• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.11 no.5
• /
• pp.1773-1777
• /
• 2010

The Application of UV curing technique for poly (vinyl chloride) (PVC) floor tiles coating has improved the quality of PVC floor. Several formulations were made including acrylated oligomers based on a polyurethane were blended with reactive monomers, photoinitiators and other additives. The used oligomers are commercial aliphatic urethane acrylates. Thin films were prepared on PVC tiles by bar coating with different formulations using UV radiation. The coating resins were characterized by FTIR. The properties of UV-cured films such as gloss and adhesion were examined. The properties of UV-cured films dependent on the influence of composition and processing conditions was studied.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.10a
• /
• pp.141-141
• /
• 2009

EHD(electrohydrodynamic) 증착법을 적용하여 코팅층 표면복합구조제어를 연구하였다. 이 방법을 이용하여 표면구조 제어를 통한 친/소수 코팅층 개발의 제반 조건들을 탐색한다. 화학적으로 안정한 코팅층을 형성할 수 있는 전구체 물질을 용매에 혼합하고, 전구체 물질의 농도를 조절하여 다양한 점도의 용액을 합성하고, 전기장을 적절한 범위에서 변화시키면서 용액의 점도와 전기장의 변화에 따른 코팅층의 표면형상을 체계적으로 조사하고, 주요 공정 변수인 용액 전구체농도와 전기장에 따른 표면형상 변화에 대한 공정 MAP을 조사하여 초친수/초발수 특성을 나타내는 최적 표면구조를 예측한다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.118-118
• /
• 2010

현재 반도체 제조 공정 중 많은 비중을 차지하는 식각 및 증착 공정에는 대부분 플라즈마를 사용하고 있으며, 이러한 반도체 장비내의 공정 부분품들은 수율과 생산성을 향상시키기 위하여 내플라즈마 특성이 우수한 세라믹 또는 세라믹 코팅막으로 구성되어 있다. 더욱이 최근에는 미세공정을 위해 고밀도 플라즈마 공정이 요구되면서, 노출된 세라믹 층이 침식되어 파티클이 떨어져 나오거나 모재와 세라믹 막 사이의 박리현상과 같은 심각한 문제들이 발생되고 있다. 따라서 보다 우수한 내플라즈마 특성을 갖는 세라믹 코팅 기술 개발이 시급한 실정이다. 현재 내플라즈마성 세라믹 코팅막 제조를 위한 코팅기술로서는 주로 용사법이 이용되고 있으나 기공률이 높고 치밀하지 못한 등의 문제점으로 인하여 사용수명이 짧다는 한계에 봉착하였다. 이에 본 연구에서는 상온에서 치밀하고 고속으로 세라믹 후막 형성이 가능한 Aerosol Deposition (AD)법과 AD법의 단점인 edge, corner, hole에서 코팅이 잘 안 되는 점을 보완할 수 있는 Arc Plasma Anodizing (APA)법을 조합하여, 상용화된 Al 모재위에 APA법을 사용하여 $Al_2O_3$ 후막 중간층을 형성한 뒤 그 위에 AD법으로 치밀한 $Al_2O_3$ 후막 성막함으로써 내 플라즈마 향상을 위한 새로운 개념의 제조기술개발을 시도하였다. 이를 위해 우선 Al 모재 위에 APA를 사용하여 중간층인 $Al_2O_3$막을 제조하였으며, 중간층의 두께에 따른 특성을 확인한 결과, $Al_2O_3$중간층의 두께가 두꺼워질수록 표면조도가 증가함을 확인 할 수 있었다. AD법으로 $Al_2O_3$중간층 위에 치밀한 $Al_2O_3$막을 제조하는데 있어 중요인자를 확인하기 위해, AD법으로 중간층 위에 $Al_2O_3$막을 제조한 후 성막특성을 관찰하였다. 그 결과, 중간층의 표면조도가 $0.8-1\;{\mu}m$인 경우에는 수 ${\mu}m$의 두께로 성막 되었으나, 표면조도가 $1\;{\mu}m$ 이상인 $Al_2O_3$중간층 위에서는 성막 되지 않았다. 이를 통해 AD법으로 치밀하고 두꺼운 $Al_2O_3$ 후막을 $Al_2O_3$중간층 위에 성막하기 위해서는 표면조도가 중요인자임을 확인하였다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.05a
• /
• pp.154-154
• /
• 2015

현재 액체로켓 엔진 연소기 내벽은 bonding layer NiCrAlY과 Top layer $ZrO_2$가 플라즈마 용사 방식으로 형성 된다. 이는 뛰어난 열 차폐 특성과 작업시간이 짧은 장점이 있지만, bonding layer와 Top layer 사이의 열팽창 계수 차이로 인한 균열 발생 가능성이 내재 되어 있고, 연소실 내벽에 균일한 두께의 코팅층을 형성하기 어렵고 설비가 비싸다는 단점으로 인하여 세라믹 코팅 층을 금속 코팅 층으로 대체 하고자 한다. 금속 코팅층은 모재와의 밀착성이 높고, 우수한 산화 및 부식방지 기능을 가지며 저렴하다는 장점이 있다. 또한 코팅 후 연마 작업이 가능해 연소실 내부형상을 설계조건 대로 유지 할 수 있는 특징이 있다. 따라서 본 연구에서는 연소실 내벽에 적용할 모재, 무전해 Ni-P 도금과 전해 Cr 도금층 사이의 밀착력 향상을 위한 방법에 대한 연구를 하였다. 밀착력 향상을 위한 요소로 전처리 용액과 열처리 시간에 따른 영향을 알아보고자 하였으며, 이를 위해서 5가지의 산세 용액으로 각 시편을 산세 한 후, 6시간, 12시간, 18시간 열처리 하여 단면을 비교하여 열처리에 영향을 알아보고자 하였다. 연구 결과 산세 용액의 영향은 크게 나타나지 않았으며, 열처리 시간이 길수록 Ni-P/Cr의 확산이 더 잘 일어나 확산층이 더 넓어지면서 밀착력이 더 좋아 진 것으로 판단되어 진다.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.38 no.6
• /
• pp.629-636
• /
• 2014

For surface modification, bulk metallic glass coatings were fabricated using metallic glass powder and a mixture of a self-fluxing alloy or/and hard metal alloys with a heat-resisting property using a high velocity oxy-fuel coating thermal spraying process. Microstructural analyses and mechanical tests were carried out using X-ray diffraction, a scanning electron microscope, an atomic force microscope, a three-dimensional optical profiler, and nanoindenation. As a result, the monolithic metallic glass coating was found to consist of solid particle and lamellae regions that included many pores. Second phase-reinforced composite coatings with a self-fluxing alloy or/and hard metal alloy additives were employed with in-situ $Cr_2Ni_3$ precipitate or/and ex-situ WC particles in an amorphous matrix. The mechanical behaviors of the solid particles and lamella regions showed large hardness and elastic modulus differences. The mechanical properties of the particle regions in the metallic glass composite coatings were superior to those of the lamellae regions in the monolithic metallic glass coatings, but indicated similar trends in matrix region of all the coating layers.

• Journal of the Korean Society of Propulsion Engineers
• /
• v.19 no.5
• /
• pp.84-90
• /
• 2015

Titanium alloys has been received an attention due to their excellent specific strength and many other superior properties in the application of components of flying subjects. In this study, Ti-6Al-4V (Ti64 alloy) has been selected in order to evaluate oxidation and degradation behaviors under the exposure of high temperature flame. The alloy has been coated with Al diffusion coating routes. The coated alloys showed an improved oxidation and degradation behaviors. The oxidation and degradation mechanism for the coated and uncoated alloys has been discussed in terms of microstructural observations.

• KOREAN JOURNAL OF PACKAGING SCIENCE & TECHNOLOGY
• /
• v.29 no.3
• /
• pp.153-161
• /
• 2023

The worldwide effects of COVID-19 have led to a surge in online shopping and contactless services. The consumption pattern has caused the issues such as the environmental pollution together with the increase of plastic waste. Reducing the reliance on the petroleum based plastic use for the package and replacing it with environmentally friendly material are the simple ways in order to solve those problems. Paper is an eco-friendly product with high recyclability as the food packaging materials but has still poor barrier properties. A barrier coating on surface of the paper can be achieved with the proper packaging materials featuring water, gas and grease barrier. Polyethylene (PE) or polypropylene (PP) coatings which are generally laminated or coated to paper are widely used in food packaging applications to protect products from moisture and provide water or grease resistance. However, recycling of packaging containing PE or PP matrix is limited and costly because those films are difficult to degrade in the environment. This study investigated the recyclability of modified acrylic emulsion coating papers compared to PE and PP polymer matrixes as well as their mechanical and gas barrier properties. The results showed that PE or modified acrylic emulsion coated papers had better mechanical properties compared to the uncoated paper as a control. PE or PP coating papers showed strong oil resistance property, achieving a kit rating of 12. Those papers also had a significantly higher percentage of screen reject during the recycling process than modified acrylic coated paper which had a screen rejection rate of 6.25%. In addition an uncoated paper had similar value of a screen rejection rate. It may suggest that modified acrylic emulsion coating paper can be more easily recycled than PE or PP coating papers. The overall results of the study found that modified acrylic emulsion coating paper would be a viable alternative to suggest a possible solution to an environmental problem as well as enhancing the weak mechanical and poor gas barrier properties of the paper against moisture.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.141-141
• /
• 2016

방식 코팅 기술은 조선해양산업은 물론 에너지, 철강 및 비철 소재, 건설 산업 등 산업 전반에서 폭넓게 적용되고 있다. 또한 산업 고도화에 따라 점차 가혹해지는 소재의 적용 환경을 고려해보면 향후 지속적으로 산업 수요가 증대될 것으로 예상할 수 있는 기술이다. 특히 아크 열용사법을 이용한 방식 코팅 기술은 미국이나 일본과 같은 선진국에서는 해양플랜트, 석유 시추시설 등 대형 해양 구조물은 물론 다리, 항만시설과 같은 철재 또는 시멘트 구조물의 방식 기술로 널리 적용되어 일반화된 기술이다. 그러나 국내에서는 아직까지도 초기 비용 상승 및 미약한 관련 기술 등의 이유로 대부분 방식도료를 사용하고 있는 실정이다. 그리하여 단기 수명에 따른 재시공 시 많은 환경오염을 유발하는 방식도료를 대체할 수 있는 아크 열용사법을 이용한 방식코팅 기술에 대한 관심과 수요가 점차 증가되고 있다. 그 일환으로 본 연구에서는 해양 구조물 강재의 방식을 위해 니켈계 용사재료를 이용하여 아크 열용사 코팅을 실시한 후 다양한 전기화학적 실험을 통해 내식성을 평가하고자 하였다. 아크 열용사 코팅은 구조용 강재 SS400강에 대하여 니켈합금 선재(1.6 Ø)를 사용하여 실시하였다. 용사 시 용사거리는 200 mm, 공기압력은 약 $7kg/cm^2$ 정도로 유지하면서 용사코팅을 실시하여 약 $200-250{\mu}m$ 두께로 코팅 층을 형성시켰다. 그리고 전기화학적 실험은 천연해수 속에서 자체 제작한 홀더(holder)를 이용하여 $3.14cm^2$의 용사코팅 층만을 노출시켜 실시하였다. 그리고 기준전극은 은/염화은 전극을, 대극은 백금전극을 사용하였다. 전기화학적 실험을 통해 부동태 특성 및 용사코팅 층 표면의 양극 용해반응 특성을 분석하기 위한 양극분극 실험은 OCP로부터 +3.0 V까지 실시하였다. 또한 부식전위 및 부식전류밀도 분석을 위한 타펠분석은 OCP를 기준으로 -0.25에서 +0.25 V까지 분극시켜 실시하였다. 그리고 주사전자현미경과 3D 분석을 통해 부식손상 표면을 관찰하였다. 그 결과 니켈합금으로 용사코팅된 강재의 내식성이 상당히 향상되었다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.502-502
• /
• 2011

기존 연구에서는 단일 타겟으로부터 증착된 코팅층 내에 다상으로 이루어진 나노 복합구조를 형성하기 위하여, 나노 합금분말을 방전플라즈마 소결법 등으로 급속 소결하여 타겟을 제조하는 방법이 고려되어 왔다. 반면, 비정질 재료가 우수한 비정질 형성능을 가지는 경우 주조 방법에 의해서도 타겟 제조가 가능하며, 특히 최근 들어 금속 비정질 합금에서 합금의 주요 구성 원소들이 양의 혼합열을 가지는 경우, 액상 또는 과냉각 액상에서 상분리 현상이 발생한다는 것이 밝혀졌다. 이러한 사실에 기초하면, 우수한 비정질 형성능을 가지는 합금 시스템에 합금 구성 원소와 양의 혼합열 관계를 갖는 원소를 첨가함으로써, 비정질 기지 내에 화학적 불균일성을 유도하여 다상으로 이루어진 복합 구조를 형성시키는 것이 가능하다. 본 연구에서는 이러한 합금 설계법을 이용하여, 비정질 기지 내에 존재할 수 있는 불균일성 정도를 합금 조성과 주조 조건의 변화를 통하여 나노 크기에서 원자 크기까지 조절하고, 이에 따른 재료 특성과의 상관관계를 밝히고자 하였다. 이를 위하여 우수한 비정질 형성능을 가지는 Cu-(Zr, Hf)-Al 벌크 비정질 합금계에서 (Zr, Hf)과 (Y, Gd)간의 양의 혼합열 관계에 주목하여 Cu-(Zr, Hf)-(Y, Gd)-Al 벌크 비정질 형성 합금계를 설계하였으며, 이 합금계 내에서 조성과 냉각속도의 조절에 따라 나타나는 불균일성의 정도와 특성변화의 영향을 체계적으로 고찰하였다. 결과로서, Cu-(Zr, Hf)-Al 합금계에서 (Zr, Hf)을 (Y, Gd)으로 15 at.% 이상 치환한 경우, Cu-(Zr, Hf)-rich 와 Cu-(Y, Gd)-rich 비정질상으로 이상분리가 일어났으며, 이렇게 생성된 비정질-비정질 복합재는 응력 하에서 소성 변형을 거의 보이지 않았다. 반면, 5 at.% 이하로 (Zr, Hf)을 (Y, Gd)으로 치환한 경우에는 비정질 기지에 SAXS 혹은 WAXS로 확인 가능한 원자 크기의 불균일성이 나타났으며, 이 경우 비정질 합금의 점성 유동의 변화를 통해 합금의 연신 특성이 향상되었다. 특히, 본 연구에서는 비정질 기지내 불균일 제어를 통한 기계적 특성 향상을 위해서 조성 제어뿐 아니라 동역학적인 요소를 고려한 냉각속도 조절을 통한 원자단위 불균일성의 최적화가 필요함을 규명하였다. 이러한 연구 결과는 분말화 및 소결 과정을 배제하고 제조된 단일 타겟을 통해 코팅층에 다수의 합금원소를 혼합하고 나노/원자 스케일의 복합구조 형성 및 고집적화가 가능한, 타겟 모물질 설계의 새로운 방향을 제시함으로써 다기능성 복합소재 코팅층의 연구에 크게 기여할 것으로 사료된다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.63-63
• /
• 2018

본 연구는 플라즈마 전해 산화 (PEO) 및 RF (Radio Frequency) 스퍼터링을 이용한 2 단계 접근법에 의해 처리 된 MgO / Ni-Cr의 고내식성 이중층 코팅을 제조하기 위해 수행되었다. 이를 위해 $100mA/cm^2$ 교류 조건에서 180 s PEO를 한 후 150W 에서 900s RF 스퍼터링을 수행 하였다. 코팅의 형태는 주사전자현미경(SEM)을 사용하여 관찰되었으며 코팅의 상조성은 X-선 회절(XRD) 및 X-선 광전자 분광법(XPS)을 사용하여 분석하였다. SEM 이미지는 스퍼터링 된 Ni-Cr이 크랙의 대부분과 미세한 미세 공극을 덮어 코팅 결함이 감소함을 보여 주었다. 따라서, 코팅 된 샘플의 거칠기 값은 스퍼터링 공정 후에 감소되었다. 단면 이미지로부터, 스퍼터링된 코팅층은 낮은 두께 때문에 거의 검출되지 않았다. EDS, XRD 및 XPS를 사용한 조성 분석은 금속 상태의 형태로 Ni 및 Cr 존재를 나타내었고 XPS에서 NiCr2O4 부동태 피막이 검출되었다. MgO / Ni-Cr 이중층 코팅의 내부식성은 MgO / Ni-Cr 이중층을 가진 샘플의 금속 원소와 비교하여 우수한 부식 특성을 나타내는 전위 역학적 분극 시험 및 전기 화학적 임피던스 분광법으로 평가 하였다.