• Journal of the Korean Ceramic Society
• /
• v.29 no.6
• /
• pp.489-495
• /
• 1992

The continuous compaction response of zirconia powders prepared by different processing treatments was investigated. Though the yield point could be or not below 1 MPa, the change of slope was always observed at high pressure range around 60 MPa. Powder compaction was mainly governed by second compaction stage and compaction rate was decreased with increasing forming pressure. Rotary vacuum dried powder favored a high compaction density, whereas freeze dried and calcined powders favored an increase in the pressing efficiency. In order to extract more reliable information about powder compaction, it was necessary to use not only compaction response diagram but also compaction rate diagram.

• Transactions of Materials Processing
• /
• v.1 no.2
• /
• pp.14-19
• /
• 1992

분말단조 공정의 해석을 위한 기초연구로서 고용 업셋에 의한 다공질 합금강 프리폼의 치밀화와 소성 변형거동에 관하여 조사하였다. 다공질 프리폼의 소성 유동응력은 용도의 상승에 떠라 감소하였고, 변형속도의 증가에 따라 증가함을 보였다. 또한, 다공질 프리폼의 초기밀도가 더 높을수록 동일한 온도와 하중조건에서 더 높은 치밀화를 보였다. 또한, 밀도변화에 따른 프와송 비를 실험치로 부터 구하였고, 배불림 현상과 체적변화를 고려하여 온도에 따른 진응력-진변형률 관계를 구하였다.

• Journal of the Korean Ceramic Society
• /
• v.38 no.8
• /
• pp.740-748
• /
• 2001

출발원료 Si 분말의 입자크기를 다양하게 하여 질화반응 및 가스압 소결시 입자크기에 따른 산소함량의 차이에서 나타나는 상변화와 그로 인한 치밀화 거동, 미세구조 발달 및 기계적 특성에 대하여 고찰하였다. 145$0^{\circ}C$의 질화반응에서는 조대분말을 사용한 경우가 미세분말을 사용한 경우보다 높은 질화율을 나타냈으며, 각 분말크기에 따른 native oxide의 함량차에 따라 각기 다른 2차 결정상들이 검출되었다. 조대분말을 사용한 경우에는 제 2상의 석출로 인한 액상량의 부족으로 고온의 소결온도에서도 치밀화를 이루지 못해 낮은 강도값을 나타내었다. 한편, 미세분말을 사용한 경우에는 질화반응 후 석출된 제 2상이 소결온도가 증가함에 따라 용융되면서 치밀화를 이루어 높은 강도값을 나타내었다. 높은 강도값은 미세분말을 사용한 시편들에서 얻어졌으나 높은 파괴인성값은 상대적으로 큰 분말을 사용한 시편들에서 얻어졌는데, 이는 미세한 입자들로 구성된 기지상 내에 잘 발달된 주상정 입자들을 갖는 미세구조에 기인된 것으로 사료된다.

• Journal of the Korean Ceramic Society
• /
• v.39 no.1
• /
• pp.45-50
• /
• 2002

Effect of sintering additives on the densification behavior of reaction-bonded silicon nitride prepared by using coarse Si powders is discussed. Sintering additives such as 6 wt% $Y_2O_3$+1wt% $A1_2O_3$ (6YlA) did not give rise to full densification, while full densification was obtained by using the sintering additives such as 6wt% $Y_2O_3$+3 wt% $A1_2O_3$+ 2wt% $SiO_2$ (6Y3A2S) and 9wt% $Y_2O_3$+ 1.5wt% $A1_2O_3$+ 3wt% $SiO_2$ (9Yl.5A3S). In the case of 6Y3A2S addition, high fracture strength of 960 MPa and the fracture toughness of $6.5 MPa.m^{1/2}$ were obtained.

• Journal of the Korean Ceramic Society
• /
• v.38 no.6
• /
• pp.582-586
• /
• 2001

방전 플라즈마 소결법을 이용하여 ZrB$_2$-ZrC 복합체를 소결하여 소결 거동과 미세구조에 대하여 조사하였다. 소결 조제로서 란타늄을 첨가하였을 경우에 첨가하지 않았을 경우보다 더 낮은 온도에서 소결 수축이 시작되었으며, 180$0^{\circ}C$에서 거의 치밀화가 완성되었다. 란타늄은 방전플라즈마 소결시 초기 분말 간 액상 형성으로 물질이동을 가속화하여 ZrB$_2$-ZrC 복합체의 치밀화에 커다란 기여를 하며, 냉각 시에 재결정화하여 결정립계와 결정립 삼중점에 란타늄이 포함된 이차상을 형성하는 것으로 확인되었다. 또한 ZrB$_2$-ZrC는 강한 공유결합성 재료임에도 불구하고 미세 구조 내에 잘 발달된 전위 구조를 형성하고 있음을 확인하였다.

• Proceedings of the KSME Conference
• /
• 2000.04a
• /
• pp.393-398
• /
• 2000

Densification behavior of mixed copper and tool steel powder under cold compaction was investigated. By mixing the yield functions originally proposed by Fleck-Gurson for pure powder, a new mixed yield functions In terms of volume fractions and contact numbers of Cu powder were employed in the constitutive models. The constitutive equations were implemented into a finite element program (ABAQUS) to compare with experimental data. and with calculated results from the model of Kim et at. for densification of mixed powder under cold isostatic pressing and cold die compaction. Finite element calculations by using the yield functions mixed by contact numbers of Cu powder agreed better with experimental data than those by volume fractions of Cu powder.