• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.38 no.9
• /
• pp.999-1004
• /
• 2014

In the present paper, the effects of initial crack location on spatial randomness of fatigue crack growth resistance (FCGR) in friction stir welded (FSWed) AA7075-T651 plates were studied. The objective of this study is to characterize the statistical properties of FCGR for three different types of initial crack location (ICL) specimens. In this work, the FCGR coefficients were treated as a spatial random process. It was found that the FCGR coefficients for all initial crack location specimens closely followed a two parameter Weibull distribution. The shape parameter of the Weibull distribution for BM-ICL specimens showed the largest value of 7.50, and that for the WM-ICL specimens showed the smallest value of 2.61. In addition, the autocorrelation functions for all the ICL specimens followed the exponential function.

• Journal of Korean Society of Steel Construction
• /
• v.11 no.4 s.41
• /
• pp.409-416
• /
• 1999

The fatigue crack growth analysis based on the fracture mechanics is useful to the estimation of the fatigue life on welded structures under cyclic loading. The analysis procedure in fatigue crack growth under uniform axial loading is applicable to bending fatigue problem as well. The intent of the present study is to show the procedure for calculating the fatigue crack propagation lifetimes of deckplates under bending stress and to explain the crack growth rates for the two dimensional crack problems. It is shown that the fatigue crack grows at a decreasing rate and the fatigue life depends on the initial crack length and the crack shape. The numerically predicted crack growth agree with the experimental data.

• The Journal of Engineering Geology
• /
• v.8 no.3
• /
• pp.275-284
• /
• 1998

Deformation behavior and microcrack development due to uniaxial compressive cyclic loading in the Pocheon granite were investigated using the ultrasonic velocity measurements and the differential strain analysis(DSA). Most microcracks were developed along the direction parallel to the loading axis. Microcracks developed at the early stage of cyclic loading were formed by propagation of pre-existing cracks. Ultrasonic velocity measurement, DSA and measurement of permanent deformation are good tools to represent microcrack development in rock. Since results from each method are slightly different, microcrack development should be interpreted from all three methods. The magnitude of microcracks developed at the early stage of cyclic loading under 80% loading level is twice compared with those under 70% loading level. The highest volumetric crack strain is about 3000, indicating that the Pocheon granite will fail with 0.3% occupation of microcrack in volume.

• Magazine of the Korea Concrete Institute
• /
• v.5 no.3
• /
• pp.179-186
• /
• 1993

본 연구는 무근 폴리에스터 폴리머 콘크리트보의 휨피로 거동을 구명키 위한 것으로서 초기균열깊이와 높이의 비 (a/h)를 0, 0.2, 0.4로 하고 응력수준을 45%, 55%, 65%로 하여 피로 시험을 실시한 것이다. 그 결과 초기균열깊이가 커질수록 피로수명이 짧아졌으며, 피로수명비에 따른 휨인장변형도는 균열깊이가 클수록 작아졌다. 또한 휨탄성계수는 피로수명비 0.2에서 0.6정도까지는 선형적인 변화를 보였으나, 초기와 말기에는 비선형적인 변화를 보여주었다. 그리고 응력수준과 균열깊이가 커질수록 취성적인 성질이 더 크게 나타남을 알 수 있었다.

• Journal of the Computational Structural Engineering Institute of Korea
• /
• v.12 no.4
• /
• pp.691-700
• /
• 1999

본 연구에서는 요소를 사용하지 않는 새로운 해석방법인 EFG(Element-Free Galerkin)법을 사용하여 복수의 초기균열을 지닌 강재가 반복피로하중을 받는 경우 균열들이 점진적으로 성장하여 부재가 파단에 이르는 과정을 해석적으로 규명하였다. 이를 위하여 본 연구에서는 일반적인 피로균열성장법칙을 EFG법을 이용한 균열해석 알고리즘에 적용하여 복수의 균열들이 각각의 응력상태에 따라 차별적으로 성장해 나가는 과정을 해석할 수 있는 알고리즘을 도입하고 이를 바탕으로 다양한 하중상태하에서 복수의 균열들의 성장경로를 추정함과 동시에 이에 따른 잔존수명을 산정할 수 있는 기법을 제시하였다. 본 연구에서 제안된 해석방법을 피로균열 발생빈도가 큰 몇가지의 강부재 형태에 적용해 본 결과 다수균열 함유 부재의 피로균열 성장거동과 균열들의 피로수명을 성공적으로 예측할 수 있었다.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.8 no.5
• /
• pp.1173-1178
• /
• 2007

A laboratory investigation is conducted to characterize and quantity fatigue life of continuously reinforced concrete pavement with initial cracks. Four specimens scaled were made based on results of finite-element analyses and stress-strain curve comparisons. Static tests were firstly performed to obtain magnitudes of static failure loads and to predict crack patterns before fatigue tests. The fatigue lives measured in the study were compared based on the initial crack spacing. The comparison indicates that the fatigue lives of most specimens increases with increasing the initial crack spacing. The results obtained in the study can be used for maintenance and retrofit of the continuously reinforced concrete pavements.

• Proceedings of the Korean Institute of Industrial Safety Conference
• /
• 1998.05a
• /
• pp.57-62
• /
• 1998

구조물이나 기계요소내의 결함이 성장하여 파손(Failure)에 이르는 현상은 공학분야에서 중요하게 평가되어 오고 있다. 반복적으로 변하는 응력에 의하여 결함이 초기 성장을 거쳐 재료의 파손에 이르게 되는 과정인 피로파괴는 파괴역학의 한 중요한 분야이다. 이에, 본 연구에서는 열처리의 특성상 부식환경에 매우 민감한 Al-Zn-Mg-Cu Alloy 7075에 대하여 Peak Aged T65l Tempering을 실시한 Al-Alloy 7075-T65l에 대하여 각기 환경(대기, 물, 해수)의 변화가 부식피로균열성장에 미치는 영향과 부식환경에서의 긴 균열(Long Crack)과 짧은 균열(Short Clark)의 부식피로균열 성장특성을 비교, 고찰하여 초기균열의 잠재시간과 안정성장 시간을 예측하여 구조물의 수명예측 및 안전성 평가에 기여 할 수 있는데 목적이 있다. (중략)

• Proceedings of the Computational Structural Engineering Institute Conference
• /
• 2010.04a
• /
• pp.326-329
• /
• 2010

항공기는 전체 수명동안 무수한 반복하중에 노출되기 때문에, 동체에 피로로 인한 다중균열이 불가피하게 발생하게 된다. 이 다중균열은 기체의 강성을 저하시킬 뿐 만 아니라, 종국적으로는 해당 기체구조의 파단을 야기할 수 있다. 초기 결함과 운용 중에 작용되는 응력 스펙트럼은 구조물의 피로수명에 영향을 끼치며 고려해야 한다. 본 논문에서는 초기결함 특성을 파악하기 위한 등가초기결함크기 분포를 산출하고 리벳 시편의 다중균열모델에 대해서 초기결함과 응력배열을 고려한 해석을 수행하였다.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.22 no.1
• /
• pp.129-136
• /
• 2018

The estimation of the fatigue design life for large welded structures is usually performed using the liner cumulative damage method such as Palmgren-Miner rule or the equivalent damage method. When a fatigue crack is detected in a welded steel structure, the residual service life has to be estimated base on S-N curve method and liner elastic fracture mechanics. In this study, to examine the 3D fatigue crack behavior and estimate the fatigue life of out-of-plane gusset fillet welded joint, the fatigue tests were carried out on the model specimens. Investigations of three-dimensional fatigue crack propagation on gusset welded joint was used the finite element analysis of FEMAP with NX NASTRAN and FRANC3D. Fatigue crack growth analysis was carried out to demonstrate the effects of aspect ratio, initial crack length and stress ratio on out-of-plane gusset welded joints. In addition, the crack behaviors of fatigue tests were compared with those of the 3D crack propagation analysis in terms of changes in crack length and aspect ratio. From this analysis result, SIFs behaviors and crack propagation rate of gusset welded joint were shown to be similar fatigue test results and the fatigue life can also be predicted.

• Journal of Korea Foundry Society
• /
• v.28 no.1
• /
• pp.37-40
• /
• 2008

본 연구는 ADI의 기계적 성질을 개선하고자 오스테나이트화 과정에서 초기 변태온도를 $900^{\circ}C$ (${\gamma}$ 구역)에서 시작하여 $800^{\circ}C$까지(${\alpha}+{\gamma}$ 구역) 일정한 냉각제어에 의해 오스템퍼링을 한다. 여기서 Full ADI에서 생성되는 고탄소 오스테나이트 조직을 저탄소 오스테나이트로 유도하고 미세한 침상의 Full ADI조직을 연성이 높은 조대한 아공석 페라이트 조직이 생성되도록 하여 Semi ADI를 만든다. Full ADI와 Semi ADI의 기계적 성질 및 피로강도를 연구한 결과 Full ADI와 Semi ADI의 정적강도는 유사하지만, 피로강도는 Semi ADI의 기지조직의 변화에 기인하여 Full ADI보다 피로강도가 높게 나타났다. 이러한 현상은 Semi ADI의 조대한 페라이트가 균열개구 저항력이 낮아 초기에는 쉽게 개구되지만, 균열개구와 동시에 균열선단에서 큰 소성역이 발생되어 균열성장이 지연하는 효과로 판단된다.