• The Journal of Engineering Research
• /
• v.1 no.1
• /
• pp.15-22
• /
• 1997

The crystallization behaviours of cordierite gel derived from sol-gel method and glass prepared from conventional melting method with or without $TiO_2$ as nucleants are compared. The densification temperature of gel is $810^{\circ}C$ and its chemical structure identified by IR analysis is same as that of glass melted by conventional method. The beginning crystallization temperature of gel is $965^{\circ}C$ lower than that of melted glass with 10wt% $TiO_2$, which is $978^{\circ}C$. The crystalline phases developed from gel during heat treatment are identified as spinel, $\beta$-quartz solid solution and $\alpha$-cordierite crystal and crystalline phases in case of glass are (Mg,Al)TiOn and $\beta$-quartz solid solution and $\alpha$-cordierite crystal, respectively. The crystallization in melted glass with nucleants occurs through bulk crystallization and in case of that without nucleants surface crystallization occurs, while the crystallization in gel is internal crystallization from interface between particles formed after densification.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.04a
• /
• pp.111.1-111
• /
• 2003

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.12
• /
• pp.3061-3071
• /
• 2000

Densification behavior of titanium alloy powder was investigated under hot pressing at various pressures and temperatures. Experimental date were obtained for densification of titanium alloy powder under an instantaneous loading and subsequent creep deformation during hot pressing. The constitutive models of Fleck et al. and the modified Gurson were employed for thermo-phastic deformation under the instantaneous loading and that f Abouaf and co-workers for creep deformation of titanium alloy powder during hot pressing. By implementing these constitutive equations into a finite element program(ABAQUS), finite element results were compared with experimental data during hot pressing. To investigate the effect of friction between the power and die wall, density distributions of power compacts were measured and compared with finite element calculations. Finite element results from the models of Fleck et al. and the modified Gurson agreed reasonably good with experimental data for densification and density distribution of titanium alloy powder under the instantaneous loading during hot pressing. Finite element results from the model of Abouaf and co-workers, however, somewhat overestimate experimental data for creep deformation of power compacts during hot pressing.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.5 no.2
• /
• pp.98-102
• /
• 2004

Ion exchange behavior and property change of soda-lime-silicate glass by advanced ion exchange process were investigated. Refractive index, specific gravity and optical transmittance were changed similarly to $K^+$ ion penetration depth, and amount of ion exchange increased with the increase of the time and temperature. Especially, thermal expansion decreased greatly because of the structural compaction and residual stress by ion exchange process.

• Journal of the Korean Ceramic Society
• /
• v.37 no.11
• /
• pp.1071-1077
• /
• 2000

표면 윤활층을 가진 나노 알루미나를 진공중에서 가압성형함으로써 결함발생없이 높은 충전압력을 가할 수 있었으며, 높은 밀도, 미세기공, 좁은 기공경 분포를 가지는 성형체를 제조할 수 있었다. 윤활제의 화학 및 기계적 특성에 의하여 변하는 모세관 현상을 조정함으로써 충전효율을 증대하고 결함발생을 억제할 수 있다. 나노분말의 소결에서도 성형 미세구조의 균일도가 치밀화 거동에 여전히 지배적인 역할을 하였다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.34 no.2
• /
• pp.73-77
• /
• 2024

The spinel-type oxide (Ni_x, Mn_y, Co_3-x-y)O₄ (NMC) is widely utilized as a material for temperature sensors with a negative temperature coefficient (NTC), finding applications across various industries including electric vehicle battery management systems. Typically, NMC is manufactured using solid-state reaction methods employing powders of Ni, Mn, and Co compounds, with the densification process through sintering recognized as a crucial factor determining the electrical properties of the temperature sensor material. In this study, NMC pellets were synthesized via solid-state reaction and their crystallographic and microstructural characteristics were investigated. Also, the activation energy for densification behavior during the sintering process was determined. According to the analysis results, the room temperature resistance of the NMC pellets was measured at 10.03 Kohm, with the sensitivity parameter, B-value, recorded at 3601.8 K, indicating their potential applicability as temperature sensors across various industrial fields. Furthermore, the activation energy for densification was found to be 273.3 ± 0.4 kJ/mol, providing valuable insights into the thermodynamic aspects of the sintering process of the NMC.

• Applied Chemistry for Engineering
• /
• v.8 no.5
• /
• pp.853-859
• /
• 1997

For asymmetric polyetherimide membranes having a dense layer gradient structure on the skin layer, the morphology change and pervaporation behaviors of water/isopropanol mixture through chemical modification of dense skin layer were investigated. The extent of the density was controlled by the evaporation, time, and when the evaporation time was increased from 0 min to 4 min, the permeation flux was decreased, the separation factor was increased. Also, the pervaporation behaviors of the polyetherimide membranes modified with sodium hydroxide solution, as the modification time of dense skin layer increased, the selectivity increased, and the permeation flux decreased. The morphology change identified by SEM shows that the density of dense skin layer tends to increase with increasing modification time, this result is consistent with above observations.

• Korean Journal of Materials Research
• /
• v.8 no.1
• /
• pp.58-63
• /
• 1998

5-64.3mol% AI$_{2}$O$_{3}$를 함유하는 AIN(1wt% $Y_{2}$O$_{3}$)의 1650-190$0^{\circ}C$ 상압소결에 따른 치밀화 거동, 미세구조, 열전도도가 검토 되었다. XRD 분석결과, AION(5NIN \ulcorner9 AI$_{2}$O$_{3}$ ), 27R AIN다형, AIN이 소결체의 주상으로서 동정되었다. AI$_{2}$O$_{3}$ 의 함량이 증가할수록 소결체의 부피밀도는 증가 하였다. AION을 기지상으로 하는 물질($\geq$ 30mol% AI$_{2}$O$_{3}$ )인 경우는 175$0^{\circ}C$ 소결에서 최대의 부피밀도를 나타내었으며, AIN을 기지상으로 하는 경우(5mol% AI$_{2}$O$_{3}$ ) 는 소결온도가 증가할수록 밀도가 감소하였다. $Y_{2}$O$_{3}$의 존재하에서 주로 185$0^{\circ}C$이상에서 AI$_{2}$O$_{3}$ 와 AIN의 반응에 으해서 액상이 생성되었다. AION을 기지로 하는 물질의 치밀화는 주로 액상의생성 및 AION의 입성장에 의해서 지배되었으나, AIN을 기지로 하는 물질에 있어서는 1$650^{\circ}C$에서 액상이 생성되었고, 소결온도가 190$0^{\circ}C$까지 상승할 동안 AIN의 입성장은 크게 일어나지 않았다. AI$_{2}$O$_{3}$ 함량이 증가할수록 낮은 열도도를 갖는 다량의 AION 및 액상의 생성으로 인하여 소결체의열전도도는 감소 하였다. 5mol% AI$_{2}$O$_{3}$ 를 함유한 190$0^{\circ}C$ 소결체가 최대의 열전도도(77.9W/(m\ulcornerk))를 나타내었다.

• Journal of the Korean Ceramic Society
• /
• v.30 no.6
• /
• pp.449-456
• /
• 1993

Sintering behaviour of zirconia powders prepared by different processing treatment was discussed. About >99% densities of theoretical were obtaiend on sintering at 140$0^{\circ}C$ for 2h in case of 300MPa uniaxially cold-pressed compact. But the lower densities were obtained on sintering above this temperature due to abnormal grain growth enabling the tetragonal to monoclinic phase transformation during cooling resulted in microcracks. All kinds of different dried powders exhibited nearly the same shrinkage behaviour with end-point shrinkage between 19 and 20%, and had maximum shrinkage rate (0.99~1.27%/min) around 120$0^{\circ}C$. During whole sintering process densification was mainly governed by grain growth and rearrangement of agglomerates. Heterogeneous abnormal grain growth and abrupt decrease in shrinkage were observed when continuous interagglomerate pore collapsed into isolated pores.

• ETRI Journal
• /
• v.13 no.2
• /
• pp.42-53
• /
• 1991

고유전율 적충세라믹 커패시터 소재인 $BaTiO_3$ 자기물은 일반적으로 큐리오도인 약 $120^{\circ}C$부근에서 유전율이 최고 약 10,000정도로 증가한 다음 급격히 감소하므로 적절한 이동체를 첨가하여 큐리온도를 상온으로 이동시켜 상온에서 최대 유전율을 이용하여야 한다. 그리고$BaTiO_3$ 자기물은 $1300^{\circ}C$이상의 고온소결시 고가인 Pd전극이 요구된다. 그러나 자기물의 소결온도를 저온화화면 저가의 Ag합금으로 전극재료를 대체할 수 있다. 본 연구에서는 이동제로서 $CaSnO_3$ 를 이용하여 큐리온도를 상온으로 이동시켰다. 또한 소결온도를 저온화하기 위하여 $BaTiO_3$ 세라믹에 여러가지 산화물을 첨가하여 소결현상을 살펴보았다. 실험결과 첨가제를 넣지 않은 경우 소결온도는 $1350^{\circ}C$의 고온이 필요한 반면, $CuO,B_2O_3$는 $1050^{\circ}C$의 낮은 온도에서도 치밀화와 입도성장이 잘 일어났다. 특히 $B_2$$O_3$ 를 첨가한 경우는 $1250^{\circ}C$이상에서 소결할 때 절연저항이 낮아 유전손실이 큰 문제점을 보였지만, 최대 유전율이 11,000 정도로 높고, 양호한 유전율의 온도변화 특성을 나타내어 우수한 고유전율 소재의 첨가제로 응용될 가능성을 보였다