This study is interested in manufacturing the concrete surface impregnants including tetra ethyl ortho silicate, alkali silicate for the repair of the exposed concrete and the color concrete requiring the advanced function in view of the concrete appearance. The surface layer change and porosity properties was tested for the review of application. The result of this study show that the effective silicate are tetra ethyl ortho silicate and alkali silicate t. The adhesion in tension is slightly increased but the reinforcement of concrete substrate is slight. So, the concrete impregnant of this study is more desirable for the improvement of durability rather than the reinforcement.

• Journal of The Korean Digital Architecture Interior Association
• /
• v.13 no.4
• /
• pp.61-68
• /
• 2013

Concrete structure is not the only material vulnerable to physical and chemical processes of deterioration associates with severe conditions. Deterioration of the concrete structure, however, occurs more progressively from the outside of the concrete exposed to severe conditions. Especially, Carbonation, chloride ion attack is more important factor of concrete durability. This study is interested in manufacturing the self-cleaning concrete surface impregnant including TEOS, lithium silicate for the repair of the exposed concrete surface and the color concrete requiring the advanced function in view of the concrete appearance. Form the results, TEOS and lithium silicate are very effective that increasing the concrete durability using self-cleaning concrete impregnant. Self-cleaning concrete impregnant specimens is satisfied with performance requirement of KS standard in adhesion test in tension but the reinforcement of concrete substrate is slight. So, the self-cleaning concrete impregnant of this study is more desirable for the improvement of durability rather than the reinforcement.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.1 no.3
• /
• pp.233-239
• /
• 2013

This study is interested in manufacturing the self-cleaning silicate concrete surface impregnant including tetra ethyl ortho silicate, lithium silicate for the repair of the exposed concrete surface and the color concrete requiring the advanced function in view of the concrete appearance. The concrete surface layer change and static contact angel was tested for the review of application. The result of this study shows that the effective silicate is tetra ethyl ortho silicate and lithium silicate. The adhesion in tension is satisfied with performance requirement of KS standard but the reinforcement of concrete substrate is slight. So, The self-cleaning silicate concrete impregnant of this study is more desirable for the improvement of durability rather than the reinforcement.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.2
• /
• pp.108-114
• /
• 2018

Degradations of durability and aesthetic performance in concrete happen during service life due to surface deterioration and dirt stains. Recently, many researches have been performed on self-cleaning and surface enhancement through surface impregnant using photocatalytic reaction with VOCs(Volatile Organic Compounds) removal. This paper is for preliminary study on surface impregnation with silicate and photocatalysis - $TiO_2$. For the work, two types of silicate based impregnants(CS - Coloidal Silica and SC - Sodium Alumina Silicate) are considered. Several tests for viscosity and surface tension are performed, and pull-off test on impregnated concrete is performed. For the surface impregnated concrete, $TiO_2$ is absorbed through submerging and spraying conditions. Through compressive strength test and SEM analysis, it is evaluated that spraying $TiO_2$ on surface impregnated concrete after 30min. of drying period is very effective both for strength enhancement and surface densification.