• 한국재료학회지
• /
• 제23권12호
• /
• pp.672-679
• /
• 2013

$Fe_4[Fe(CN)_6]_3$ coated on a mica or $TiO_2$/mica surface as infrared reflective blue pigment was prepared by a hydrothermal method. $Fe_4[Fe(CN)_6]_3$, used as coloring agent, was uniformly coated on mica or $TiO_2$/mica under the optimized condition of a 1.2 : 1 weight ratio between iron(III) chloride hexahydrate and potassium ferrocyanidetrihydrate at the initial pH level of 4.5 at $70^{\circ}C$. The infrared (IR)-reflective pigments were characterized by SEM, Zeta-potenial, FT-IR, and UV-VIS NIR spectrophotometry. Especially the CIE color coordinate and total solar reflectance(TSR) properties of the pigments were investigated in relation to variation of the coating and coated substrate thicknesses. Isolation-heat paint was prepared with 20 wt% blue pigments fully dispersed in acryl-urethane resin and several additives to coat the film uniformly. The films were also measured with CIE color coordinate, TSR, and the surface temperature was recorded by an isolation-heat measuring system. The pigments and films of $Fe_4[Fe(CN)_6]_3$ coated on mica and $TiO_2$/mica showed high TSR values compared with the TSR value of $Fe_4[Fe(CN)_6]_3$ itself. According to the increase of TSR value, the property of isolation-heat is effective. To realize the optimal blue color, we applied the the pigment to $TiO_2$ coated mica(TM(b)) which has blueish interference color. The pigment of $Fe_4[Fe(CN)_6]_3$ coated on TM(b) shows a strong blue color compared with that of $Fe_4[Fe(CN)_6]_3$ coated on $TiO_2$/Mmca(TM(w)), which has a whitish interference color.

• 한국재료학회지
• /
• 제17권8호
• /
• pp.447-451
• /
• 2007

We investigated the dependence of the various annealing conditions and thickness ($6\sim45nm$) of the Ti-doped $Al_2O_3$ coating on the electrochemical properties and the capacity fading of Ti-doped $Al_2O_3$ coated $LiCoO_2$ films. The Ti-doped-$Al_2O_3$-coating layer and the cathode films were deposited on $Al_2O_3$ plate substrates by RF-magnetron sputter. Microstructural and electrochemical properties of Ti-doped-$Al_2O_3$-coated $LiCoO_2$ films were investigated by transmission electron microscopy (TEM) and a dc four-point probe method, respectively. The cycling performance of Ti-doped $Al_2O_3$ coated $LiCoO_2$ film was improved at higher cut-off voltage. But it has different electrochemical properties with various annealing conditions. They were related on the microstructure, surface morphology and the interface condition. Suppression of Li-ion migration is dominant at the coating thickness >24.nm during charge/discharge processes. It is due to the electrochemically passive nature of the Ti-doped $Al_2O_3$ films. The sample be made up of Ti-doped $Al_2O_3$ coated on annealed $LiCoO_2$ film with additional annealing at $400^{\circ}C$ had good adhesion between coating layer and cathode films. This sample showed the best capacity retention of $\sim92%$ with a charge cut off of 4.5 V after 50 cycles. The Ti-doped $Al_2O_3$ film was an amorphous phase and it has a higher electrical conductivity than that of the $Al_2O_3$ film. Therefore, the Ti-doped $Al_2O_3$ coated improved the cycle performance and the capacity retention at high voltage (4.5 V) of $LiCoO_2$ films.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.257-257
• /
• 2007

고밀도 FeRAM (Ferroe!ectric Random Access Memory) 소자를 개발하기 위해서는 강유전체 물질을 이용한 안정적인 스텍형의 커패시터 개발이 필수적이다. 특히 $(Bi,La)_4Ti_3O_{12}$ (BLT) 강유전체 물질을 이용하는 경우에는 낮은 열처리 온도에서도 균질하고 높은 값의 잔류 분극 값을 확보하는 것이 가장 중요한 과제 중의 하나이다. 불행히도, BLT 물질은 a-축으로는 약 $50\;{\mu}C/cm^2$ 정도의 높은 잔류 분극 값을 갖지만, c-축 방향으로는 $4\;{\mu}C/cm^2$ 정도의 낮은 잔류 분극 값을 나타내는 동의 강한 비등방성 특성을 보인다. 따라서 BLT 박막에서 각각 입자들의 크기 및 결정 방향성을 세밀하게 제어하는 것은 무엇보다 중요하다. 본 연구에서는 16 Mb의 1T/1C (1-transistor/1-capacitor) 형의 FeRAM 소자를 BLT 박막을 적용하여 제작하였다. 솔-젤 (sol-gel) 용액을 이용하여 스핀코팅법으로 BLT 박막을 증착하고, 후속 열처리 공정을 RTP (rapid thermal process) 공정을 이용하여 수행하였다. 커패시터의 하부 전극 및 상부 전극은 각각 Pt/IrOx/lr 및 Pt을 적용하였다. 반응성 이온 에칭 (RIE: reactive ion etching) 공정을 이용하여 커패시터를 형성시킨 후, 32k-array (unit capacitor: $0.68\;{\mu}m$) 패턴에서 측정한 스위칭 분극 (dP=P*-P^) 값은 약 $16\;{\mu}C/cm^2$ 정도이고, 웨이퍼 내에서의 균일도도 2.8% 정도로 매우 우수한 특성을 보였다. 그러나 단위 셀들의 특성을 평가하기 위하여 bit-line의 전압을 측정한 결과, 약 10% 정도의 커패시터에서 불량이 발생하였다. 그리고 이러한 불량 젤들은 매우 불규칙적으로 분포함을 확인할 수 있었다. 이러한 불량 원인을 파악하기 위하여 양호한 젤과 불량이 발생한 셀에서의 BLT 박막의 미세구조를 분석하였다. 양호한 셀의 BLT 박막 입자들은 불량한 셀에 비하여 작고 비교적 균일한 크기를 갖고 있었다. 이에 비하여 불량한 셀에서의 BLT 박막에는 과대 성장한 입자들이 존재하고 이에 따라서 입자 크기가 매우 불균질한 것으로 확인되었다. 또 이러한 과대 성장한 입자들은 거의 모두 c-축 배향성을 나타내었다. 이상의 실험 결과들로부터, BLT 박막을 이용하여 제작한 FeRAM 소자에서 발생하는 불규칙한 셀 불량의 주된 원인은 c-축 배향성을 갖는 과대 성장한 입자의 생성임을 알 수 있었다. 즉 BLT 박막을 이용하여 FeRAM 소자를 제작하는 경우, 균일한 크기의 입자 및 c-축 배향성의 입자 억제가 매우 중요한 기술적 요소임을 알 수 있었다.

• 한국재료학회지
• /
• 제7권3호
• /
• pp.188-195
• /
• 1997

비정질 실리콘 박막 위에 구리용액을 스콘코팅하여 구리이온을 흡착시킨 후 이를 표면 핵생성 site로 이용하는 새로운 저온 결정화 방법에 관하여 연구하였다. 구리 흡착으로 LPCVD비정질 실리콘 박막의 결정화온도를 $500^{\circ}C$까지 낮출 수 있었고 결정화시간도 크게 단축되었다. $530-600^{\circ}C$에서 어닐링시 구리가 흡착된 비정질 실리콘 막은 나뭇가지 형태의 fractal을 이루며 결정화되었다. 이때 fractal크기는 구리용액의 농도에 따라 $30-300{\mu}m$로 성장하였다. Fractal의 내부는 새 털 모양의 타원형 결정립으로 구성되어 있으며 TEM 에 의한 최종 결정립의 크기는 $0.3-0.4{\mu}m$로 intrinsic 비정질 실리콘 박막을 $600^{\circ}C$에서 어닐링하였을 때화 크기가 비슷하였다. 구리용액의 농도 증가에 따라 핵생성 활성화 에너지와 결정성장 활성화 에너지가 감소하였다. 결과적으로 구리 흡착이 표면에서 우선 핵생성 site를 증가시키고 핵생성 및 fractal 성장에 필요한 활성화 에너지를 모두 낮추어 저온에서도 결정화가 촉진되었음을 알 수 있었다.

• 한국재료학회지
• /
• 제22권7호
• /
• pp.379-383
• /
• 2012

$TiO_2$ thin films consisting of positively charged poly(diallyldimethylammonium chloride)(PDDA) and negatively charged titanium(IV) bis(ammonium lactato) dihydroxide(TALH) were successfully fabricated on glass beads by a layer-by-layer(LBL) self-assembly method. The glass beads used here showed a positive charge in an acid range and negative charge in an alkaline range. The glass beads coated with the coating sequence of(PDDA/TALH)n showed a change in the surface morphology as a function of the number of bilayers. When the number of bilayers(n) of the(PDDA/TALH) thin film was 20, Ti element was observed on the surface of the coated glass beads. The thin films coated onto the glass beads had a main peak of the (101) crystal face and were highly crystallized with XRD diffraction peaks of anatase-type $TiO_2$ according to an XRD analysis. In addition, the $TiO_2$ thin films showed photocatalytic properties such that they could decompose a methyl orange solution under illumination with UV light. As the number of bilayers of the(PDDA/TALH) thin film increased, the photocatalytic property of the $TiO_2$-coated glass beads increased with the increase in the thin film thickness. The surface morphologies and optical properties of glass beads coated with $TiO_2$ thin films with different coating numbers were measured by field emission scanning electron microscopy(FE-SEM), X-ray diffraction(XRD) and by UV-Vis spectrophotometry(UV-vis).

• 한국재료학회지
• /
• 제32권4호
• /
• pp.200-209
• /
• 2022

In this study, defects generated in the YSZ coating layer of the IN738LC turbine blade are investigated using an optical microscope and SEM/EDS. The blade YSZ coating layer is composed of a Y-Zr component top coat layer and a Co component bond coat layer. A large amount of Cr/Ni component that diffused from the base is also measured in the bond coat. The blade hot corrosion is concentrated on the surface of the concave part, accompanied by separation of the coating layer due to the concentration of combustion gas collisions here. In the top coating layer of the blade, cracks occur in the vertical and horizontal directions, along with pits in the top coating layer. Combustion gas components such as Na and S are contained inside the pits and cracks, so it is considered that the pits/cracks are caused by the corrosion of the combustion gases. Also, a thermally grown oxide (TGO) layer of several ㎛ thick composed of Al oxide is observed between the top coat and the bond coat, and a similar inner TGO with a thickness of several ㎛ is also observed between the bond coat and the matrix. A PFZ (precipitate free zone) deficient in γ' (Ni₃Al) forms as a band around the TGO, in which the Al component is integrated. Although TGO can resist high temperature corrosion of the top coat, it should also be considered that if its shape is irregular and contains pore defects, it may degrade the blade high temperature creep properties. Compositional and microstructural analysis results for high-temperature corrosion and TGO defects in the blade coating layer used at high temperatures are expected to be applied to sound YSZ coating and blade design technology.

• 한국재료학회지
• /
• 제34권4호
• /
• pp.208-214
• /
• 2024

To fabricate intermetallic nanoparticles with high oxygen reduction reaction activity, a high-temperature heat treatment of 700 to 1,000 ℃ is required. This heat treatment provides energy sufficient to induce an atomic rearrangement inside the alloy nanoparticles, increasing the mobility of particles, making them structurally unstable and causing a sintering phenomenon where they agglomerate together naturally. These problems cannot be avoided using a typical heat treatment process that only controls the gas atmosphere and temperature. In this study, as a strategy to overcome the limitations of the existing heat treatment process for the fabrication of intermetallic nanoparticles, we propose an interesting approach, to design a catalyst material structure for heat treatment rather than the process itself. In particular, we introduce a technology that first creates an intermetallic compound structure through a primary high-temperature heat treatment using random alloy particles coated with a carbon shell, and then establishes catalytic active sites by etching the carbon shell using a secondary heat treatment process. By using a carbon shell as a template, nanoparticles with an intermetallic structure can be kept very small while effectively controlling the catalytically active area, thereby creating an optimal alloy catalyst structure for fuel cells.

• 한국산학기술학회논문지
• /
• 제19권5호
• /
• pp.618-625
• /
• 2018

외부환경에 노출된 콘크리트 구조물은 사용기간 동안 시간의 경과함에 따라 여러 가지 환경적, 화학적, 물리적 요인들이 콘크리트 내부로 서서히 침투 및 확산되면서 콘크리트 초기의 우수한 내구성능을 저하시켜, 열화발생으로 인한 성능저하의 규명과 유지관리에 대한 중요성이 크게 부각되고 있다. 특히, 해안에 근접한 콘크리트 구조물이 동결융해 작용을 받는 경우, 동결융해의 과정에서 콘크리트 조직이 팽창 수축을 반복하면서 콘크리트의 조직이 이완되고 이때, 해수에 존재하는 염화물이온이 콘크리트 내부에 침입하게 되면, 콘크리트 구조물의 철근부식으로 인한 열화를 가속화시키기 때문에 내륙 콘크리트 건축물에 비해 내구성능의 저하가 급속히 진행됨으로 특별한 주의가 필요하다. 본 연구에서는 해수에 접한 콘크리트 구조물의 내구성 확보를 위해 광물성 혼화재료를 혼입한 코팅용 고성능 모르타르의 개발을 목적으로 하고 있으며, 모르타르의 강도 및 내구 특성에 대한 실험적 연구가 진행 되었다. 모르타르에 광물성 혼화재료인 실리카퓸, 메타카올린, 초고분말 플라이애시를 혼입하였다. 혼입률은 실리카퓸과 메타카올린은 각각 3, 7, 10%로 혼입하였으며, 초고분말 플라이애시는 5, 10, 15, 20%로 혼입하여 실험을 진행하였다. 혼화재료 혼입을 통해 제작된 모르타르 시험편을 재령 1일과 28일에 정적 강도시험을 진행하였으며, 재령 28일에 염소이온 침투저항성 시험, 황산 저항성 시험, 염해 저항성 시험 등의 열화 촉진실험을 실시하여 내구 특성을 분석하였다. 촉진 염화물이온 확산 침투 시험 결과를 이용해 국내 콘크리트학회에서 제안하는 방법과 미국, 유럽의 방법으로 내구수명을 평가해 보았다. 메타카올린 혼입 시 모든 규정에서 우수한 내구 수명으로 평가 되었으며, 메타카올린 10%혼입 시 KCI를 기준으로 약 470년의 내구수명이 예측되었다.

• 공업화학
• /
• 제31권1호
• /
• pp.43-48
• /
• 2020

본 연구에서는 침전과 수열처리에 의해 나노입방체와 나노막대구조를 갖는 Fe₂O₃ 나노입자를 합성하였다. Fe₂O₃ 나노 입자 표면에 TiO₂가 20 nm 두께로 코팅된 Fe₂O₃/TiO₂ core-shell (CS) 복합재료를 합성하였다. Fe₂O₃/TiO₂ CS를 화학적 에칭과 열처리에 의해 Fe₂O₃/TiO₂ CS에서 Fe₂O₃/TiO₂ yolk-shell (YS) 형태의 복합재료를 제조하였다. FE-SEM, HR-TEM, XRD 분석을 통하여 Fe₂O₃와 Fe₂O₃/TiO₂ CS 및 Fe₂O₃/TiO₂ YS 안료의 물리적 특성을 측정하였다. 안료를 poly acrylate (PA) 수지에 혼합한 도료들의 일사반사율과 색상변화는 UV-Vis-NIR 분석으로 차열 온도는 실험실에서 제작한 차열 온도 측정기를 통해 측정하였다. Fe₂O₃/TiO₂ YS 적색 안료를 사용한 PA 도료는 우수한 근적외선 반사율을 보였으며, Fe₂O₃ 안료를 사용한 도료에 비해 차열 온도가 13 ℃ 감소하였다.

• 한국산학기술학회논문지
• /
• 제19권7호
• /
• pp.504-509
• /
• 2018

본 연구에서는 광범위로 사용되고 있는 황색안료 중에서 고기능성을 갖는 티탄옐로우 제조하고자 하였다. Anatase Type의 $TiO_2$를 골격제로 하고 발색제 산화물인 $Cr_2O_3$을 고용시키기 위하여 $Sb_2O_3$ 산화물을 발색보조제로 사용하였으며, 안료의 제조에 사용된 출발원료로는 $TiO_2$(98%), $Sb_2O_3$(99.5%), $Cr_2O_3$(99.5%)를 사용하였다. 출발원료를 건식으로 혼합하고, 고온($1,000{\sim}1,200^{\circ}C$)으로 소결하여 결정화하고 Jar Mill을 이용하여 $1{\mu}m$이하로 습식분쇄한 후에 건조온도 $100^{\circ}C$로 12시간 건조하고 믹서기로 미분쇄하여 안료를 제조하였다. 안료의 최적 소결온도를 선정하기 위하여 소결온도 $1000^{\circ}C$, $1100^{\circ}C$, $1150^{\circ}C$, $1200^{\circ}C$의 4구간을 설정하고, X선 회절분석을 통하여 결정상을 확인한결과 $1150^{\circ}C$에서의 결정구조 Peak가 가장 좋은 것을 확인할 수 있었다. 이렇게 제조된 Rutile구조를 갖는 황색세라믹안료를 컬러강판의 코팅재료로 적용하고자 하였다. 제조된 안료에 대하여 내후성, 내산성, 내알카리성, 내열성 시험을 하여 색상변화를 측정하였으며, 유해중금속($Cr^{+6}$)검출시험을하였다. 내후성(2000hr)시험결과의 색상변화(${\Delta}E$)는 0.74, 내산성, 내알카리성, 내열성시험의 색상변화(${\Delta}E$)는 각각 0.16, 0.07, 0.29로 거의 변색되지 않은 것을 알 수 있었으며, 유해중금속($Cr^{+6}$)검출시험결과는 34ppm이었다.