• Journal of the Korean Wood Science and Technology
• /
• v.43 no.1
• /
• pp.36-42
• /
• 2015

This study examined true modulus of elasticity (MOE) and modulus of rigidity (G) for domestic woods with different slenderness ratios (L/D) using the static bending and stress wave tests. Bending properties of small clear wood specimen of three domestic wood species were determined at 12% moisture content. The results of this study indicated that both MOR and MOE of domestic woods were affected by the slenderness ratio. As the slenderness ratio increased, MOR and MOE increased. G and true MOE of domestic timber beams were obtained at different slenderness ratios by flexure test and stress wave test. The values reported here can be useful if these species woods are used for structural purposes. However, the reported values are only indicative and do not represent the true average of wood species due to the limited number of specimens tested.

• Journal of the Korean Wood Science and Technology
• /
• v.42 no.3
• /
• pp.275-281
• /
• 2014

In this study, accelerated weathering test was performed with wood, a major material for wooden cultural building. In order to evaluate the deterioration of wood, ultrasonic transmission times were measured to evaluate dynamic modulus of elasticity (MOE), which was verified by determining static MOE using three-point bending test. Ultrasonic transmission time was decreased with an increase in the weathering time levels (0, 500, 1000 hours) while it increased in 1500 and 2000 hours. Distribution of dynamic and static MOE was similar to that of the ultrasonic transmission time measurements. The results mean that the measurement of ultrasonic transmission time was very effective to evaluate MOE of wooden cultural buildings for their preservation and management. This method could be utilized to assess wooden cultural buildings as a way of preserving them in a scientific manner.

• Korean Journal of Materials Research
• /
• v.5 no.3
• /
• pp.268-274
• /
• 1995

세라믹재료의 동탄성계수 측정을 위한 공진주파수 측정장치를 구성하였다. 구조용 세라믹 재료로 이용되는 $Al_{2}$O_{3}$, SiC, $Si_{3}$N_{4}$의 온도를 120$0^{\circ}C$까지 5$0^{\circ}C$의 온도간격으로 올리면서 torsional resonant frequency와 flexural resonant frequency를 측정하고, 측정된 공진주파수로부터 각 재료의 탄성계수를 구하였다. SiC의 경우는 120$0^{\circ}C$의 온도까지 탄성계수가 선형적으로 감소하였으나, $Al_{2}$O_{3}$와 $Si_{3}$N_{4}$의 경우에는 각각 100$0^{\circ}C$와 80$0^{\circ}C$까지는 선형적으로 감소하나, 그 이상의 온도에서는 탄성게수의 감소폭이 증가하는 현상을 보였다. 이러한 현상은 다결정재료에서의 grain boundary sliding에 의한 것으로 알려져 있다. 상온에서 공진법으로 측정된 동탄성계수의 측정결과는 초음파법으로 측정한 결과와 비교하였는데, 4% 내에서 서로 일치하는 결과를 보였다.

• Composites Research
• /
• v.23 no.1
• /
• pp.17-22
• /
• 2010

The compressive and dynamic properties of magnetorheological elastomers were investigated as functions of magnetizable particle volume fraction, alignment of the embedded particle and magnetic force. The specimens consisted of pure and filled silicons with randomly dispersed, longitudinal and transverse aligned magnetizable particle chains. To align the embedded particles in the elastomer, the cross-linking of the elastomer composites took place in a magnetic field. The compression and dynamic tests in the absence and the presence of different magnetic forces were carried out. The modulus and loss factor of the elastomer composites increase with increasing volume fraction at the same magnetic force. The case of longitudinal alignment shows a high modulus and loss factor when compared to the case of transverse alignment or random dispersion.

• Geophysics and Geophysical Exploration
• /
• v.1 no.3
• /
• pp.183-187
• /
• 1998

Seismic waveform estimation is based on the assumption that the seismic trace tying a well is one dimensional convolution of the propagating seismic waveform and the reflectivity series derived from well logs (sonic and density). With this assumption, the waveform embedded in a seismic trace can be estimated using a Wiener match filter. In this paper, I experimented a preprocessing procedure that applies both on the seismic trace and on the reflectivity series. The procedure is based on the assumption that the travel time can be estimated better from the seismic trace and that the instantaneous reflectivity values can be measured better on the well log. Thus the procedure is, 1) start-time adjustment and dynamic differential stretches are applied on the sonic log, and 2) seismic amplitudes are balanced such that the low frequency part of the seismic are matched to that of the reflectivities derived from well logs.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.30 no.2C
• /
• pp.85-93
• /
• 2010

The shear stiffness has become an important design parameter to understand the soil behavior. In particular, the elastic moduli and void ratio has been considered as important parameters for the design of the geotechnical structures. The objective of this paper is the development of the penetration type Field Velocity and Resistivity Probe (FVRP) which is able to assess the elastic moduli and void ratio based on the elastic wave velocities and electrical resistivity. The elastic waves including the compressional and shear wave are measured by piezo disk elements and bender elements. And the electrical resistivity is measured by the resistivity probe, which is manufactured and installed at the tip of the FVRP. The penetration tests are carried out in calibration chamber and field. In the laboratory calibration chamber test, after the sand-clay slurry mixtures are prepared and consolidated. The FVRP is progressively penetrated and the data are measured at each 1 cm. The field experiment is also carried out in the southern part of Korea Peninsular. Data gathering is performed in the depth of 6~20 m at each 10 cm. The elastic moduli and void ratio are estimated based on the analytical and empirical solutions by using the elastic wave velocities and electrical resistivity measured in the chamber and field. The void ratios based on the elastic wave velocities and the electrical resistivity are similar to the volume based void ratio. This study suggests that the FVRP, which evaluates the elastic wave velocities and the electrical resistivity, may be a useful instrument for assessing the elastic moduli and void ratio in soft soils.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.22 no.2
• /
• pp.140-148
• /
• 2002

Anisotropic elastic constants of Zr-2.5Nb pressure tube materials were determined by a high temperature resonant ultrasound spectroscopy (RUS). The resonant frequencies were measured using alumina wave-guides and wide band ultrasonic transducers in a small furnace. The rectangular parallelepiped specimens were fabricated along with the axial, radial and circumferential direction of the pressure tube. A nine elastic stiffness tensor for orthotropic symmetry was determined in the range of room temperature ${\sim}500^{\circ}C$. As the temperature increases, the elastic constant tensor, cij gradually decreases. Higher elastic constants along the transverse direction compared to those along the axial or radial direction are similar to the case of Young's modulus or shear modulus. A crossing of shear elastic constants along axial direction and radial direction was observed near $150^{\circ}C$. This fact corresponds to the crossing of c44 and c66 of single crystal zirconium.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.20 no.5
• /
• pp.390-396
• /
• 2000

The dynamic elastic constants of the simulated weld HAZ (heat-affected zone) of SA 508 Class 3 reactor pressure vessel (RPV) steel were investigated by resonant ultrasound spectroscopy (RUS). The resonance frequencies of rectangular parallelepiped samples woe calculated from the initial estimates of elastic stiffness $c_{11},\;c_{12}\;and\;c_{44}$ with an assumption of isotropic property, dimension and density. Through the comparison of calculated resonant frequencies with the measured resonant frequencies by RUS, very accurate elastic constants of SA 508 Class 3 steel were determined by iteration and convergence processes. Clear differences of Youngs modulus and shear modulus were shown from samples with different thermal cycles and microstructures. Youngs modulus and shear modulus of samples with fine-grained bainite were higher than those with coarse-grained tempered martensite. This tendency was confirmed from other results such as micro-hardness test.

• International Journal of Highway Engineering
• /
• v.12 no.2
• /
• pp.115-121
• /
• 2010

To evaluate the engineering characteristics of aggregate base materials, cyclic triaxial, CBR and permeability tests were performed for 15 samples. The CBR values of aggregate base materials have wide range from 32 to 110(average 81) and the amount of swelling in submerged conditions has below 0.04mm. The Modulus of aggregate base materials were significantly affected by volumetric stress, linear volumetric model was best for fitting. The modulus of aggregate base materials were determined within range of 100MPa~600MPa, 80~270 and 0.1~0.6 for model coefficient $k_1$ and $k_2$ respectively. The empirical correlation model was suggested that prediction the modulus from the basic properties obtained from particle size distribution test and compaction test. The coefficient of determination of the proposed correlation model was 0.423 for model coefficient $k_1$, 0.920 for model coefficient $k_2$ and 0.872 for modulus with stress level.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.19 no.3
• /
• pp.180-188
• /
• 1999

The dynamic elastic properties of metal matrix composites were investigated by resonant ultrasound spectroscopy(RUS). The composites used in this study consisted of 2124 aluminum alloy reinforced with different concentrations of SiC particles. RUS can determine the nine independent elastic stiffness($C_{ij}$) for the orthorhombic symmetry on a small specimen simultaneously. The elastic constants were determined as a function of the volume fraction. A concept of effective aspect ratio. which combine the aspect ratio and the orientation of reinforcement. was used to calculate the initial moduli from Mori-Tanaka theory for the input of RUS minimization code. Young's moduli can be obtained from the measured stiffnesses. The results show that the elastic stiffness increases with increment of the particle content. The behavior of elastic stiffness indicates that the particle redistribution induced by the extrusion process enlarges the transversely isotropic symmetry as the fraction of reinforced particles increase. This relationship could be used for determination of the volume fractions of reinforcement as a potential tool of nondestructive material characterization.