In this paper the influence of postweld heat treatment on mechanical properties of SMAW and FCAW stainless steel weldments was examined and the obtained results are as follows ; (1) The amount of $\delta$-ferrite formed by SMAW and FCAW process decreased with increasing holding temperature and time in post weld heat treatment(PWHT), and it was found that the reduced ferrite was transformed into sigma phase after $800^{circ}C{\times}50hr$ PWHT. This sigma phase, even though it was very small, resulted in brittleness of dissimilar weldment between carbon steel and stainless steel in bending test, however in similar weldment between stainless steel and stainless steel was not occured. (2) The chemical composition of sigma phase was measured to 28-30%Cr, 7-9%Mo, 4-6Ni in 316L weldment, and also 35-37%Cr, 0.9-1.0Mo, 6-8%Ni in 309L weldment by EDS analysis.

• 한국산학기술학회:학술대회논문집
• /
• 한국산학기술학회 2011년도 추계학술논문집 2부
• /
• pp.379-381
• /
• 2011

본 논문에서는 피복아크용접(SMAW)을 자동용접으로(GMAW) 전환시키기 위한 기초 연구로서 GMA용접가스가 기공율에 미치는 영향을 보고자 한다. 기공율 평가를 위해 반자동 소방용 분기배관실험장치를 제작하였다. 분기배관의 기공율을 평가하기 위해 보호가스 3종(Ar, $CO_2$, 8:2 혼합가스), 전압을 변수로 설정하여 GMA용접을 실시하였다. 용접을 실시한 시편을 용접방향으로 절단하여 기공율 평가를 실시하였다.

• 한국가스학회:학술대회논문집
• /
• 한국가스학회 1998년도 추계학술발표회 논문집
• /
• pp.188-192
• /
• 1998

• 한국해양공학회지
• /
• 제13권2호통권32호
• /
• pp.83-89
• /
• 1999

In this paper an experimental study on the development of the shielded metal are welding(SMAW) optimization technique for the dissimilar materials SS41 and STS304 of Auto-Lifting Magnet core plate was carried out. It was confirmed that the optimum welding heat input range was 37.5 to 45 kj/cm by considering on the strength and fatigue life of the welded joints more than 100% joint efficiency. And the quantitative relationship empirical wquation between the strength toughness adn fatigue life and the weld heat input was obtained.

• Journal of Welding and Joining
• /
• 제12권4호
• /
• pp.41-49
• /
• 1994

This study is to compare the welding quality of API 5L-X65 Steel- pipe's for natural gas transmission piping applied by SAW at shop and by GTAW-SMAW at site. The results can be summarized as follows; 1) Tensile strength of the welded zone by SAW(611.5 MPa) and by GTAW-SMAW(608.6 MPa) was maintained greater than that of the base metal(583.5 MPa). 2) Hardness of the welded zone and HAZ by SAW(Hv 194.8) & GTAW-SMAW (Hv 196.1) was slightly increased above that of the base metal (Hv 168.8), but less than the maximum allowable hardness(Hv 248). 3) Impact value of the welded zone by SAW(126.8 J) & GTAW-SMAW(88 J) became lower than that of the base metal(282.5 J), but was above the requirement of API 5L(68J). 4) Microscopic structure of the welded zone and HAZ by both SAW & GTAW-SMAW became fine-grained.

• Journal of Welding and Joining
• /
• 제10권4호
• /
• pp.33-38
• /
• 1992

우리나라의 용접재료는 산업구조 및 그 발전 속도와 용접재료 제조업체의 기술 및 연구개발 수 준과 더불어 발전하여 왔다. 용접이 본격적으로 이용되기 시작하여 약 40년이 경과되고 용접재료 제조업체가 현대적인 제조설비를 도입하여 체계적으로 용접재료를 생산하고 개발하기 시작하여 30년이 경과되었다. 용접재료가 양 및 질에 있어서 비약적인 발전으로 이룩할 수 있는 계기가 마련된 것은 제1차 경제개발5개년 계획의 수립과 추진으로 다양한 종류의 수요창출과 높은 수 준의 품질이 요구되면서 부터다. 1970년대에 조선공업등 강구조물을 주류로 하는 양적 수요 증 가의 기반이 조성되고 화학 프랜트, 원자력 발전등의 건설이 주축이 되어 관련 주변 기술이 발 전하므로서 용접재료의 품질보증 SYSTEM확보등 기술 발전의 획기적인 전기를 맞이하게 되 었다. 용접재료용 고품질의 원재료 및 일부 부재료가 국산화되고 용접재료 제조업체의 연구소 설립과 기술 및 연구개발 인력 확보, 그리고 대학 및 관공 연구소에서의 용접재료 관련 연구의 활성화에 힘입어 용접재료 기술은 국내 자체 기술로서 정착하게 되었다. 1941년 용접봉의 FLUX를 수제로 피복한 피복아크 용접봉(일미나이트계와 고산화철계의 혼합계통) 년산 17톤을 생산하기 시작하여 현재 년 12만톤을 생산하는 장족의 발전을 하게 되었다. 특히 1985년부터 1991년까지 용접재료의 고도성장은 종례가 없었던 기간이지만 1992년부터는 수요가 진정되고 경제의 불황이 예고되면서 저성장 추세는 상당기간 지속될 전망이다.

• 한국해양공학회지
• /
• 제15권4호
• /
• pp.73-79
• /
• 2001

Underwater wet bead-on-plate welds were experimentally performed on 11mm thick SS400 steel plate as base metal by using six different types of flux coated electrodes of 3.2mm diameter. Two kinds of different flux coated wet arc electrodes (UW-1, UW-2) were individually designed flux materials, three kinds of the electrodes (E4301, E4311, E4313) were terrestrial electrodes and the another one (TN20) was an imported underwater wet welding electrode. As results, the individually designed flux coated underwater electrode, UW-2 and TN20 had a good starting and the excellent arc stability compared with other electrodes. No significant difference of bead appearance could be detected, but the slag detachability of TN20 electrodes was relatively undesirable. By rapid cooling rate, the hardness value and the portion of martensite of HAZ were increased, but it was considerably maintain stable for TN20 and UW-2 electrodes. The individually designed flux coated electrode, UW-2 could be used in practice for underwater bead welds.

• Journal of Welding and Joining
• /
• 제14권2호
• /
• pp.19-27
• /
• 1996

재료의 표면개질은 표면층의 조직변화에 대한 개질법과 표면피복에 의한 개질 법으로 나눌 수 있다. 조직변화에 의한 개질법으로는 침탄, 질화, 이온주입 및 금속 확산 등이 있고, 표면피복에 의한 개질법으로는 도장, 도금, 육성용접, 물리증착(PVD) 및 화학증착(CVD) 등이 있는데, 용사법은 표면피복에 의한 개질법에 속한다. 용사기술 은 비교적 최근에 발달된 표면피복 기술로서 그림1과 같이 플라즈마, 가스화염 또는 아크열원을 이용하여 금속 또는 비금속 재료를 용융 혹은 반용융 상태로 모재에 고속 도로 분사하여 충돌 적층시켜 피복하는 공정으로 다른 표면개질기술에 비해서 여러 가지 잇점을 가지고 있다. 이것은 거의 모든 재질의 모재(금속, 세라믹, 유기재료 등) 에 대해 피막의 형성이 가능하고, 용사재료의 종류도 다양하다(금속, 합금, 각종 세라 믹, 플라스틱, 각종 복합재료 등). 또한 노재크기의 제한이 없고, 대형의 재료에 대해 서 한정된 부위의 피복이 가능하며, 모재의 열영향이 적고, 피막의 형성속도가 다른 피막법에 비해 빠른 장점을 가지고 있다. 그 예로 알루미나(Al$_{2}$O$_{3}$)를 피복할 경우 화학증착(CVD)법에 의해서는 피막형성 속도가 약 2 * $10^{-4}$mm/min 인데 비해 용사법에 의해서는 약 7.5 * $10^{-1}$mm/min로 매우크다. 이와같은 많은 장점을 갖고있는 용사법을 이용한 표면개질에 대해 본 기술보고에서 서술하고자 한다.

• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2001년도 춘계학술대회 논문집
• /
• pp.276-281
• /
• 2001

Wet Underwater arc welding process is inverstigated by using experimentally developed flux coated underwater arc welding electrode and SS400 steel plate of 12mm thickness as base metal. Two kinds of different flux covered wet arc welding electrode of 3.2mm diameter (UW-1, UW-2) are individually developed and one of the improved underwater welding electrode (UW-2) may be put to practical use for underwater arc welding process.

• Journal of Welding and Joining
• /
• 제1권2호
• /
• pp.1-6
• /
• 1983

용접중 발생되는 흄(Fume) 및 가스는 용접작업 환경을 오염시킬 뿐만 아니라 인체에 매우 유해하다. 용접 흄(Fume)은 금속 산화물로 구성된 아주 작은 입자이며 가스는 일반적으로 CO, CO$_{2}$, NO$_{x}$, SO$_{x}$, XF 등으로 구성되어 있다. 일반 피복 아아크 용접봉에서 발생되는 용접 흄은 인체에 매우 해로운 영향을 미친다. 즉 다량 흡입하게 되면 두통, 발열 등 급성 증상이 발생한다. 또한 소량을 장시간 흡입해도 진폐 등 만성증상을 일으킨다. 그러므로 현 국내 용접장에서는 흄에 의한 장해 방지를 위하여 충분한 환기시설과 완벽한 보호구 착용, 그리고, 용접 재료 자체의 흄 발생량을 감소시킨 저흄 용접봉(low fume type electrode)의 사용 방법 등이 검토 실시되고 있다. 본 보고서에서는 흄에 대한 올바른 인식을 꾀하는 한편, 용접자의 건강 보호를 목적으로 개발된 조선 및 철구조물의 주요 용접 재료인 철분 산화철계 저흄 용접봉에 관하여 소개하고자 한다.