• Journal of Conservation Science
• /
• v.37 no.6
• /
• pp.821-830
• /
• 2021

The weapons excavated from the de-militarized zones (DMZ) of Korea are vulnerable to corrosion due to the immediate and drastic environmental change. Especially, the chloride ions (Cl^-) in iron weapons cause active corrosion and require removal. In this study, conservation treatment and de-salination was performed for the discovered weapons from excavation sites of soldiers killed in action during the Korean War. Furthermore, an attempt was made to prepare the most stable plan for conservation treatment through the comparative study of soaking weapons in distilled water without chemicals and in a solution of sodium (SSC) at different temperatures. In the preliminarily experiments, the comparison of the eluted Cl^- ions according to different conditions of de-salination showed that the highest number of ions were detected from the de-salination with SSC at a temperature of 100℃, and its duration was much smaller, i.e., 1~2 weeks. Accordingly, for the parts from the guns and rifles amongst other objects, a six-time de-salination was conducted in the SSC solution for 8 hours at 100℃ and subsequently, for 16 hours at room temperature during which the distilled water and SSC were exchanged every week. However, in the case of a loaded rifle, the de-salination was not conducted, considering the risk that the high temperature and pressure by impregnation in vacuum could cause an explosion

• Journal of the Korean Vacuum Society
• /
• v.17 no.6
• /
• pp.538-543
• /
• 2008

Recently a nano-scale diamond is possible to manufacture forms of powder(below 100 nm) by new processing of explosion or deposition method. Using a sintering of nano-scale diamond is possible to manufacture of grinding tools. We have need of a processing development of coated uniformly inorganic to prevent an abnormal grain growth of nano-crystal and bonding obstacle caused by sintering process. This paper, in order to improve the sintering property of nano-scale diamond, we coated ZnO thin films(thickness: $20{\sim}30\;nm$) in a vacuum by ALD(atomic layer deposition) Economically, in order to deposit ZnO all over the surface of nano-scale diamond powder, we used a new modified fluidized bed processing replaced mechanical vibration effect or fluidized bed reactor which utilized diamond floating owing to pressure of pulse(or purge) processing after inserted diamond powders in quartz tube(L: 20 mm) then closed quartz tube by porosity glass filter. We deposited ZnO thin films by ALD in closed both sides of quartz tube by porosity glass filter by ALD(precursor: DEZn($C_4H_{10}Zn$), reaction gas: $H_2O$) at $10^{\circ}C$(in canister). Processing procedure and injection time of reaction materials set up DEZn pulse-0.1 sec, DEZn purge-20 sec, $H_2O$ pulse-0.1 sec, $H_2O$ purge-40 sec and we put in operation repetitive 100 cycles(1 cycle is 4 steps) We confirmed microstructure of diamond powder and diamond powder doped ZnO thin film by TEM(transmission electron microscope) Through TEM analysis, we confirmed that diamond powder diameter was some $70{\sim}120\;nm$ and shape was tetragonal, hexagonal, etc before ALD. We confirmed that diameter of diamond powders doped ZnO thin film was some $70{\sim}120\;nm$ and uniform ZnO(thickness: $20{\sim}30\;nm$) thin film was successfully deposited on diamond powder surface according to brightness difference between diamond powder and ZnO.