We have investigated tunneling magnetoresistance (TMR) properties of Fe/$Al_2O_3$/Co magnetic trilayer junctions sputtered on single-crystal Si (001) substrates. $Al_2O_3$ layers with thicknesses of 50~200 $\AA$ were deposited directly on the bottom ferromagnetic layer by a reactive rf sputtering. For comparsion, we prepared Pt/$Al_2O_3$/Pt tunnel junctions whose current-voltage (I-V) characteristics measured at 300 K indicated that reactively sputtered $Al_2O_3$ is a particularly good material for thin insulating barriers and allows us to form pinhole-free tunnel barriers. The magnetic tunnel junctions exhibit changes of tunnel resistance of about 0.1% at 300 K with an applied magnetic field and it was found that most junctions with Co as a top electrode have rather good I-V and TMR characteristics compared to those with Fe as a electrode. These results were discussed in relation to interfacial on the basis of those for Pt/$Al_2O_3$/Pt.

• Journal of the Korean Vacuum Society
• /
• v.20 no.1
• /
• pp.57-62
• /
• 2011

We have studied the electrical and magnetic transport properties of tunneling device with FePt magnetic quantum dots. The FePt nanoparticles with a diameter of 8~15 nm were embedded in a $SiO_2$ layer through thermal annealing process at temperature of $800^{\circ}C$ in $N_2$ gas ambient. The electrical properties of the tunneling device were characterized by current-voltage (I-V) measurements under the perpendicular magnetic fields at various temperatures. The nonlinear I-V curves appeared at 20 K, and then it was explained as a conductance blockade by the electron hopping model and tunneling effect through the quantum dots. It was measured also that the negative magneto-resistance ratio increased about 26.2% as increasing external magnetic field up to 9,000 G without regard for an applied electric voltage.

• Journal of the Korean Magnetics Society
• /
• v.16 no.6
• /
• pp.271-275
• /
• 2006

We investigated the magnetoresistance of perpendicularly magnetized magnetic tunnel junction composed of Co/Pd multilayers. The magnetoresistance was maximized with Co electrodes of about 5 nm thickness, which evidenced the important role of the interface in tunneling process. Both the change in perpendicular magnetic anisotropy and improvement of junction resistance were observed with changing Co sublayers, while the spin scattering became dominant with increasing Pd sublayers.

• Journal of the Korean Magnetics Society
• /
• v.26 no.6
• /
• pp.201-205
• /
• 2016

In this report, we measured the impedance spectrum in TMR device, and the relaxation behavior of the real and imaginary impedance spectrum was analyzed by using the equilibrant circuit of tunneling capacitance ($C_T$) and tunneling resistance ($R_T$). The relaxation frequency was increased with AC voltage in both the parallel and antiparallel alignment of two magnetic layers. The $R_T$ with AC voltage showed the typical bias voltage dependence. However, the $C_T$ showed large value than the expected geometrical capacitance. The huge increase of $C_T$ was affecting as a limiting factor for the high speed operation of TMR devices. Thus, the supercapacitance of $C_T$ should be considered to design the high speed TMR devices.

• Journal of the Korean Magnetics Society
• /
• v.11 no.5
• /
• pp.202-210
• /
• 2001

Spin dependent tunneling (SDT) junction devices of Ta/NiFe/Ta/NiFe/FeMn/NiFe/AlOx/CoFe/NiFe/Al with in-situ naturally oxidized Al barrier were fabricated using ion beam deposition and dc sputtering in UHV chamber of 10$^{-9}$ Torr. The maximum tunneling magnetoresistance (TMR) and the product resistance by junction (R$_{j}$ A) are 16-17% and 50-60 $\Omega$${\mu}{\textrm}{m}$$^2$, respectively. The values of TMR and (R$_{j}$ A) with field annealing were slightly increased. The TMR and (R$_{j}$ A) dependence versus the junction area size was observed. These results were explained by using sheet resistance effect of bottom electrode and spin channel effects.

• Journal of the Korean Magnetics Society
• /
• v.10 no.3
• /
• pp.118-122
• /
• 2000

MR characteristics of $Al_2$ $O_3$ based magnetic tunneling juction with various $Al_2$ $O_3$ thicknesses were investigated. Spin-dependent tunneling junctions, in which the tunneling barrier $Al_2$ $O_3$ is formed by depositing a 1-3 nm thick Al layer, followed by thermal oxidation at room temperature in an $O_2$atmosphere, were fabricated on 4$^{\circ}$tilt(111)Si substrate in 3-gun magnetron sputtering system. The top and bottom ferromagnetic electrodes were Ni$_{80}$Fe$_{20}$ and Co. A maximum Tunneling MR ratio of 14% was obtained in the junction of which insulating barrier thickness was 2 nm. By increasing the tunneling voltage across the junction, maximum MR ratio reduced and finally showed no MR characteristics.s.

• Journal of the Korean Magnetics Society
• /
• v.12 no.6
• /
• pp.201-205
• /
• 2002

The tunneling magnetoresistance (TMR) of a ramp-edge type junction has been studied. The samples with a structure of NiO(60)/Co(10)/NiO(60)/Si$_3$N$_4$(2-6)/NiFe(10) (nm) were prepared by the sputtering and etched by the electron cyclotron (ECR) argon ion milling. Nonlinear I-V characteristics was obtained from a ramp-type tunneling junctions having the dominant difference between zero and ＋90 Oe perpendicular to the junction edge line. The voltage dependence of TMR was stable up to a bias volt of $\pm$10 V with a TMR ratio of about -10%, which may be very peculiar magnetic tunneling properties with asymmetric tunneling process between wedge Co pinned layer and NiFe free layer.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2011.06a
• /
• pp.138-139
• /
• 2011

• Journal of the Korean Magnetics Society
• /
• v.6 no.2
• /
• pp.98-105
• /
• 1996

스퍼터링 방법으로 제작된 NiFe 박막에서 Ar 압력이 자기 및 자기저항 성질에 미치는 여향을 조사하였다. 타겟으로는 Ni$_{81}$$Fe_{19}$ 조성의 합금타겟을 사용하였다. TEM을 써서 박막의 미세구조를 조사하였으며, 보자력과 포화자화는 VSM으로 측정하였다. 합금박막의 조성은 ICPS로 분석 확인하였다. 10 mTorr 이상의 높은 Ar 압력에서 제작된 박막에서 갈라진 틈새(crack-like void)를 갖는 주상구조가 관찰되었다. 이러한 주상 결정립경계(columnar grain boundary)가 자화 과정에서 자구벽 핀닝자리(pinning site)가 되어, Ar 압력이 커짐에 따라 보자력이 증가 하였으며, 박막의 밀도가 감소하여 포화자화가 줄어드는 것을 볼 수 있었다. 한편, Ar 압력이 증가하면서 자기저항비가 감소하는 결과를 얻었다. 결정립 경계 산란과 결정립간 터널링에 의한 박막의 비저항의 증가가 이러한 자기저항비 감소의 주원인임을 알 수 있었다.다.

• Proceedings of the Korean Magnestics Society Conference
• /
• 1999.10a
• /
• pp.116-117
• /
• 1999