• Journal of Industrial Technology
• /
• v.23 no.A
• /
• pp.187-191
• /
• 2003

A hollow-fiber type polysulfone UF membrane was surface-coated with hydroxyethylmethacrylate (HEMA). The effect of various coating parameters on permeation flux, such as concentration ratio of AIBN/HEMA, solvent(water or methanol), and UV irradiation time, was investigated. The water permeation flux of oil-emulsion increased with concentration ratio of AIBN/HEMA, and increased with UV irradiation time. The flux of the membrane coated in solution using methanol as a solvent was greater than that of the membrane coated in solution using water as a solvent. The flux of both the coated and the uncoated membrane declined with the operation. The flux decline means that the membrane fouling by oil-emulsion occurs. However, the fouling of the coated membrane was much less than that of the uncoated membrane.

• Membrane Journal
• /
• v.12 no.4
• /
• pp.240-246
• /
• 2002

New polysulfone scintillation proximity membranes were prepared by impregnating Cerium Activated Yttrium Silicate (CAYS), an inorganic fluor, in a membrane structure. The membranes were applied to detect the radionuclide contamination directly without the aid of a scintillation cocktail. The preparation of membranes was divided into two processes. A supporting polymer film was made of casting solutions consisting of polysulfone and solvent, their cast film being solidified by vacuum evaporation. CAYS-dispersed polymer solutions were cast over the first, solidified polymer films and coagulated either by evaporating solvent or by exchanging solvent in the solution with nonsolvent in a coagulation bath. The prepared membranes had two distinguished, but tight1y attached, double layers: one is the supporting layer of dense polymer film and the other the detecting layer consisting of CAYS and polymer. The radionuclide counting results revealed that the prepared membranes were efficient to monitor radioactivity contamination with reliable counting ability.

• Journal of Korean Society of Environmental Engineers
• /
• v.36 no.2
• /
• pp.147-152
• /
• 2014

In this research, polysulfone hollow fiber membrane was used to recover $CO_2$ which is one of greenhouse gases from flue gas stream being emitted after the combustion of fossil fuels. The prerequisite requirement is to design the membrane process producing high-purity $CO_2$ from flue gas. For separation of $CO_2$, a membrane module and flue gas containing 10% carbon dioxide was used. The effects of operating conditions such as pressure, temperature, feed gas composition and multi-stage membrane on separation performance were examined at various stage cuts. Higher operating pressure and temperature increased carbon dioxide concentration and recovery ratio in permeate. Recovery ratio and separation efficiency increased if a higher content of $CO_2$ injection gas composition. Three-stage membrane system was producing a 95% $CO_2$ with 90% recovery from flue gas. The separation efficiency of three-stage membrane system was higher than one-stage system.

• Journal of the Korean Electrochemical Society
• /
• v.7 no.2
• /
• pp.89-93
• /
• 2004

Sulfonated polysulfone (SPSF) with poly(phenylmethyl silsesquioxane, PPSQ) composite polymer electrolyte membranes were prepared and their proton conductivity, water uptake and methanol permeability of membranes were characterized. By controlling the ratio of $(CH_3)_3SCI\;and\;CISO_3H$ and reaction time, SPSF with $37\~75\%$ degree of sulfonation were synthesized. The increase of sulfonate groups in the base polymer resulted in the increase of the water uptake in the membranes as well as methanol permeability. Composite membranes were prepared by casting of DMF solution of SPSF and PPSQ. The proton conductivity of the composite membrane at room temperature was $2.8\times10^{-3}\~4.9\times10^{-2}S/cm.$ The increase of PPSQ contents in composite membranes resulted in a decrease in water uptake and methanol permeability. Composite membranes containing $5\%$ PPSQ did not make a significant effect on the proton conductivity nO methanol permeability compared with that of pristine SPSF, but a significant decrease of water uptake was observed.

• Membrane Journal
• /
• v.29 no.2
• /
• pp.105-110
• /
• 2019

Porous membranes are widely used in industry for removing particulate matter. Unlike conventional porous membrane fabrication methods, the solution spreading phase separation method can form pores very simply. The first step is to wet the mesh with the support layer, then to let the polysulfone solution flow into a solvent without water. The solvent is readily vaporized and the polysulfone is made into a thin film. When the polysulfone solution is mixed with water to form pores, the pore size can be adjusted according to the concentration ratio of the polysulfone solution. The thickness of the membrane is easily controlled by the concentration of the solution. The porous separator has the formation of meshes intact and is very useful for forming a three-dimensional structure. The solution spreading phase separation method proposed in this study is characterized by its high cost competitiveness compared with conventional membranes due to its low production cost and easy process control.

• Membrane Journal
• /
• v.21 no.4
• /
• pp.367-376
• /
• 2011

Huge amount of $CH_4$ mixtures has been emitted from landfills and organic wastes via anaerobic digestion. The recovery of high purity $CH_4$ from these gases has two merits: reduction of green house gases and production of renewable fuels. Membrane technology based on polymeric materials can be used in this application. In this study, asymmetric gas separation hollow fiber membranes were fabricated to develop the membrane-based bio-gas purification process. Polyethersulfone (PES) was chosen as a polymer materials because of high $CO_2$ permeability of 3.4 barrer and $CO_2/CH_4$ selectivity of 50[1]. Acetone was used as a non-solvent additive because of its unique swelling power for PES and highly volatile character. The prepared PES hollow fiber showed excellent separation properties: 36 GPU of $CO_2$ permeance and 46 of $CO_2/CH_4$ selectivity at optimized preparation conditions: 9wt% acetone content, 10cm air-gap and 4wt% PDMS coating processes. With the PES hollow fiber membranes developed, mixed $CO_2/CH_4$ test was done by changing various operating conditions such as pressures and feed compositions to meet the highest recovery of CH4 with 95% purity. High $CH_4$ recovery of 58 wt% was observed at 10 atm feed pressure for the 50 vol% of $CO_2$ in $CO_2/CH_4$ mixture.

• Proceedings of the Membrane Society of Korea Conference
• /
• 2005.05a
• /
• pp.46-48
• /
• 2005

• Membrane Journal
• /
• v.11 no.2
• /
• pp.89-95
• /
• 2001

Polysulfone membranes containing an inorganic fluor, cerium activated yttrium silicate (CA Y5), were prepared via the phase inversion technique. The casting solutions with the fluor' were solidified to result in a membrane by using two different nonsolvent coagulants, water and isopropanol. In the process, the fluor worked as a monitioring agent for investigating the characteristics of the phase inversiun process. On the initial contact with water as nonsolvent, the induction of rapid polymer collapse results.in the entrapment of the fluor in the formed membrane structure. Impregnated fluor is dispersed in the polymer structure rather than being enveloped by polymer molecules. In comparison, the fluor is localized in the cell-like structure of membrane, as the cast solution film is cuagulated by immersion into a isopropanol bath.

• Membrane Journal
• /
• v.9 no.1
• /
• pp.43-50
• /
• 1999

The effects of water vapor on the permeation rates of oxygen and nitrogen through poly sulfone hollow-fiber membrane were investigated. The permeation rates of both 02 and $O_2$ were decreased significantly owing to the presence of water vapor. The permeation rate of oxygen with 100% relative humidity was reduced by as much as 20%, while the permeation rate of nitrogen decreased by 14% at 30 "C and 3kgf/$cm^2$ of upstream pressure. The permeation rates of $O_2$ were declined monotonously with running time and arrived at steady state values by the presence of water vapor. However, those of $N_2$ increased tentatively and then decreased to the steady state.tate.

• Membrane Journal
• /
• v.9 no.2
• /
• pp.132-139
• /
• 1999

Solid scintillation proximity membranes were prepared for measuring the amount of radioactivity in laboratories contaminated by the radionuclide of $^3H$-cortisol. The membranes, consisting of polysulfone as a polymer matrix and cerium activated yttrium silicate as a fluor, were used to monitor the amount of radioactivity without the aid of a scintillation cocktail required for the conventional wipe test. The test results of the cocktail-free wipe test showed that the prepared membranes were efficient to monitor radionuclide-contaminated areas with the good counting ability as well as with the decrease of overall production of radioactive waste. On the other hand, solvent treatment of the prepared membranes could induce a significant variation of membrane morphology, but the counting efficiency of the solvent-treated membranes was not improved than that of the untreated one.