0.486{\mu}$ and ${\omega}{\upsilon}_3=0.656{\mu}$ in composite lens optics system & ocular optical system were respectively here, Entrance Beam Radius(mm) 1 mm, Field angle(deg) 5.7296e-0.5 mm, Image Aperture 0.053055 mm, Exit Aperture 0.903711 mm, Reflective focal length 25.181544 mm, Petzval radius -19.21839 mm, n = 1.523. It was found that a range of spot size was 0.002 mm~0.07 mm when a range of back curvature radius was 1 mm~30 mm, and 0.0005 mm~0.002 mm when of it more than 50 mm. Focus shift, 50 mm a range 3 kinds of lens was small, and it saw that of all tendency was high up to 1 mm~15 mm and up to 25 mm beyond that limits, it was going down and then going up again, optical focus 100 mm lens was best and the value when optimization with this lens was $60{\pm}1mm$.

• Applied Chemistry for Engineering
• /
• v.24 no.3
• /
• pp.320-326
• /
• 2013

In this study, various polyimide films were synthesized via low temperature cure in order to understand changes in their physical properties when using 4,4'-oxydianiline (ODA) as a diamine and dianhydride molecules with different backbones on a single diamine such as 4,4'-Oxydiphthalic anhydride (ODPA), 4,4-hexafluoroisopropylidene diphthalic dianhydride (6FDA), and 3,3', 4,4'-benzophenone tetracarboxylic dianhydride (BTDA). After the synthesis of poly(amic acid), polyimide films were fabricated by adding 1,4-diazabicyclo [2.2.2]octane (DABCO), a low-temperature catalyst, at various wt% to poly(amic acid)s. Changes of optical and thermal properties were compared and analyzed between polyimide films without catalyst and polyimide films with catalyst by FT-IR, UV-Vis transmittance, DSC/TGA, and WAXD analysis. Wide-angle X-ray diffraction (WAXD) analysis revealed that the mean intermolecular distance decreased with the use of a catalyst by the type of dianhydride. Thus, while the optical properties of the films improve by a low-temperature cure performed using a catalyst, their thermal properties decrease. These changes can be explained by the changes in the morphological structure of the films triggered by a catalyst-induced reduction in the mean intermolecular distance. Moreover, the results show that the type of dianhydride determines the degree of change in the optical and thermal properties in each types of polyimide, demonstrating that changes in the optical and thermal properties are directly associated with the backbone of the polyimide structure.

• 한국신재생에너지학회:학술대회논문집
• /
• 2011.11a
• /
• pp.50.2-50.2
• /
• 2011

염료감응형 태양전지는 기존의 실리콘 태양전지에 비해 저렴한 가격과 다양한 날씨 조건에서도 태양광과의 반응성이 안정하다는 여러 가지 장점을 갖고 있다. 하지만 광전 변환 효율이 기존의 실리콘 태양전지에 비해 현저히 떨어진다는 문제점과 장기적으로 안정하지 못하다는 단점을 가지고 있다. 이러한, 염료감응형 태양전지에서 크게 광전 변환 효율을 향상시킬 수 있는 재료는 염료, $TiO_2$와 같은 반도체 산화물전극 재료, 전해질이다. 이 중 $TiO_2$의 특성 및 크기는 염료감응형 태양전지의 효율에 영향을 미친다. 염료감응형 태양전지의 광전 변환 효율을 증가시키기 위해서 $TiO_2$는 넓은 비표면적, 높은 전자의 이동성 및 태양광과의 우수한 반응성을 가져야 한다. Microwave hydrothermal 방법에 의해 제조된 hollow $TiO_2$를 염료감응형 태양전지에 적용시킬 경우 기존의 $TiO_2$의 광흡수 반응이 200~400 nm 사이에서 발생하는 반면, hollow $TiO_2$의 광흡수 반응은 기존의 UV 영역인 200~400 nm 뿐만 아니라 가시광 영역인 400~460 nm 에서도 광흡수 반응이 가능하기 때문에 염료감응형 태양전지에서 광전 변환효율을 증가 시킬 수 있을 것으로 기대된다. 또한, microwave hydrothermal법에 의해 제조된 hollow $TiO_2$는 150-200 nm의 크기를 갖으며 20-30 nm 크기의 $TiO_2$ particle들로 이루어져 있다. hollow $TiO_2$ (150-200 nm)를 기존의 $TiO_2$ (10-20 nm) 층 위에 올려 염료감응형 태양전지의 electrode에 적용할 경우 기존의 $TiO_2$ 단층을 이용한 것보다 우수한 light-scattering 효과를 갖게 되어 광전 변환 효율 증가에 긍정적인 영향을 미칠 것이다. 본 연구에서는 hollow $TiO_2$의 광학적 특성 및 결정성이 염료감응형 태양전지에 미치는 영향을 조사하였다. hollow $TiO_2$의 광학적 특성 및 결정성의 변화를 위하여 microwave hydrothermal 법의 합성 온도 및 합성시간에 변화를 주었다. hollow $TiO_2$의 광학적 특성은 UV-visible spectrometer를 이용하여 조사하였으며, hollow $TiO_2$의 형상과 결정학적 특성은 TEM과 SEM 그리고 X선 회절 분석을 이용하여 관찰되었고, hollow $TiO_2$의 비표면적 측정은 BET 측정법을 이용하였다. 또한 염료감응형 태양전지 cell을 제작하여 $100mW/cm^2$(AM 1.5G) 기준에서 광전 변환 효율을 측정하였다.

• Korean Journal of Microbiology
• /
• v.55 no.2
• /
• pp.143-148
• /
• 2019

The synthesis of captopril as an important chiral drug in commerce needs expensive resolution process of racemic mixture. Microorganisms, producing a thermostable esterase that catalyzes the stereo-selective hydrolysis of methyl DL-${\beta}$-acetylthioisobutyrate (DL-ester) to D-${\beta}$-acetylthioisobutyric acid (DAT) were screened from soils. Among the strains tested, strain No CJ-317 and strain No CJ-187 with highest activity were selected as the best DAT producer. The newly isolated microorganisms were identified respectively, as Klebsiella pneumoniae and Pseudomonas putida. The cell activity of esterase from K. pneumoniae CJ-317 and P. putida CJ-187 were showed an optimal reaction activity at $75^{\circ}C$ and $60^{\circ}C$, respectively. Also the cell activity of K. pneumoniae CJ-317 was stable up to $80^{\circ}C$ for 1 h, while that of P. putida CJ-187 was not over $60^{\circ}C$. By varying the concentration of DAT in the reaction mixture, the cell activity of P. putida CJ-187 showed about 55% and 80% of product inhibition in the presence of 2.5% (w/v) and 5.0% of DAT respectively. K. pneumoniae CJ-317 had less product inhibition than P. putida CJ-187 by about 35% and 44% at the same concentrations respectively. The esterase of newly isolated K. pneumoniae CJ-317 could be useful for the stereo-selective hydrolysis of DL-ester to DAT.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.154-154
• /
• 2015

최근에 백색 발광 소자와 조명 장치에 응용하기 위하여 희토류 이온이 도핑된 산화물 형광체의 제조에 많은 노력이 경주되고 있다. 본 연구에서는 $Eu^{3+}$ 이온이 첨가된 $La_2MoO_6$ 형광체를 고상반응법을 사용하여 합성하였다. $La_2MoO_6:Eu^{3+}$ 형광체 분말 시료는 활성체 $Eu^{3+}$ 이온의 함량을 0, 0.01, 0.05, 0.10, 0.15, 0.2 mol로 변화시켜 볼밀과 건조 작업을 거쳐 $400^{\circ}C$에서 3시간 동안 하소 공정과 $1100^{\circ}C$에서 5시간 동안 소결 공정을 수행하여 합성하였다. 흡광 스펙트럼의 경우에, 양이온 $Eu^{3+}$와 음이온 $O^{2-}$ 사이의 전하 전달 밴드에 의해 250~370 nm 영역에 폭넓게 발생한 흡광 신호와 370~450 nm 파장 영역에 발생한 다수의 약한 $Eu^{3+}$ 이온의 흡광 스펙트럼으로 구성되었다. 발광 스펙트럼의 경우에, 파장 333 nm로 여기시켰을 때, 620 nm에서 최대 세기를 갖는 적색 발광 신호, 593 nm의 주황색 발광 스펙트럼과 704 nm의 적색 발광 스펙트럼이 관측되었다. 620 nm에서 관측된 적색 발광 신호의 세기는 활성체 이온 $Eu^{3+}$의 함량이 0.20 mol일 때 최대이었다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.10a
• /
• pp.15.2-15.2
• /
• 2011

비휘발성 저항 메모리소자인 resistance random access memory (ReRAM)는 간단한 소자구조와 빠른 동작특성을 나타내며 고집적화에 유리하기 때문에 차세대 메모리소자로써 각광받고 있다. 현재, 이성분계 산화물, 페로브스카이트 산화물, 고체 전해질 물질, 유기재료 등을 응용한 저항 메모리소자에 대한 연구가 활발히 진행되고 있다. 그 중 ZnO를 기반으로 하는 amorphous InGaZnO (a-IGZO) 박막은 active layer 로써 박막트랜지스터 적용 시 우수한 전기적 특성을 나타내며, 빠른 동작특성과 높은 저항 변화율을 보이기 때문에 ReRAM 에 응용 가능한 재료로써 기대되고 있다. 또한 가시광선 영역에서 광학적으로 투명한 특성을 보이기 때문에 투명소자로서도 응용이 기대되고 있다. 본 연구에서는 indium tin oxide (ITO) 투명 전극을 적용한 ITO/a-IGZO/ITO 구조의 투명 소자를 제작하여 저항 메모리 특성을 평가하였다. Radio frequency (RF) sputter를 이용하여 IGZO 박막을 합성하고, ITO 전극을 증착하여 투명 저항 메모리소자를 구현하였고, resistive switching 효과를 관찰하였다. 또한, 열처리를 통해 a-IGZO 박막 내의 Oxygen vacancy와 같은 결함의 정도에 따른 on/off 저항의 변화를 관찰할 수 있었다. 제작된 저항 메모리소자는 unipolar resistive switching 특성을 보였으며, 높은 on/off 저항의 차이를 유지하였다. Scanning electron microscope (SEM)을 통해 합성된 박막의 형태를 평가하였고, X-ray diffraction (XRD) 및 transmission electron microscopy (TEM)을 통해 결정성을 평가하였다. 제작된 소자의 전기적 특성은 HP-4145 를 이용하여 측정하고 비교 분석하였다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.18 no.2
• /
• pp.76-80
• /
• 2008

In this study, we synthesized ATO films using RF magnetron sputtering method consisted of $SnO_2$ target added Sb of 6 wt% and investigated the effect of $O_2$ on structural, electrical, and optical properties of ATO films. As a result, in case of $O_2$/Ar ratio of 0.11, we obtained ATO films exhibit the properties such as the resistivity about $8{\times}10^{-3}[{\Omega}-cm]$, the transmittance of 85.17%, and retile structure.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.29 no.6
• /
• pp.379-382
• /
• 2019

Synthesis of gold nanoparticles (NPs) made an aqueous environment via the reduction of HAuCl₄ by ascorbic acid (AC) with the surfactant of polyvinylpyrrolidone (PVP). Highly monodisperse gold particles with size ranges from 4 to 20 nm were prepared in high-yield by pH control. The synthesized gold nanoparticles were analyzed for structural and optical properties using transmission electron microscopy (TEM) and UV-vis spectroscopy. In this study, we could reveal that the prepared nanoparticles exhibited efficient surface-enhanced Raman scattering (SERS) properties, and their SERS activities depends on size.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.384-384
• /
• 2011

양자점 감응형 태양전지는 염료감응형 태양전지와 비슷한 구조를 가지지만, 유기물 염료를 대신하여 무기물 양자점을 사용함으로서 기존 유기물 염료가 가지는 한계점을 극복할 수 있다. 양자점을 광감응 염료로 사용하는 경우 양자제한효과(quantum confinement effect)에 의해 양자점의 사이즈조절만으로 밴드갭을 조절할 수 있어 광학적 특성 조절이 용이하며, 유기물 염료보다 광흡수 능력도 뛰어나다. 더불어, 하나의 광자를 흡수하여 두개 이상의 전자-정공쌍을 만들 수 있는(multiple exciton generation) 가능성이 있어 기존 태양전지가 가지는 이론적 한계효율(Shockley-Queisser limit)을 뛰어넘을 수 있다. 본 연구에서는 고효율의 양자점 감응형 태양전지 개발을 위해, ZnO 나노선 구조에 CdS, CdSe 양자점을 증착한 CdSe/CdS/ZnO 나노선 헤테로구조를 수열합성법으로 합성하였다. 증착한 CdSe/CdS 양자점이 태양광의 가시광 전 영역을 흡수하여 전자-정공을 생성하며, 세 물질 간의 밴드구조를 통해 양자점에서 생성된 전자가 ZnO 나노선으로 포집되고, 바닥전극으로 직접연결이 되어있는 1차원의 나노선 구조를 통해 전자를 효율적으로 운반할 수 있다.