The purpose of this study was to determine the effect of sodium hypochlorite and steam autoclaving on the cyclic fatigue of nickel-titanium endodontic files. Two types of files with a .06 taper and #30 were used, $K3^{(R)}$ (SybronEndo, Glendora, California, USA) and Hero $642^{(R)}$(Micro-Mega, BesanCon, France). The files were divided into 6 experimental groups containing 10 files each group depending the soaking time in 6% sodium hypochlorite solution and number of cycles of steam autoclave. After sterilization, a cyclic fatigue test was performed on each file, and the fracture time was recorded in seconds. The control group underwent the cyclic fatigue test only. After the test, the surface characteristics of the files were observed using scanning electron microscopy (SEM). All groups containing the Hero 64~ files showed a similar cyclic fatigue fracture time. However, the cyclic fatigue fracture time with the $K3^{(R)}$ files was significantly shorter in groups which were treated with sodium hypochlorite than in the control group (P < 0.05), SEM revealed both Hero $642^{(R)}$ and $K3^{(R)}$ files to have significant corrosion on the file surface in groups treated with sodium hypochlorite, compared with the sharp and regular blades of the control group. $K3^{(R)}$ files showed more corrosion than the Hero $642^{(R)}$ files. Bluntness of the blades of the $K3^{(R)}$ file was observed in groups treated with steam autoclave. Although there was no obvious destruction on the surface of steam autoclaved Hero $642^{(R)}$ files, slight bluntness was observed. Sterilizing with a steam autoclave is much less destructive to $K3^{(R)}$ files than sodium hypochlorite. The longer time exposed to sodium hypochlorite, the more destructive pattern was shown on the blades of the files. Therefore, when using sodium hypochlorite solution, the exposure time should be as short as possible in order to prevent corrosion and increase the cyclic fatigue fracture time.

• Restorative Dentistry and Endodontics
• /
• v.31 no.2
• /
• pp.96-102
• /
• 2006

There are various factors affecting the fracture of NiTi rotary files. This study was performed to evaluate the effect of cross sectional area, pecking motion and pecking distance on the cyclic fatigue fracture of different NiTi files. Five different NiTi $files-Profile^{(R)}$ (Maillefer, Ballaigue, Switzerland), $ProTaper^{TM}$(Maillefer, Ballaigue, Switzerland), $K3^{(R)}$ (SybronEndo. Orange, CA) , Hero $642^{(R)}$ (Micro-mega, Besancon, France), Hero $Shaper^{(R)}$ (Micro-mega, Besancon, France)-were used. Each file was embedded in temporary resin, sectioned horizontally and observed with scanning electron microscope. The ratio of cross-sectional area to the circumscribed circle was calculated. Special device was fabricated to simulate the cyclic fatigue fracture of NiTi file in the curved canal,. On this device, NiTi files were rotated (300rpm) with different pecking distances (3 mm or 6 mm) and with different motions (static motion or dynamic pecking motion) . Time until fracture occurs was measured. The results demonstrated that cross-sectional area didn't have any effect on the time of file fracture. Among the files, $Profile^{(R)}$ took the longest time to be fractured. Between the pecking motions, dynamic motion took the longer time to be fractured than static motion. There was no significant difference between the pecking distances with dynamic motion, however with static motion, the longer time was taken at 3mm distance. In this study, we could suggest that dynamic pecking motion would lengthen the time for NiTi file to be fractured from cyclic fatigue.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.25 no.4
• /
• pp.349-360
• /
• 2009

Purpose: As the esthetic demands of dental implant patients are increased, the demands of zirconia as implant abutment material are also increased. It has non-metalic color, good biocompatibility, high strength and high toughness. Even thought the advatage of zirconia abutment, there are a few studies about mechanical properties of zirconia abutment. This study evaluated the mecanical strength with compressive bending strength and endurance limit of implant-zirconia abutment assembly. Materials and Methods: Static and cyclic loading of implant-Zirconia abutment assembly were simulated under worst case condition according to ISO. Test groups were implants of external butt joint with straight regular diameter and angled regular diameter zirconia abutment, implant of external butt joint with narrow straight diameter zirconia abutment and implant of internal conical joint with straight narrow diameter zirconia abutment. All test group were evaluated the mecanical strength with compressive bending strength and endurance limit. After fatique testing, fracture surface were examined by SEM. Results: The compressive bending strengths exceed 927N. Regular diameter zirconia abutment were stronger than narrow diameter zirconia abutment(P<.05). The endurance limits ranged from 503N to 868N. Conclusion: Within the limitation of this study, zirconia implant abutment exceeded the estabilished values for maximum incisal biting forces reported in the literature.

• The Journal of Korean Academy of Prosthodontics
• /
• v.48 no.1
• /
• pp.61-68
• /
• 2010

Purpose: This article attempted to determine the factors affecting the preload and screw loosening. Methods: Available clinical studies from 1981 to 2008 from the PUBMED that presented screw loosening data and review articles regarding screw joint stability were evaluated. Eleven studies dealing the biomechanical principles of the screw mechanics were reviewed. Moreover, the results of our data were included. Results: The frequency of screw loosening was consequently reduced due to the advancement in torque tightening with torque wrench, screw material, coating technique for reducing the frictional force, and thread design, etc. If preload in the screw falls below a critical level, joint stability may be compromised, and the screw joint may fail clinically. The types of fatigue failure of screw were divided to adhesive wear, plastic deformation, and screw fracture. Conclusion: An optimum preload is essential to the success of the implant-abutment complex. To maintain optimum preload, using a torque wrench and re-tightening at recall time were needed.