• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.11a
• /
• pp.769-772
• /
• 2004

Very-Early-Strength Latex-Modified Concrete(VESLMC) provides the repairing material with short curing time as well as excellent bond strength, flexural strength and impermeability against water and chloride. In 2001, VESLMC introduced in Korea and improved superior material through research and development on material properties and durability. In 2003, the field test progressed for study problems of VESLMC field application. This paper introduced equipment improvement for bridge deck repair save both repair time and labor, while producing quality VESLMC structures.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.1029-1034
• /
• 2001

The purpose of this research is to develop rapid setting cement latex modified concrete (RSLMC) which will be used to overlay bridge deck for maintaining and repairing. The main experimental variables were the types of rapid setting cement and variation of latex and antifoam agent contents were selected as admixture factor, then the properties of workability and strength development and durability properties were investigated. The results of this study show that latex content give increment of a slump due to surface tension in polymer particles and reduce unit weight of water for preservation of workability. In addition, When no and 1.6~3.2% antifoam agent were mixed, 8%, 2.0~3.8% were respectively obtained. An increasing the amount of latex produced concrete with increased flexural strength, but with slightly lower compressive strength. Rapid chloride permeability and freezing-thawing test carried out. As a results, according to increment of containing ratio antifoamer, strength of RSLMC increase, permeability showed lower value than ignorable 100 coulombs. Also, in the case of more than antifoamer 1.6%, the relativity dynamic modulus is mantained more than 90%, but in case of 0, 5%, it decrease. In consequence, with the view of strength and workability of RSLMC, it is considered that appropriate content ratio of antifoam agent and latex solid are respectively 1.6% by latex weight, 15% by cement weight.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.11a
• /
• pp.269-272
• /
• 2004

After concrete casts, temperature decent and shrinkage bring volume changes of concrete pavement. Microcracking and cracking in concrete pavement are caused by these volume changes. As a result, durability of concrete pavement is deteriorated. Recently, Very-Early Strength Latex Modified concrete(below:VESLMC) from the beginning of High-Way is used as urgent repair material for bridge deck. The advantage of VESLMC is that compressive and flexural strength at 3 hours age are 4.5MPa and 21MPa respectively. It allows the traffic to open in 3 hours. But, this material has the problem which is early-age shrinkage cracking caused by water self-dissipation with rapid hydration reaction and water evaporation with body dry. Unfortunately, until now, the research about early-age shrinkage of VESLMC leaves something to be desired. Therefore, the purpose of this study is to present the early-age shrinkage of VESLMC respect to latex contents and shrinkage ratio to maximum length change that can help field engineers' skill. Latex contents of 0, 5, 10, 15, $20\%$ in standard of same workability in VESLMC are selected by experimental variables. After initial set, shrinkage value was measured with 10mm LVDT for 3 days. The results of maximum shrinkage ratio were 0.019, 0.017, 0.023, $0.027\%$ respectively.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.11 no.3
• /
• pp.1040-1046
• /
• 2010

The main disadvantage of rapid setting concrete is the occurrence of cracking because of fast hydration reaction due to high thermal expansion and shrinkage. However, if the fly ash is used in concrete, it is possible to prevent cracking since the hydration heat can be decreased. Although Very-Early Strength-Latex Modified Concrete(VES-LMC) is an excellent material, occurrence of cracking has been reported because of high hydration heat. In the present study, new method which can apply the fly ash to the VES-LMC was developed. Research for the new method to improve the safety for the cracking was conducted. Safety was confirmed by reducing the shrinkage and hydration heat in the condition of overcoming the low early-age strength. Detailed conclusions are follows. Early-age compressive strength was decreased a little with increase of UFFA content. However, 28-d compressive strength was statistically insignificant regardless of UFFA contents. If the UFFA is replaced 15% to 20% of unit cement weight in concrete, maximum shrinkage can be reduced up to 43% to 47%. Usage of UFFA in VES-LMC guarantees the safety for cracking since it is very effective to control of early-age shrinkage.