• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.3
• /
• pp.338-347
• /
• 2021

This paper aims to evaluating the interlayer strength of 3D-printed concrete with interlayer reinforcement. According to lap splices, two reinforcement methods were considered. One method did not include lap splices of interlayer reinforcement, but the other method included lap splices with length of 40mm. In addition, two different curing conditions were applied: air curing conditions and water curing conditions. The compressive, splitting tensile, and flexural tensile strengths of 3D-printed concrete specimens were measured in three loading directions with different reinforcement methods and curing conditions. Splitting and flexural tensile strengths decreased considerably when tensile stresses acted over the interlayers of 3D-printed concrete specimens. However, the flexural tensile strength or interlayer bonding strength of the printed specimens increased significantly at the interlayers when the longitudinal interlayer reinforcement penetrated printed layers. Interlayer bonding strength of printed concrete decreased after air curing treatment was applied because interlayers of printed concrete with more pores formed by the air cu ring conditions are more vulnerable to the load.

• Composites Research
• /
• v.24 no.5
• /
• pp.34-38
• /
• 2011

Carbon nanotubes (CNTs) have been widely investigated as reinforcements of CNT/polymer nanocomposites to enhance mechanical and electrical properties of polymer matrices since their discovery in the early 90's. Furthermore, the number of studies about incorporating CNTs into carbon fiber reinforced plastics (CFRP) to reinforce their polymer matrices is increasing recently. In this study, single-walled carbon nanotubes (SWNT) were dispersed in epoxy with 0.2 wt.% and 0.5 wt.%. Then, the SWNT/epoxy mixtures were processed to carbon fiber composites by a vacuum assisted resin transfer molding (VARTM) and a wet lay up method. The processed composite samples were tested for the interlaminar shear strength (ILSS). The relationship between the interlaminar shear strengths and processing, and the reinforcement mechanism of carbon nanotubes were investigated. CNT/epoxy nanocomposite specimens showed the increased tensile properties. However, the ILSS of carbon fiber composites was not enhanced by reinforcing the matrix with CNTs because of processing issues caused by increased viscosity of the matrix due to addition of CNTs particularly for a VARTM method.

• Composites Research
• /
• v.20 no.6
• /
• pp.8-14
• /
• 2007

Debonding failure characteristics of the composite skin-stiffener specimens were experimentally investigated. The influences of bonding methods, types of stiffener shape and various secondary bonding parameters were evaluated. Present test results combined with the previous test results[1] showed that the failure displacement of the skin-stiffener specimens well evaluates the skin-stiffener debonding failure strength of the composite stiffened panels. The specimens with an open type stiffener had lower bending stiffness and larger failure displacement than those with a closed type stiffener. Secondary bonding and co-curing with adhesive had better failure strength than co-curing without adhesive film. Secondary bonded specimens failed by adhesive failure and co-cured specimens failed by delamination failure. As the bondline thickness was thinner, the skin-stiffener specimens had higher failure strength. The fillets had no influence on failure strength of the specimens. The influence of the surface roughness was shown according to types of stiffener shape.

• Applied Chemistry for Engineering
• /
• v.9 no.5
• /
• pp.715-718
• /
• 1998

In this work, bisphenol type vinyl ester was impregnated into the three-dimensional glass fabrics fabricated from different thickness changes. Their mechanical properties of the specimens have been investigated by three-point bending and flatwise compression tests. Also, interlaminar shear strength (ILSS) has been determined through short-beam test for the evaluation of interfacial adhesion at interfaces between fibers and matrix of the composites. The effect of thickness changes in three-dimensional glass fabric-reinforced composites have been described in this work.

• Composites Research
• /
• v.24 no.5
• /
• pp.39-43
• /
• 2011

For the last twenty years, nanocomposites composed of polymer matrices reinforced with carbon nanotubes (CNTs) have been an active research area. Also, the polymeric nanocomposites reinforced with CNTs are being investigated to be used matrices of carbon fiber composites. Carbon tiber composites have achieved advanced properties in the direction of carbon fibers due to enhanced carbon fiber properties. However, the matrix dominated properties need to be improved further to fully utilize the advanced carbon fiber properties. In particular, delamination is a typical and critical reason for fracture of carbon fiber composites. Mode I fracture toughness test which is also often called double cantilever beam (DCB) test shows the resistance to delamination of carbon fiber composites and this test is performed on carbon fiber composite samples incorporated with carbon nanotubes functionalized with various functional groups. The specimens with mat-like CNT layers showed the increased fracture toughness by 10.6%.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.36 no.6
• /
• pp.550-557
• /
• 2008

Delamination damage at a bolt hole in a composite stiffened panel was detected using a built-in piezoelectric active sensor array. Various signal processing techniques were used to detect an invisible small scale delamination around a fastener hole due to localized transverse loading. A built-in piezoelectric sensor array was used to generate diagnostic signals and to measure response signals. Then, the response signals were processed to extract damage-sensitive features. Damage indexes were calculated to estimate the severity and location of the damage from the features.

• Composites Research
• /
• v.26 no.2
• /
• pp.129-134
• /
• 2013

The strength of adhesive joints employed in composite structures under cryogenic environments, such as LNG tanks, is affected by thermal residual stress generated from the large temperature difference between the bonding process and the operating temperature. Aramid fibers are noted for their low coefficient of thermal expansion (CTE) and have been used to control the CTE of thermosetting resins. However, aramid composites exhibit poor adhesion between the fibers and the resin because the aramid fibers are chemically inert and contain insufficient functional groups. In this work, electrospun meta-aramid nanofiber-reinforced epoxy adhesive was fabricated to improve the interfacial bonding between the adhesive and the fibers under cryogenic temperatures. The CTE of the nanofiber-reinforced adhesives were measured, and the effect on the adhesion strength was investigated at single-lap joints under cryogenic temperatures. The fracture toughness of the adhesive joints was measured using a Double Cantilever Beam (DCB) test.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.3 no.2
• /
• pp.199-204
• /
• 1999

A recent application of advanced composite materials, primarily fiber-reinforced plastic (FRP) composites, in structures is the reinforcement of conventional structural materials, such as concrete and glued-laminated timber (glulam), to increase their performance. In particular, the construction of large-scale glulam structures usually requires members with large depths and to significantly increase the stiffness and strength of glulam, the members can be reinforced with FRP at top and bottom surfaces. In this paper, glulam beams reinforced with GFRP strip are tested under 2-point bending and results are compared with numerical solution using layer-wise beam theory.

• Journal of Korean Society of Steel Construction
• /
• v.21 no.1
• /
• pp.71-81
• /
• 2009

In this study, the seismic performance of the Buckling Restrained Knee Bracing (BRKB) system was evaluated through a pin-connected one-bay, one-story frame. The BRKB system developed in this study was composed of a steel plate as a load-resisting core member and two channel sections to restrain local and global buckling of the core plate. The main purpose of the BRKB system is to restrengthen/rehabilitate old low- and mid-rise RC buildings, which, it is assumed, were designed with non-seismic designs and details. The main variables for the test specimens were the size of the core plates and the stiffeners, and the condition of the end plates. The test results showed that the size of the core plate, which was the main element of the load-resisting member, was the most important parameter in achieving a ductile behavior under tension as well as compression until the maximum displacement exceeds twice the design drift limit.

• Composites Research
• /
• v.35 no.4
• /
• pp.269-276
• /
• 2022

In this paper, a composite stiffened panel was fabricated using a three-dimensional weaving method that can reduce the risk of delamination, and mechanical properties such as buckling load and natural frequency were investigated. The preform of the stringer and skin of the stiffened panel were fabricated in one piece using T800 grade carbon fiber and then, resin (EP2400) was injected into the preform. The compression test and natural frequency measurement were performed for the stiffened panel, and the results were compared with the finite element analyses. In order to compare the performance of 3D weaving structures, the stiffened panels with the same configuration were fabricated using UD and 2D plain weave (fabric) prepregs. Compared to the tested buckling load of the 3D woven panel, the buckling loads of the stiffened panels of UD prepreg and 2D plain weave exhibited +20% and -3% differences, respectively. From this study, it was confirmed that the buckling load of the stiffened panel manufactured by 3D weaving method was lower than that of the UD prepreg panel, but showed a slightly higher value than that of the 2D plain weave panel.