• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.31 no.2A
• /
• pp.129-136
• /
• 2011

Recently studies on functional concrete with a photocatalytic material such as $TiO_2$ have actively been carried out in order to remove air pollutants. The absorbtion of $TiO_2$ from those studies is applied by it being directly mixed into concrete or by suspension coated on the surface. When it comes to the effectiveness, the former process is less than that of the latter compared with the $TiO_2$ use. As a result, the direct coating of $TiO_2$ on materials' surface is more used for effectiveness. The Surface spread of it needs to have a more than $400^{\circ}C$ heat treat done to stimulate the activation and adhesion of photocatalysis. Heat treat consequently leads hydration products in concrete to be dehydrated and shrunk and is the cause of cracking. The study produces $TiO_2$ used Sol-gel method which enables it to be coated with a low temperature treat, applies it to pearlite using Lightweight Aggregate Concrete fixed with a low temperature treat and evaluates the spread performance of it. In addition to this, the size of pearlite is divided into two types: One is 2.5 mm to 5.0 mm and the other is more than 5.0 mm for the benefit of finding out the removal characteristics of $CH_3CHO$ whether they are affected by pearlite size, mixing method and ratio with $TiO_2$ and elapsed time. The result of this experiment shows that although $TiO_2$ produced by Sol-gel method is treated with 120 temperature, it maintains a high spread rate on the XRF(X ray Florescence) quantitative analysis which ranks $TiO_2$ 38 percent, $SiO_2$ 29 percent and CaO 18 percent. In the size of perlite from 2.5 mm to 5.0 mm, the removal characteristic of $CH_3CHO$ from a low temperature heated Lightweight concrete appears 20 percent higher when $TiO_2$ with Sol-gel method is spreaded on the 7 percent of surface. In other words, the removal rate is 94 percent compared with the 72 percent where $TiO_2$ is mixed in 10 percent surface. In more than 5.0 mm sized perlite, the removal rate of $CH_3CHO$, when $TiO_2$ is mixed with 10 percent, is 69 percent, which is similar with that of the previous case. It suggests that the size of pearlite has little effects on the removal rate of $CH_3CHO$. In terms of Elapsed time, the removal characteristic seems apparent at the early stage, where the average removal rate for the first 10 hours takes up 84 percent compared with that of 20 hours.

• Membrane Journal
• /
• v.33 no.4
• /
• pp.168-180
• /
• 2023

H₂ generation from renewable sources is crucial for ensuring sustainable production of energy. One approach to achieve this goal is biohydrogen production by utilizing renewable resources such as biomass and microorganisms. In contrast to commercial methods, biohydrogen production needs ambient temperature and pressure, thereby requiring less energy and cost. Biohydrogen production can reduce greenhouse gas emissions, particularly the emission of carbon dioxide (CO₂). However, it is also associated with significant challenges, including low hydrogen yields, hydrodynamic issues in bioreactors, and the need for H₂ separation and purification methods to obtain high-purity H₂. Various technologies have been developed for hydrogen separation and purification, including cryogenic distillation, pressure-swing adsorption, absorption, and membrane technology. This review addresses important experimental developments in dense polymeric membranes for biohydrogen purification.

• Analytical Science and Technology
• /
• v.22 no.6
• /
• pp.488-497
• /
• 2009

In this study, analytical methodology for several organic fatty acids (OFA: propionic acid (PA), butyric acid (BA), isovaleric acid (IA), and valeric acid (VA)) designated as new offensive odorants in Korea (as of year 2010) was investigated along with some odorous VOCs (styrene, toluene, xylene, methyl ethyl ketone, methyl isobutyl ketone, butyl acetate, and isobutyl alcohol). For this purpose, working standards (WS) containing all of these 13 compounds were loaded into adsorption tube filled with Tenax TA, and analyzed by gas chromatography (GC) system thermal desorber interfaced with. The analytical sensitivities of organic fatty acids expressed in terms of detection limit (both in absolute mass (ng) and concentration (ppb)) were lower by 1.5-2 times than other compounds (PA: 0.24 ng (0.16 ppb), BA: 0.19 ng (0.11 ppb), IA: 0.15 ng (0.07 ppb), and VA: 0.28 ng (0.13 ppb)). The precision of BA, IA, and VA, if assessed in terms of relative standard error (RSE), maintained above 5%, while the precison of other compounds were below 5%. The reproducibility of analysis improved with the aid of internal standard calibration (PA: $1.1{\pm}0.4%$, BA: $10{\pm}0.46$, IA; $12{\pm}0.3%$, VA: $4{\pm}0.1%$), respectively. The results of this study showed that organic fatty acid can be analyzed using adsorption tube and thermal desorber in a more reliable way to replace alkali absorption method introduced in the odor prevention law of the Korea Ministry of Environment (KMOE).

• Clean Technology
• /
• v.17 no.2
• /
• pp.166-174
• /
• 2011

The xAl-yCe oxide catalysts with different mol ratios of Al/(Al+Ce) were prepared by a co-precipitation method and Pt supported on xAl-yCe oxide catalysts were synthesized by an incipient wetness impregnation method. The catalysts were characterized by X-ray Diffraction (XRD), $N_2$ sorption, and $H_2$/CO-temperature programmed reduction ($H_2$/CO-TPR) to correlate with catalytic activities in co oxidation. Among the catalysts studied here, Pt/1Al-9Ce oxide catalyst showed the highest activity in dry and wet reaction conditions and the catalytic activity showed a typical volcano-shape curve with respect to Al/(Al+Ce) mol ratio. When the presence of 5% water vapor in the feed, the temperature of $T_{50%}$ was shifted ca. $30^{\circ}C$ to lower temperature region than that in dry condition. From CO-TPR, the desorption peak of $CO_2$ on Pt/1Al-9Ce oxide catalyst showed the highest value and well correlated the catalytic performance. It indicates that the Pt/1Al-9Ce oxide catalyst has a large amount of active sites which can be adsorbed by co and easy to supplies the needed oxygen. In addition, the amount of pentacoordinated $Al^{3+}$ sites obtained through $^{27}Al$ NMR analysis is well correlated the catalytic performance.

• Clean Technology
• /
• v.26 no.2
• /
• pp.131-136
• /
• 2020

Biomass bamboo charcoal is utilized as anode for lithium-ion battery in an effort to find an alternative to conventional resources such as cokes and petroleum pitches. The amorphous phase of the bamboo charcoal is partially converted to graphite through a low temperature graphitization process with iron oxide nanoparticle catalyst impregnated into the bamboo charcoal. An optimum catalysis amount for the graphitization is determined based on the characterization results of TEM, Raman spectroscopy, and XRD. It is found that the graphitization occurs surrounding the surface of the catalysis, and large pores are formed after the removal of the catalysis. The formation of the large pores increases the pore volume and, as a result, reduces the surface area of the graphitized bamboo charcoal. The partial graphitization of the pristine bamboo charcoal improves the discharge capacity and coulombic efficiency compared to the pristine counterpart. However, the discharge capacity of the graphitized charcoal at elevated current density is decreased due to the reduced surface area. These results indicate that the size of the catalysis formed in in-situ graphitization is a critical parameter to determine the battery performance and thus should be tuned as small as one of the pristine charcoal to retain the surface area and eventually improve the discharge capacity at high current density.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.211.2-211.2
• /
• 2016

그래핀은 본연의 우수한 물성으로 인하여 전자소자, 에너지 저장매체, 유연성 전도막 등 다양한 분야로의 응용가능성이 제기되었으나, 실제적인 응용을 위해서는 구조적인 결함을 최소화하며, 특성을 자유로이 제어하거나 향상시키는 공정의 개발이 요구된다. 특히 그래핀을 전자소자로 응용하기 위해서는 전기적 특성을 제어하는 것이 요구된다. 일반적으로 화학적 도핑은 그래핀의 전기적 특성을 제어하는 효율적인 방법으로 알려져 있다. 화학적 도핑은 그래핀을 구성하는 탄소원자를 이종원자로 치환하거나 표면에 흡착시켜 기능화 된 그래핀을 얻는 방법으로, 특정 가스 분위기에서 고온 열처리하거나 활성종들이 존재하는 플라즈마에 노출시키는 방법이 제시되었다. 특히 플라즈마를 이용한 도핑방법은 저온에서 단시간의 처리로 도핑이 가능하고, 플라즈마 변수를 변경하여 도핑정도를 수월하게 제어할 수 있다는 장점을 가지고 있다. 그러나 플라즈마내의 극성을 띄는 다양한 활성종들의 충돌효과로 인하여 구조적인 손상이 발생하여 오히려 특성이 저하될 수 있어 이를 고려한 플라즈마 공정조건의 설정이 필수적이다. 따라서 본 연구에서는 플라즈마에 노출된 그래핀의 Raman 특성을 고찰함으로써 화학적 도핑과 구조적인 결함의 경계를 확립하고 구조결함의 형성을 최소화한 효율적인 도핑조건을 도출하였다. 그래핀은 물리적 박리법을 이용하여 300 nm 두께의 실리콘 산화막이 존재하는 실리콘 웨이퍼 위에 제작하였으며, 평행 평판형 직류 플라즈마 장치를 이용하여 전극의 위치, 인가전력, 처리시간을 변수로 암모니아($NH_3$) 플라즈마를 방전하여 그래핀의 Raman 특성변화를 관찰하였다. 그래핀의 구조적 결함 및 도핑 효과는 라만 스펙트럼의 D, D', 2D밴드의 강도와 G밴드의 위치와 반치폭(Full width at half maximum; FWHM)의 변화를 통해 확인하였다. 그 결과, 인가전력과 처리시간에 따라 결함형성과 질소도핑 영역이 구분 가능함을 확인하였으며, 이를 바탕으로 결함형성을 최소화한 효율적인 도핑조건이 접지전위, 0.45 W의 인가전력, 처리시간 10초이며, 최적조건에서 계산된 도핑레벨은 $1.8{\times}10^{12}cm^{-2}$임을 확인하였다.

• Applied Chemistry for Engineering
• /
• v.9 no.6
• /
• pp.878-883
• /
• 1998

The methane combustion reaction was conducted over Pb-ZSM-5 catalysts. ZSM-5 synthesized at low temperature and atomospheric pressure was used as a support. The change of methane conversion with $SiO_2/Al_2O_3$ molar ratio was tested. The methane conversions of the synthesized Pb-ZSM-5 catalyst was compared with those of a commercial Pd-ZSM-5(PQ Co.) and $PdO/{\gamma}-Al_2O_3$. The methane conversion increased with the decrease in $SiO_2/Al_2O_3$ molar ratio. The combustion rate of methane also increased with the decrease in $SiO_2/Al_2O_3$ molar ratio. The synthesized Pb-ZSM-5 showed better methane conversion than that of the commercial one. It is found that a crucial factor in methane combustion reaction is oxygen adsorption strength on the catalysts.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.238.1-238.1
• /
• 2015

2차원 탄소나노재료인 그래핀은 본연의 우수한 물성으로 인하여 전자소자, 에너지 저장매체, 유연성 전도막 등 다양한 분야로의 응용가능성이 제기되었다. 그러나 실제적인 응용을 위해서는 그래핀의 구조적인 결함을 최소화하며, 특성을 자유로이 제어하거나 향상시키는 공정의 개발이 필요하다. 일반적으로 화학적 도핑은 그래핀의 전기적 특성을 제어하는 효율적인 방법으로 알려져 있다. 화학적 도핑의 방법으로는 그래핀을 특정 가스 분위기에서 고온 열처리하거나 활성종들이 존재하는 플라즈마에 노출시킴으로써, 그래핀을 구성하는 탄소원자를 이종원자로 치환하거나 표면에 흡착시켜 기능화 된 그래핀을 얻는 방법 등이 제시되었다. 특히 플라즈마를 이용한 도핑방법은 저온에서 단시간의 처리로 효율적인 도핑이 가능하고, 인가전력, 처리시간 등의 플라즈마 변수를 변경하여 도핑정도를 수월하게 제어할 수 있다는 장점을 가지고 있다. 그러나 플라즈마 내에 존재하는 극성을 띄는 다양한 활성종들로 인하여 그래핀에 구조적인 결함을 형성하여 오히려 특성이 저하될 수 있어 이를 고려한 플라즈마 공정조건의 설정이 필수적이다. 따라서 본 연구에서는 플라즈마에 노출된 그래핀의 Raman 특성을 고찰함으로써 화학적 도핑과 구조적인 결함의 경계를 확립하고 구조결함의 형성을 최소화한 효율적인 도핑조건을 도출하였다. 고품질 그래핀은 물리적 박리법을 이용하여 300 nm 두께의 실리콘 산화막이 존재하는 실리콘 웨이퍼 위에 제작하였으며, 평행 평판형 직류 플라즈마 장치를 이용하여 전극의 위치, 인가전력, 처리시간을 변수로 암모니아(NH3) 플라즈마를 방전하여 그래핀의 Raman 특성변화를 관찰하였다. 그래핀의 구조적 결함 및 도핑은 라만 스펙트럼의 D, G, D', 2D밴드의 강도비와 G밴드의 위치와 반치폭(Full width at half maximum; FWHM)의 변화를 통해 확인하였다. 그 결과, 인가전력과 처리시간이 증가함에 따라 그래핀의 도핑레벨이 증가되고, 이후에는 도핑효과가 없어지고 결함의 정도가 상승하는 천이구역이 존재하며, 이를 넘어서는 너무 높은 인가적력의 처리는 그래핀에 결함을 형성하여 구조적인 붕괴를 야기함을 확인하였다.

• Applied Chemistry for Engineering
• /
• v.19 no.5
• /
• pp.512-518
• /
• 2008

The present work studied the selective catalytic reduction (SCR) of NO to $N_2$ by $NH_3$ over $V/TiO_2$ focusing on NOx control for the stationary sources. The SCR process depends mainly on the catalyst performance. The reaction characteristics of SCR with $V/TiO_2$ catalysts were closely examined at low and high temperature. In addition, adsorption and desorption characteristics of the reactants on the catalyst surface were investigated with ammonia. Seven different $TiO_2$ supports containing the same loading of vanadia were packed in a fixed bed reactor respectively. The interaction between $TiO_2$ and vanadia would form various non-stoichiometric vanadium oxides, and showed different reaction activities. There were optimum calcination temperatures for each samples, indicating different reactivity. It was finally found from the $NH_3-TPD$ test that the SCR activity was nothing to do with $NH_3$ adsorption amount.

• Korean Chemical Engineering Research
• /
• v.55 no.2
• /
• pp.156-162
• /
• 2017

CuO(x)/0.3Al-0.7Ce catalysts with different CuO loadings (x = 2~20 wt%) were prepared by impregnation method and investigated the effects of CuO loadings on the low temperature CO oxidation. Of the used catalysts, the CuO(10)/0.3Al-0.7Ce catalyst showed the highest catalytic performance in the absence or presence of water vapor. In the presence of water vapor, the catalytic performance was drastically decreased, with a temperature of 50% CO conversion ($T_{50%}$) shifted to higher temperature by $50^{\circ}C$ compared to the those in dry conditions because of the competitive adsorption of water vapor on the active sites. The copper metal surface area calculated from $N_2O$-titration analysis and the oxygen capacity from CO-pulse experiments were increased with the CuO loadings and showed a maximum at 10 wt%CuO/0.3Al-0.7Ce catalyst. These trends are in good agreement with the tendency of $T_{50%}$ of the catalysts. From these characteristic aspects, it could be deduced that the catalytic performance was closely related to the oxygen capacity and the copper metallic surface area.