• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2020.11a
• /
• pp.100-101
• /
• 2020

In this study, the temperature history and compressive strength of the concretes according to the type of cement were measured and analyzed in comparison as part of the experiment on the material mixing side to reduce the hydration heat crack of the mat foundation constructed with mass concrete. As a result, the peak temperature and maximum temperature reach time of concrete using high rapid cement were shown to be similar to that of semi rapid cement. In particular, in compressive strength after three days, semi rapid cement was measured higher than that of concrete using high rapid cement. Therefore, if semi rapid cement is used in accordance with the site conditions, it is deemed possible to shorten the air due to reduction of temperature cracks and improvement of initial strength.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2013.11a
• /
• pp.48-49
• /
• 2013

This test investigates early strength and durability of concrete using early strength type materials(cement, Polycarboxylate acid). The goal of this test is to secure the strength of 5.0 MPa in 12 hours early age and strength of 14 MPa for 24 hours correspondingly. This type of admixtures, concrete curing temperature, amount of binder and other concrete properties were confirmed by experimental factors. Comparing outcomes from two cases on using early strength type materials and common materials resulted in reducing of costs and shortening of the construction period, that determined the economical benefits of using early strength materials in construction.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.7
• /
• pp.4644-4652
• /
• 2014

This study examined the effects of the cement type and sand to cement ratio on the properties of grout for offshore PSC structures. Types I and III cement were used and the sand to cement ratio was varied from 0.5 to 1.5. When type I cement was used, considerable bleeding occurred on the all S/C after 3 hours and 20 hours. When type III cement was used, bleeding was reduced but the flowability decreased. A comparison of a superplasticizer containing naphthalene with that containing polycarboxylate showed that the problem of flowability could be solved using polycarboxylate.

• Resources Recycling
• /
• v.31 no.5
• /
• pp.42-51
• /
• 2022

Aggregate resources in Korea are expected to run out owing to an increase in development demand and construction investment. Recycled concrete aggregates (RCA), extracted from waste concrete, have a lower quality than natural aggregates. However, RCA can produce concrete similar in quality to the normal concrete by aggregate pretreatment, use of admixtures, and quality control. RCA are most suitable for use in precast concrete products such as sidewalk blocks and revetment blocks. Herein, the feasibility of producing revetment blocks using recycled aggregate concrete (RAC), similar in quality to normal concrete, was analyzed. The amount of RCA was varied, and moderate high early strength cement and steam curing were used to produce the concrete test blocks. In the block test, the load resistance characteristics of the blocks were evaluated to determine optimal RAC and glass fiber reinforced polymer (GFRP) rebar compositions. Thus, the variable that reduced the cement content was determined at the same level as that of natural aggregate concrete by the control of steam curing. In the concrete block test, although this depends on the reinforcement ratio, the RAC block exhibited the same or better performance than a normal concrete block. Therefore, the low quality of RCA in RAC is no longer a problem when concrete mixing and curing are controlled and appropriate reinforcement is used.

• Journal of the Korea Concrete Institute
• /
• v.24 no.6
• /
• pp.659-666
• /
• 2012

To secure the thermal crack resistance of mass concrete, researches and the field applications of low heat portland cement (LPC), ternary blended cement (TBC) which is produced by blending ordinary portland cement with blast furnace slag and fly ash, and early strength low heat blended cement (EBC) increased in recent years. Although the model for adiabatic temperature rise is necessary for estimating the risk of thermal cracking of concrete structures, sufficient data have not been accumulated for these mixtures. In addition, the differences in adiabatic test results have been reported for the volume of test specimens. Therefore, the present study evaluated the characteristics of adiabatic temperature rise based on the type of binder and the volume of the adiabatic test specimen. Test results indicated that the maximum temperature rise ($Q_{\infty}$) and the reaction factor (r) of TBC were the lowest. Test results also showed that $Q_{\infty}$ and r changed with respect to the volume of test specimen. $Q_{\infty}$ and r obtained from 6l equipment were lower than those of 50l equipment. Therefore, corrections with respect to this phenomenon was confirmed and the corrections factors are presented.