• Journal of Ocean Engineering and Technology
• /
• v.9 no.1
• /
• pp.132-141
• /
• 1995

The purpose of the present study is to investigate the statistical characteristics of m and C in the fatigue crack propagation law, da/dN=C(.DELTA.K)/sup m/ and to studies on the randomness of fatigue crack propagation and retardation behavior. Fatigue tests were perfomed on 32 CT specimens of SPV50 steel under the same one condition. First, the value of m and C were determined for each specimen, and all the data were analyzed statistically. second, the material's resistance to fatigue crack propagation is modeled as a stchastic process, which varies randomly along the crack path. The statistical analysis of the material resistance is performed with the data obtained by constant load controlled tests. Finally, retardation behavior was examined experimentally by using a CT specimen, and a retardation parameters were analyzed statistically.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 1998.10a
• /
• pp.140-145
• /
• 1998

In this study, analysis for fatigue crack propagation behavior of interface and aroud interface under rotary bending stress. Though K values are nearly the same in around interface by BEM 2-D, fatigue crack propagated H.A.Z. Around Interface crack propagation speed is m=0.678 in H.A.Z by Paris' law. In this case(friction welded materials: STS304, SM15C), fatigue crack growth is considered SM15C metal microstructure and elastic flow from this result. Result is more metal microstructute dependence than stress dependence by analysis (BEM 3-D, BEM 2-D) and fatigue crack propagation

• Journal of Power System Engineering
• /
• v.5 no.2
• /
• pp.50-56
• /
• 2001

In this study, the effect of specimen thickness and stress ratio on fatigue crack growth in S45C steel was investigated. Acoustic emission was monitored during the fatigue crack growth test. Both crack closure and AE technique were used in assessing fatigue crack growth behavior. Constant amplitude loading tests were performed on CT type specimen with three different thicknesses and stress ratios. Crack closure was investigated to explain the influence of specimen thickness and stress ratio on the fatigue crack growth in the second growth region. The crack closure effect was decreased with specimen thickness and stress ratio.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.5 s.176
• /
• pp.1288-1296
• /
• 2000

In this study, fatigue crack behavior between arbitrarily located defects was investigated by experiment. Especially, stress interaction between micro hole defects and fatigue cracking, and fatigue crack initiation life following the variation of location of micro hole defects were considered. In addition, crack initiation position by micro hole stress interaction and the relationship between stress concentration factor and fatigue initiation life are studied in detail.

• The Journal of Engineering Geology
• /
• v.8 no.3
• /
• pp.275-284
• /
• 1998

Deformation behavior and microcrack development due to uniaxial compressive cyclic loading in the Pocheon granite were investigated using the ultrasonic velocity measurements and the differential strain analysis(DSA). Most microcracks were developed along the direction parallel to the loading axis. Microcracks developed at the early stage of cyclic loading were formed by propagation of pre-existing cracks. Ultrasonic velocity measurement, DSA and measurement of permanent deformation are good tools to represent microcrack development in rock. Since results from each method are slightly different, microcrack development should be interpreted from all three methods. The magnitude of microcracks developed at the early stage of cyclic loading under 80% loading level is twice compared with those under 70% loading level. The highest volumetric crack strain is about 3000, indicating that the Pocheon granite will fail with 0.3% occupation of microcrack in volume.

• Journal of Korean Society of Steel Construction
• /
• v.16 no.3 s.70
• /
• pp.387-396
• /
• 2004

In this paper, stress analysis anda 3-point bending fatigue test were conducted on the full-scale specimen to investigate the effects of misalignment at the U-rib welded joint due to misfitting in the steel deck bridge. In addition, the researchers investigated the direction and starting point of fatigue cracks by SEM (Scanning Electron Microscope) and beach mark. The results of the stress analysis show that maximum stress occurred at the bottom corner of the U-rib, and that the stress was large when the magnitude of the misalignment was large. On the other hand, the results of the static loading test of the full-scale specimen show that stress was large at the bottom corner of the U-rib. In addition, fatigue life was short when the misalignment was large and fatigue life was short when the misalignment was large and fatigue life was short when the misalignment was large and fatigue life was large when the misalignment was small, as indicated by the results of both the static loading test and the fatigue test. From the observation of the failure surface, fatigue cracks began manifesting at the root of the base metal and proceeded to the bead surface (weld toe).

• Journal of the Korean Society for Precision Engineering
• /
• v.18 no.5
• /
• pp.74-83
• /
• 2001

In this study, internal fatigue crack initiation and propagation behavior were investigated by triple piece spot welded specimen. To estimate fatigue life of the specimen varied with shape and thickness, Crack tip opening angle(CTOA) correlated with stress intensity factor was used as the stiffness parameter. The relation between fatigue life and CTOA can be arranged by the quantitative equation for each specimen by experiment. In addition, the variation of stress distribution was solved and the effect on fatigue crack behavior was examined by finite element method(FEM).

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1997.10a
• /
• pp.829-832
• /
• 1997

It is difficult to explain the effects of complex variable loading experienced by the machine and the structure only with the studies of the single-overload itself. Hence, it is thought that the variation of overload-holding time are required to explain the effects more clearly. The effects of the overload were analyzed by means of the crack retardation, and the fractography on retardation zone. A characteristic of the fractography on retardation zone was that striation distribution did not appear due to decreased crack driving force. Rotary bending fatigue tests were performed with the circular shaft which has two hole defects.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.19 no.4
• /
• pp.908-917
• /
• 1995

The constant .DELTA.K fatigue tests are performed in SS41 and its weldments to investigate crack opening behavior and fatigue crack propagation behavior at each parts of weldment and its boundary layer. The weldments were annealed after welding for the purpose of relieving residual stress. Every weldments has notch at weld metal zone, and fatigue crack propagates from weld metal zone to vase metal zone perpendicular to weld line. The Laser ISDG method is used in order to determine the crack opening ratio, this method is more precise than indirect measurement method, and faster and easier than other direct measurement method.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.34 no.4
• /
• pp.439-446
• /
• 2010

Fracture mechanics is used for the detailed analysis of the failure of high-speed rotating cylindrical vessels. The general procedure for the analysis of fatigue life and failure used in this study is summarized; the initial material properties are also described. The results of the theoretical stress analysis are compared to the observed magnitude of the stress under the operational condition. The fracture-surface configurations observed under both optical and scanning electron microscopes are used to investigate the progress of fatigue crack propagation. Fatigue life estimates obtained by using the Paris model are compared to the actual service life of the high-speed rotating pressure vessel.