• Composites Research
• /
• 제22권2호
• /
• pp.24-29
• /
• 2009

본 연구에서는 알루미늄 허니컴 코어와 카본 면재가 적용된 샌드위치 복합재 구조에 대해 준정적 압입 손상 이후의 잔류 강도 평가에 대한 연구를 수행하였다. 3점 굽힘 시험과 압축 시험을 통해 시편의 강도를 확인하고 시편에 손상을 모사하기 위하여 준정적 압입 손상을 가하였다. 손상된 시편을 손상 전 시편과 동일한 시험을 통해 손상 전의 강도와 비교하였다. 압입 손상 이후 압축 강도와 굽힘 강도는 압입 깊이의 증가에 따라 강도가 감소하였고 손상 단계에 따른 잔류 강도 정도를 확인하였다.

• 대한기계학회논문집A
• /
• 제20권12호
• /
• pp.3847-3855
• /
• 1996

In order to study the relationship between static and cynamic behaviors of silion caride, both quasi-static indentaiton and impact experiments of spherical particle have been conducted. The difference inmaterial behavior when using the two mehtods suggests a loading rate difference in the damate pattrern and fracture strength of silicon carbide. This investigation showed some difference in damage pattern according to particla property, especially inthe case of particle impact. There was no differences in deformation behaviors according to the loading rate when the crater profiles were compared with each other at the same contact radius. From the result of residual strength evaluation, it was found that the strength degradation began at the initiation of ring crack and its behavior was colsely related to morphologies of the damage developed which was also dependent upon the extent of deformation atthe loaidng point. In the case of static indentation, there didnot exist the particle property effects onthe strength degradation behavior.

• 대한기계학회논문집A
• /
• 제27권10호
• /
• pp.1630-1635
• /
• 2003

The deformation and fracture behaviors of a bulk amorphous metal, Zr-based one (Zr$\_$41.2/Ti$\_$13.8/Cu$\_$12.5/Ni$\_$10/Be$\_$22.5/: Vitreloy), were investigated over a strain rate range (7x10$\^$-4/～4 s$\^$-1/). The uniaxial compression test and the indentation test using 3mm-diameter WC balls were carried out under quasi-static loading conditions. As a result, at the uniaxial compressive state, the fracture stress of the material was very high (～1,700MPa) and the elastic strain limit was about 2%. The fracture strength showed a strain rate independent behavior up to 4 s$\^$-1/. Using indentation tests, the plastic deformation behavior of the Zr-based BAM up to a large strain value of 15% could be achieved, even though it was the deformation under locally constrained condition. The Meyer hardness of the Zr-based BAM measured by static indentation tests was about 5 GPa and it revealed negligible strain hardening behavior. At indented sites, the plastic indentation occurred forming a crater and well-developed multiple shear bands were generated around it along the direction of 45 degree when the indentation load exceeded 7kN. With increasing indentation load, shear bands became dense. The fracture surface of the specimen after uniaxial compressive tests showed vein-like pattern, typical morphology of many BAMs.