• Journal of the Korean Applied Science and Technology
• /
• v.35 no.4
• /
• pp.1088-1095
• /
• 2018

In this study, reduced graphene oxide/polyaniline composite was fabricated tomaximize their advantages with electrochemical performances and use as a electrodematerial for supercapcaitor. Polyaniline as an electrode material was synthesized bychemical polymerization of aniline monomer and reduced graphene oxide wasintroduced to prepare composite with polyaniline without any pre-treatment. Thereduced graphene oxide, polyaniline and their composite electrodes were fabricatedon gold coated PET(polyethylene terephthalate) substrate through spray coatingmethod which can also apply to industrial scale. we have also prepared reducedgraphene oxide and polyaniline single material electrode to compare theirelectrochemical properties with reduced graphene oxide/polyaniline composite electrode. We have analyzed and compared electrochemical properties of eachelectrodes by using cyclic voltammetry(CV), galvanostaticcharge-discharge(GCD) and electrochemical impedancespectroscopy(EIS) at same condition. As a result, reduced graphene oxide /polyaniline composite electrode showed higher capacitance value more thanpolyaniline and reduced graphene oxide electrode, respectively. Internal resistanceof reduce graphene oxide/polyaniline composite electrode was 24% and 58% lessthan polaniline and reduced graphene oxide electrode respectively. These resultsconsidered that reduced graphene oxide/polyaniline composite electrode has potential ability and enable to apply flexible energy storage and wearable devices.

• Korean Chemical Engineering Research
• /
• v.47 no.4
• /
• pp.418-423
• /
• 2009

MWCNT(multi-wall carbon nanotube)-doped PEDOT:PSS(poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate)), used as a HIL(hole injection layer) material in OLEDs(organic light emitting diodes), was spin-coated on to the ITO glass to form PEDOT:PSS-MWCNT nano composite thin film. Morphology and transparency characteristics of nano composite thin films with respect to the loading percent of MWCNT have been investigated using FT-IR, UV-Vis and SEM. Furthermore, ITO/PEDOT:PSS-MWCNT/NPD/$Alq_3$/Al devices were fabricated, and then J-V and L-V characteristics were investigated. Functional group-incorporated MWCNT was prepared by acid treatment and showed good dispersion property in PEDOT:PSS solution. PEDOT:PSS-MWCNT thin films possessed good transparency property. For multi-layered devices, it was shown that as the loading percent of MWCNT increased, the current density increased but the luminance dramatically decreased. It might be conclusively suggested that the enhanced charge mobility by MWCNT could increase the current density but the hole trapping property of MWCNT could dramatically decrease the hole mobility in the current devices.

• Science of Emotion and Sensibility
• /
• v.25 no.1
• /
• pp.67-78
• /
• 2022

Interest in bio-signal monitoring of wearable devices is increasing significantly as the next generation needs to develop new devices to dominate the global market of the information and communication technology industry. Accordingly, this research developed a resistive textile strain sensor through a wetting process in a single-wall carbon nanotube dispersion solution using an E-Band with low hysteresis. To measure the resistance signal in the E-Band to which electrical conductivity is applied, a universal material tester, an Arduino, and LCR meters that are microcontroller units were used to measure the resistance change according to the tensile change. To effectively handle various noises generated due to the characteristics of the fabric textile strain sensor, the filter performance of the sensor was evaluated using the moving average filter, Savitsky-Golay filter, and intermediate filters of signal processing. As a result, the reliability of the filtering result of the moving average filter was at least 89.82% with a maximum of 97.87%, and moving average filtering was suitable as the noise filtering method of the textile strain sensor.

• Composites Research
• /
• v.19 no.5
• /
• pp.7-11
• /
• 2006

The improved SWNTs/PANi composite actuator films applicable to an artificial muscle were fabricated successfully using a new process of manufacture that consists of 90% pure single-walled carbon nanotubes (SWNT) and chemical polymerization. PANi is electrically conducting polyaniline polymer. The conductivities of the composite SWNTs/PANi film-type actuators and the pure PANi films fabricated were measured as 56.15 S/cm and 17.38 S/cm, respectively, by the 4-prove method. The conductivity of the composite actuator is 3.2 times higher than the pure PANi film. The fabricated composite actuator showed higher conductivity than any other similar ones. The quality of samples was investigated by an electron scanning microscope (SEM). To measure the actuating strains, a specially designed beam balance apparatus was developed and strains of the composite actuators was measured by a laser displacement sensor subjected to electric currents. During the operation, the sample was soaked in the $NaNO_3$ solution and the sine-wave voltage in the range of $+1V{\sim}-1V$ was applied. The length of the composite actuator changed from $l_0=12.690$ mm to $l_1=12.733$ so that the change of length was l=0.043 mm and the strain was 0.34 %. This is a very high strain for this kind of a composite actuator. Other result reported by Tahhan showed 0.23 % strain, so that the present result is improved by 48%.