Prediction of Concrete Corrosion using Electrodchemical Technique

전기화학적인 콘크리트 부식의 예측

The effect of chloride content on the corrosion of reinforced bar in concrete was studied. The mixing ratio of the concrete was 1 : 1.78 : 5.35 : 4.73 (water : content : ballast : sand). The studied chloride content was in the range of 0∼3.5 wt%. The corrosion potentials were measured in every week for two years. The copper-copper sulfate electrode (CSE) was employed as a reference electrode. After two years, the corroded structure was examined and compared to measured corrosion potential. Any visible difference was founded in the specimen located indoor and outdoor. The chloride concentration enhanced rusting and reinforced bar, shifting the potential to active range. The results showed good argument with Van daveer criteria. In 3.5 wt% chloride, the potential shifted belong -350 mV after 58week. Specimen in 1.75 wt% chloride, showed the potential between -200 mV∼-350 mV. However those in free chloride solution maintained above -200 mV for the studied period. It can the concluded that the chloride enhanced corrosion of rebar in concrete and the electrochemical potential can be a promising corrosion monitoring technique.

본 연구는 콘크리트 배합시 염분의 함량이 구조물의 부식에 미치는 영향을 조사하기 위하여 수행되었다. 콘크리트는 물 : 포틀랜트 cemente : 자갈 : 모래의 비율을 1 : 1.78 : 5.35 : 4.73의 비율로 하여 배합하였으며 염분의 함량은 0∼3.5wt%의 범위에서 철근의 부식을 연구하였다. 부식특성을 연구하기 위하여 부식전위를 2년간 측정하였으며 이를 콘크리트 파괴후의 철근의 외관 부식도와 비교하였다. 옥내와 옥외에 두었을 때 부식속도의 차이는 없었으며 염분의 함량이 증가함에 따라 활성이 큰 전위값이 측정되었다. 전위값이 낮은 시편은 부동태 피막이 파괴되어 부식이 진행하고 있었으며, 전위값이 높은 시편에서는 부식생성물이 관찰되지 않았다. 본 실험의 결과로 보강용 강재의 부식손상 정도를 자연전위 측정방법을 통하여 콘크리트내 보강용 철근의 부식거동 및 부식속도에 대한 비괴적인 전기화학적 기술로서 구조물의 손상여부를 확인할 수 있었다.