• Transactions of the Korean Society of Mechanical Engineers
• /
• v.16 no.8
• /
• pp.1446-1450
• /
• 1992

A method of prediction for the fatigue life of surface crack, that is, initial cracks grow and penetrate through the thickness, was presented in the previous study of the authors. Effects of parameters such as the initial crack depth, material factors, etc., for the life were also discussed. However, in the case of adapting the concept of LBB(Leak Before Break), the break fatigue life after the penetration of the thickness must be taken into account. Hence, a method to predict the break fatigue life is presented in this paper. Effects of the parameters for the break fatigue life are discussed and compared with the penetration fatigue life.

• Journal of the KSME
• /
• v.55 no.10
• /
• pp.26-30
• /
• 2015

이 글에서는 제4세대 원전 고온구조재료인 Gr. 91강을 대상으로 하여 장시간 크리프 수명을 예측하고 파단수명을 확률적 신뢰도를 가지고 평가할 수 있는 방법에 대해 실 예제를 통하여 서술한다.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.15 no.3
• /
• pp.907-915
• /
• 1991

본 연구에서는 피로 크랙 발생 및 파단수명의 통계학적 분포특성을 명확히 하 기 위해서 단축인장을 받고, 크랙 선단 곡율반경이 일정한 중앙 크랙을 가진 81개의 시험편을 사용하여 4개의 응력 레벨하에서 피로 시험을 행한후 많은 데이터들로 부터 피로크랙의 발생, 파단특성에 대한 신뢰성 있는 통계학적 확률특성을 제시하고, 이들 데이터를 활용하여 수명예측을 행해보고저 한다.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.15 no.5
• /
• pp.1455-1461
• /
• 1991

본 연구에서는 Kachanov의 재료손상(material damage)모델을 이용하여 새로운 수명예측식을 만들고, 이 수명예측식의 타당성을 조사하기 위하여, 최근에 발표된 크 립 수명과 기공분포와의 실험결과와 비교하였다.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.19 no.5
• /
• pp.1182-1189
• /
• 1995

Several methods have been developed to predict the creep rupture time of the steam pipes in thermal power plant. However, existing creep life prediction methods give very conservative value at operating stress of power plant and creep rupture strain cannot be well estimated. Therefore, in this study, creep rupture time and strain prediction method accounting for material damage and grain boundary sliding is newly proposed and compared with the existing experimental data. The creep damage evolves by continuous cavity nucleation and constrained cavity growth. The results showed good correlation between the theoretically predicted creep rupture time and the experimental data. And creep rupture strain may be well estimated by using the proposed method.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.36 no.2
• /
• pp.147-154
• /
• 2000

실온 대기 중에서 탄소강배관(STS370)의 피로시험을 행하였다. 배관에는 외부결함을 인공적으로 상정하여, 피로균열진전 및 관통의 거동, 균열형상, 누설 및 파단수명, 균열개구변위를 실험과 이론의 양면으로부터 비교·검토하였다. 특히, 배관의 벽두께 관통후에 있어서의 응력확대계수를 평가하기 위하여 새로운 식을 제안하였다. 피로균열이 관벽을 관통하기 전에 있어서는 판모델에 의한 Newman-Raju의 응력확대계수 평가식을 이용하므로서 aspect비와 누설수명 등 관통전의 피로균열성장거동을 평가할 수 있음을 나타내었다. 또한, 피로균열이 관벽을 관통한 후에 있어서는 본 논문에서 제안한 배관모델에 의한 응력확대계수의 평가식을 이용하여 관통후의 균열형상, 파단수명 및 균열개구변위 등 관통후의 피로균열성장거동을 평가하였다.

• Journal of Ocean Engineering and Technology
• /
• v.10 no.1
• /
• pp.47-52
• /
• 1996

This paper deals with a study on improvement of long-time creep life prediction of steam turbine rotor steels by using initial strain method as a new approach at high temperatures of 500 to 70$0^{\circ}C$ . The main result shows that the inital strain method could be reliably utilized to predict and evaluate the long-time creep life as creep rupture strength and that the predicting equation for long-time creep life under a certain creep stress at a certain high temperature could be empirically derived out from each initial instantaneous strain measured.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.14 no.6
• /
• pp.1583-1591
• /
• 1990

Life prediction and residual life prediction of structures of machines are one of the most strongly world wide needed problems as requirement in the stage of slowly developing economy which comes after rapidly and highly developing stage. For the purpose of statistical life prediction, fatigue test was conducted under the 4 stress levels, and for each stress level, about 20 specimens are used. The statistical properties of crack growth parameter m and C in the fatigue crack growth law of da/dN=C(.DELTA.K)sup m/, and the relationship between m and C, and the statistical distribution pattern of fatigue crack growth rate can be obtained by experimental results.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.11
• /
• pp.2812-2822
• /
• 2000

Several methods have been developed to predict the rupture time of the boiler tubes in thermal power plant. However, existing life prediction methods give very conservative value at operating stress of power plant and rupture strain cannot be well estimated. Therefore, in this study, rupture time and strain prediction method accounting for creep, corrosion and heat transfer is newly proposed and compared with the current research results. The creep damage evolves by continuous cavity nucleation and constrained cavity growth. The corrosion damage evolves by steam side and fire side corrosion. The results showed good correlation between the theoretically predicted rupture time and the current research results. And rupture strain may be well estimated by using the proposed method.

• The tire
• /
• s.65
• /
• pp.3-9
• /
• 1976

가유 고무에 대변형의 반복왜를 외부자극으로서 부여하면 초기에는 대폭의 응력의 변화현상이 보여져 서서히 일정응력치에 접근하여 파단에 이른다. 이 응력의 변화현상과 피로수명(파단하기까지의 회수)이 여하한 기계적 화학적 인자의 영향을 받는가를 천연고무의 순고무 가유물로 검토했다. 그 결과 실온으로 고무에 반복신장피로를 부여하면 가교구조, 망목밀도 및 신장률이 응력변화의 대소, 피로수명의 증감에 영향을 주었다. 고온으로 고무에 반복신장피로를 주면 열산화에 의하여 어느 온도로부터 현저한 응력연화(화학응력연화) 현상이 보였다. 연이나 고무에 열화방지제를 첨가하면 고온에 있어서의 산화반응이 억제되기 때문에 무첨가의 경우와 달라서 파단이나 현저한 응력연화가 일어나지 않았다. 피로수명(F)와 파괴신장(εb),반복신장률(ε)사이에 F=A(εb-ε)n 의 관계가 성립함이 인정되었다. An은 고유의 파라메에터어이며 천연고무의 순고무가유물로서 n은 4.0~4.5의 거의 일정치를 표시했다.