• Proceedings of the Korean Institute of Navigation and Port Research Conference
• /
• 2004.04a
• /
• pp.23-27
• /
• 2004

Developing of electromagnetic wave absorbers for GHz frequency, we used cast Alnico magnets. It is the first research paper to show that electromagnetic wave absorbers with Alnico magnets have good reflectivity in the GHz frequencies. Especially in this study, we used recycled cast Alnico magnets for natural resources problems and natural environment problems. New electromagnetic wave absorbers developed in this study are useful for X-band and C-band.

• Proceedings of the Korean Institute of Navigation and Port Research Conference
• /
• 2010.10a
• /
• pp.13-15
• /
• 2010

본 논문에서는 Flake Sendust 금속분말을 이용하여 ISM 대역에서 PCB 노이즈 억제용 전파흡수체를 설계 제작하고 검토한 결과를 보고한다. 먼저 자성손실 재료인 Sendust 금속분말을 사용한 전파흡수체의 특성을 예비 시험한 후, 그 특성을 개선하기 위하여 Flake Sendust 분말과 CPE의 조성비를 각각 60 : 40 wt.%, 70 : 30 wt.%, 80 : 20 wt.%로 하고, 두께 1 mm, 2 mm의 sheet형 전파흡수체 샘플을 제작하였다. Network Analyzer를 이용하여 제작한 샘플의 반사계수를 측정하고, -2법으로 재료정수(복소비유전율, 복소비투자율)을 계산하였다. 계산된 재료정수값을 이용하여 최적의 전파흡수체를 설계하여, 조성비 Flake Sendust : CPE = 70 : 30 wt.%, 두께 0.55 mm의 전파흡수체를 제작하였다. 이 전파흡수체는 2.44 GHz 대역에서 5.45 dB의 흡수능을 나타냄으로써 목표치인 5 dB를 달성하였다.

• Journal of the Korean Magnetics Society
• /
• v.1 no.2
• /
• pp.49-54
• /
• 1991

In this study the correlation between material constants and microwave absorbing characteristics of ferroxplana composite microwave absorber used in X-band was investigated. The real part of permeability(${\mu}_{r}'$) was decreased and the imaginary part of permeability(${\mu}_{r}"$) of ferroxplana composite was increased with increaing ferroxplana loading ratio(F/R). The frequency showing maximum attenuation was shifted to lower frequency with increasing absorber thickness. The absorber 2.6 mm thick showed good band width property and 3.2 mm thick showed good attenuation property. From the apphcation of ferroxplana composite's material constants to the region of material constants which satisfy broad band width, it is found that the absorbing characteristics were estimated quantitatively. Estabhshment of material constants' region which satisfies broad band width can make practical application to design of high performance ferrite microwave absorber.

• The Journal of Korean Institute of Electromagnetic Engineering and Science
• /
• v.12 no.6
• /
• pp.1002-1008
• /
• 2001

The absorbing structure composed of multi-layered fiber reinforced composite materials was designed and microwave absorbing properties are investigated. On the basis of transmission line theory, the theoretical equations to predict the reflection loss and the appropriate composite material for each functional layer are suggested. The most significant result of this study is the successful design and fabrication of triple-layered composite laminates which has the superior microwave absorbing porperties (more than 10 dB in 4∼12 GHz range), without using the ferrite filler in the impedance transforming layer. In the two-layered composite laminate (absorber/substrate), however, the use of ferrite filler (about 40 wt %) in the absorbing layer is necessary to obtain the certain level of microwave absorbance. By combining the glass-fiber composite with ferrite filler and carbon-fiber composite substrate, the microwave absorbing properties more than 10 dB in 4∼12 GHz frequencies than be obtained.

• The Proceeding of the Korean Institute of Electromagnetic Engineering and Science
• /
• v.5 no.4
• /
• pp.40-46
• /
• 1994

Design and microwave absorbing properties of ferrite plate are investigated for the application to the radiowave absorbers used in anechoic chamber. The required frequency-dependence of complex permeability is determined on the basis of wave-impedance-matching relationship. The plate thickness and matchingfrequency are determined from the complex permeability and dielectric constant, and then compared with the directly measured reflection loss. A systematic variation of material constants and their influence on the microwave absorbing properties are demonstrated.

• Journal of the Korean Magnetics Society
• /
• v.18 no.3
• /
• pp.115-119
• /
• 2008

The raw materials of permalloy were processed the ball-mill for 30 hours and the shape of permalloy particles was changed from sphere to flake type, which was observed using scanning electron microscope. The complex permittivity and permeability spectra and reflection loss of permalloy-rubber composite was measured using Network Analyzer in order to investigate the relationship between the microwave absorption and the material constants. The flake type permalloy-rubber composite showed high reflection loss, which was due to the high complex permittivity and permeability. Also, the matching frequency shifted toward lower frequency range with microwave absorber thickness, and the maximum reflection loss of -6.1 dB was observed in $1.65\;GHz{\sim}1.86\;GHz$ for a 1.3 mm thickness.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.3 no.1
• /
• pp.51-58
• /
• 1999

In this Paper, the Performance of the semi-anechoic chamber which is to be constructed by the cross-shaped ferrite absorbers with broadband frequency characteristics, has been evaluated by the image method. As a result it was confirmed that the cross-shaped absorber has excellent performance over the frequency range from 30 MHz to 3,000 MHz, while the tile and the gird-type ferrite absorbers have the bandwidth of 30 - 1,000 MHz.

• Proceedings of the Korean Institute of Navigation and Port Research Conference
• /
• 2007.12a
• /
• pp.14-16
• /
• 2007

본 논문에서는 UHF대역 RFID 통신 시스템 간에 발생하는 리더 간섭을 방지하기 위한 전파흡수체를 설계 및 제작하였다. 먼저 자성손실 재료인 Amorphous와 지지재인 CPE(Chlorinated Polyethylene)를 이용하여 조성비별 전파흡수체 샘플을 제작하였고, 이 전파흡수체 샘플로부터 구한 재료정수를 이용하여 시뮬레이션을 한 결과 최적의 조성비가 Amorphous: CPE = 80 : 20 wt.% 임을 확인하였다. 그리고 시뮬레이션 결과를 토대로 전파흡수체를 실제작하여 전파흡수능을 비교 ${\cdot}$ 분석하였다. 그 결과 Amorphous : CPE = 80 : 20 wt.%의 조성비 일 때, 두께 4mm 의 전파 흡수체가 860 MHz ${\sim}$ 960 MHz의 주파수 범위에서 전파흡수능 20 dB 이상의 특성을 얻음으로써 UHF대역의 RFID 리더 간섭을 억제할 수 있음을 확인하였다.

• Journal of Navigation and Port Research
• /
• v.27 no.1
• /
• pp.71-74
• /
• 2003

Electromagnetic wave absorbers with sheet type have been fabricated and their absorption properties are measured. The absorbtion properties of the fabricated ferrite absorbers were improved with decreasing the particle size in the frequency range of 2.4~3.2 GHz.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2000.05a
• /
• pp.160-164
• /
• 2000

In this paper, we studied the relation between using amount of Ferrite and electromagnetic wave absorbing properties of ferrite-rubber composite. The variation of using amount of Ferrite have been 52 wt.% ~ 62 wt.%. As s result, it has been shown that the electromagnetic wave absorbing properties of ferrite-rubber composite are related to the using amount of Ferrite in composite. And, we can control electromagnetic wave absorbing properties of ferrite-rubber composite by the control of using amount of Ferrite.