• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.2 no.1
• /
• pp.60-69
• /
• 1992

Fine $TiO_2$ powders were synthesized from ammonium titanium sulphate which produced from $TiCI_4$, and$(NH_4)_2$ SO. solution. Rutile single crystal were grown by the verneuil method with anatase powders and investigated the property of rutile crystal. The optimun growing conditions were as follows $\cdot$The ratio of hydrogen gas and oxygen gas; 3: 1 $\cdot$Growing temperature: $1900^{\circ}C$ $\cdot$The feeding rate of powders: 10g/hr

• Electrical & Electronic Materials
• /
• v.4 no.3
• /
• pp.201-210
• /
• 1991

본 논문에서는 (B $i_{1-x}$ P $b_{x}$)$_{2}$S $r_{2}$C $a_{2}$C $u_{3.6}$ $O_{y}$ (x=0~0.5)로 조성된 분말의 최적 하소온도를 결정하고 시편의 최적 소결온도를 규명하기 위하여 열분석을 하였다. 또 단일상의 고온 초전도체를 제작하기 위하여 열처리 온도, 시간 및 Pb 함량 변화에 따라 제작된 시편의 미세구조, 조성, 전기저항 및 전류밀도를 측정하여 상호 연관성을 종합적으로 분석, 검토하여 상변이에 관한 원인을 규명하고자 하였다. 또한 실용화 전 단계로서 임계특성 해석을 위하여 성형조건을 변화시켜 시편을 제작, 전류밀도값을 측정하였다.였다.다.

• Korean Journal of Materials Research
• /
• v.6 no.12
• /
• pp.1155-1161
• /
• 1996

Pb(In1/2Nb1/2)O3 (PIN)세라믹스에서 Pb+2이온 대신에 Ca+2, Sr+2, Ba+2 이온을 부분적으로 치환하여 상합성 과정 및 유전특성을 조사하였다. 페로브스카이트 PIN을 얻기위한 최적조건을 도출하기위하여 하소, 치환 이온의 종류 및 그량, 소결민돌, 유전특성의 관점에서 관찰하였다. 페로브로스카이트 PIN상을 합성하기 위해서는 Ba+2이온의 치환이 가장 효과적이었다.

• Journal of the Korean Ceramic Society
• /
• v.28 no.1
• /
• pp.37-45
• /
• 1991

The critical current density, electrical conductivity, critical magnetic field, Meissner effect, apparent density, and microstructure of YBa2Cu3O7-x ceramic superconductor prepared by polymeric precursor, while varing calcining and sintering conditions, were investigated. The best superconducting properties could be obtained from the body sintered at 93$0^{\circ}C$ for 10h after calcining at 90$0^{\circ}C$ for 10h, which gave 383A/$\textrm{cm}^2$ of critical current density(Jc), 96K of onset temperature(Tonset), 94. 8K of zero temperature (Tzero) 225 Oe of critical magnetic field (Hc1), 72.8% of superconducting volume fraction measured by Meissner effect and 6.28g/㎤ of apparent density.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.4
• /
• pp.521-527
• /
• 1997

Ruby single crystals of 6-7 mm in dialneter and 20-25 mm in length were grown by the xenon-arc type floating zone method using a self-designed FZHY1, Calcination and sintering conditions were investigated and optimum growth conditions were established for controlling the factors such as growth rates, rotation speeds and cooling rates. Also the available energy levels of $Cr^{3+}$ were calculated from transmission data. The growth direction of the crystals was [1010] direction identified by Laue back reflection pattern. The distribution of refractive indices on the wafer of the grown crystals was homogeneous except for the edges of the wafer. The crystals could be used as a laser material with a wavelength of 693 nm and a metastate level.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.221-223
• /
• 1999

In this work, samples were manufactured variously by changing conventional calcining and sintering conditions and we tried the utilization by making the heat treatment time, which is demanded to high-Tc phase formation, much shorter. We found out optimal heat treatment conditions with the analysis on formation process at superconducting phase in term of the change of calcining and sintering time and then, examined X-ray diffraction(XRD) patterns, scanning electron microscope(SEM) measurement and energy dispersive X-ray spectrometer(EDX) of the samples manufactured under heat treatment conditions which we suggest here. As a result, 2223 high-$T_c$, phase of (Bi,Pb)SrCaCuO superconductor starting with ($Bi_l$ xPbx,)$_2$$Sr_2$$Ca_2$$Cu_3$$O_y$, composition was formed from 1 hr sintering sample at temperature nearby melting point and also the completed sample with calcining and sintering time of 9 hr was formed high-$T_c$.low-$T_c$ phase appearing in sight above the critical temperature of liquid $N_2$.

• Resources Recycling
• /
• v.13 no.6
• /
• pp.31-36
• /
• 2004

This experiment was carried out to examine the effects of morphology on properties of La-Co substituted SrM ferrite. The magnetic properties of calcined and sintered materials were varried with the substitutional amount of La and Co elements in Sr-ferrite. In the substituted SrM ferrite, the atomic fraction x of La is directly related to the mole ratio n of iron oxide and the atomic fraction y of Co by equation x=2ny. The Hcj values of the calcined powder were about 270 kA/m and 240 kA/m with x=0.3 and x=0.2, respectively at stoichiometry, n=6.0. Crystallites of the sintered material were grown with a plate shape, and their size decreased with increasing mole ratios. Such a shape was caused by the initial state of crystallite formed after calcination. In case of x=0.3 and n=6.0, Br was 415 mT and Hcj was 355 kA/m, and in x=0.2 and n=6.0, Br was 410 mT and Hcj was 370 kA/m. The squareness in 2nd quarter of BH curve with x=0.2 was smoothly improved to compared with x=0.3.

• Proceedings of the Korean Institute of Resources Recycling Conference
• /
• 2004.12a
• /
• pp.27-34
• /
• 2004

This experiment was carried out to examine the effects of morphology on properties of La-Co substituted SrM ferrite. The magnetic properties of calcined and sintered materials varied with the substitutional amount of La and Co elements in Sr-ferrite. In the substituted SrM ferrite, the atomic fraction x of La is directly related to the mole ratio n of iron oxide and the atomic fraction y of Co by equation x=2ny. The HcJ values of the calcined powder were about 270 kA/m and 240 kA/m with x=0.3 and K=0.2, respectively at stoichiometriy, n=6.0. Crystallites of the sintered material were grown with a plate shape, and their size decreased with increasing mole ratios. Such a shape was caused by the initial state of crystallite formed after calcination. In case of x=0.3 and n=6.0, Br was 415 mT and HcJ was 355 kA/m, and in x=0.2 and n=6.0, Br was 410 mT and HcJ was 370kA/m. The squareness in 2nd quarter of BH curve with x=0.2 was smoothly improved compared with x=0.3

• Korean Journal of Materials Research
• /
• v.7 no.2
• /
• pp.140-144
• /
• 1997

The effects of the particle size of precursor powder on the microstructure and Jc of Ag-sheathed Ri-2223 tapes were investigated. The calcined powder with overall composition of $Bi_{1-89}Pb_{0-41}Sr_{2-01}Ca_{2-23}Cu_{3-03}O_{y}$ was milled for various times using planetary ball mill. The transport property of the tapes were found to depend strongly on the particle size of the precursor powder Enhanced reactivity of the milled powder facilitated the formation of 2223 phase and resulted in an increase of Jc. Excessive milling, however, led to the amorphisation of the powder and degraded the electrical property of the tapes.

• Resources Recycling
• /
• v.6 no.4
• /
• pp.31-37
• /
• 1997

The Mg-ferrite powders were recovered from acid leaching Mg waste by hydrothermal method. Recovering conditions ofMg-Ferrite were investigated m this system and the powders prepared were characterized, using X-ray analysis, chemicalanalysis, SEM. TEM, and VSM. In this study, pH of solution and the kind of neutralizer wcre important factors on thecharacteristics of the product. The optimum condition of recovering MgPenite was the mole ratio of Fe" : Mg"=2'1, reactiontemperature : ZOWC, reaction time.lhr, at pH=lZ, and Oi partial pressure af 2000 psi. And the powders ~ccovered have amonodispersed and spherelike shapes with the narrow sue distribulion.ow sue distribulion.