• Journal of the Korean Recycled Construction Resources Institute
• /
• 제9권4호
• /
• pp.609-616
• /
• 2021

In this experimental, water-repellent powder, which is a metal salt-based inorganic substance, and natural zeolite powder, which is a pozzolan-based material, were mixed into cement mortar, and their physical properties and resistance to moisture were confirmed. It was confirmed that the test specimen using natural zeolite at the same time had excellent resistance in the water permeation test and the chloride penetration test as compared with the test specimen in which the inorganic metal salt-based water-repellent powder was mixed alone. When a metal salt-based water-repellent powder is used, it cannot be uniformly dispersed inside water due to its insoluble property, and is limited to the surface. When used at the same time as natural zeolite, the setting time at the initial stage of hydration is fast due to the pozzolan reaction, and the water-repellent powder adheres to the porous of the natural zeolite and is evenly distributed inside the test specimen to generate some water resistance.

• Journal of the Korea Institute of Building Construction
• /
• 제22권4호
• /
• pp.337-345
• /
• 2022

The foundation of high-rise concrete building in coastal areas generally must be installed in an integrated manner, not separately, in order to prevent defects caused by stress on the upper and lower parts of the mounting surface and to manage the process smoothly. However, when performing integrated punching, there is a concern that temperature stress cracks may occur due to hydration heat. Due to the large member size, it is difficult to make a sufficient commitment, so it is necessary to mix concrete with high self-charging properties to ensure workability. In this research, the amount of high-performance spray and admixture used was adjusted as experimental variables to satisfy this required performance. Through the analysis of the results for each blending variable, it was found that the unit quantity was 155kg/m³ and the cement ratio in the binder was 18%, and the target values of the pre-concrete properties and compressive strength were satisfied. A four-component binder(18% cement, 50% slag fine powder, 27% fly ash, 5% silica fume) was used.

• Journal of the Korea Concrete Institute
• /
• 제13권2호
• /
• pp.107-113
• /
• 2001

This study was conducted preliminarily to develop the crack source location technique for plain concrete beam using acoustic emission(AE). Before the main experiment, the test of virtual An source location was achieved in plain concrete block. The sensor layout was mutually compared between triangular layout and rectangular layout. As the results of test, AE source location by triangular layout was evaluated more effective than that by rectangular layout. The specimen to apply he source location technique was man in total nine specimens (each three in 40 %, 50%, 60% of W/C ratio) which the experiment variable was the compressive strength level(W/C ratio). The bending loading method is selected by cyclic loadings to evaluate the degree of concrete damage. It is seen that Kaiser effect and Felicity effect exists through analysis of AE parameters in coming failure experiment. As a result of analyzing the felicity ratio(FR) values, it is shown that this values can be used for evaluating the degree of concerto damage. AE activity is started highly at the 70% of failure load without the compressive strength level. Thus considered by a index in constructing the system of the failure warning at application of the field structure. And the results compared the real cracking location with the source location has perceived by AE monitoring before it is appeared the primary crack by visual observation.

• Journal of the Korean Recycled Construction Resources Institute
• /
• 제6권2호
• /
• pp.67-73
• /
• 2011

In this study, it was investigated compressive strength generation of concrete using high volume mineral admixture obtaining fundamental data for the application of concrete structure in construction field. For this, it was evaluated compressive strength with unit binder contents($310{\sim}410kg/m^3$), replacement ratio of mineral admixture(70~90%), unit water contents($140{\sim}150kg/m^3$) and curing temperature in the normal strength range. Also, after producing mock-up structure, hydration heat and compressive strength generation was evaluated to examine properties in the concrete member. In case of concrete using a large amount of industrial byproducts which was reviewed in this study, it is possible to secure compressive strength more than 24MPa at age 28days with about $13^{\circ}C$ ambient temperature of curing condition and that is considered to be applied to structure at construction site.

• Journal of the Korean Geotechnical Society
• /
• 제19권2호
• /
• pp.247-254
• /
• 2003

While the interests in the environmental problem during the construction are increasing, the use of low noise-vibration auger-drilled pilling is increasing to solve noise and vibration problem in pilling. Therefore, in Korea, SIP (Soil-Cement Injected Precast Pile) method is mainly used as auger-drilled pilling. However, there is no proper design criteria compatible with the ground condition of Korea, so which is most wanted. To improve and supplement this situation, direct shear tests for the friction between SIP pile skin interface and soil were executed on various conditions. Through the analysis of test results, skin friction characteristics of SIP were investigated thoroughly Also, hyperbolic model parameter fomulas which describe the friction behavior and the new non-linear unit skin friction capacity model with SM, SC soil were suggested.

• Journal of the Mineralogical Society of Korea
• /
• 제16권1호
• /
• pp.75-90
• /
• 2003

Ettringite and thaumasite were observed in some concrete. The morphology and occurrence of these minerals were closely examined by performing SEM/EDAX analyses. We also experimentally induced the concrete deterioration using $Na_2SO_4$ solution with application of various environmental conditions. The stability of these minerals and deterioration characteristics under applied experimental conditions were determined. Abundant ettringite formed by“through solution reaction”occurred in many open spaces, and some microscopic ettringite formed by "tophochemical replacement" of calcium aluminate also occurred in cement paste. Severe cracking of cement paste causing premature deterioration was often associated with ettringite location. Under specific condition, ettringite was transformed to thaumasite, tricthloroaluminate, or decomposed. Thaumasite occurred with association of ettrinsite in concrete containing carbonate aggregate being subject to dedolomitization or in some concrete being subject to carbonation. Thaumasite appears to be formed under the similar condition to the general ettringite forming condition, but it formed solid solution with ettringite by substituting pre-existing ettringite. Ettringite can also be transformed to trichloroaluminate in the presence of abundant chlorides, but trichloroaluminate changed back to ettringite in late sulfate attack. It is considered that the substitution reaction direction solely depend on the concentration of chloride and sulfate ion.

• Journal of the Korean Recycled Construction Resources Institute
• /
• 제4권2호
• /
• pp.143-148
• /
• 2016

The aim of research is inducing the optimum proportion of fly ash(FA) and blast furnace slag(BS) for ternary cement. In this research, hence, the fundamental properties of mortar mixtures were evaluated depending on various proportion of FA and BS. The results of the experiment, within the scope of the study, obtained the following conclusions. Flow of the mixtures was increased with addition of binary supplementary cementitious material(SCM), and especially, portion of FA. The air content of the mixtures was increased with addition of binary SCMs, while it was decreased with increased FA content. In the case of unit mass, increased value was obtained due to the increased air content within 25 to 45% of binary SCM content, while it was increased within 65 to 100% of binary SCM up to only 20% of FA content and decreased more than 20% of FA because of the low density of FA. The setting time of the mixtures was delayed with addition of binary SCM and FA. In the case of compressive strength, at 91-day age, the highest value was obtained with 25 and 45% of binary SCM with the proportion of FA to BS of 40 to 60. Therefore, based on the compressive strength, it is considered that the binary SCM content of 25 and 45% with the proportion of FA to BS of 2 : 3 is the most favorable conditions in this research scope.

• Journal of the Korean Recycled Construction Resources Institute
• /
• 제7권4호
• /
• pp.383-388
• /
• 2019

The present study evaluated experimentally the effects of the type and content of plastic fine aggregates on cement mortar in order to utilize waste platics as raw materials of concrete. The two kinds of plastics, LLDPE and HDPE were used, and the mixing rate of plastic fine aggregates was increased 0, 25, 50, 75, 100%. The mortar of LLDPE fine aggregate and HDPE fine aggregate showed similar tendency in flow and material separation resistance, density and water absorption, compressive strength and flexural strength by age. The flowability of mortar mixed with plastic fine aggregates was increased up to 50% but decreased at 75% or more. The material separation resistance of mortar with plastic fine aggregates was also dramatically decreased. On the other hand, due to the low density of plastics, the density of mortar decreased with the mixing of plastic fine aggregates. Due to the low adhesion between plastic fine aggregates and cement, the compressive strength by age was decreased in proportion to the mixing ratio of plastic aggregate, but the flexural strength of each age decreased with maintaining a certain level at 50% or more of plastic fine aggregate content.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• 제28권2A호
• /
• pp.297-304
• /
• 2008

It is well known that cracks in concrete decrease permeability and durability of concrete because cracks enhance the penetration of water or corrosive chemicals like as chlorides, carbon dioxides, sulfates and some others. But some of cracks in hardened cements may be sealed in case of contacting water. This phenomenon is called "self healing" and it has a close relation to hydration products newly formed on surfaces of cracks. Many studies on self healing in concretes commonly showed that CSH gel has been observed on crack surfaces. And some studies have reported that calcium hydroxides and ettringite were observed as well as CSH gel on crack surfaces. This study was carried out to investigate hydration products formed by self healing process and also examine the influence of waterproof admixture for concretes on self healing of cement. As a result of XRD, DSC, SEM and EDX analysis of crack surfaces, it was found that self healing of cement was related to CSH gel, calcium hydroxides and ettringite. And waterproof admixture increased fibrous (needle-like) hydration products which were in network form. It is estimated that such fibrous products are effective for self healing process of cement system.

• Magazine of the Korean Society of Agricultural Engineers
• /
• 제17권2호
• /
• pp.3778-3783
• /
• 1975

The objective of this study is to determine an appropriate cement of soil-cement in which silty soil of salty tidal flat with low plasticity was used. Physical, chemical and mechanical tests were conducted to find out the standard properties of the soil to be used. Various cement contents used in this test were 8%, 10%, 12%, and 14%, and the compressive strength was tested after 7 days and 28 days of standard curing in the above each cement content respectively. The results obtaind are summarized as follows. 1. As the cement content was increased from 8% to 14%, Maximum dry density (M.D.D.) and optimum moisture content (O.M.C.) were not changed remarkably. 2. Density of soil-cement was directly proportional to cement content and inversely proportional to water content. 3. OMC was generally decreased in proportion to the increase of cement content. 4. Compressive stranth was directly proportional to centent and inversely proportional to water content. 5. In freezing and thawing test, maximum loss of 10% in the total Weight was found on the 8% cement mixture. and This loss was rapidly decreased to 2% when the Cement content of the mixture was more than 10%.