• Proceedings of the KWS Conference
• /
• 1995.04a
• /
• pp.99-102
• /
• 1995

• Journal of Welding and Joining
• /
• v.14 no.3
• /
• pp.75-85
• /
• 1996

In this paper the influence of postweld heat treatment on mechanical properties of SMAW and FCAW stainless steel weldments was examined and the obtained results are as follows ; (1) The amount of $\delta$-ferrite formed by SMAW and FCAW process decreased with increasing holding temperature and time in post weld heat treatment(PWHT), and it was found that the reduced ferrite was transformed into sigma phase after $800^{circ}C{\times}50hr$ PWHT. This sigma phase, even though it was very small, resulted in brittleness of dissimilar weldment between carbon steel and stainless steel in bending test, however in similar weldment between stainless steel and stainless steel was not occured. (2) The chemical composition of sigma phase was measured to 28-30%Cr, 7-9%Mo, 4-6Ni in 316L weldment, and also 35-37%Cr, 0.9-1.0Mo, 6-8%Ni in 309L weldment by EDS analysis.

• Journal of Welding and Joining
• /
• v.13 no.1
• /
• pp.127-137
• /
• 1995

The possibility of new GMAW process using economic shielding gases including CO$_{2}$ gas was investigated on the effect of shielding gas on weldabilty. In the optimum welding condition using 600A power source, FCAW process showed low depositions rate, 114 g/min at 300A, but new GMAW using other mixed shielding gases exhibited high deposition rate, 208-224 g/min at 450A. TIME gas, Ar+CO$_{2}$ gas and Ar+CO$_{2}$+O$_{2}$ gas as a shielding gas were able to be used to the very high welding current(450A), moreover TIME gas and Ar+CO$_{2}$ gas showed the highest arc stability among shielding gases studied in this experiments. The weld penetration was performed by axial spray transfer mode of weld droplet. On the basis of workability, weldability and economic point of view, Ar mixture (80%Ar+20%CO$_{2}$) gas was recommended as a shielding gas for the development and application of new GMAW process. This shielding gas showed the low spatter, good weld quality, stable arc and low cost at the region of high welding current.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.6 no.2
• /
• pp.122-128
• /
• 2005

A feasibility study on the application of self?shielded flux cored arc welding to the on-site SM520 steel bridge box fabrication for express trains and high way construction instead of gas-shield flux cored arc welding was conducted in terms of weld soundness, mechanical properties, toughness and microstructures. All welded specimens made with the self?shielded FCAW process were tested by magnetic particle and ultrasonic techniques and they were found to be sound. All multipass weld specimens made with both self-shielded and gas-shielded FCAW processes showed yield and tensile strengths of $462{\sim}549\;MPa$ and $548{\sim}640\;MPa$, respectively. The impact values of Charpy V-Notch weld specimens also met with the required value of 40J at $-20^{\circ}C$. The hardness values of the top area of weldments were higher than those of the bottom area because of higher residual stresses in the near surface. It was found that welding characteristics of SM520 steel by the on-site welding conditions with self-shielded FCAW showed almost equivalent to those by gas-shielded FCAW in terms of sound welds, mechanical properties and microstructure.

• Journal of Korean Society of Steel Construction
• /
• v.18 no.5
• /
• pp.665-675
• /
• 2006

With building structures becoming higher and longer-spanned, the need for high-strength and reliable steel is increasing. For this reason, the SM570TMC steel plate was developed. Despite its excellent mechanical properties, however, its welding properties, which are well-known to be superior to those of other equivalent steel plates, have not been verified yet. In this study, welding specimens fabricated via SA and FCA welding, with two domestic welding materials and one Japanese welding material in site welding conditions, were evaluated.

• Journal of Welding and Joining
• /
• v.10 no.4
• /
• pp.190-198
• /
• 1992

Among the variety of welding processes available, the flux cored arc welding is one of the most frequently used process, because of its wide range of application and high productivity. The weld joint tracking is indispensable to improve the flexibility of the arc welding robot application for the flux cored arc welding (FCAW) process. In this study, an arc sensor which utilizes the electrical signal obtained from the welding arc itself was developed for weld joint tracking in FCAW. Because a model of the welding arc in flux cored arc welding was required to develop the arc sensor, a mathematical model was proposed by analysing the welding arc behaviour, and also an experimental model by using the factorial experiment and least square method. For overcoming the fluctuation in the welding current signal during tracking the weld joint, it was fitted to a curve which is inversely proportional to a trace of tip-to-workpiece distance by using the quadratic curve-fitting method.

• Journal of Welding and Joining
• /
• v.11 no.4
• /
• pp.57-69
• /
• 1993

In the present study, the microstructure and Charpy V notch toughness of multipass $CO_2$ FCA weldment in three different heat inputs(1-3KJ/mm)were investigated. The weldments using two different domestic FCAW wires(AWS E71T-1 and E71T-5 equivalent) in C-Mn steel were chemically analysed. The following conclusions can be inferred. 1. T-1 wire Showed a stable arc transfer, less spatter and harsh, a better bead spreading and easy slag removal, whereas T-5 wire suffered from the arc stability, which tended to increase spatter and produce a more convex bead. 2.The microsturctures of the top beads of the weldments in three different heat inputs consisted of coarse-grained boundary ferrite and Widmanstatten ferrite side plate with increasing heat inputs. The modest fraction of acicular ferrite in the two wire weldments was observed in the 2KJ/mm heat input. 3.The fine-grained reheated zones of both welds consisted of a duplex microstructure of polygonal ferrite and second phases. 4. The basic flux weldment of T-5wires showed a higher Charpy impact property than that of T-1 wires because of a higher fraction of acicular ferrite in the weld microstructure.

• Journal of the Society of Naval Architects of Korea
• /
• v.35 no.4
• /
• pp.65-75
• /
• 1998

The $CO_2$ welding with 100% $CO_2$ gas is commonly used because of its cost and efficiency. Arc phenomena and spattering ratio of the $CO_2$ welding are influenced by various factors such as chemical compositions of welding wire, shielding gas, welding condition and welding power source etc.. Spattering ratio is predominantly influenced by the welding condition which determines a droplet transfer rode. In this study, arc phenomena and spattering ratio are investigated by using two type of FCW(titania type, semi-metal type). Then, the welding quality and optimum welding condition can be selected. From this study, the following results ware obtained; 1) In low current range(140A), FCW up to welding voltage(22V) resulted in a typical short circuit transfer, increase of spattering ratio and growth of spatter diameter. 2) In high current range(320A), the arc stability in titania FCW of a typical globular transfer is better than that of semi-metal FCW.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.21 no.6
• /
• pp.860-864
• /
• 2012

The contact tip is higher the wear of resistance and the longer life are demanded to GMA welding process. In this study, four different contact tips with three different compositions by two wires were evaluated their wear resistance by measuring in every one hour the area of enlarged hole at the exit side during actual wleding. Experimental results clearly showed that the Cr-containing tips strengthened by precipitation hardening have much better resistance to wear than those made by work hardening. In addition, flux cored wire is excellent abrasion resistance test results showed. Based on these results, the domestic industry, the life of the contact tip to know will be used as basic data.

• Special Issue of the Society of Naval Architects of Korea
• /
• 2006.09a
• /
• pp.128-133
• /
• 2006

Generally, porosity which was formed by pyrolysis of the primer is usually generated in the weld metal in respect of increase of the welding speed. in order to analyze the cause of porosity generation, this study was performed using FCAW(flux cored arc welding) process for three kinds of inorganic.zinc primer. in addition the evaluation by influence of welding method on porosity generation is conducted to compare between FCAW and MAG(metal active gas) welding with the same inorganic zinc primer. As the result of this investigation, not only primer of lower organic binder and zinc but also FCAW process than MAG in fillet welding have been verified the excellent resistance to the porosity generation for horizontal fillet welding.