• Journal of the Korean Vacuum Society
• /
• v.16 no.6
• /
• pp.453-457
• /
• 2007

Zinc oxide (ZnO) and Ga doped zinc oxide (GZO) with different thickness in range of 10nm to 100nm are prepared on glass substrate by RF magnetron sputtering at room temperature. The structural and optical properties of the thin films is evaluated. The structural properties of ZnO and GZO are investigated by Tunneling Electron Microscopy (TEM) and scanning electron microscopy (SEM). Optical properties are also investigated by UV-VIS-NIR spectrophotometer (200$\sim$1400nm). The much larger grain size of ZnO compared to GZO decreased the light scattering at the grain boundary and improved the transmittance. The transmittance of ZnO is higher than that of GZO through all of the ranges of wavelengths. In case of over 50nm, we found that the transmittance of ZnO is 20% higher than that of GZO.

• Journal of the Korean Vacuum Society
• /
• v.20 no.5
• /
• pp.356-360
• /
• 2011

Indium oxide ($In_2O_3$) single layer and $In_2O_3$/copper (Cu) bi-layer films were prepared on glass substrates by RF and DC magnetron sputtering without intentional substrate heating. In order to determine the effect of the Cu bottom layer on the optical, electrical and structural properties of $In_2O_3$ films, 3-nm-thick Cu film was deposited on the glass substrate prior to deposition of the $In_2O_3$ films. As-deposited $In_2O_3$ films had an optical transmittance of 79% in the visible wavelength region and a sheet resistance of 2,300 ${\Omega}/{\square}$, while the $In_2O_3$/Cu film had optical and electrical properties that were influenced by the Cu bottom layer. $In_2O_3$/Cu films had a lower sheet resistance of 110 ${\Omega}/{\square}$ and an optical transmittance of 71%. Based on the figure of merit, it can be concluded that the Cu bottom layer effectively increases the performance of $In_2O_3$ films for use as transparent conducting oxides in flexible display applications.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.697-698
• /
• 2013

최근에 유연한 성질을 갖는 전자기기들의 수요가 증가하면서, 그에 따라서 유연 전자기기를 뒷받침 해줄 수 있는 에너지 저장체의 유연한 성질도 중요성이 점점 부각되고 있으며 많은 연구가 진행되고 있다. 유연한 에너지 저장체의 많은 연구들이 유연한 금속 박막이나 특수 공정처리가 필요한 고분자를 이용하고 있으나, 대부분의 유연 에너지 소자들은 에너지 저장체의 성능에 비해 고온과 산 약품과 같은 환경이 필요하며, 비용과 시간이 많이 소모되고 있다. 그에 반해 섬유는 앞에서와 같이 특수 공정 처리가 따로 필요하지 않으며 상온에서도 손 쉽게 이용 가능하며, 신축성이 뛰어난 장점이 있기 때문에 효율적, 비용적으로 유연한 에너지 저장체에 유리한 소재이다. 몸에 해로운 산과 같은 약품처리의 필요도 없으며, 용매를 흡수하는 능력이 뛰어나기 때문에 용매를 이용한 도포 방법을 사용하면 다양한 물질을 폭넓게 적용 가능하다. 그리고 적용 분야에 맞춰서 섬유의 종류를 조절하면 다양한 성질을 갖는 천 기반의 에너지 저장체가 형성되며, 면 섬유가 수소 결합과 높은 반데르 발스 결합에 의해 탄소나노튜브와 결합하여 높은 에너지 밀도를 갖는 에너지 저장체를 형성하는 것을 분석한 논문들도 보고되고 있다. 면 섬유의 특수한 성질을 이용하여 에너지 저장체를 제작하고 이를 확인하기 위해서 일반 합성 섬유인 polyester와 면 섬유를 비교 제작하였으며, 용매의 형태로 손쉽게 도포 가능한 물질은 탄소 계열의 활물질들이며, 탄소 나노 튜브나 그래핀 등이 분산된 용액을 이용해 천에 도포 가능하다. 탄소 계열의 활물질들은 대표적인 슈퍼캐패시터 물질이며, 천에 도포를 함으로써 천 기반의 슈퍼캐패시터를 제작하였다. 일반 합성 섬유 polyester와 CNT를 결합한 형태의 전극은 최대 에너지 축전 용량(Maximum specific capacitance)이 53.6 F/g으로 나타났으며, 면 섬유와 CNT를 결합한 형태의 전극은 최대 에너지 축전 용량이 122.1 F/g으로 나타났다. 따라서 면 섬유에서 높은 에너지 저장 능력을 보이는 것을 실험적으로 확인하였으며, 에너지 저장 능력이 뛰어난 면 섬유를 다음 전극 디자인에서도 일률적으로 적용하였다. 슈도캐패시터의 대표적 물질인 금속 산화물인 망간 산화물(MnO2)을 3전극 도금 시스템을 이용하여 에너지 축전 용량과 에너지 밀도를 올리는 전극을 제작하였다. 특히 망간 산화물의 형태는 표면적을 극대화하기 위해서 평균 지름은 200~300 nm 정도 되는 나노 입자의 형태로 제작하였다. 그 결과, 확연하게 에너지 축전 용량이 향상되었으며, 최대 에너지 축전 용량은 282.0 F/g, 에너지전력 밀도는 14.2 Wh/kg으로 나타나서 금속 산화물의 형태가 주는 효과를 확인할 수 있었다. 하지만 나노 입자의 형태로 제작된 금속 산화물은 문제점이 발생하였다. 금속 산화물의 전기 전도성이 매우 낮기 때문에, 전기 전도성에 비례해서 전력 밀도의 값이 표현되는데, 전기 전도성이 급격히 감소하기 때문에 전력 밀도도 급격한 감소가 나타난다. 다음과 같이 전기 전도성 물질을 첨가하는 방법은 추가의 공정이 필요한 단점이 있지만 오직 기계적인 인장응력만을 가해서 에너지 밀도와 전력 밀도를 증가시키는 전극을 제작하였다. 인장응력을 섬유 기반의 전극에 가했을 시에 가닥들간의 접촉 증가와 CNT가 정렬되면서 특정 변형률(strain) 이전에서는 전기 전도성이 최대 50% 이상 증가하는 것을 확인할 수 있었으며, 선행 연구에서 보고되었다. 이를 이용해서 전기 전도성과 직결되는 전력 밀도의 양도 증가시키고 에너지 밀도의 증가 여부까지 확인한 결과 인장을 가하기 전 면 섬유의 전력 밀도와 에너지 밀도는 6.4 kW/kg and 6.1 Wh/kg으로 나타났으나 30% 변형 인장 후에는11.4 kW/kg과 7.1 Wh/kg으로 나타났다. 그리고 망간 산화물을 첨가한 전극 역시 4.9 kW/kg과 14.2 Wh/kg으로 나타났었으나 인장 이후 전력 밀도는 14.2 kW/kg, 에너지 밀도는 17.6 Wh/kg으로 확연하게 증가한 것을 확인하였다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.364-364
• /
• 2013

현재 투명전극은 주로 ITO를 사용하고 있으며, ITO는 인듐산화물(In2O3)과 주석산화물(SnO2)이 9대 1의 비율로 혼합된 화합물로 인듐이 주성분이다. 따라서 ITO 사용량의 증가는 인듐의 수요 증가를 이끌어 2003년 이후 인듐 잉곳의 가격이 급등하였다. LCD에 응용되는 금속재료의 가격추이를 비교해보면, 인듐이 가장 큰 변화를 보이고 있으며, 2005년 인듐 가격은 2002년 대비 1,000% 이상 상승하였다가 2007년 이후 500%p 하락하여 2008년 2월 22일 기준으로 톤당 49만 달러에 거래되고 있다. 같은 기간 동안 알루미늄의 가격은 76.6% 상승하였으며 구리는 394%, 주석은 331% 상승하였다. 이러한 인듐의 가격 상승폭은 동일한 기간 동안 다른 금속 재료와 비해 매우 크며, 단위 질량당 가격도 20배 이상 높은 수준이다. ITO의 주성분인 인듐의 이러한 가격의 급등 및 향후 인듐의 Shortage 예상으로 인해 ITO 대체재 확보의 필요성이 증가되고 있다. 태양광 발전산업에서 현재 주류인 결정질 실리콘 태양전지의 변환효율은 꾸준히 향상되고 있으나, 태양전지의 가격이 매년 서서히 하강되고 있는 실정에서 결정질 실리콘 가격의 상승 등으로 고부가 가치 산업유지에 어려움이 있으며, 생산 원가를 낮출 수 있는 태양전지 제조기술로는 2세대 태양전지로 불리는 박막형이 현재의 대안으로 자리매김하고 있으며, 박막태양전지 산업분야가 현재의 정부정책 지원 없이 자생력을 갖추고 또한 시장 경쟁력을 확보하기 위해서는 박막태양전지 개발과 더불어 저가의 재료개발도 시급한 상황이다. 본 연구에서는 In-line magnetron sputtering system을 사용하여 소다라임 유리기판 위에 박막태양전지용 투명전도성 ZnO(Al) 박막 및 ZnO(AlGa) 박막을 각각 제작하였다. 각각 박막의 표면특성 및 성장구조, 결정성을 조사하였고, 또한 전기적 특성, 홀이동도와 개리어농도, 박막의 두께, 광투과율 특성을 연구하였다. ZnO(Al)박막, ZnO(AlGa)박막 대한 각각 특성을 평가하고 그 결과들을 논하고자 한다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.615-615
• /
• 2013

탄소나노튜브(carbon nanotubes; CNT)는 강철보다 10~100배 견고할 뿐만 아니라 영률과 탄성률 은 각각 1.8 TPa, 1.3 TPa에 달하는 매우 우수한 기계적 강도를 지니고 있으며, 구리보다 좋은 전기 전도도와 다이아몬드의 2배에 이르는 열전도도를 지닌 물질이다. 이러한 탄소나노튜브의 우수한 특성을 이용하여 나노섬유, 고분자-탄소나노튜브의 고기능 복합체, 나노소자, 전계방출원(field emitter), 가스센서 등 다양한 분야로의 활용을 위한 연구가 진행되고 있다. 특히, 수백 ${\mu}m$ 이상의 길이로 수직 성장된 탄소나노튜브(VA-CNTs)의 합성은 길이 대 직경의 비(aspect ratio)가 비약적으로 증가하여 앞서 언급한 분야로의 활용이 더욱 유리하며, 그 중에서도 대량 생산, 나노섬유 및 나노복합체로서의 활용에 극히 유용하다. 최근에는 열 화학기상증착(thermal chemical vapor deposition; TCVD)법을 이용하여 탄소나노튜브의 구조를 제어하는 연구들이 많이 보고되고 있다. 열 화학기상증착을 이용한 수직 정렬된 탄소나노튜브의 합성에서 합성조건의 변화는 탄소나노튜브의 길이, 벽의 수, 직경, 결정성 등 구조에 큰 영향을 미친다. 탄소나노튜브는 이러한 구조에 따 라 물리적 특성이 달라지기 때문에 다양한 분야로의 응용을 위해서는 합성에 대한 근본적인 이해 가 절실히 요구된다. 본 연구에서는 열 화학기상증착법을 이용한 합성에서 성장압력의 변화에 따른 탄소나노튜브의 구조적 특성을 조사하였다. 성장압력의 변화는 탄소나노튜브의 밀도, 길이, 결정성에 큰 영향을 미치는 것을 주사전자현미경과 라만분광법을 이용하여 확인하였다. 이러한 결과 는 탄소나노튜브 박막(CNT forest)의 가장자리(edge)에 비정질 탄소(amorphous carbon)의 흡착으로 인한 나노튜브사이의 간격(intertube distance)이 좁아짐에 따른 가스공급 차단 효과로 설명이 가능 하다. 또한, 마이크로웨이브 플라즈마 화학기상증착법을 이용하여 탄소나노튜브를 합성하였다. 합성과정 중 산소(O2)를 주입 하였을 경우, 그렇지 않은 경우에 비하여 성장 속도가 증가하여 3시간 합성 시 2 mm가 넘는 수직 정렬된 탄소나노튜브를 합성 할 수 있었다. 이러한 결과는 과잉 공급 되어 탄소나노튜브로 합성되지 못하고 촉매금속의 표면과 탄소나노튜브의 벽에 비정질의 형태로 붙어있는 탄소 원자들을 추가 주입해 준 산소에 의하여 CO 또는 CO2 형태로 제거해 줌으로써 활성화된 촉매금속의 반응 시간을 향상 시켜주어 탄소공급이 원활하게 이루어졌기 때문이라 생각된다.

• Journal of the Korean Vacuum Society
• /
• v.15 no.4
• /
• pp.374-379
• /
• 2006

In this study, carbon nanotubes (CNTs) were grown on glass substrates coated with Ni/Cr by an atmospheric pressure plasma enhanced chemical vapor deposition(AP-PECVD) and their structural and electrical characteristics were investigated as a possible application to the field emitter of field emission display (FED) devices. The substrate temperature ($400{\sim}500^{\circ}C$) were varied and the grown CNTs were multi wall CNTs (at $500^{\circ}C$, 15 - 20 layers of graphene sheets, distance of each layer : 0.3nm, inner diameter: 10 - 15nm, outer diameter: 30 - 40nm). The ratio of defective carbon peak to graphite carbon peak of the CNTs grown at $500^{\circ}C$ (C measured by fourier transform(FT)-Raman was 0.772 $I_D / I_G$ ratio. When field emission properties were measured, the turn-on field was $2.92V/{\mu}m$ and the emission field at $1mA/cm^2$ was $5.325V /{\mu}m$.

• Journal of the Korean Vacuum Society
• /
• v.21 no.1
• /
• pp.62-68
• /
• 2012

The conversion efficiency of solar cells depending on incident angle of light is important for building-integrated photovoltaics (BIPV) applications. The quantum efficiency is the ratio of the number of charge carriers collected by the solar cell to the number of photons of a given energy shining on the solar cell. The analysis of angle dependence of quantum efficiencies give more information upon the variation of power output of a solar cell by the incident angle of light. The variations in power output of solar cells with increasing angle of incidence is different for the type of cell structures. In this study we present the results of the quantum efficiency measurement of single-crystalline silicon solar cells and a-Si:H thin-film solar cells with the angle of incidence of light. As a result, as the angle of incidence increases in single-crystalline silicon solar cells, quantum efficiency at all wavelength (300~1,100 nm) of light were reduced. But in case of a-Si:H thin-film solar cells, quantum efficiency was increased or maintained at the angle of incidence from 0 degree to about 40 degrees and dramatically decrease at more than 40 degrees in the range of visible light. This results of quantum efficiency with increasing incident angle were caused by haze and interference effects in thin-film structure. Thus, the structural optimization considering incident angle dependence of solar cells is expected to benefit BIPV.

• Journal of the Korean Vacuum Society
• /
• v.7 no.4
• /
• pp.293-299
• /
• 1998

We have investigated the atomic and electronic structures of Cu-adsorbed Si(100)-2$\times$1 surface, by using LEED and UPS. In the UPS spectra, the weak structures (peaks) related to Cu silicide appeared for low coverages less than 1.3 ML at room temperature, and the intensity of Cu 3d band rapidly increased with respect to Cu coverages. The Cu silicide peaks become clear after Cu deposition at room temperature followed by high temperature annealing ($\geq 300^{\circ}C$) or for Cu deposited surface at the substrate temperature of $400^{\circ}C$. On the other hand, these structures disappeared by annealing at $750^{\circ}C$. At very low coverage, a surface state near Fermi level $(E_F)$ was observed at $400^{\circ}C$. According to the rigid band model, it seems to be originated from the surface empty state occupied partially with Cu 4s electron. In the LEED patterns, no Cu-induced superstructure observed for RT-depositions and post annealing, while there were several surface structures which depend on substrate temperatures and coverages. we observed the clean surface 2$\times$1+2$\times$2 phase for 1.5 ML at $400^{\circ}C$, the clean surface 2$\times$1+5$\times$1 phase for 0.5 ML at $450^{\circ}C$ and the clean surface 2$\times$1+2$\times$2+5$\times$2+5$\times$5+10$\times$2 mixed phases for 3 ML at $450^{\circ}C$.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.84-84
• /
• 1999

최근 큰 잔류분극을 가진 강유전체 Pb(Zr, Ti)O3 박막을 이용한 비휘발성 기억소자의 연구가 활발히 진행되고 있다. 그러나 Pb(Zr, Ti)O3 박막을 비휘발성 기억소자로 응용하는 경우 분극피로(polarization fatigue), imprint, 누설전류 등의 문제점이 나타나는 것으로 알려져 있다. 특히 분극반전 횟수가 증가할수록 잔류분극이 감소하는 분극피로 현상은 비휘발성 기억소자의 응용에 있어서 치명적인 장애가 되므로 기억소자의 실용화를 위해서는 분극피로 현상의 개선이 무엇보다 중요하다. 본 연구에서는 Pb(Zr, Ti)O3 강유전체 박막의 분극피로 현상을 규명하고 개선하기 위해서 다음과 같은 세가 실험적 방법으로 접근하였다. 먼저 Pt와 금속산화물인 LaNiO3을 이용하여 상·하부 전극을 달리하여 제조한 축전기에 대해서 분극피로 특성을 관찰하고 이로부터 분극피로 현상에 대한 전극의 효과를 조사하였다. 여기서 금속산화물인 LaNiO3 박막과 Pt 박막은 r.f. 스퍼트 법으로 증가하였으며 Pb(Zr, Ti)O3 박막은 LaNiO3/Si(100)/와 Pt/Ti/SiO2/i(100) 기판위에 졸겔법으로 제조하였다. 다음으로 분극피로된 박막의 상부전극에 극성이 다른 직류전압을 인가해주었을 때 나타나는 분극회복 현상을 광범위하게 관찰하였으며, 특히 직류전압의 극성에 따라 비대칭적인 분극회복 특성을 보였다. 마지막으로 이와 같은 직류전압에 대한 비대칭적인 분극회복현상에 착안하여 양과 음의 방향으로 바이어스된 스윗칭 펄스를 인가하여 분극피로 특성을 조사한 결과 비대칭적인 분극피로 현상을 관찰할 수 있었다. 이와 같은 Pv(Zr, Ti)O3 박막의 분극피로와 회복의 비대칭적인 현상은 분극피로 현상의 기구를 밝히는 중요한 근거가 되었으며, 본 연구에서는 하부 계면에서의 산소빈자리의 역할로 분극피로 현상을 모형화하였다.식각하기 시작하였으며, 19.5J/cm2에서 유리기판의 rudraus(격벽 두께 130$\mu\textrm{m}$)까지 식각하였다. 대한 정보(RDF)는 명확하게 얻을 수 있었다.nospec과 SEM으로 관찰하였다. 또한 Ge 함량 변화에 따른 morphology 관찰과 변화 관찰을 위하여 AFM, SEM, XRD를 이용하였으며, 이온주입후 열처리 온도에 따른 활성화 정도의 관찰을 위하여 4-point probe와 Hall measurement를 이용하였다. 증착된 다결정 SiGe의 두게를 nanospec과 SEM으로 분석한 결과 Gem이 함량이 적을 때는 높은 온도에서의 증착이 더 빠른 증착속도를 나타내었지만, Ge의 함량이 30% 되었을 때는 온도에 관계없이 일정한 것으로 나타났다. XRD 분석을 한 결과 Peak의 위치가 순수한 Si과 순수한 Ge 사이에 존재하는 것으로 나타났으며, ge 함량이 많아짐에 따라 순수한 Ge쪽으로 옮겨가는 경향을 보였다. SEM, ASFM으로 증착한 다결정 SiGe의 morphology 관찰결과 Ge 함량이 높은 박막의 입계가 다결정 Si의 입계에 비해 훨씬 큰 것으로 나타났으며 근 값도 증가하는 것으로 나타났다. 포유동물 세포에 유전자 발현벡터로써 사용할 수 있음으로 post-genomics시대에 다양한 종류의 단백질 기능연구에 맡은 도움이 되리라 기대한다.다양한 기능을 가진 신소재 제조에 있다. 또한 경제적인 측면에서도 고부가 가치의 제품 개발에 따른 새로운 수요 창출과 수익률 향상, 기존의 기능성 안료를 나노(nano)화하여 나노 입자를 제조, 기존의 기능성 안료에 대한 비용 절감 효과등을 유도 할 수 있다. 역시 기술적인 측면에서도 특수소재 개발에 있어 최적의 나노 입자 제어기술 개발 및 나노입자를 기능성 소재로 사용하여 새로운 제품의 제조와 고압 기상 분사기술의 최적화에

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.143-144
• /
• 2010

3-5족 화합물 반도체를 이용한 집광형 삼중 접합 태양전지는 40% 이상의 광변환 효율로 많은 주목을 받고 있다[1]. 삼중 접합 태양전지의 하부 셀은 기계적 강도가 높고 장파장을 흡수할 수 있는 Ge이 사용된다. Ge위에 성장될 III-V족 단결정막으로서 Ge과 격자상수가 일치하는 GaInP나 GaAs가 적합하고, 성장 중 V족 원소의 열확산으로 인해 Ge과 pn접합을 형성하게 된다. 이때 GaInP의 P의 경우 GaAs의 As보다 확산계수가 낮아 태양전지 변환효율향상에 유리한 얇은 접합 형성이 가능하고, 표면 에칭효과가 적기 때문에 GaInP를 단결정막으로 선택하여 p-type Ge기판 위 성장으로 단일접합 Ge구조 제작이 가능하다. 하지만 이종접합 구조 성장으로 인해 발생한 계면사이의 전위나 미세결함들이 결정막내부에 존재하게 되며 이러한 결함들은 광학소자 응용 시 비발광 센터로 작용할 뿐 아니라 소자의 누설전류를 증가시키는 원인으로 작용하여 태양전지 변환효율을 감소시키게 된다. 이에 결함감소를 통해 소자의 전기적 특성을 향상시키고자 수소 열처리나 플라즈마 공정을 통해 수소 원자를 박막내부로 확산시키고, 계면이나 박막 내 결함들과 결합시킴으로서 결함들의 비활성화를 유도하는 연구가 많이 진행되어 왔다 [2][3]. 하지만, 격자불일치를 갖는 GaInP/Ge 구조에 대한 수소 열처리 및 불순물 준위의 거동에 대한 연구는 많이 진행되어 있지 않다. 따라서 본 연구에서는 Ga0.45In0.55P/Ge구조에 수소 열처리 공정을 적용을 통하여 단결정막 내부 및 계면에서의 결함밀도를 제어하고 이를 통해 태양 전지의 변환효율을 향상시키고자 한다. <111> 방향으로 $6^{\circ}C$기울어진 p-type Ge(100) 기판 위에 유기금속화학증착법 (MOCVD)을 통해 Si이 도핑된 200 nm의 n-type GaInP층을 성장하여 Ge과 단일접합 n-p 구조를 제작하였다. 제작된 GaInP/Ge구조를 furnace에서 250도에서 90~150분간 시간변화를 주어 수소열처리 공정을 진행하였다. 저온 photoluminescence를 통해 GaInP층의 광학적 특성 변화를 관찰한 결과, 1.872 eV에서 free-exciton peak과 1.761 eV에서 Si 도펀트 saturation에 의해 발생된 D-A (Donor to Acceptor)천이로 판단되는 peak을 검출할 수 있었다. 수소 열처리 시간이 증가함에 따라 free-exciton peak 세기 증가와 반가폭 감소를 확인하였고, D-A peak이 사라지는 것을 관찰할 수 있었다. 이러한 결과는 수소 열처리에 따른 단결정막 내부의 수소원자들이 얕은 불순물(shallow impurity) 들로 작용하는 도펀트들이나, 깊은 준위결함(deep level defect)으로 작용하는 계면근처의 전위, 미세결함들과의 결합으로 결함 비활성화를 야기해 발광세기와 결정질 향상효과를 보인 것으로 판단된다. 본 발표에서는 상술한 결과를 바탕으로 한 수소 열처리를 통한 박막 및 계면에서의 결함준위의 거동에 대한 광분석 결과가 논의될 것이다.