• Title/Summary/Keyword: 피로크랙발생

Search Result 42, Processing Time 0.031 seconds

Behavior of Initiation and Propagation of Fatigue Crack under Periodic Overstressing (In the case of Fatigue Limit Stresses) (과대, 과소 응력하에서의 피로크랙 발생거동 (피로한도 응력을 중심으로))

  • 송남홍;원시태
    • Transactions of the Korean Society of Mechanical Engineers
    • /
    • v.15 no.6
    • /
    • pp.1839-1851
    • /
    • 1991
  • Fatigue crack behavior is studied through the two-level rotary bending test with the deep non-through radial holed notch specimens of low carbon steels(SM22C). The main factors investigated are the effects of the damage zone size around crack tip and phenomena of closing or opening of the crack tip. Obtained results are summarized as follows. Fatigue crack behavior in second level stressing slightly lower than fatigue limit is closely related to the size of damage zone produced by the first level stress higher than fatigue limit and to the phenomena of crack closing and opening for the second level stress. The non-propagating crack limit condition depends upon the crack length l$_{1}$ propagated under the first level stress and the magnitude of second level stress .sigma.$_{2}$ lower than the fatigue limit. The non-propagating crack limit condition is expressed by following eq. $\sigma_2^{6.1}{\times}l_{1}=7.35{\times}10^{6}[(kg_{f}mm^{6.1}(mm)]$

Thermographic Inspection of Fatigue Crack by Using Contact Thermal Resistance (접촉 열저항 효과를 이용한 피로균열의 적외선검사)

  • Yang, Seungyong;Kim, Nohyu
    • Journal of the Korean Society for Nondestructive Testing
    • /
    • v.33 no.2
    • /
    • pp.187-192
    • /
    • 2013
  • Fatigue crack was detected from a temperature change around surface crack using the thermographic technique. Thermal gradient across the crack decreased very much due to thermal resistance of contact surface in the crack. Heat diffusion flow passing through the discontinuity was visualized in temperature by infrared camera to find and locate the crack. A fatigue crack specimen(SM-45C), which was prepared according to KS specification and notched in its center to initiate fatigue crack from the notch tip, was heated by halogen lamp at the end of one side to generate a heat diffusion flow in lateral direction. A abrupt jump in temperature across the fatigue crack was observed in thermographic image, by which the crack could be located and sized from temperature distribution.

Behavior of Fatigue Crack Propagation of Micro-Hole and Micro-Slit Specimensns - For High-Frequency Heat Treantment Specimens - (微小圓孔 및 微小슬릿材의 疲勞크랙 傳播擧動)

  • 송삼홍;윤명진
    • Transactions of the Korean Society of Mechanical Engineers
    • /
    • v.10 no.1
    • /
    • pp.78-85
    • /
    • 1986
  • This study has been made to investigate Behavior of the fatigue crack propagation for the purpose of taking into consideration the fatigue behavior Which initiate and propagate in tip of defect of the defected specimens, Which Contain the micro-hole or micro-slit. Especially, the specimens have been conducted with high-freguency heat treatment of 850.deg. C, 1050.deg. C to consider strength elevation of defected specimens. The results of this study are as follow; (1) The case of the same in the length of crack, the fatigue crack propagation rate of the micro-slit is always faster than that of micre-hole. But, the first step of the fatigue crack propagation it is not always so. (2) Fatigue crack propagation rate of specimens with micro-slit or micro-hole which have been treated with high-frequency heat treatment satisfy the following formula between the fatigue crack propagation rate and nominal stress; dl/dN .var..sigma.$^{m}$ *l$^{n}$ .

Effect of a Matrix Structure on the Initiation of Fatigue Crack and Fatigue Strength in Nodular Graphite Cast Iron (구상흑연 주철재의 피로크랙 발생 및 피로강도에 미치는 기지조직의 영향)

  • Yoon, Myung-Jin;Lee, Kyoung-Mo
    • Journal of the Korean Society of Manufacturing Technology Engineers
    • /
    • v.7 no.5
    • /
    • pp.66-71
    • /
    • 1998
  • It is required the superior materials for the parts of machines or structures, which could be endurable in severe load and environment. According to advancement of casting technology, nodular graphite cast iron is used as suitable for such condition. But nodular graphite cast iron is scattering of fatigue strength and low reliability. Therefore in this study, the effect of matrix structure and number of nodular graphite on the initiation of fatigue crack and fatigue strength. It was found that the material which has relatively high ferrite volume fraction was more easily cracked than other materials and fatigue limit was low. The material which has not found pinhole on the surface, the crack was initiated in graphite went through ferrite and propagated into through graphite, but separated graphite and ferrite grain boundary and combined with other cracks to fro large one.

  • PDF

A Propagation Behavior of Crack in Material with Holes or Another Materials (구멍 또는 이종재료를 가진 재료에서의 크랙의 전파 거동)

  • Cho Jae-Ung
    • Journal of the Korea Academia-Industrial cooperation Society
    • /
    • v.6 no.6
    • /
    • pp.531-535
    • /
    • 2005
  • This study investigates the behavior of fatigue crack propagating between holes or holes lilted with another materials. It is experimentally and analytically confirmed that the center crack stops when its tip reaches near the center line of the holes and a small crack is initiated from the boundaries of holes or the holes filled with another materials and it propagates to final fracture. The mechanical behaviors of center crack near the another materials are also investigated. The phenomenon that this crack propagates to fracture is investigated by compliance method.

  • PDF

A Study on the Life Span Prediction of Railroad Wheels caused by Rolling Contact Fatigue (철도차륜의 구름접촉피로에 의한 수명예측에 관한 연구)

  • Chun, C.K.;Yang, J.S.;Park, S.J.;Yi, G.S.;Ma, Y.S.
    • Journal of the Korea Academia-Industrial cooperation Society
    • /
    • v.7 no.6
    • /
    • pp.1012-1020
    • /
    • 2006
  • The crack that occurs on the wheels of railroad cars can be categorized into a surface crack that starts from the surface or a subsurface crack that starts from the inside and can be detrimental to safe railroad operations. Therefore, estimating the growth life span of this type of crack is very important. In this research, the stress distributions, displacements, and the growth-life spans of both surface cracks and subsurface cracks have been studied. By using the finite element analysis, especially in the life span prediction process, the stress conditions and the stress intensity factors of the crack tip have been discovered. The Paris formula has been used to analyze the growth-life span prediction.

  • PDF

종의 Crack과 용접에 관하여

  • 염영하
    • Journal of Welding and Joining
    • /
    • v.7 no.1
    • /
    • pp.2-16
    • /
    • 1989
  • 종은 타명기로서, 소리(음향)를 내기 위해서는 동양종은 외부에서 타격하고 서양종은 내부에서 타격한다. 그러므로 종을 사용하는 사이에 이 타격으로 인하여 종에는 누적된 피로(Cumulated fatigue)가 생기고, 이것이 원인이 되어 크랙의 발생.rarw.성장.rarw.파괴로 진전되어 사용 불가 능케 된다는 것은 잘 알려진 사실이다. 이와같은 사례는 국내에서 그 실례를 많이 볼 수 있다. 예 1) 상원사종(국보 36호), 2) 보신각종(보물 2호), 3) 완주송광사종, 또한 외국의 경우, 미국의 자유의종 (Liberty Bell)등 대단히 많다. 여기서는 위의 종에 대한 크랙과 상원사종의 용접을 중 심으로 달아보겠다.

  • PDF

Behavior of Fatigue Crack Propagation from Surface Flaw (表面欠陷 에 發생하는 疲勞크랙擧動)

  • 송삼홍;오환섭
    • Transactions of the Korean Society of Mechanical Engineers
    • /
    • v.9 no.2
    • /
    • pp.150-157
    • /
    • 1985
  • In terms of behavior of fatigue cracks propagated after build-up around the artificial drilled miro-hole, this study has been made of the build-up process of slips and micro cracks, behavior of micro-crack propagation and the definition of fatigue limit under the rotating bending stress with low carbon steel. The results of this study are as follows: (1) The fatigue limit is the repropagating critical stress for the nonpropagating cracks which have grown to some limit around the micro-hole in regard of the magnitude of micro-hole. (2) Behavior of the slips and micro-cracks initiation are occurring simultaneously in front and in rear of micro-hole tips in the view of the rotational direction, regardless of the magnitude of micro-hole. (3) Behavior of fatigue crack propagation is different from magnitude of micro-hole, its behavior is propagation of single crack about respectively large hole, but about respectively small hole, fatigue crack propagated joining phenomena of micro-cracks. (4) The behavior of fatigue fracture is affected by the factor of its defects in the view of magnitude of micro-hole when the diameter of the micro-holes are smaller than 50.mu.m, and this is also affected with the size effect of micro-hole diameter.

Analysis of Fatigue Crack Opening: Belhlavioll Using Direct Measuring Method (직접측정법에 의한 피로크랙 개구거동의 해석)

  • Song, Sam-Hong;Kim, Hyun
    • Transactions of the Korean Society of Mechanical Engineers
    • /
    • v.16 no.8
    • /
    • pp.1493-1502
    • /
    • 1992
  • The purpose of this study is to identify the effects of loading variables on fatigue crack opening behavior, using structural steel SS41. To use various stress ratios, three kinds of the methods varying stress ratio were used; .DELTA.P const., P$_{max}$ const., and P$_{min}$ const.. To measure the opening load, the direct measuring method which measures the distance between two micro indentations 20 .mu.m behind crack tip and the elastic compliance method were used. As the results of present study, the following conclusions are obtained. First, using the direct measuring method, it was possible to measure the COD at any location behind crack tip. Second, as measuring point becomes farther from crack tip, opening load becomes smaller. Third, the acceleration of da/dN near notch is due to crack opening behavior. Finally, opening ratio is a function of not only R, but .DELTA.K.K.K.

An Empirrical Study on Low and High Cycle Fatigue Properties of Dual Phase Steel (I) -Low Cycle Fatigue Properties - (복합조직강의 저 및 고사이클 피로특성에 관한 실험적 연구(I) - 저사이클 피로특성 -)

  • 옹장우;성낙원
    • Transactions of the Korean Society of Mechanical Engineers
    • /
    • v.10 no.4
    • /
    • pp.477-486
    • /
    • 1986
  • 본 연구에서는 SM20C를 모재로 하여 입경의 크기가 다른 3종의 복합조직강을 제작 동일한 분위기에서 저 및 고사이클 전영역에 걸쳐 피로특성을 검토하고져 한다. 제일보는 그 중 저사이클특성에 대한 보고이다. 일반적으로 저사이클 피로현상은 재 료가 탄소성 상태하에서 전위, 미소크랙, 보이드(void) 등의 인자가 복합적으로 작용 하여 발생함으로 변형률속도, 제어파형, 온도, 시험방법 및 분위기에 따라 많은 영향 을 받는다. 따라서 본 연구에서는 두가지 실험방법을 사용, 응력-변형율거동을 검토 복합조직강의 피로특성과 입경크기가 피로거동 및 강도에 미치는 영향을 비교 고찰하 였다.