• Journal of the KSME
• /
• v.21 no.1
• /
• pp.32-39
• /
• 1981

전자 비임 용접법을 이용하게 될 때 알루미늄과 철과의 용접이 가능하다는 것을 알 수 있는데 그러면 다음은 알루미늄과 철과의 식접이 곤란한 이유와 원인을 설명하고 그 원인을 제거하는 방법을 검토하여 끝으로 양호한 용접이음을 얻을 수 있는 용접법을 기술하기로 한다.

• Journal of Welding and Joining
• /
• v.2 no.1
• /
• pp.25-29
• /
• 1984

In order to investigate the predominant factors which determine penetration depth and bead width in electron beam welding, bead-on-plate welding was carried out using 7075-T6 Al alloy. The results obtained from the present experiments can be summarized as follows; 1) With increasing accelerating voltage, bead width (B.W) decreases but penetration increases remarkably. 2) Increasing beam current results in increase of bead width and penetration respectively, and decrease of the ratio of penetration increment to beam current increment. 3) With increasing welding speed penetration decreases remarkably, while bead width creases.

• Journal of Welding and Joining
• /
• v.10 no.4
• /
• pp.103-106
• /
• 1992

건설기계는 우리나라의 산업발전과 성장해 왔으며, 또한 발전과정에서 기여한 바도 크다. 건설 기계의 수요는 1970년대 초부터 지하철, 고속도로등 사회간접자본 개발이 활발해 짐에 따라 건 설기계에 대한 투자나 내수가 성장하기 시작하여 1980년대 후반 국가 산업규모가 확대됨에 따 라서 크게 신장하여, 1982년 내수규모가 약 2100여대이던 것이 1991년에는 16,000여대로 증가해 왔다. 이 중 대표기종인 굴삭기가 전 건설중장비의 약 76%('91년도 금액비)를 점하고 있고, 또한 건설기계는 건설작업의 성역화에 기여해 왔으며 앞으로도 이 역할은 변함없을 것이다. 최근에는 건설기계의 안전성, 공정의 자동화, 로봇화 등이 크게 요구되고 있다. 건설기계는 구조상 연강 후판(두께10-50mm)이 주류를 이루고 내마모부품이 많다. 구성부는 강판이 사용이나(총 중량의 약 30%)일부 주강과 단조품이 사용되고 있다. 경량화를 위하여 고장력강이 사용되고, 기어나 샤프트 등에는 합금강이나 탄소강이 쓰이고 있다. 생산공정은 자동화, 무인화가 추진되고 있고, 설계는 CAD/CAM화가 보편적으로 활용되고 있다. 용접은 탄산가스 아아크 용접이 대부분이고, 일부 MAG또는 플락스 충전 와이어(FLUX CORED WIRE)를 사용하고 있다. 합금강 등에는 마찰용접이나 전자 비임용접이 활용되기도 한다.

• Journal of Welding and Joining
• /
• v.4 no.2
• /
• pp.21-29
• /
• 1986

The influence of welding heat input variation(600-900J/cm) and heat-treatment condition after welding on tensile strength of butt welded joint in $175Kg/mm^2$ strength level Maraging steel(Co-free and Co-containing) sheets was investigated on the basis of hardness distribution, microstructure of weld metal and fracture surface. The obtained main results are as follows; 1. The strength of weldment (UTS, NTS), joint efficiency showed a little decreasing tendency with the increase in welding heat input, and the elongation showed a little increasing tendency with the increase in the width of weld metal. It was considered because of the plastic constraint of the high strength base metal. 2. The strength of weldment was better in the solution treatment and aging than the aging only after welding due to the disappearance of almost denverite in weld metal. 3. The hardness distribution in weldment after welding and heat-treatment was almost similar to both Co containing and Co free Maraging steel with change in welding heat input. 4. The fracture was occurred at weld metal, and the fracture surface showed a relatively shallow dimples in both Co containing and Co free Maraging steel.