• Korean Journal of Food Science and Technology
• /
• v.34 no.5
• /
• pp.924-926
• /
• 2002

The effects of inlet air temperature and atomizing pressure on the coating efficiency were evaluated using peanuts. Broken peanut pieces were coated with dextrin and sodium caseinate solution by a fluidized bed coater. The coating efficiency was significantly influenced by inlet air temperature and atomizing pressure, with the optimal efficiency achieved at $70^{\circ}C$ and 3 bar, respectively. The coating material consisting of dextrin and sodium caseinate could be used for preventing rancidity of broken peanut.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.161-161
• /
• 2014

열플라즈마는 주로 아크 방전에 의해 발생시킨 전자, 이온, 중성입자(원자 및 분자)로 구성된 부분 이온화된 기체로, 국소열평형상태를 유지하여 구성입자가 모두 수천에서 수만도에 이르는 같은 온도를 갖는 고속의 제트 화염 형태를 이루고 있다. 이렇게 고온, 고열용량, 고속, 다량의 활성입자를 갖는 열플라즈마의 특성을 이용하여, 종래 기술에서는 얻을 수 없는 다양하고 효율적인 산업적 이용이 활발히 진행되고 있다. 용사코팅은 노즐 출구를 통해서 외부로 방출되는 열 플라즈마 화염을 이용하는 것으로 이 화염의 와류 특성으로 인하여 외기의 가스가 화염내부로 침투하는 특성을 가진다. 이러한 현상은 열원의 냉각효과 외에도 외기를 구성하는 기체 분자의 내부 유입을 의미하는 것으로 대기 상태에서 공정이 이루어진다면 열원 내로 유입되는 대기 내의 산소가 모재 표면과 반응하여 산화가 진행된다. 이러한 산화과정은 용사 코팅의 품질을 저하시키는 요인이 되므로, W, Ti 등과 같은 반응성이 높은 재료의 코팅은 산화과정을 방지하기 위하여 진공에서 코팅을 하여야만 한다. 진공 플라즈마용사코팅은 진공 또는 저압의 불활성 분위기 중에서 열플라즈마 화염에 용사재료를 투입하여 플라즈마 화염 내부에서 순간적으로 이를 용융시킨 후 고속으로 분출, 모재에 적층시키는 코팅공정이다. 이때 분말상의 용사재료를 고속으로 화염 중심에 투입하여 최대 에너지 전달이 이루어지도록 하는 것이 적층효율 및 코팅품질을 향상에 필수적이다. 하지만 플라즈마 화염 내부를 고속으로 이동하는 입자의 온도와 속도 및 궤적을 측정하여 제어하는 것은 매우 어렵기 때문에, 통상 형성된 코팅의 구조와 두께로부터 경험적으로 파라미터를 결정하는 것이 일반적이다. 본 연구에서는 초고속 레이저 카메라와 이미지 분석용 소프트웨어를 이용하여 플라즈마 화염내의 비행입자 궤적을 추적하고, 이를 통해 분말 이송가스의 유량이 코팅 효율 및 미세구조에 미치는 영향을 조사하였다. 플라즈마 화염은 중심부가 가장 높은 온도와 속도를 가지고 있기 때문에, 분말 이송가스의 유량이 적을 경우 투입된 분말은 단지 플라즈마 화염의 상부 경계면을 지나는 궤적을 갖게된다. 이로 인해 분말의 용융이 충분히 이루어지지 않아 적층 효율이 낮고 미용융 입자 및 기공이 많은 미세구조를 보였다. 이송가스 유량을 증가시키게 되면, 분말의 궤적은 플라즈마 화염의 중심부를 지나게 되어 적층 효율이 증가하고 미세구조 또한 개선되었다. 하지만 이송가스 유량이 지나치게 클 경우, 투입된 분말 입자는 플라즈마 화염을 조기에 관통하게 되어 비행궤적은 온도와 속도가 낮은 영역에 형성되었다.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.4 no.3
• /
• pp.214-217
• /
• 2003

본 연구에서는 IPA(isopropyl alcohol)를 분해물질로 선정하여 플라스틱 광섬유(Plastic Optical Fiber, POF)에 TiO₂ 를 코팅하여 오염물질을 분해하였다. P-25가 코팅된 POF의 표면은 유기계, 무기계, 유ㆍ무기 바인더를 사용한 것 모두 깨끗하였고, 무기계 바인더를 사용하여 코팅한 POF는 부착력이 현저히 떨어졌다. IPA분해 결과, 무기계 바인더를 사용한 경우, 다른 종류의 바인더와는 다르게 IPA의 초기농도 값이 매우 작게나왔는데 이러한 결과는 반응기에 주입된 IPA가 평형이 될 때까지 기다리는 동안 흡착이 일어났기 때문으로 생각된다. 유기계 바인더를 사용하여 코팅한 POF는 IPA 분해 효율이 매우 저조하였고 유ㆍ무기 바인더를 사용하여 코팅한 POF의 IPA분해 효율은 우수하였다. P-25와 IPA의 분해 효율이 우수한 유ㆍ무기 바인더의 비율을 10 : 10, 10 : 8, 10 : 6, 10 : 4, 10 : 2로 바꾸어 IPA를 분해한 결과, P-25와 유 ㆍ 무기 바인더의 비율이 10 : 2 일 매 IPA 분해 효율이 가장 우수하였다. 또한 P-25와 코팅액 제조 시 희석제로 사용되는 에탄올의 질량비를 1 : 7, 1 : 11, 1: 15로 바꾸어 IPA를 분해한 결과, P-25와 에탄올의 비율이 1 : 15일 때 IPA분해 효율이 가장 우수하였다.

• Proceedings of the KAIS Fall Conference
• /
• 2003.06a
• /
• pp.343-346
• /
• 2003

본 연구에서는 IPA(isopropyl alcohol)를 분해물질로 선정하여 플라스틱 광섬유(Pastic Optical Fiber, POF)에 TiO₂를 코팅하여 오염물질을 분해하였다. P-25가 코팅된 POF의 표면은 유기계, 무기계, 유ㆍ무기 바인더를 사용한 것 모두 깨끗하였고, 무기계 바인더를 사용하여 코팅한 POF는 부착력이 현저히 떨어졌다. IPA 분해 결과, 무기계 바인더를 사용한 경우, 다른 종류의 바인더와는 다르게 IPA의 초기농도 값이 매우 작게나왔는데 이러한 결과는 반응기에 주입된 IPA가 평형이 될 때까지 기다리는 동안 흡착이 일어났기 때문으로 생각된다. 유기계 바인더를 사용하여 코팅한 POF는 IPA 분해 효율이 매우 저조하였고 유ㆍ무기 바인더를 사용하여 코팅한 POF의 IPA 분해 효율은 우수하였다. P-25와 IPA의 분해 효율이 우수한 유ㆍ무기 바인더의 비율을 10 : 10 : 8, 10 : 6, 10 : 4, 10 : 2로 바꾸어 IPA를 분해한 결과, P-25와 유ㆍ무기 바인더의 비율이 10 : 2일 때 IPA 분해 효율이 가장 우수하였다. 또한 P-25와 코팅액 제조 시 회석제로 사용되는 에탄올의 질량비를 1 : 7, 1 : 11, 1 : 15로 바꾸어 IPA를 분해한 결과, P-25와 에탄올의 비율이 1 : 15 일 때 IPA 분해 효율이 가장 우수하였다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.252.2-252.2
• /
• 2015

야외에 설치 운영되는 태양광발전 시설과 설비들은 여러 요인들로 인해 쉽게 오염이 되고 이로 인한 효율 저하 및 유지 비용증가로 인하여 경제성이 저하되는 문제점을 가지고 있다. 본 연구에서는 기능성 나노코팅을 이용한 태양광 묘듈의 표면 코팅으로 내오염 특성을 향상시켜 오염에 의한 태양광 발전효율과 유지비용의 절감에 대한 방안을 제시하였다. 기능성 나노코팅은 태양광 모듈 커버글라스와 재질이 같은 유리 기판위에 코팅하였고, 코팅 방식에 따른 변화를 실험하였고, 코팅 방식으로는 딥핑(dipping), 스프레이, 천, 브러쉬를 사용하여 수행하였다. 유리 기판 위에 합성된 기능성 나노코팅의 특성분석은 내오염 특성, 광투과도, 접촉각, 부착력을 수행하였고, 실험에 활용된 기능성 나노코팅이 유리 기판 표면 오염방지에 탁월한 효과를 가짐을 확인하였다.

• Aerospace Engineering and Technology
• /
• v.8 no.1
• /
• pp.138-143
• /
• 2009

Thermal barrier efficiency and endurance of coatings in liquid rocket engine combustor were evaluated for air plasma spray coating and electro/electroless plating. The result of firing tests has revealed occasional occurrence of local delamination of $ZrO_2$, NiCrAlY coating obtained by the method of air plasma spray in the region of supersonic flow and it necessitated a new coating method as a substitution. It was found that Ni-Cr coating by means of electro/electroless plating can substitute $ZrO_2$, NiCrAlY coatings of air plasma spray in terms of thermal barrier efficiency and endurance.

• Korean Chemical Engineering Research
• /
• v.48 no.4
• /
• pp.506-510
• /
• 2010

Electron recombinations in electrolyte solution reduce light-to-energy conversion efficiency at the nanoporous electrode surface of dye sensitized solar cells. In this study, we improved the conversion efficiency using an energy barrier at the nanoporous electrode surface to control the recombination process. The energy barrier was formed by coating nanoporous $TiO_2$ electrode with $Nb_2O_5$ material. We investigated the influence of energy barrier on the cell efficiency depending on the coating thickness. Nanoporous $TiO_2$ electrode was coated about 5 nm thickness by 12 times coatings, and so the coating layer was grown about 0.417 nm for every time. Enhancement of conversion efficiency from 2.55% to 4.25% was achieved at 0.834 nm coating thickness, and it was believed as the optimum thickness for minimizing the electron recombination process in our experimental system.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.300.1-300.1
• /
• 2013

반사방지막 코팅(Anti-reflection coating)은 태양전지(Solar cell), 발광다이오드(LED) 등의 반사율을 낮추어 효율을 증대시키기 위하여 사용되고 있다. 본 실험에서는 유리 기판 위에 실리콘 타겟을 이용한 Reactive magnetron sputtering 장비를 활용하여, 50~100 mTorr의 높은 공정 압력(High pressure)에서 증착하여 SiO2 반사방지막 코팅층을 형성하였다. Ellipsometer를 이용하여 SiO2 박막층의 굴절률(Refractive index)을 측정한 결과, 공정 압력에 따라 SiO2 박막이 다양한 굴절률을 가지는 것을 확인할 수 있었다. 또한, UV-Vis spectrometer를 이용하여, 450~600 nm 파장에서의 반사율(Reflectance)과 투과율(Transmittance)을 측정하여 비교, 분석하였다. 나아가 증착된 SiO2 반사방지막을 비정질 실리콘 박막 태양전지에 적용하여 효율 향상 효과를 실험하였다. 이를 활용하여 낮은 굴절률을 갖는 반사방지용 SiO2 코팅층을 형성하여 태양전지의 광 변환 효율을 상승 시킬 수 있고, 발광다이오드의 광 추출 효율을 증가시킬 있을 것으로 여겨진다.

• Journal of Korean Society of Environmental Engineers
• /
• v.27 no.7
• /
• pp.697-703
• /
• 2005

Iron-coated sand(ICS) was prepared with variation of particle size of Joomoonjin sand, primary and secondary coating temperature, coating time, and dosage of initial Fe(III). An optimum condition of the preparation ICS was selected from the coating efficiency, stability of coated Fe(III), and removal efficiency of As(V). Coated amount of Fe(III) increased as primary coating temperature increased with smaller particle size of sand. Coating efficiency was quite similar over the investigated secondary coating temperature and time, while adsorption efficiency of As(V) onto ICS was severely reduced with ICS prepared at higher secondary coating temperature. By considering these results, an optimum secondary coating temperature and time for the preparation of ICS was selected as $150^{\circ}C$ and 1-hr, respectively. Coating efficiency increased us the dosage of initial Fe(III) up to 0.8 Fe(III) mol/kg sand and then no distinct increase was noted. Maximum As(V) adsorption was observed at 0.8 Fe(III) mol/kg sand. Secondary coating temperature and time were important parameters affecting stability of ICS, showing decreased dissolution of Fe(III) from ICS prepared at higher coating temperature and at longer coating time. From anionic type adsorption of As(V) onto ICS, it is possible to suggest the application of ICS for the removal of As(V) contaminated in acidic water system.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.168.2-168.2
• /
• 2014

반사방지막 코팅(Anti-reflection coating)은 태양전지(Solar cell), 발광다이오드(LED) 등의 반사율을 낮추어 효율을 증대시키기 위하여 사용되고 있다. 본 실험에서는 유리 기판 위에 실리콘 타겟을 이용한 반응성 high power impulse magnetron sputtering (HIPIMS) 장비를 활용하여, 높은 공정 압력(High-pressure)에서 펄스폭(Pulse width)을 조절하여 $SiO_2$ 반사방지막 코팅층을 형성하였다. 또한, 기공이 더 많은 박막을 제작하기 위해 빗각증착(Oblique-angle deposition)을 적용하여 더 좋은 광학 특성을 갖는 반사방지막 코팅층을 형성하였다. UV-Vis spectrometer를 이용하여, 380~800 nm 파장에서 투과율(Transmittance)을 측정하여 비교, 분석하였다. Ellipsometer를 이용하여 $SiO_2$ 박막층의 굴절률(Refractive index)을 측정한 결과, 반사방지막 코팅층 내부 기공에 따라 다양한 굴절률을 가지는 것을 확인할 수 있었다. 또한, 코팅층 내부 기공의 형상을 확인하기 위해 SEM(Secondary electron microscopy)을 활용하여 코팅층 단면(Cross section)을 측정하였다. 이를 활용하여 낮은 굴절률을 갖는 반사방지용 $SiO_2$ 코팅층을 형성하여 태양전지의 광 변환 효율을 상승 시킬 수 있고, 발광다이오드의 광 추출 효율을 증가시킬 있을 것으로 여겨진다.