• Journal of Korean Society of Steel Construction
• /
• v.16 no.4 s.71
• /
• pp.415-423
• /
• 2004

To investigate the long-term corrosion resistance of an uncoated weathering steel, an important outdoor constructional steel material, skyward surfaces of the weathering steel and a control steel initially exposed to rural and industrial atmospheres for 9 years were electrochemically tested in neutral artificial rain in terms of electrochemical potentials, impedances, and anodic potentiodynamic polarization curves. Their results were then discussed. A quite passive and stable rust layer to the artificial rain was well formed on the skyward surface of the weathering steel exposed to the industrial and rural atmospheres, and its corrosion rate in the artificial rain was measured to be about a low $3{{\mu}m}/y$. Continuous immersion of all the weathered surfaces in the artificial rain revealed the gradual degradation of the weathered corrosion layers on the steel, resulting in a cathodically controlled corrosion of the substrate steel by the electrochemical measurements. Alloy components of the weathering steel were found to retard the degradation of the weathered corrosion layers on the steel in the artificial rain. For better corrosion evaluation of the weathering steel, more electrochemical measurements of surfaces that have been exposed for more than 9 years to more closely simulated atmospheric waters are needed. These measurements are almost non-destructive and can provide online and in situ information on the corrosion rate, the development of corrosion and the conditions of rust layers on any interested surface and at any exposure time of the steel, so they can be effectively applicable to the corrosion evaluation of steel structures such as bridges, towers, and architectures by forming an electrochemical cell on an interested structural surface and by using a portable electrochemical instrument.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.143-143
• /
• 2016

알루미늄 합금은 내구성과 내식성이 우수할 뿐만 아니라 다양한 표면개질을 통해 그 표면 특성을 더욱 향상시킬 수 있다. 특히 Al-Mg계 5083-H321 Al 합금의 경우 가공성 및 용접성이 우수하여 선체 재료로 널리 이용되는데, 이는 선체중량의 경량화가 가능하여 연료비 절감과 빠른 선속 등 다양한 이점을 지니기 때문이다. 그러나 선속의 고속화에 따라 선체에 가해지는 유체충격이 증가하고 정압 저하에 기인하여 캐비테이션-침식 손상이 증가할 뿐만 아니라 해수환경 특성 상염소이온의 존재로 부식이 가속화되는 등 침식 및 부식의 시너지효과로 손상은 크게 증가한다. 이에 대한 방지대책으로 다양한 표면개질 기법이 제안되고 있으나 강한 충격압이 동반된 캐비테이션 침식-부식 복합 손상 환경에서는 표면처리만으로는 불가능할 수 있다. 따라서 본 연구에서는 양극산화된 5083-H321을 대상으로 캐비테이션 환경 하에서 일정 전위를 인가하여 침식-부식 손상이 최소화되는 최적전위를 규명하고자 한다. 이를 위해 먼저 분극 실험을 통해 재료의 전기화학적 거동을 바탕으로 임의의 전위를 선정하고 해당 전위를 인가한 상태에서 캐비테이션 실험을 실시하였다. 이때 분극실험과 캐비테이션-전기화학 복합실험 모두 $25^{\circ}C$의 해수에서 실시하였으며, 전기화학적 분극실험은 유효면적이 $3.24cm^2$인 시편에 2 mV/s의 분극속도로 0 ~ -3 V 까지 인가하였고, Ag/AgCl 기준전극과 백금대극을 사용하였다. 캐비테이션-전기화학 복합 실험은 정전위를 인가한 상태에서 $30{\mu}m$의 진폭으로 20분간 실시하였으며, 혼팁과 시험편 사이의 거리는 1 mm로 일정하게 유지하였다. 실험 후 표면 손상의 정량적 분석을 위해 인가된 전위별 전류밀도를 비교하고, 무게감소량을 측정하였으며, 손상특성 분석을 위해 3D현미경과 주사전자현미경(SEM)을 통해 표면을 분석하였다.

• Journal of the KSME
• /
• v.28 no.4
• /
• pp.313-321
• /
• 1988

어떤 구조물이 반복하중을 받으면 피로파괴를 일으킨다. 만일 이 구조물이 부식환경 속에 앗 으면 불활성 분위기나 공기 중에서 보다 빨리 파괴에 이르게 된다. 이러한 현상을 흔히 부식 피로라고 한다. 부식피로에 크게 영향을 미치는 변수들을 대략 기계적 변수, 금속학적 변수, 환경 변수로서, 기계적 변수에는 최대응력 확대계수, 응력확대계수범위, 응력비, 반복하중 주파수, 반복하중파형, 응력상태, 잔류응력, 균열의 크기 및 모양 등이 있으며 금속학적 변수로는 합금 조성, 합금원소와 불순물의 분포, 미세조직과 결정구조, 열처리, 소성가공, 집합조직 등이며 환 경변수에는 온도, 환경의 형태(기체, 액체), 부식성분의 분압 또는 농도, 전기화학적 전위, pH, 수용성 환경의 점성, 피복, 부식억제제 등이 있다. 이와 같이 부식환경 속에 있는 구조물의 파 손을 이해하기 위하여는 응력부식과 부식피로를 공부하여야 한다. 이 현상은 매우 복잡한 문 제이기 때문에 아직도 완전히 이해되지 않은 상태이고 따라서 중요한 연구대상이 되고 있다. 여기서는 응력부식과 부식피로의 파괴역학적인 측면을 소개하고자 한다.

• Journal of the Korean Institute of Gas
• /
• v.9 no.1 s.26
• /
• pp.21-25
• /
• 2005

This paper was studied on the corrosion behavior of STS 304 for gas boiler in the condensed water, the electrochemical polarization test of STS 304 for gas boiler in the condensed water was carried out. And the corrosion behavior of STS 304 was considered. The main results are as following: 1) As corrosion environment is acidified from neutrality, the polarization resistance of STS 304 decreases and the corrosion potential is less noble. 2) The corrosion reaction mechanism of STS 304 is cathodic control. 3) As corrosion environment is acidified, the passive potential range of STS 304 decreases. Also, the passive current density of STS 304 increases.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.3 no.2
• /
• pp.80-83
• /
• 2002

The effect of chloride content on the corrosion of reinforced bar in concrete was studied. The mixing ratio of the concrete was 1 : 1.78 : 5.35 : 4.73 (water : content : ballast : sand). The studied chloride content was in the range of 0∼3.5 wt%. The corrosion potentials were measured in every week for two years. The copper-copper sulfate electrode (CSE) was employed as a reference electrode. After two years, the corroded structure was examined and compared to measured corrosion potential. Any visible difference was founded in the specimen located indoor and outdoor. The chloride concentration enhanced rusting and reinforced bar, shifting the potential to active range. The results showed good argument with Van daveer criteria. In 3.5 wt% chloride, the potential shifted belong -350 mV after 58week. Specimen in 1.75 wt% chloride, showed the potential between -200 mV∼-350 mV. However those in free chloride solution maintained above -200 mV for the studied period. It can the concluded that the chloride enhanced corrosion of rebar in concrete and the electrochemical potential can be a promising corrosion monitoring technique.

• Applied Chemistry for Engineering
• /
• v.9 no.6
• /
• pp.907-913
• /
• 1998

Corrosion behavior of steel reinforcements embedded in concrete containing various chloride ion concentrations was investigated by an electrochemical impedance spectroscopy(EIS). Chloride ions were introduced into the concrete by dissolving the NaCl and $CaCl_2$ in the water with a given weight of cement. Based on the impedance parameters measured by EIS, more complete equivalent circuit, a schematic physical model, and the mechanism of concrete reinforcement corrosion were suggested. By the implement of experimental impedance parameters obtained from the model with corresponding CNLS-fitting data, the corrosion rate of steel reinforcement with chloride ions could be predicted.

• Journal of the Korean Chemical Society
• /
• v.18 no.6
• /
• pp.391-399
• /
• 1974

Corrosion and passivation of metallic cobalt was studied by means of electrochemical experiments including potentiostatic and galvanostatic measurements and cyclic voltammograms. The mechanisms of active dissolution and passivation of cobalt at the metal/borate buffer solution interface are deduced from the Tafel slope, pH dependence of the Flade potential, and dissolution kinetic data. Hydroxyl group adsorbed on cobalt surface seems to participate in surface oxidation and formation of the passive layer. The growth kinetic data as measured by the current density suggests a mechanism in which the growth of the passive layer is determined by field-assisted transport of ions through the layer. Thickness of the passive layer was estimated by coulometry to be about 10${\AA}$ at the lowest passive potential and to grow gradually with anodic potential to about 20${\AA}$.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.188-188
• /
• 2016

GZO 박막은 상업적으로 사용되는 ITO를 경제적으로 대체할 수 있는 유망한 투명 전도 물질이며, 인체에 무해하고, 공급이 쉬우며, 화학적으로 안정하다. 특히, CIGS와 같은 광전변환 소자 전극에서는 부식 저항이 매우 중요한데, 습한 환경에서 견뎌낼 수 있다는 장점이 있다. GZO는 3가 갈륨이 2가 아연에 도핑된 n타입의 반도체 물질이다. 그리고 육각형의 황화아연 물질의 전기 전도도는 산소 결핍에 매우 의존한다. GZO의 수소는 산소 결핍 집중에 영향을 끼친다. 따라서 이 연구에서는 RF 마그네트론 스퍼터링 실험 동안 수소 함유량을 다양화 시키고, 면 저항, 광 투과도, 부식저항의 효과를 조사한다. 수소량이 증가할수록, 면 저항은 향상되어지고, 특정 지점을 넘으면 감소한다. 분극 실험에 의해 측정되어진 부식 저항은 박막의 미세조직과 결정립계의 특성에 더 의존되어진다. 훨씬 더 많은 수소를 함량한 비정질이 부식 저항성에 있어서 유효한 차이를 나타내지 못하는 동안 결정 내에서 많은 수소를 지닌 작은 결정의 결정립계는 낮은 분극저항, 즉 낮은 부식 저항성의 결과를 도출한다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.163-163
• /
• 2016

아연계 도금 강판은 우수한 내식성을 가지며 특히 아연의 희생방식기구에 의해 철의 부식을 억제하므로 선박, 건축자재, 전자기기 및 자동차 등 다양한 분야에서 그 수요와 사용범위가 증가하고 있다. 또한 도금 조성비 변화 및 다양한 표면처리 방법을 통해 가혹한 환경에서의 우수한 내식성에 대한 연구가 활발히 진행되고 있다. 그 중 갈바륨(Galvalume)은 55%의 알루미늄(Al)과 45%의 아연(Zn)으로 되어 있으며, 아연의 장점인 희생방식성과 내알카리성, 알루미늄의 장점인 내구성과 내열성, 내산성을 이상적으로 결합시킨 알루미늄(Al)-아연(Zn) 고내식 합금용융도금강판이다. 본 연구에서는 갈바륨 소재를 여러 산업현장에서 강관 형태로 사용할 경우의 내식성을 파악하기 위해 갈바륨 강관과 기존에 사용되고 있는 용융도금재인 용융아연도금 강관을 비교하며 실험을 진행하였다. 냉간압연강관에 용융아연도금 약 $25{\mu}m$, 갈바륨 약 $20{\mu}m$ 두께로 제작된 강관을 사용하였으며 제작된 도금층 표면 모폴로지는 SEM을 통해 관찰하였고, XRD 분석을 통해 결정 구조를 확인하였다. 또한 5% 염수분무 환경 중 노출시험(Salt spray test), 3% NaCl 용액에서의 자연침지 시험 및 3% NaCl 용액 중 전기화학적 양극분극 시험을 진행하여 평가하였다. 5% NaCl 환경에서의 염수분무 시험 결과 용융아연도금의 경우 단면에서는 90시간, 표면에서는 260시간 경과 후 적청이 발생하였다. 반면, 갈바륨의 경우에는 단면에서 210시간 경과 후에 적청이 발생하였고, 표면의 경우에는 900시간 이상에서도 적청이 발생하지 않았다. 이 결과를 통해 용융아연도금에 비해 갈바륨 도금의 내식성이 단면에서는 3배, 표면에서는 4~5배 이상 향상된 것으로 확인되었다. 또한 3% NaCl 용액 중 자연침지 시험 결과 용융아연도금 강관 표면은 24시간 경과 후 열화부를 중심으로 흑변하는 것을 확인할 수 있었으나 갈바륨의 경우에는 900시간 이상 실험이 진행되는 동안 No Scribe 및 Scribe 시편 모두 외관상 변화가 거의 없었다. 단면의 경우, 용융아연도금 시편은 900시간 이상 실험이 진행되는 동안 외관상 변화가 없었으며, 갈바륨 시편의 경우 300시간 경과 하면서 흰색의 아연 부식생성물이 나타났으나 900시간 이후로도 적청은 발생하지 않았다. 자연전위 측정결과 용융아연도금 및 갈바륨 시편 모두 유사한 전위거동을 나타냈지만 단면의 경우 갈바륨 시편이 용융아연도금에 비해 안정적인 거동을 보였다. 3% NaCl 용액 중 전기화학적 양극 분극 시험 결과 용융아연도금이 갈바륨에 비해 귀한 방향의 부식 전위 값을 나타냈으며, 부식 전류밀도도 용융아연도금이 갈바륨에 비해 더 높은 값을 나타내는 것을 확인할 수 있었다. 이상의 염수분무시험, 자연침지시험 및 전기화학적 양극분극시험을 통해 종합적으로 분석-고찰하여 보면, 그 부식이 진행되는 과정은 융융아연도금과 달리 갈바륨 도금의 경우가 다단계적인 부식 과정을 거치면서 우수한 내식 특성을 나타낸다는 것을 알 수 있었다. 즉, 갈바륨 도금은 그 도금 막에 분포된 합금상 원소 성분들이 상호 갈바닉(Galvanic) 작용하며 형성된 부식생성물이 수평적으로 자체 차단(Barrier) 역할을 하는 과정과 부분적 부식-회복 과정을 거치면서 다단계적으로 부식속도를 감소시키게 된다는 것을 확인 할 수 있었다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.145-145
• /
• 2016

해양환경용 구조물은 극심한 부식 환경에 노출되어 있고 부식손상으로 인한 직간접적 경제적 손실이 발생하고 있는 상황이다. 이에 대한 방식대책으로써 음극방식법이 선박, 교량, 각종 화학장비에 널리 이용되고 있으며, 이러한 산업분야에 가장 흔히 적용되고 있는 음극방식 중 하나가 피방식체에 일정 전류 또는 음극 전위를 인가하는 외부전원법이다. 이는 전도성 부식환경인 해수환경 하에서 철강 및 해양환경용 구조 재료의 내식성을 월등히 향상시킬 수 있기 때문에 설계에 있어서 고급 내식재료 대신 경제적인 상용 재료를 적용할 수 있어 비용 절감효과를 가질 수 있다. 한편 적정 방식전위에서는 부식손상으로부터 강재를 보호하지만, 과방식 전위에서는 취성이 발생함으로써 내구성 감소의 역효과가 나타날 수도 있기 때문에 최적 방식전위의 규명은 반드시 필요하다. 따라서, 본 연구에서는 S355ML강에 대하여 천연해수 용액에서 다양한 정전위를 조건으로 전기화학실험을 실시하여 최적 방식전위를 규명하고자 하였다. 시험편은 에머리 페이퍼로 2000번까지 연마하였고, 아세톤과 증류수로 세척하여 실험하였다. 전기화학(정전위) 실험은 천연해수 속에서 $1.28cm^2$의 면적만을 노출시켜 진행하였으며, OCP로부터 -2.0V까지의 음극분극 곡선을 분석하여 정전위 조건들을 선정하였다. 그리고 외부 직류전원장치를 이용하여 1,200초 동안 다양한 정전위를 인가하였으며, 기준전극은 Ag/AgCl 전극을 이용하였다. 실험 후에는 주사전자현미경과 3D 현미경을 통해 시험편 표면을 관찰하였으며, 그 결과 일부 음극분극 구간에서 강재 표면에 전착물에 의한 뷸균일한 피막이 형성되었다. 또한, 일정 전위구간에서 용해 및 과전압에 대하여 표면손상 정도를 관찰하여, 해수환경 하에서 S355ML강의 최적 방식전위를 규명하였다.