• 한국문화재보존과학회:학술대회논문집
• /
• 2007.10a
• /
• pp.51-52
• /
• 2007

• The korean journal of orthodontics
• /
• v.27 no.5 s.64
• /
• pp.839-852
• /
• 1997

It has been submitted that different ion solutions containing sulfate induce crystal growth and might substitute conventional acid etching for pretreatment of enamel in orthodontic bonding(${\AA}rtun$ et al., Am. J. Orthod. 85, 333, 1984). This investigation was designed to evaluate the relevance of crystal growth on the enamel surface as an alternative to conventional acid etching in direct bonding of orthodontic brackets. Annexing Li2SO4, MgSO4, K2SO4 respectively in the solution with $25\%$ polyacrylic md 0.3M sulfuric acids were employed to enhance the crystal growth. Human bicuspids were treated with various parameters as combinations of crystal growth and glass ionomer cement, crystal growth and orthodontic resin, acid etching and orthodontic resin for an investigative purpose. Crystal growth solution containing MgSO4 showed the highest shear bond strength(15.6MPa) within the groups of bonding brackets with glass ionomer cement(p<0.01). Bonding with glass ionomer cement on the surface of crystal growth demonstrated higher shear bond strength than with orthodontic resin(p<0.001). Bonding with glass ionomer cement on the surface treated with crystal growth solution containing MgSO4 or K2SO4 was not different shear bond strength statistically from bonding with orthodontic resin on the acid-etched surface. It suggests that bonding brackets with glass ionomer cement on the surface treated with crystal growth solution containing MgSO4 or K2SO4 is a potential alternative to bonding with resin on the acid etched sufrace.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.12 no.2
• /
• pp.103-112
• /
• 2008

Pull-off test is generally used to evaluate bond strength of FRP composite with concrete at job site. However, some damages on FRP composites can not be avoided during pull-off test and moreover test range of pull-off strength is limited by maximum tensile strength of concrete. Accordingly, it is required to set-up a test method that can evaluate mechanical properties of structural adhesive indirectly prior to pull-off test. In this study, the standard test methods for structural adhesive which can simply evaluate mechanical performance of adhesive were suggested through comparative experiments from each different standard in various countries. Particularly, gluing thickness of adhesive in tensile lap-shear tests, the section dimension of compression and bending test specimens become unified, and standard test specimen size is achieved by test results.

• Proceedings of the KAIS Fall Conference
• /
• 2010.05b
• /
• pp.981-984
• /
• 2010

생산성 증가 및 비용 절감을 위해 반도체 공정 기술을 단순화 시키는 것이 필요하다. WBL(Wafer Backside Lamination) 기술을 이용해 필름(film) 형태로 얇은 다이접착제를 웨이퍼(wafer)에 접착하여 반도체 칩과 PCB를 붙이는 방법과 직접 PCB에 다이접착제를 붙이는 방법을 사용하면 획기적으로 공정을 단순화 시킬 수 있다. 하지만 Lamination 기법은 고온을 이용하여 모듈화된 PCB에 접착하므로 전도와 복사에 의해 주변 접착제 필름이 녹아 버리는 문제점이 발생한다. 본 연구에서는 고온으로 인한 필름 융해 현상을 방지하기 위하여 배크라이트를 설치하였으며 CFD 해석을 통해 PCB와 반도체 칩을 접착시킬 때 열이 PCB에 미치는 영향을 살펴보았다.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.30 no.12 s.159
• /
• pp.1683-1689
• /
• 2006

Precedent researches on lyocell are mostly on lyocell structure, characteristics, physical properties by finishing and dyeability, and the like; there are little cases of researches on interlining for lyocell clothes production. To serve as a base information helpful to select fusible interlining and improve the efficiency of sewing process considering the characteristics of lyocell, this study performed t-est, F-test toward to the difference in the appearance-related properties and the mechanical properties of lyocell-interlining bonded fabric in accordance with the characteristics of fusible interlining and lyocell face fabric. This study reached following conclusions. Drapability and Crease recovery of lyocell-interlining bonded fabric are influenced by the structure of fusible interlining; stiffness of lyocell-interlining bonded fabric, by the structure of fusible interlining and the yam number of lyocell face fabric. WT is influenced by the mixture rate and yam number of lyocell face fabric. RT is influenced by the yam number of lyocell face fabric; G, 2HG, 2HG5, by the structure(woven and non-woven) of fusible interlining; B, HB, by the weight, structure(woven and non-woven) of fusible interlining, and yam number of lyocell face fabric; WC, by the weight, structure of fusible interlining; RC, by the structure of fusible interlining; thickness, by the weight of fusible interlining and the yarn number of lyocell face fabric; weight, by mixture rate and yam number of lyocell face fabric.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.30 no.2
• /
• pp.102-111
• /
• 2014

Purpose: Surface damage and bonding strength difference after micromechanical treatment of zirconia surface are to be studied yet. The aim of this study was to evaluate the difference of fracture resistance and bonding strength between more surface-damaged group from higher air-blasting particle size and pressure, and less damaged group. Materials and Methods: Disk shape zirconia ($LAVA^{TM}$) was sintered and air-blasted with $30{\mu}m$ particle size (Cojet), under 2.8 bar for 15 seconds, $110{\mu}m$ particle size (Rocatec), under 2.8 bar for 15 seconds, and $110{\mu}m$ particle size (Rocatec), under 3.8 bar for 30 seconds respectively. Biaxial flexure test and bonding failure load test were performed serially (n = 10 per group). For bonding test, specimens were bonded on the base material having similar modulus of elasticity of dentin with $200{\mu}m$-thick resin cement for tension of surface damage. Failure load of bonding was detected with acoustic emission (AE) sensor. Results: There were no significant differences both in the biaxial flexure test and bonding failure load test between groups (P > 0.05). Sub-surface cracks were all radial cracks except for two specimens. Conclusion: Within the limitations of no aging under monotonic load test, surface damage from higher air-blasting particle size and pressure was not significant. Evaluations of failure load with bonded zirconia disks was clinically relevant modality for surface damage and bonding strength, simultaneously.

• The korean journal of orthodontics
• /
• v.30 no.1 s.78
• /
• pp.83-89
• /
• 2000

The purposes of this study were to evaluate clinical applicability of resin modified glass ionomer cements and to determine the effect of salivary contamination on the tensile bond strength. Fourty extracted human permanent premolars were prepared lot bonding and standard edgewise brackets were bonded with Ortho-One, Fuji Ortho LC, Vitremer and Advance. Fourty extracted human permanent premolars were contaminated with saliva, dried and bonded with same materials above. The tensile bond strength was tested by Instron testing device aster storage in normal saline at ,$37^{\circ}C$ for 24 hours from bonding. The results were as follows : 1. The tensile bond strength of Ortho-One group was $7.68\pm1.76$, Advance group was $7.87\pm2.80$, Fuji Ortho LC group was $4.99\pm2.53$, Vitremer group was $2.80\pm0.88$ MPa. The tensile bond strength in contaminated condition of Ortho-One group was $4.12\pm1.67$, Advance group was $5.37\pm0.68$, Fuji Ortho LC group was $4.41\pm1.61$, Vitremer group was $2.60\pm1.10$ Mpa. 2. Salivary contamination did not affect the tensile bond strength when compared with the uncontaminated enamel group in Fuji Ortho LC and Vitremer (p>0.05) and there was great significant difference in the tensile bond strength of Ortho-One and Advance. 3. Advance, Ortho-One and Fuji Ortho LC seemed to have clinically a proper bond strength.

• Journal of Adhesion and Interface
• /
• v.12 no.4
• /
• pp.125-132
• /
• 2011

As the enhancement of indoor air quality is increasingly compelling the use of natural materials without any emission, this study reports the preparation and performance of natural garlic adhesives for wallpaper. The natural garlic adhesives were successfully prepared by the extraction of the clove of raw garlic with water to isolate carbohydrates and proteins. Properties of the prepared garlic adhesives such as the non volatile solids content, viscosity, density, and pH were 62%, 2,789 mPa.s, $1.3g/cm^3$, and 6.6, respectively. The non-volatile solids content has a great impact on the adhesion performance of the prepared garlic adhesives, which was adequate about 60%. Bonding strength of prepared garlic adhesives was greater than the requirement of a Korean standard for wallpaper. In addition, the garlic adhesives showed antibacterial activity inheriting from the garlic. It is expected that the prepared garlic adhesives could be used as safe and natural adhesives without emitting any volatile organic compounds and formaldehyde gas.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.8 no.1
• /
• pp.35-44
• /
• 1999

In a view point of earth environmental protection and social requirement, adhesively bonded structures of aluminum alloys have become to be employed for the purpose of decreasing fuel ratio by weight reduction and to improve performance in various engineering fields such as aircrafts, automobiles, rolling stocks and so on. In spite of such wide applications in adhesively bonded structures of aluminum alloys, the quantitative fracture criterion and evolution method of its bonded strength have not been established yet. The objective of this paper is to establish fracture criterion considering stress singularity at interface edges in adhesively bonded structures of aluminum alloys. Through the analyses of boundary element method and static fracture experiments with three different types of specimens in the adhesively bonded joints of aluminum alloys, its fracture criterion was proposed and discussed about strength evolution of adhesively bonded structures.

• Restorative Dentistry and Endodontics
• /
• v.25 no.3
• /
• pp.399-406
• /
• 2000

The effect of inlay surface treatment on bonding was investigated when resin inlay was bonded to resin-modified glass-ionomer base with resin cement. For the preparation of glass-ionomer base, resin-modified glass-ionomer cement (Fuji II LC, GC Co., Japan) was filled in class I cavities of 7mm in diameter and 2mm in depth made in plastic molds. Eighty eight resin inlay specimens were made with Charisma$^{(R)}$ (Kulzer, Germany) and then randomly assigned to the four different surface treatment conditions: Group I, $50{\mu}m$ aluminium oxide sandblasting and silane treatment ; Group II, silane treatment alone ; Group III, sandblasting alone, and Group IV (control), no surface treatment. After a dentin bonding agent with primer (One-Step$^{TM}$, Bisco Inc., IL., U.S.A.) was applied to bonding surface of resin inlay and base, resin inlay were cemented to glass-ionomer base with a resin cement (Choice$^{TM}$, Bisco Inc., IL., U.S.A.). Shear bond strengths of each specimens were measured using Instron universal testing machine (4202 Instron, lnstron Co., U.S.A.) and fractured surfaces were examined under the stereoscope. Statistical analysis was done with one-way ANOVA and Dunkan's multiple range test. The results were as follows: 1. Sandblasting and silane treatment provided the greatest bond strength(10.56${\pm}$1.95 MPa), and showed a significantly greater bond strength than sandblasting alone or no treatment (p<0.05). 2. Silane treatment provided a significantly greater bond strength(9.77${\pm}$2.04 MPa) than sandblasting alone or no treatment (p<0.05). However, there was no significant difference in bond strength between sandblasting treatment and silane one (p>0.05). 3. Sandblasting alone provided no significant difference in bond strength from no treatment (p>0.05). 4. Stereoscopic examination of fractured surface showed that sandblasting and silane treatment or silane treatment alone had more cohesive failure mode than adhesive failure mode. 5. In relationship between shear bond strength and failure mode, cohesive failure occurred more frequently as bond strength increased.