• Journal of the Korea Concrete Institute
• /
• v.15 no.2
• /
• pp.246-253
• /
• 2003

Although concrete members are not normally designed to resist direct tension, the knowledge of tensile strength is of value in estimating the cracking load. In general, there are three types of test method for tensile strength ; direct tension test, flexural tension test, and splitting tension test. Though direct tensile strength represents the real tensile strength of concrete, direct tension tests are seldom carried out, mainly because it is very difficult to applicate a pure tension force. The purpose of this paper is to investigate the test methods, effect of aspect ratio, and the size effect on the direct tensile strength. Direct tension test, using bonded end plates, follows RILEM and U.S.Bureau of Reclamation. And other test methods follow ASTM provisions. Four kinds of aspect ratio and two kinds of size effect are tested. Same variables are tested by direct tension test and splitting tension test for comparison between the two test methods. Test results show that direct tensile strength of concrete is more affected by aspect ratio and size than other kinds of strength.

• Journal of the Korea Institute of Building Construction
• /
• v.18 no.2
• /
• pp.125-132
• /
• 2018

In this study, a direct tensile test was planned to identify the tensile performance of UHPC, and the irregularity of cracks, which is a problem of the direct tensile test, was complemented through the introduction of notches at the center of a specimen. In this regard, a number of specimens divided by batch to reduce the deviation of direct tensile test values were fabricated to present reference data with respect to highly reliable direct tensile strength values. In addition, the mechanical properties and reliability of the specimens were examined under the curing conditions of the specified design strength of 120MPa for the steel fiber reinforced concrete with 1.5% fiber volume fraction, which is most suitable for the field application. As a result, the deviation of averages by batch between compressive strength and direct tensile strength did not show a large difference, and all cracks occurred within 20mm in the direct tensile test. At the 95% confidence interval of the direct tensile strength, the range was considerably small in the mean and the standard deviation, and there was no significant difference depending on the curing conditions. The results confirmed that a stable direct tensile test was performed, and highly reliable results were obtained through the fabrication of specimens by batch and test progress.

• Magazine of the Korea Concrete Institute
• /
• v.9 no.5
• /
• pp.177-187
• /
• 1997

철근 콘크리트 구조부재는 철근과 콘크리트로 구성된 합성부재이므로, 철근콘크리트 구조부재의 피로강도는 철근과 콘크리트 고유의 피로특성에 따라 변화하게 된다. 철근자체의 피로특성은 철근의 정적강도 특성과 상이함으로, 실험을 통하여 규명할 필요가 있다. 본 논문에서는 대표적인 국내 2개사에서 생산되는 철근에 대하여 직접인장 피로실험을 실시하여 이들의 피로특성을 규명하였으며, 철근콘크리트 휨부재 내부의 철근 피로특성과 철근만의 직접인장 피로특성의 비교 분석으로부터 직접인장 피로실험만으로 철근콘크리트 휨부재의 피로특성을 평가할 수 있음을 밝혔다. 또한 반복하중을 받는 철근콘크리트 부재의 피로점토를 위한 기준을 제시하였다.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.433-436
• /
• 2008

In order to estimate the mechanical properties of ultra high performance concrete, the most important is to evaluate its tensile behavior. The tensile behavior of concrete is generally characterized by the elastic behaviour before cracking and tensile stress-crack width relationship after cracking. We carried out the direct tensile and flexural tensile test and compared the tensile behaviors obtained by the direct tensile test and by inverse analysis of the flexural tensile test results. We compared the obtained tensile behavior with that of JSCE recommendations for ultra high performance concrete as well. we could see that the tensile stress-crack width relationship obtained from the flexural tensile test results using inverse analysis had good agreement with directly obtained tensile behaviour with direct tensile test and showed similar tensile softening behaviour introduced in JSCE recommendations for ultra high performance concrete.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.34 no.5
• /
• pp.1505-1516
• /
• 2014

In this study, a cylinder embedded within cemented soils was used to cause directly tensile failure of cemented soils. An existing dumbbell type direct tensile test and a split tensile test that is most general indirect tensile test were also carried out to verify the developed built-in cylinder tensile test. Testing specimens with two different sand/cement ratios (1:1 and 3:1) and two curing periods (7 and 28 days) were prepared and tested. Total 10 specimens were prepared for each case and their average value was evaluated. Unconfined compression tests were also carried out and the ratio of compressive strength and tensile strength was evaluated. The tensile strength determined by built-in cylinder tensile test was slightly higher than that by dumbbell type direct tensile test. The dumbbell type test has often failed in joint part of specimen and showed some difficulty to prepare a specimen. Among three tensile testing methods, the standard deviation of tensile strength by split tensile test was highest. It was shown that the split tensile test is applicable to concrete or rock with elastic failure but not for cemented soils having lower strength.

• Journal of the Korea Institute of Building Construction
• /
• v.17 no.2
• /
• pp.175-181
• /
• 2017

The purpose of this study is evaluating the characteristics of tensile strength of UHPC and examining tensile performance of notched specimens by direct tensile test. For test variables, 120, 150, and 180MPa of target design standard strength were aimed at. With general water curing and $90^{\circ}C$ high temperature steam as curing conditions, the properties were reviewed. Overall, it was represented that the specimens of notch-type direct tensile strength concrete was effective in inducing central cracks compared with existing direct tension specimens. Through this, it was judged that data construction with high reliability was possible. Above all, in a graph of direct tensile strength and strain, in the case of steam curing at high temperature, there was great difference of initial tensile strength compared with water curing. As passing of ages, an aspect that the difference gradually decreased was shown. Maximum tensile strength was found to increase steadily with increasing age for all target design strengths in water curing, in the case of steam curing, the tendency to increase significantly due to the initial strength development effect at 7 days of age. The initial crack strength increases with age in case of underwater curing, in the case of steam curing, it was higher than that of water curing in 7 days, while the strength of 28 days was lowered. In this part, it is considered necessary to examine the arrangement condition of the steel fiber.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.33 no.3
• /
• pp.1153-1163
• /
• 2013

Bonded concrete overlay is a favorable maintenance method since the material properties are similar to existing concrete pavements. In addition, bonded concrete overlay has advantage of structural performance based on being bonded together, both for the overlay layer and the existing pavement which perform as one monolithic layer. Therefore, it is important to have a suitable bond strength criteria for long term performance of bonded concrete overlay. This study aimed to investigate the affecting of bond strength on various bond characteristics, and to compare the bond strength between direct tensile test and indirect tensile test due to various conditions such as overlay materials, compressive and flexure strength of existing pavement, and deterioration status of existing pavement. As a result of this study, bond strength occurred by both of direct and indirect tensile test due to monotonic load is highly correlated such as coefficient of determination of 0.75 and P-value of 0.002. However, bond strength by indirect tensile test was relatively higher than bond strength by direct tensile test. It was known that correlation between direct and indirect tensile test was possible to use the characteristics analysis of bond fatigue behavior based on bond strength due to cyclic load which can simulate real field behavior of bonded concrete overlay.

• Journal of the Korea Concrete Institute
• /
• v.23 no.6
• /
• pp.791-797
• /
• 2011

This paper presents the test results of 12 direct tensile specimens to investigate the effect of cover thickness on the tension stiffening behavior in axially loaded reinforced concrete tensile members. Six concrete cover thickness ratios are selected as a main experimental parameter. The results showed that, as cover thickness became thinner, more extensive split cracking along the reinforcement occurred and transverse crack spacing became smaller, making the effective tensile stiffness of thin specimens at the stabilized cracking stage to be much smaller than that of thick specimens. This observation is not implemented in the current design provisions, in which the significant reduction of tension stiffening effect can be achieved by applying thinner cover thickness. Based on the present results, a modified tension stiffening factor is proposed to account for the effect of the cover thickness.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.36 no.6
• /
• pp.1109-1116
• /
• 2016

There are various test methods for evaluating the reflective cracking resistance of asphalt concrete pavement. Repeated direct tensile test is cheap and simple compared to the other traditional experimental methods. Determination of failure criteria is needed to apply a repeated direct tensile test. Various methods were used to determine the number of failure of repeated direct tensile test. The number of failure was defined as the time to reach 10% of the initial load, this method can be satisfied with specified tolerance of 10%. When the thickness of specimen is increased to 50 mm from 30 mm, the failure number is increased by 13.6 times. Thus, this result shows that the thickness of pavement is a big influence on the reflective cracking resistance. Reflective cracking resistance of asphalt concrete is decreased according to the increase in opening displacement. The repeated direct tensile test can be used as a reflective cracking resistance factor in pavement design, because it can evaluate the reflective cracking resistance according to the pavement thickness, opening displacement, material properties etc.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.12 no.1
• /
• pp.47-52
• /
• 2024

The demand for FRPs that are corrosion-free and have an excellent tensile strength-to-weight ratio. However, there is a lack of research on the mechanical properties of FRP in the form of rebars, especially the changes in performance due to heating. Therefore, in this paper, 60 tensile and compression specimens of CFRP rebars with a diameter of 12 mm were fabricated and subjected to direct tensile and direct compression tests, and their performance was evaluated according to the heating temperature. It was found that as the heating temperature increases above 300 ℃, the performance decrease becomes larger due to the burning of epoxy. The compressive strength was found to be much lower than the tensile strength, but the modulus of elasticity was found to be the same in tension and compression.