• Journal of the korean academy of Pediatric Dentistry
• /
• v.44 no.3
• /
• pp.335-340
• /
• 2017

Composite resin becomes an essential material in pediatric dentistry. However, incremental filling of composite resin to minimize the polymerization shrinkage takes time. To reduce the polymerization shrinkage, clinicians and researchers have focused on bulk-filling materials. Bulk-base composite resin is newly introduced as bulk-filling composite resin. The purpose of this study was to evaluate microhardness profile of bulk-base composite resin according to the depth of cure. A high flow bulk-base material and a low flow bulk-base material were used for experimental group, and a conventional composite resin was used for control group. Each group consist of 20 specimens, $3.5{\times}3.5{\times}5.0mm$ mold was used to make specimen. Specimens were sectioned at the 2 mm and the 3 mm depth with milling machine. Microhardness profile was measured at the surface, 2 mm depth, 3 mm depth, and 4 mm depth. Microhardness of control group showed statistically significant difference (p < 0.05) according to the polymerization depth. In contrast, experimental group showed no statistically significant difference, except between 0 mm and 4 mm at HFB, 0 mm and 2 mm, 0 mm and 3 mm at MFB. At the surface and the 2 mm depth, the control group showed higher microhardness than the experimental groups (p < 0.05). However, at the 4 mm depth, the experimental groups showed significantly higher microhardness (p < 0.05). The results from this study, the bulk-base composite resin showed higher microhardness at the 4 mm and lower microhardness at the surface and the 2 mm depth. Therefore, if bulk-base resin overcomes the mechanical weakness, it could be considered using in pediatric dentistry.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2011.05a
• /
• pp.193-195
• /
• 2011

강판재 사용에 있어 수소취성현상은 강판재가 고강도화됨에 따라 그 감수성이 커지는 것으로 알려져 있다. 특히 노출강판재의 경우, 표면으로부터 침투해 들어가는 수소에 의한 수소취화 거동에 대한 연구가 필요하다. 본 연구에서는 고강도 DP강을 시험편으로 하여, 음극전기분해법에 의해 수소를 강제주입시킨 후, DP강 표면하 subsurface zone의 수소취화 거동을 평가하고자 하였다. 미소경도분포 측정결과, 수소주입시간이 증가함에 따라 표면하 subsurface zone의 경도 또한 증가하는 것으로 조사되었다. 이는 수소에 의해 표면하 subsurface zone의 경화가 일어나 DP강의 기계적 특성에 영향을 미친것으로 판단된다. 미소경도분포의 측정결과와 미세조직 관찰결과로부터 수소임계침투깊이를 평가하였고, 이를 통해 DP강내 수소확산에 의한 수소임계침투깊이가 존재함을 확인할 수 있었다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2007.04a
• /
• pp.136-138
• /
• 2007

최근 기계가공기술의 발달에 따라 내마모용 TiN 박막의 수요가 증가하였고, TiN박막은 내마모용으로 높은 경도 및 밀착력을 필요로 한다. TiN박막을 증착시키는 방법은 PVD, CVD 등 여러 가지가 있으나 본 연구에서 공구강 SKD 61기판 표면과 Radical Nitriding(RN) 처리된 SKD 61 기판에 arc ion plating(AIP)를 이용하여 TiN 박막을 증착시켜 표면경도를 향상시키고, 이 코팅층의 미세구조가 기계적 특성에 미치는 영향을 연구하였다. 그 결과 RN처리된 SKD61에서 코팅 두께가 많이 나왔고, 스크래치테스트 결과 접착력이 향상되었음을 알 수 있었다.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.34 no.4
• /
• pp.613-622
• /
• 2007

The purpose of this study was to evaluate the effect of fluoride varnish on prevention of enamel demineralization. Eighty bovine enamel blocks were divided randomly into 4 groups of 20 specimens: Group I served as the control with no topical application of fluoride. Group II was treated with APF gel for 4 minutes. Group III was treated with Fluor $Protector^{(R)}$. Group IVV was treated with $CavityShield^{TM}$. After 24 hours of treatment, samples were brushed with a soft bristled tooth brush to stimulate normal mechanical wear of varnish. Early caries lesions were produced by placing each specimen into demineralization solution at pH 4.0 for 48 hours. Then the optical density of the lesions was measured by light fluorescence induced by plasma light and the surface microhardness were measured by the vicker's hardness test. The results were as follows: 1. The optical densities of group III, IV were significantly higher than that of group II, but no significant difference was noted between group III and IV. 2. The surface microhardness of group IV was the highest, followed by group III, II, and I(p<0.05). 3. There were no significant differences between group III and IV in optical density. However, the surface microhardness of group IV was significantly higher than that of group III. The results of present study indicate that the fluoride varnish is more effective than APF gel for prevention of dental caries.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2003.05a
• /
• pp.50-51
• /
• 2003

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2014.11a
• /
• pp.184-184
• /
• 2014

본 연구에서는 치과용 주조합금의 개발을 위하여 Ni-Cr 및 Ni-Cr-Ti합금을 소결체를 제조하고 기계적 특성 및 표면특성을 조사하였다. Ti원소가 첨가됨에 따라 결정조직의 결정립이 미세화하는 경향을 보였으며 조직이 다르게 나타났다. Ti 원소가 증가할수록 경도는 더욱 높게 나타났으며 Ti가 10 wt. %로 증가되었을 때 경도가 가장 높았다. 또한 압분체, 소결체, 벌크상태 순으로 경도가 증가하였다. 표면의 거칠기와 결합력에서도 Ti의 함유량이 증가함에 따라 개선되었다.

• The Journal of the Korea Contents Association
• /
• v.13 no.12
• /
• pp.893-899
• /
• 2013

This study was to determine the efficacy in the remineralization on premary teeth following the application of toothpaste with and without sodium fluoride. All tooth were checked using microhardness tester and the calcium (Ca) and phosphorous (P) concentration by electron probe microanalyzer (EPMA) analysis for the 4 weeks. The collected data was analysed using the statistical software program SPSS, 20.0. The applied enamel of premary teeth with 0.243% fluoridated toothpaste resulted in significant differences in the microhardness values (p>0.05). The Ca and P concentrations of applied premary teeth with fluoridated toothpaste were also significant difference in norm wt% (p>0.05). As a results, a increasing the surface microhardness of the premary teeth and providing a remineralizing effect by increased Ca and P concentrations.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.10a
• /
• pp.161-162
• /
• 2009

하이브리드 코팅장비를 이용해 WC-CO기판위에 Ti-Si-N박막을 증착 시켰다. 이 연구는 Ti-Si-N박막의 기계적 성질에 온도와 바이어스가 미치는 영향에 대해 실험을 하였다. 증착온도가 $300^{\circ}C$까진 Ti-Si-N박막의 미세경도와 탄성률은 증가했지만 증착온도가 $300{\sim}350^{\circ}C$에서는 탄성률은 감소하고 결정 성장으로 인해 미세경도는 감소하였다. 기판 바이어스는 박막과 미세구조에 압축 잔류 응력을 야기 시킨다. 그러나 기판바이어스가 -400V 이상에서는 re-sputtering에 의해 Si함량이 감소한다. Ti-Si-N 박막의 가장 우수한 기계적 성질은 $300^{\circ}C$, -100V에서 얻을 수 있었다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.05a
• /
• pp.28-28
• /
• 2015

현재 인쇄전자 소자 생산을 위해 사용되고 있는 대부분의 그라비아 롤러는 미세 패턴의 보호와 인쇄 중 마찰에 대한 내구성을 향상시키기 위해 경질 크롬 도금 막이 사용되고 있다. 그러나 경질 크롬 도금 막의 경우 구현할 수 있는 경도(~1000 HV)와 이형성, 내마찰(마찰계수: ~ 0.6) 특성 등에 한계가 있다. 이러한 경질 크롬 도금이 적용된 그라비아 롤은 그 수명과 내구성, 구현할 수 있는 인쇄 품질 및 신뢰성 그리고 인쇄처리 속도 등에 있어 여러 문제가 있다. DLC(Diamond Like amorphous Carbon)는 낮은 마찰계수 값인 0.2 이하와 뛰어난 내마모성, 상대재료에 대한 이형성 등을 겸비한 표면강화 기술로 경질 크롬 도금막 대비 우수한 표면 경도(>1,800 HV) 특성을 갖으며, 합성된 DLC 코팅 막의 경우 정밀 인쇄 제판이 요구하는 표면거칠기를 구현할 가능성이 높다는 장점이 있다. 특히 실리콘이 첨가 된 Si-DLC의 경우 표면의 마찰계수를 0.1 이하까지 낮출 수 있는데 닥터블레이드 및 잉크, 인쇄 기재와의 마찰 훼손을 최소화시켜 그라비아 인쇄 롤의 수명을 향상시킬 수 있다. 또한 PECVD 공정을 이용하여 합성한 Si-DLC는 표면거칠기를 10nm 이하의 경면으로 구현할 수 있으며, 높은 접촉각에 의한 우수한 이형성을 통해 미세 패턴 내부에 전자잉크/페이스트가 잔류되는 현상을 억제할 수 있다. 이는 기존 경질 크롬 도금이 적용된 그라비아 롤에서 발생하는 패턴 내 잉크 잔류-고형화와 그에 의한 사용수명 단축현상을 현저히 개선시킬 수 있다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2007.11a
• /
• pp.40-40
• /
• 2007