• Journal of the Microelectronics and Packaging Society
• /
• v.6 no.3
• /
• pp.25-35
• /
• 1999

LTCC (Low Temperature Cofired Ceramic) or LTCC-M (Low Temperature Cofired ceramic on Metal) technology is one of MCM-C (Multichip Module on Ceramic) technologies and becomes to be widely used in consumer, RF and automotive electronics. As green sheets for LTCC are cofired below $1000^{\circ}C$ in comparison with those for HTCC (High Temperature Cofired Ceramic), high conductivity metal traces such as gold, silver and copper can be used. The dimensional stability in LTCC-M technology enables embedded passives to be integrated inside modules, which enhances the electrical performance and increases the reliability of the modules. Coefficient of thermal expansion and dielectric constant can be controlled by changing composition and heating profile for cofiring. In this technical review, LTCC and LTCC-M technologies are introduced and advantages of those technologies are explained.

• Proceedings of the Computational Structural Engineering Institute Conference
• /
• 2010.04a
• /
• pp.504-507
• /
• 2010

본 논문에서는 저온용 오스테나이트계 스테인리스강(ASS)의 온도 및 변형률 속도의 영향을 고려한 통합 구성 방정식 및 손상 모델을 제안하였다. 저온 영역에서, 304L ASS의 온도 및 변형률 속도별 인장 실험을 시행하였다. 그 결과, 변형 유기 마르텐사이트 상변태에 의해 상변태 유기 소성(TRIP)이 저온에서 현저히 나타났으며 온도 및 변형률 속도의 영향이 지대하였다. 실험 결과를 바탕으로 ASS의 저온 거동 및 특성을 규명하여 수치 모델에 반영하였다. 저온에서 일어나는 2차 경화 현상을 표현하기 위해, Bodner/Partom 점소성 구성 방정식을 수정하고 Tomita/Iwamoto 변형 유기 상변태 모델을 구성 방정식에 적용시켰다. 저온 연성 파단 현상을 표현하기 위해, Bodner/Chan 손상모델을 수정하여 접목시켰다. 제안된 모델을 유한요소 프로그램에 탑재시키고, 온도 및 변형률 속도 의존 재료 정수를 결정하였다. 저온 영역에서, 온도 및 변형률 속도별 재료 거동을 시뮬레이션하고 이를 실험 결과와 비교 및 검증하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.200-200
• /
• 2009

상용의 디스플레이로 널리 사용되고 있는 PDP(Plasma Display Panel)는 LCD와의 시장 경쟁으로 인하여 극한의 원가 경쟁 하에 있다. 따라서 각 공정에 대한 공정단가를 낮추기 위한 다양한 공정 및 소재 연구가 진행되고 있다. 그 가운데 하나가 Address와 Bus 전극으로 사용되고 있는 Ag 전극의 저온 소결이다. 이 공정은 저온소결 소재의 개발과 전극에 접촉하는 유전체 층과 matching이 중요하기 때문에 이들 소재의 동시 개발이 필요한 실정이다. 본 연구에서는 Ag 전극의 저온 소성을 위한 다양한 가능성을 검토하였다. 또한, 유전체와 동시 소결 가능한 소재의 특성 향상 및 저온 소성 연구를 동시에 수행하였다. Glass에 대한 유전체 층의 인쇄와 유전체 위에 전극 입자의 크기제어를 통한 기본 조성의 matching 특성을 비교하고 입자 크기가 전극의 소결 온도에 미치는 영향을 비교 평가 하였다. 유전체 층과의 matching 특성을 향상하기 위하여 유전체 조성의 일부를 전극에 첨가하여 두 소재간의 결합력을 증대시키기 위한 실험을 진행하였다. 그 결과를 바탕으로 저온 동시소성이 가능한 전극 소재의 최적화 실험을 실시하고 그 결과 최적의 전극 소재를 제시하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.66-66
• /
• 2010

잉크젯용 저온 Cu ink의 소성 특성을 향상 시키기 위해 소성 분위기롤 조절 하였다. 일반적으로 Cu는 산화가 잘되는 물질로 환원 분위기에서 소성이 이루어져야만 하기 때문에 acid, alcohol, aldehyde, ether와 같은 환원제를 소성시 사용하였다. 또한 1종의 환원제가 아닌 2종의 환원제롤 일정 비율로 섞음으로써 환원력를 조절하여 소성 품질을 향상 시킬 수 있었으며, 이러한 환원 분위기 조절을 통하여 300도 이하 저온에서 소성이 가능하였다. 또한 optical microscopy와 field emission scanning electron microscopy를 통해 막 품질과 미세조직의 치밀도를 확인하였고 배선 재료로써의 적용을 위해 resistance를 측정 비교하였다.

• Ceramist
• /
• v.8 no.3
• /
• pp.44-47
• /
• 2005

• Ceramist
• /
• v.8 no.3
• /
• pp.20-24
• /
• 2005

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.33 no.2
• /
• pp.475-481
• /
• 2013

Although the lightly burnt MgO at $850{\sim}1000^{\circ}C$ has expansibility, it does not lead to unsound concrete. The expansion of MgO could compensate for shrinkage of concrete for a long-term, because the hydration of MgO occurs at a slow pace. Recently, the study and application of mineral admixture such as fly ash and blast furnace slag have increased for the hydration heat reduction, durability improvement, and reducing $CO_2$ emission in the construction industry. Thus, it is necessary to research on the concrete that contains both a mineral admixture and MgO as an expansion agent. This study investigates fundamental properties of fly ash concrete with lightly burnt MgO through various experiments. The adiabatic temperature test results showed that the fly ash concrete with MgO of the 5% replacement ratio had the slower pace of the temperature rise and the lower final temperature than the fly ash concrete. The influences of MgO on long-term compressive strength varied depending on water-binder ratio, and the long-term length change test results indicated the expansion effects of the FA concrete containing MgO.

• Clean Technology
• /
• v.14 no.1
• /
• pp.14-20
• /
• 2008

In this study we have manufactured and characterized the low temperature calcined phosphor paste that can be used as a flat light source for LCD BLU. For the phosphor paste, the low temperature calcined acryl resin was used as the binder. From the result of thermal decomposition measurement, residual carbonaceous materials was found to be less than 0.1 wt% at $400^{\circ}C$. A flat light source device that was made by screen printing using the manufactured paste showed a near 100% luminous efficiency compared to the luminance of the phosphor.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.4
• /
• pp.619-625
• /
• 1998

The effect of softening point and glass amount of glass frit on the sintering behavior of low temperature cofirable glass/ceramic composites was studied and according to these results, glass/ceramic composites with high sintered density was fabricated. The density of composites was increased as the glass amount was increased. In case of using the glass with low softening point, the deformation of specimen was occurred though the ratio of the glass amount in the specimen was low. But, in case of using the glass with high softening point, the sintered density of composites was increased in accordance with glass amount. With the specimen of high softening point, the deformation was not happened. Therefore, it was found that the densification was progressed continuously in high glass amount. From the study on the effect of softening point of glass on sintering behavior, the suitable softening point and glass amount for fabrication of glass/ceramic composites can be anticipated. When glass frit with softening point of $790^{\circ}C$ was chosen according to this result, low temperature cofirable glass/ceramic composites with high density (97%) at $900^{\circ}C$ was fabricated.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.714-717
• /
• 2004

알루미노 보로실리케이트계 유리 기본조성 중 알칼리 토류 산화물의 종류 및 함량 변화에 따른 저유전율/저 LTCC 배선 기판의 저온 소성 거동 및 유전 특성을 조사하였다 알칼리 토류 산화물의 종류 및 함량 변화를 통해서 LTCC의 적정 소성온도인 $875^{\circ}C$ 부근을 포함하는 넓은 대역으로 소성수축이 시작되는 온도를 제어할 수 있었으며 유리 프리트와 알루미나 필러의 배합 비율의 변화에 따른 소성거동 및 유전특성의 변화 거동을 조사하였다. 알칼리 토류 산화물 중 유리 조성내의 CaO의 함량이 증가할수록 유리전이점 및 연화점을 증가하는 경향을 보였으며, 알루미나 필러의 첨가량이 증가할수록 소성수축이 시작되는 온도영역은 상향되고 유전율 및 품질계수는 증가하였다. 알칼리 토류 산화물의 조성과 필러인 알루미나의 함량을 제어함으로서 $875^{\circ}C$에서 18% 이상의 선수축율과 유전율 $5.1\sim5.5$ 및 유전손실 0.1% 이하의 우수한 특성을 갖는 저온소결용 LTCC 배선 기판을 얻을 수 있었다.