• 한국재료학회지
• /
• 제11권4호
• /
• pp.300-304
• /
• 2001

Al-Cu-Mn 주조합금의 피로성질에 미치는 Cd 첨가의 영향을 저주기 및 고주기 피로시험을 통하여 조사하였다. Cd 첨가량이 증가함에 따라 피로수명이 증가하였으며, 인장강도도 증가하였다. 고주기 피로시험결과 피로강도는 115MPa이었으며 피로비는 0.31이었다. 피로시험 결과 균열이 표면에서 발생하여 입계를 따라 전파되었는데 이러한 입계파괴는 입계를 따라 존재하는 무석출대의 영향으로 생각된다. 인장강도값은 Cd이 첨가되지 않았을 경우 330MPa이었으나 0.15%의 Cd이 첨가됨으로써 401MPa 까지 증가되었다.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2008년도 추계학술대회A
• /
• pp.256-259
• /
• 2008

An micro-probe tip must be manufactured using thin film to evaluate integrity of the semiconductor with narrow distance between pads. In this study, fatigue tests were performed for BeCu thin film which is used in micro-probe tip of semiconductor test machine. The thin film was manufactured by electro plating process, and the specimens were fabricated by wire-cut electric discharge method to make hour glass type specimen of $5000{\mu}m$ width, $29200{\mu}m$ length and $30{\mu}m$ thickness. The fatigue test of load control with 10Hz frequency was performed, in ambient environment. The fatigue cycles were tension-tension with mean stress, at stress ratio, R=0.1.

• 대한조선학회지
• /
• 제26권2호
• /
• pp.41-48
• /
• 1989

본 연구에서는 기계적 성질이 상이한 4가지 박용재료에 대한 피로실험을 통하여, 일정 진폭하중 피로실험에서의 피로균열 전파거동과 단일 과부하하중 피로실험에서의 피로균열 전파거동을 비교함으로써, 재료의 변형경화지수(n)와 단일과부하하중에 의한 피로균열 지연효과와의 관계를 규명하고자 하였다. 본 실험의 결과를 요약하면 다음과 같다. (1) 단일 과부하하중을 작용시키면 피로 균열 전파속도는 지연되며, 이 지연효과의 정도는 재료의 기계적 성질 특히 변형경화지수와 밀접한 관계가 있다. (2) 단일 과부하하중에 의한 피로 균열 전파속도는 변형경화지수의 값이 작은 재료에서는 피로균열 지연효과가 작고, 변형경화지수의 값이 큰 재료일수록 지연효과가 커진다. (3) 단일 과부하하중에 의한 균열 closure의 현상은 변형경화지수의 값이 큰 재료에서 뚜렷이 나타나며, n이 0.2보다 큰 재료에서 단일 과부하하중에 의한 피로수명 연장이 효과적임을 알 수 있다.

• 한국주조공학회지
• /
• 제28권1호
• /
• pp.37-40
• /
• 2008

본 연구는 ADI의 기계적 성질을 개선하고자 오스테나이트화 과정에서 초기 변태온도를 $900^{\circ}C$ (${\gamma}$ 구역)에서 시작하여 $800^{\circ}C$까지(${\alpha}+{\gamma}$ 구역) 일정한 냉각제어에 의해 오스템퍼링을 한다. 여기서 Full ADI에서 생성되는 고탄소 오스테나이트 조직을 저탄소 오스테나이트로 유도하고 미세한 침상의 Full ADI조직을 연성이 높은 조대한 아공석 페라이트 조직이 생성되도록 하여 Semi ADI를 만든다. Full ADI와 Semi ADI의 기계적 성질 및 피로강도를 연구한 결과 Full ADI와 Semi ADI의 정적강도는 유사하지만, 피로강도는 Semi ADI의 기지조직의 변화에 기인하여 Full ADI보다 피로강도가 높게 나타났다. 이러한 현상은 Semi ADI의 조대한 페라이트가 균열개구 저항력이 낮아 초기에는 쉽게 개구되지만, 균열개구와 동시에 균열선단에서 큰 소성역이 발생되어 균열성장이 지연하는 효과로 판단된다.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2007년도 춘계학술대회A
• /
• pp.1708-1711
• /
• 2007

This paper presents high cycle fatigue properties of an Al-3%Ti thin film, used in a RF (radio-frequency) MEMS switch for a mobile phone and also describes new test method for obtaining static and dynamic characteristics of thin film and reliability evaluation method on MEMS device with thin film developed by authors. Durability should be ensured for such devices under cycling load. Therefore, with the proposed specimen and test procedure, tensile and fatigue tests were performed to obtain mechanical and fatigue properties. The specimen was made with dimensions of $1000{\mu}m$ long, $1.0{\mu}m$ thickness, and 3 kinds of width, 50, 100 and $150{\mu}m$. High cycle fatigue tests for each width were also performed, from which the fatigue strength coefficient and the fatigue strength exponent were found to be 193MPa and .0.02319 for $50{\mu}m$, 181MPa and -0.02001 for $100{\mu}m$, and 164MPa and -0.01322 for $150{\mu}m$, respectively. We found that the narrower specimen is, the longer fatigue life of Al-3%Ti is and the wider specimen is, the more susceptible to stress level fatigue life of Al-3%Ti was.

• 기계저널
• /
• 제16권4호
• /
• pp.12-18
• /
• 1976

기계 및 구조물들이 등진폭하중만을 받는 경우는 극히 드물어서 대부분이 진폭과 주파수가 불규 칙하게 변하는 하중을 받는다. 실하중이력이 불규칙(random)한 모양을 갖는 것은 비행기, 자동차, 선박 등의 많은 기구물들이 공기의 터블런스, 거치론 도로표면 및 대양의 파도와 같이 random한 주위환경에 접하기 때문이다. 이 random한 환경과 구조물의 탄성성질들로 인해서 구조물로부터 측정된 하중응답신호들(응신율,변위 혹은 가속도)은 건폭과 주파수가 random하게 변하는 특정한 형태의 파형을 갖는다. 현금 우리나라에 이 방면의 연구가 활발하지 못하여 complex load history가 피로에 미치는 영향과 이에 관련된 피로시험들을 간략히 소개한다.

• 콘크리트학회지
• /
• 제5권3호
• /
• pp.179-186
• /
• 1993

본 연구는 무근 폴리에스터 폴리머 콘크리트보의 휨피로 거동을 구명키 위한 것으로서 초기균열깊이와 높이의 비 (a/h)를 0, 0.2, 0.4로 하고 응력수준을 45%, 55%, 65%로 하여 피로 시험을 실시한 것이다. 그 결과 초기균열깊이가 커질수록 피로수명이 짧아졌으며, 피로수명비에 따른 휨인장변형도는 균열깊이가 클수록 작아졌다. 또한 휨탄성계수는 피로수명비 0.2에서 0.6정도까지는 선형적인 변화를 보였으나, 초기와 말기에는 비선형적인 변화를 보여주었다. 그리고 응력수준과 균열깊이가 커질수록 취성적인 성질이 더 크게 나타남을 알 수 있었다.

• 대한치과보철학회:학술대회논문집
• /
• 대한치과보철학회 1993년도 추계학술대회
• /
• pp.53-54
• /
• 1993

• 동력기계공학회지
• /
• 제16권4호
• /
• pp.66-73
• /
• 2012

본 연구는 횡방향 TIG 용접된 Al6013-T4 알루미늄 합금 용접부의 피로균열전파거동에 미치는 용접후열처리(PWHT)의 영향을 조사하는 것이 주목적이다. 기초적으로 인장시험, 경도 및 미세조직이 조사되었으며, 피로균열전파거동을 고찰하기 위한 피로 시험은 모두 중앙균열인장(CCT) 시험편에 대하여 수행되었다. T82열처리에 있어서 시효시간은 피로균열전파율, 인장강도 및 경도에 대단히 민감함을 나타내었으며, 모재와 열영향부재의 경우가 용접재보다 기계적 성질이 우수하였다. 횡방향 TIG 용접한 Al6013-T4 시험재의 용접후열처리 조건에 따라서 피로균열전파 저항에는 차이가 나타났으며, 본 실험의 조건하에서 24시간 인공시효 PWHT-82 시험편이 피로균열전파 저항이 가장 우수한 결과를 나타내었다.

• 한국방재학회 논문집
• /
• 제11권2호
• /
• pp.75-80
• /
• 2011

본 연구의 주목적은 에너지 비율 인자와 위상각을 이용한 연성포장의 피로예측 모델을 개발하는 것이다. 본 연구에서 도입된 에너지 비율 인자와 위상각은 점탄성 재료의 기본적인 성질을 반영하기 위하여 사용되었다. 에너지 비율 인자는 가상 방출 에너지와 시험 중 파괴시 까지의 누적 방출 에너지의 비로 정의된다. 위상각은 아스팔트 혼합물의 응력과 변형률의 차이로부터 발생한다. 아스팔트 콘크리트 혼합물의 실험결과를 이용하여 위상각이 측정 되었으며 초기 stiffness와 초기 위상각의 관계가 제시 되었다. 본 연구 결과 아스팔트 콘크리트 혼합물의 점탄성 재료라는 고유한 성질을 반영할 수 있는 에너지 비율 인자와 위상각을 활용한 연성포장용 피로 예측 모델이 제안되었다.