• Journal of the Microelectronics and Packaging Society
• /
• v.17 no.3
• /
• pp.43-49
• /
• 2010

Direct printing technology is an attractive metallization method, which has become immerging as "Green technology" to the conventional photolithography, on account of low cost, simple process and environment-friendliness. In order to commercialize the printed electronics in industry, it is essential to evaluate the electrical properties of conductive circuits using direct printing technology. In this contribution, we focused on the electrical characteristics of inkjet-printed circuits. A Cu nanoink was inkjet-printed onto a Bisaleimide triazine(BT) substrate with parallel transmission line(PTL) and coplanar waveguide(CPW) type, then was sintered at $250^{\circ}C$ for 30 min. We calculated the resistivity of printed circuits through direct current resistance by the measurement of I-V curve: the resistivity was approximately 0.558 ${\mu}{\Omega}{\cdot}cm$ which is about 3.3 times that of bulk Cu. Cascade's probe system in the frequency range from 0 to 30 GHz were employed to measure the Scattering parameter(S-parameter) with or without a gap between the substrate and the probe station chuck. The result of measured S-parameter showed that all printed circuits had over 5 dB of return loss in the entire frequency range. In the curve of insertion loss, $S_{21}$, showed that the PTL type circuits had better transmission of radio frequency (RF) than CPW type.

• Journal of the Korea Organic Resources Recycling Association
• /
• v.11 no.4
• /
• pp.120-129
• /
• 2003

The anodic alumina is synthesized using 0.3M oxalic acid and the barrier layers of the anodic alumina are removed using the 20wt% $H_2SO_4$ solution. The structure of the anodic alumina is analyzed by XRD and SEM. It is observed by SEM that the size of anodic alumina pore is about 60nm. And the uniformity of the anodic alumina surface under the 20wt% $H_2SO_4$ solution is poorer than the unifomity of the the normal anodic alumina surface. The anodic alumina and the carbon are used cathode and anode in$Cd(NO_3)_2{\cdot}4H_2O$, $Co(NO_3)_2{\cdot}6H_2O$ and $PbSO_4$ solutions. In this study, the constant D.C. electrical current is flowed in each solution for 24hours. It is found that the voltages so far as 4.6, 3.4 and 5.1V at $Cd(NO_3)_2{\cdot}4H_2O$, $Co(NO_3)_2{\cdot}6H_2O$ and $PbSO_4$ solutions increase with increasing the flowing current time and after the voltage does not change which values are 4.2, 2.7 and 2.4V, respectively. The amount of metal ions in solutions decrease with increasing the flowing current time until the flowing current time is 18hours and the metals are formed at the surface of anodic alumina. After the metal ions are removed using the anodic alumina, and $Cd^{2+}$, $Co^{2+}$ and $Pb^{2+}$ ions are removed again using flow cell with retriculate vitreous carbon(RVC) working electrode. The concentration of $Cd^{2+}$, and $Co^{2+}$ions decrease until the flowing time of the solutions is 20minutes and the concentration of $Pb^{2+}$ ion decreases until that time is 30minutes. In this case, the removal effects of $Cd^{2+}$, $Co^{2+}$ and $Pb^{2+}$ ions are 34.78, 28.79 and 86.38%, respectively. And it is possible that both $Cd^{2+}$ and $Co^{2+}$ions are adsorbed in pore of RVC at the same time and the removal effects of $Cd^{2+}$ and $Co^{2+}$ions are 32.30 and 31.37%.

• Restorative Dentistry and Endodontics
• /
• v.32 no.4
• /
• pp.377-384
• /
• 2007

Present tooth bonding system can be categorized into total etching bonding system (TE) and self-etching boding system (SE) based on their way of smear layer treatment. The purposes of this study were to compare the effectiveness between these two systems and to evaluate the effect of number of themocycling on microleakage of class V composite resin restorations. Total forty class V cavities were prepared on the single-rooted bovine teeth and were randomly divided into four experimental groups: two kinds of bonding system and another two kinds of thermocycling groups. Half of the cavities were filed with Z250 following the use of TE system, Single Bond and another twenty cavities were filled with Metafil and AQ Bond, SE system. All composite restoratives were cured using light curing unit (XL2500, 3M ESPE, St. Paul, MN, USA) for 40 seconds with a light intensity of $600mW/cm^2$. Teeth were stored in distilled water for one day at room temperature and were finished and polished with Sof-Lex system. Half of teeth were thermocycled 500 times and the other half were thermocycled 5,000 times between $5^{\circ}C$ and $55^{\circ}C$ for 30 second at each temperature. Teeth were isolated with two layers of nail varnish except the restoration surface and 1 mm surrounding margins. Electrical conductivity (${\mu}A$) was recorded in distilled water by electrochemical method. Microleakage scores were compared and analyzed using two-way ANOVA at 95% level. From this study, following results were obtained: There was no interaction between variables of bonding system and number of thermocycling (p = 0.485). Microleakage was not affected by the number of thermocycling either (p = 0.814). However, Composite restoration of Metafil and AQ Bond, SE bond system showed less microleakage than composite restoration of Z250 and Single Bond, TE bond system (p = 0.005).