• Journal of the Korean Magnetics Society
• /
• v.4 no.2
• /
• pp.94-99
• /
• 1994

This work addresses the relationship between initial complex permeability and porosity in polycrystalline Mg-ferrite material. The initial permeability corresponds to Snoek theory except the sample with large grains. The frequency which initial real permeability, $\mu$' equal 1 due to domain rotation are found in the frequency range 50-80 [MHz]. Internal magnetic field which is considered as mainly anisotropy field is 100[Oe] which is obtained from the relationship between initial complex permeability and porosity in polycrystalline Mg-ferrite material. This is almost the half value of reported anisotropy field of single Mg-ferrite. The difference between them is almost due to domain wall effect in polycrystalIine Mg-ferrite material.

• Journal of the Korean Magnetics Society
• /
• v.11 no.1
• /
• pp.26-31
• /
• 2001

The effect of MoO$_3$ addition on the permeability of Mn-Zn ferrites was studied. 600 ppm, 800 ppm and 1,000 ppm of MoO$_3$ were added to the main composition after calcination. Ferrite cores were sintered at 135$0^{\circ}C$ for 3hrs, followed by cooling according to the equilibrium oxygen concentration. The initial permeability was about 8,000 with heating rate 5$^{\circ}C$/min for 3hrs without MoO$_3$ addition. When 600 ppm and 800 ppm of MoO$_3$ were added, the initial permeabilities, 13,200 and 13,550 were obtained, respectively. However, the sample with 1,000 ppm MoO$_3$ showed lower permeabilities because of abnormal grain growth. At the heating rate 1$0^{\circ}C$/min, the ferrite cores with 1,000 ppm MoO$_3$ demonstrated the highest initial permeability greater than 15,000, without exaggerated grain growth.

• Journal of the Korean Magnetics Society
• /
• v.7 no.2
• /
• pp.69-75
• /
• 1997

The effect of oxide additive system and $Po_2$ condition on the power loss, microstructure, initial permeability, ${\mu}_i$ vs. temperature curve of Mn-Zn ferrites has been investigated. The density and permeability increased with various additive systems while the power loss decreased. It was confirmed that the oxide additives are grain boundary materials and do not change the magnetic properties of Mn-Zn ferrites such as $T_{spm}$ and $T_c$. The ${\mu}_i$ vs. T curve indicated that $T_{spm}$ moved to the higher temperature as $Po_2$ increased. It was also confirmed that the microstructure of Mn-Zn ferrites was independent of the $Po_2$ control during cooling.

• Resources Recycling
• /
• v.7 no.4
• /
• pp.27-34
• /
• 1998

In this research, the processing control of NiCuZn Ferrite (NCZF) had been studied. NiCuZn Ferrite, which calcined at $700^{\circ}C$ for 3 bours, was ball milled for about 60 hours to ill김ke a size of $0.5\mu\;extrm{m}$ followed by granulation using spray dryer Apparent densincatioo rate and initial permeability of NiCuZn Ferrite with an initial packing density had been investigated as f follows. 1.The relative packing density of NCZF green body increas$\xi$d in the range of 48.6-56.8% with an increased forming pressure of 20-170 MPa. 2. The higher the relative pac퍼ng density of NCZF and the sintering temperature are, the higher the initial densification rate. The increased bulk rlcnsity of NCZF was attributed to the densification rate with decreased open pore and increased closed pore as the relative packing density, sintering temperature, and sinteriog tim$\xi$ increased. 3. The initial P permeability of NCZF with constant composition is logarithmically proportional to the bulk density of NCZF sintered at $875~925^{\circ}C$ for 0-5h, and strongly depended on the relative packing density of NCZF green body. The empirical equation is as f follows; log $\mu$i=$G1{\times}BD$+$G2{\times}RPD$+b(0);where, G1, G2; gradient, B.D: bulk density, RPD; relative packing density, b(0); intercept.

• Journal of the Korean Magnetics Society
• /
• v.2 no.2
• /
• pp.105-113
• /
• 1992

조성이 Mn$_{x}$Zn$_{1-x}$ Fe$_{2}$O$_{4}$ 훼라이트(x=0.75, 0.52)를 pusher type 연속 전기로를 이용하여 질소 분위기하에서 1360 .deg. C 로 3시간 동안 소결하여 얻어냈다. 본 연구에서는 스피넬 구조인 Mn-Zn 훼라이트의 FMR(Ferrimagnetic Resonance) 스펙트럼 특징과 초기투자율과의 상관성을 조사하고자 EPR X-band 스펙 트로미터를 이용 9.50 GHz의 microwave frequency에서 FMR 실험을 수행하였다. FMR 공명흡수선은 주 자기공명 흡 수선외에 낮은 자기장에서 약한 subsidiary 공명흡수선을 나타내는데 온도변화에 따른 주 자기공명 흡수선과 sub- sidiary 공명흡수선(제2, 제3 공명흡수선)의 세기, 공명선폭, g값 등의 온도 의존성을 연구함으로써 제2 공명흡수 선이 나타나는 원인을 분석하였으며, 자기공명 흡수선의 g값, 자기공명선 세기, 그리고 공명선폭과 초기투자율의 상관성을 연구하였다. 실험 결과 주 자기공명 흡수선의 g값, 자기공명선 세기, 공명선폭은 초기투자율 값과 밀접 한 관련이 있음을 확인할 수 있었다.었다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.237-238
• /
• 2007

전동기 코어 소재로 사용하는 무방향성 규소강판을 토로이달 형태가 아닌 전동기 적용 모형과 동일한 적층형으로 회전자 코어를 제작하여 초기 및 포화 자화 특성에 대한 고찰을 하였다. 초기자화 특성은 전동기가 처음 기동할 때 토크나 기동전류에 큰 영향을 미친다. 초기 자화 특성을 향상시키면 기동 전류를 줄일 뿐 아니라 전동기의 장기간 수명에도 영향을 미친다. 본 연구에서는 무방향성 규소강판의 가공, 설계, 제작 특성이 초기 기동 특성에 미치는 영향을 간접적으로 조사하기 위하여 초기로 포화 히스테리시스 특성에 대한 고찰을 실시하고 이들 요소가 갖는 여러 가지 가능성을 제시하였다.

• Journal of the Korean Magnetics Society
• /
• v.11 no.5
• /
• pp.226-231
• /
• 2001

The effect of interface reaction between Mn-Zn ferrite single crystal and 61 SiO$_2$-23Pbo-6ZnO-8Na$_2$O-2K$_2$O (mol%) glass on the magnetic properties of the ferrite was investigated. After the reaction, the hump of Zn concentration appeared at the ferrite adjacent to the interface. The initial permeability of the ferrite bonded with the glass at 700 $^{\circ}C$ was 1766 at 100 KHz and reduced to 907 after reaction at 1000$^{\circ}C$. The permeability degradation with increasing reaction temperature was considered to be attributed not only to the sixe diminution of the ferrite due to the its dissolution into the glass but also to the residual stress due to the difference in expansion coefficient between the ferrite and the diffusion layer-the region of the hump of Zn concentration-adjacent to the interface.

• 한국신재생에너지학회:학술대회논문집
• /
• 2011.05a
• /
• pp.199-199
• /
• 2011

ATES(Aquifer Thermal Energy Storage) 열펌프 시스템은 기존의 다양한 열원 적용 시스템 대비 효율이 우수한 것으로 알려져 유럽과 미국에서 건물 냉난방 시스템으로 적용되고 있다. 특히, ATES 시스템은 기존의 냉난방 시스템 대비 경제성이 우수한 것으로 알려져 있으나 국내에서는 이에 대한 연구 결과는 전무한 실정이다. 본 연구에서는 ATES 열펌프 시스템의 실증 성능 결과를 분석하였으며, LNG 보일러와 에어컨을 사용하는 기존의 냉난방 시스템을 비교시스템으로 ATES 열펌프 시스템의 경제성 평가를 수행하였다. ATES 시스템의 연간 실증 성능 실험결과 ATES 시스템은 외기온도와 무관하게 연중 안정적인 성능을 나타내었다. 경제성 평가시에 생애주기법(Life Cycle Cost)을 적용하여 ATES 열펌프 시스템의 설치 및 운전에 필요한 총 소요비용을 산정하고, 이 결과를 바탕으로 투자회수기간법을 통해 ATES 시스템의 투자회수 기간을 산정하였다. 생애주기법 적용 시에 현재가치법을 사용하였으며, 현재가치법은 수명주기에 발생하는 모든 투자비용과 절감액을 일정한 시점을 기준으로 등가환산하는 방법을 의미한다. 현재가치법에 사용되는 현재가치는 초기비용과 현재가치계수의 곱으로 나타나는데, 여기에서 현재가치계수는 임의의 이자율로 일정기간 동안 정기적인 할부금액이 적립될 때의 현재금액을 구하기 위해 사용하는 계수를 의미한다. 전기와 LNG는 각각 2009년 7월의 (주)한국전력공사와 (주)한국가스공사의 고시요금을 적용하였다. 본 시스템은 실증 설비용량인 20RT를 대상 건물로 가정하였고, 초기투자비는 크게 공사비와 냉난방 설비 구입비로 구성되어 있으며, 기본적인 물가지표는 (사)한국물가정보(KPI)의 고시 데이터를 참조하였다. 각 시스템의 초기투자비는 ATES 시스템이 비교대상 기존 냉난방 시스템 대비 5.7배 높게 나타났다. 일일 8시간 사용기준으로 계절별 전력요금을 고려한 연간운전 비용은 ATES 시스템이 기존 시스템 대비 냉난방 시에 각각 77%와 16%를 나타내어 운전비용이 연간 절감되었고, 난방 운전 시 절감 비율이 냉방시보다 크게 나타났다. 두 시스템에 대한 생애주기비용을 산정하기 위하여 에어컨과 보일러의 기존시스템과 ATES 시스템의 가용연수를 모두 20년으로 설정하였고, 유지보수 비용은 초기투자비용의 2%로 설정하고, 할인율은 은행 예금이자를 기준으로 5%로 설정하였다. 전기와 LNG의 요금 상승률은 (사)한국물가정보를 바탕으로 각각 2%와 8%로 가정하였다. 이러한 조건에서 생애주기법을 이용한 경제성평가는 ATES 시스템의 경우 생애운전비용이 초기투자비용보다 작게 나타났으며, 기존 냉난방 시스템은 생애운전비용이 초기투자비용에 비하여 높게 나타났다. 본 연구 대상 ATES 열펌프 시스템의 실증 성능 데이터와 기존 문헌으로부터 얻은 냉난방 시스템의 성능 결과를 이용하여 생애주기 비용을 적용한 결과 ATES 시스템의 기존 시스템 대비 투자회수 기간은 6.62년으로 나타났다. 특히, 본 연구에서는 ATES 시스템이 국내 최초로 적용됨에 따라 스크린 등의 부품을 다소 고가의 제품으로 시스템에 적용하였으므로 ATES 시스템의 신뢰성과 안정성이 확보되면 초기 투자비 감소가 가능할 것으로 예상되며, 기존 시스템 대비 투자회수 기간은 더욱 감소될 수 있을 것으로 예상된다.

• Journal of the Korean Magnetics Society
• /
• v.16 no.5
• /
• pp.234-239
• /
• 2006

We measured the microwave permeability in the frequency range of 100 MHz$\sim$9 GHz in the exchange biased CoFe/MnIr films. The results were analyzed based on the Landau-Lifshitz-Gilbert theory. The initial permeability and ferromagnetic resonance frequency was tuned by controlling the CoFe thickness and unidirectional anisotropy. The tunable range of ferromagnetic resonance frequency was up to 20 GHz in the thin CoFe layer of 1.5 nm. The CoFe/MnIr films showed the high permeability and low loss properties in the microwave frequency range. Thus, this material could be applied to the microwave devices.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.30 no.5
• /
• pp.464-470
• /
• 2010

The integrity of the industrial equipment in use under high temperature and high pressure must be assessed by regularly measuring the degraded mechanical properties during service time. In order to nondestructively monitor the degraded mechanical properties of industrial equipment, a measuring method of the reversible permeability(RP) using surface type probe is presented. The method for measuring the RP is based on that RP is the differential value of hysteresis loop. The RP is exactly the foundation hatmonics induced in a detecting coil measured by lock-in amplifier tuned to a frequency of the alternating perturbing magnetic field. The peak of RP is measured around the coercive force. Steel material used in this work was 12Cr ferritic heat resisting steel. The eleven kinds of samples aged during different times under same temperature ($700^{\circ}C$) were prepared. Peak interval of reversible permeability(PIRP), Vickers hardness, and tensile strength measured for the aged samples decreased abruptly for short aging time (below 500 h), but the change became small at a long aging time. Vickers hardness and tensile strength linearly decreased as RIRP decreased, so the degraded mechanical properties of 12Cr ferritic heat resisting steel could be nondestructively evaluated by measuring RIRP.